CN106435808A - Manufacturing method of spun dyeing regenerated ATY fiber used outdoors - Google Patents
Manufacturing method of spun dyeing regenerated ATY fiber used outdoors Download PDFInfo
- Publication number
- CN106435808A CN106435808A CN201610790050.3A CN201610790050A CN106435808A CN 106435808 A CN106435808 A CN 106435808A CN 201610790050 A CN201610790050 A CN 201610790050A CN 106435808 A CN106435808 A CN 106435808A
- Authority
- CN
- China
- Prior art keywords
- pet
- fiber
- aty
- batch
- regeneration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of fiber manufacturing, and particularly relates to a manufacturing method of spun dyeing regenerated ATY fiber used outdoors. The manufacturing method comprises the steps of using PET regenerated colored POY fiber as a raw material or using two fibers of PET colored POY fiber and PET regenerated POY fiber as raw materials, and conducting air texturing and heat shaping on the raw materials to obtain the spun dyeing regenerated ATY fiber used outdoors. According to the manufacturing method of the spun dyeing regenerated ATY fiber used outdoors, PET regenerated sections are used as main processing materials, a spun dyeing spinning technology is adopted, three-waste pollutions such as waste water, waste gas and waste residue during the manufacturing method do not generate, and a follow-up product does not need to be dyed again. The spun dyeing regenerated ATY fiber used outdoors not only conducts reutilization on a renewable resource, but also effectively avoids continuous pollution problems of the environment, and is an environmentally friendly green fiber.
Description
Technical field
The present invention relates to fabric manufacturing area, particularly a kind of outdoor colours the production method of regeneration ATY fiber before spinning.
Background technology
Polyethylene terephthalate, is called for short polyester (PET), is that terephthalic acid (TPA) is poly-with the height that ethylene glycol polycondensation obtains
Thing, because of its good fibre forming property, physical and mechanical property and excellent taking, has obtained extremely quick in synthetic fibers field
Development.China's polyester consumption figure occupies first place in the world always, and the high speed development in outdoor in recent years field also gives chemical fibre new material
Application brings more opportunity.Although polyester will not produce to naturally virulent material after entering natural environment, but it has
Chemical inertness make it difficult to be fallen by air and microbial degradation.Polyester fiber synthesis material derives from oil, if we are right
Such substantial amounts of discarded object does not recycles, and not only can threaten environment (environmental pollution), is also to resource one
Plant significant wastage.Therefore, how high efficiente callback utilizes Polyester waste is long-standing technical problem, reclaims in prior art
The process utilizing Polyester waste spinning again to colour again is required to cause chronic pollution to environment so that recycles polyester and gives up
Gurry is restricted.
Content of the invention
The present invention, in order to overcome the deficiency of above-mentioned technical problem, provides and colours before a kind of environmentally friendly outdoor spins again
The production method of raw ATY fiber, can be fully solved above-mentioned technical problem.
The technical scheme solving above-mentioned technical problem is as follows：
A kind of outdoor colours the production method of regeneration ATY fiber before spinning, regenerate (polyethylene terephthalate with PET
Ester) a kind of fiber of coloured POY fiber is raw material or with the coloured POY fiber of PET (polyethylene terephthalate) and PET again
Raw (polyethylene terephthalate) coloured POY two kinds of fibers of fiber are raw material, obtain after air-texturing and thermal finalization
Coloring before outdoor spins regenerates ATY fiber, and described air-texturing pressure is 6.8～12kgf/cm2, the temperature of thermal finalization is
200～240 DEG C.
Further, the specification of described PET coloured POY fiber is 172～540dt/36～192f, and the coloured POY of PET is fine
The preparation method of dimension is：Being raw material by PET section and color master-batch, the addition of described color master-batch is PET coupon weight
2.0～8.0%, through pre-crystallized, dry, mixing, extrusion, filtration, spinning, cross air blasting cooling, oil and winding obtains；Its
In, color master-batch is inorganic, organic pigment, the PET/PBT master batch carrier of high light fastness, the mixing of LONGM2# antistatic additive
Thing；PBT can increase the effect of the pigment in master batch, dyestuff and PET section melt mixed.PET section is bright chip, partly disappears
Light section or full-dull polyester any one；Wherein, spinning temperature is 270～285 DEG C, and biphenyl temperature is 272～285 DEG C, cold
But using cross air blasting mode, blowing wind-warm syndrome is 18～30 DEG C, and cooling wind speed is 0.35～0.7m/s, winding speed is 2800～
3400m/min.
PET cuts into slices physical index：Relative viscosity 0.685 ± 0.02, fusing point 258 ± 2 DEG C, terminal hydroxyl content 30 ± 2mol/
T, form and aspect (b) 3.1, aggregated particle (＞ 10 μm)≤1.0/mg, moisture content is less than 600ppm.
Further, the specification of the described coloured POY fiber of PET regeneration is 172～540dt/36～192f, and PET regenerates
The preparation method of coloured POY fiber is：It is raw material by PET regenrated slice and color master-batch, the addition of described color master-batch
For the 2.0～8.0% of PET regenrated slice weight, through pre-crystallized, dry, mixing, extrusion, filtration, spinning, cross air blasting cooling,
Oil and winding obtains；Wherein, color master-batch be high light fastness inorganic, organic pigment, PET/PBT master batch carrier,
The mixture of LONGM2# antistatic additive；PBT can increase the effect of the pigment in master batch, dyestuff and PET section melt mixed.
PET regenrated slice be bright chip, semi-dulling chips or full-dull polyester any one；Wherein, spinning temperature is 263～280
DEG C, biphenyl temperature is 265～282 DEG C, and cooling uses cross air blasting mode, and blowing wind-warm syndrome is 20～30 DEG C, and cooling wind speed is 0.35
～0.7m/s, winding speed is 2500～3300m/min.PET regenrated slice physical index：Relative viscosity 0.680 ± 0.02, molten
Point 256 ± 2 DEG C, terminal hydroxyl content 30 ± 2mol/t, form and aspect (b) 3.3, aggregated particle (＞ 10 μm)≤1.0/mg, aqueous
Rate is less than 600ppm.
Wherein, PET regenrated slice of the present invention both can be commercially available prod and can be recycled PET section discarded object
Product after processing through regeneration.
The invention has the beneficial effects as follows：
The outdoor that the present invention produces spin before coloring regeneration ATY fiber with PET regenrated slice for mainly processing raw material, employing
Spinning front coloring spinning technique, production process is without three-waste pollutions such as waste water,wastes gas and industrial residue, and subsequent product is without again dyeing.Due to
Employing PET regenrated slice is mainly to process raw material, and the still once recycling to regenerated resources, not effectively prevent ring yet
The chronic pollution problem in border, is a kind of environmental protection fiber very friendly to environment.
The outdoor that the present invention produces colours regeneration ATY fiber weaving fabric style before spinning is special, owing to using air
Yarn is processed by mode of texturing, and the looped pile of yarn extexine has the style of similar short fibre, with fiber weaving of the present invention
Fabric feel is substantially better than the fabric using other modes of texturing processing fiber weaving, and feel is close to acrylic (acrylic staples) face
Material, greatly improves the application in terylene woven fabric textile field out of doors, and product processing technique is simple, it is low to consume energy.
Coloring before the outdoor that the present invention produces spins regenerates ATY fiber, is particularly well-suited to make outdoor decoration fabric etc. and wants
Seeking the textile fabric compared with high durable color fastness, fiber of the present invention uses high light fastness color master-batch and PET regenrated slice
Co-blended spinning, has higher weather resistance, and end product is applied to outdoor boudoir, back cushion, outdoor sun shade, external wall dress
The high-end outdoor products such as decorations cloth.
Brief description
The present invention is further detailed explanation with detailed description of the invention below in conjunction with the accompanying drawings.
Fig. 1 is the schematic diagram of the production method of embodiment 1；
In figure：1 is first roller, and 2 is the second roller, and 3 is the 3rd roller, and 4 is the 4th roller, and 5 is fast sale, and 6 is air
Deformation case, roller based on 7,8 is heat-setting box, and 9 is oil tanker, 10 products obtaining for winding.
Detailed description of the invention
Embodiment 1：
As it is shown in figure 1, a kind of outdoor colours the production method of regeneration ATY fiber before spinning, concretely comprise the following steps：Have with PET
Look POY fiber and the coloured POY fiber of PET regeneration are raw material, wherein, with PET coloured POY fiber for space-variant skin silk, with PET regeneration
Coloured POY fiber is space-variant core filaments, and the mass percent of Pi Si and core filaments is 1:3～3:1, use first roller 1 and second sieve
2 are drawn to enter silk, and through fast-selling 5 hot-stretch, then after the 3rd roller 3 and the stretching of the 4th roller 4, core filaments is respectively through first roller 1 He
3rd roller 3, skin silk, respectively through the second roller 2 and the 4th roller 4, enters air-texturing in space-variant case 6, described air-texturing
Pressure is 6.8kgf/cm2, wherein, humidifying water nozzle and air texturing nozzle are set in air texturing box and carry out squirting process to fiber, so
Rear wire vent carries out thermal finalization process in guiding heat-setting box 8 through main roller 7, and the temperature of thermal finalization is 200 DEG C, finally by oil tanker 9
It is wound into product 10 after oiling.
Wherein, the specification of PET coloured POY fiber is 172～540dt/36～192f.
The preparation method of PET coloured POY fiber is：It is raw material by PET section and color master-batch, described color master-batch
Addition is the 2.0～8.0% of PET coupon weight, through pre-crystallized, dry, mixing, extrusion, filtration, spinning, side-blown air-cooled
But, oil and winding obtains；Wherein, color master-batch be high light fastness inorganic, organic pigment, PET/PBT master batch carrier,
The mixture of LONGM2# antistatic additive；PET section is bright chip, semi-dulling chips or full-dull polyester any one；Its
In, spinning temperature is 270～285 DEG C, and biphenyl temperature is 272～285 DEG C, and cooling uses cross air blasting mode, and blowing wind-warm syndrome is 18
～30 DEG C, cooling wind speed is 0.35～0.7m/s, and winding speed is 2800～3400m/min.
The specification of the coloured POY fiber of PET regeneration is 172～540dt/36～192f, the system of the coloured POY fiber of PET regeneration
Preparation Method is：Being raw material by PET regenrated slice and color master-batch, the addition of described color master-batch is PET regenrated slice weight
The 2.0～8.0% of amount, cool down through pre-crystallized, drys, mixing, extrusion, filtration, spinning, cross air blasting, oil and winding obtains；
Wherein, color master-batch is the mixed of inorganic, organic pigment, PET/PBT master batch carrier, the LONGM2# antistatic additive of high light fastness
Compound；PET regenrated slice be bright chip, semi-dulling chips or full-dull polyester any one；Wherein, spinning temperature is 263
～280 DEG C, biphenyl temperature is 265～282 DEG C, and cooling uses cross air blasting mode, and blowing wind-warm syndrome is 20～30 DEG C, and cooling wind speed is
0.35～0.7m/s, winding speed is 2500～3300m/min.
Before this outdoor spins, coloring regeneration ATY elastomer final color regenerates with PET coloured POY fiber color and PET
On the basis of coloured POY fiber color.
Wherein, before outdoor spins, coloring regeneration ATY elastomer specification is 360～1000dt/72～384f.Wherein, main
Roller process velocity 250～600m/min, fast-selling temperature 98～150 DEG C, core filaments overfeeding 8～28%, skin silk overfeeding 16～48%,
Sizing uses the sizing of closed hot tank.
Embodiment 2：
A kind of outdoor colours the production method of regeneration ATY fiber before spinning, concretely comprise the following steps：With PET coloured POY fiber and
The coloured POY fiber of PET regeneration is raw material, wherein, with the coloured POY fiber of PET regeneration for space-variant skin silk, with PET coloured POY fiber
For space-variant core filaments, the mass percent of Pi Si and core filaments is 1:3～3:1, use first roller 1 and the second roller 2 to enter silk, and warp
Fast-selling 5 hot-stretch, then after the 3rd roller 3 and the stretching of the 4th roller 4, core filaments is respectively through first roller 1 and the 3rd roller 3, skin
Silk, respectively through the second roller 2 and the 4th roller 4, enters air-texturing in space-variant case 6, and described air-texturing pressure is 12kgf/
cm2, wherein, humidifying water nozzle and air texturing nozzle are set in air texturing box and carry out squirting process to fiber, then wire vent is through main sieve
Carrying out thermal finalization process in drawing 7 guiding heat-setting box 8, the temperature of thermal finalization is 240 DEG C, rolls up after finally being oiled by oil tanker 9
It is coiled into product 10.
Wherein, the specification of PET coloured POY fiber is 172～540dt/36～192f.
The preparation method of PET coloured POY fiber is：It is raw material by PET section and color master-batch, described color master-batch
Addition is the 2.0～8.0% of PET coupon weight, through pre-crystallized, dry, mixing, extrusion, filtration, spinning, side-blown air-cooled
But, oil and winding obtains；Wherein, color master-batch be high light fastness inorganic, organic pigment, PET/PBT master batch carrier,
The mixture of LONGM2# antistatic additive；PET section is bright chip, semi-dulling chips or full-dull polyester any one；Its
In, spinning temperature is 270～285 DEG C, and biphenyl temperature is 272～285 DEG C, and cooling uses cross air blasting mode, and blowing wind-warm syndrome is 18
～30 DEG C, cooling wind speed is 0.35～0.7m/s, and winding speed is 2800～3400m/min.
The specification of the coloured POY fiber of PET regeneration is 172～540dt/36～192f, the system of the coloured POY fiber of PET regeneration
Preparation Method is：Being raw material by PET regenrated slice and color master-batch, the addition of described color master-batch is PET regenrated slice weight
The 2.0～8.0% of amount, cool down through pre-crystallized, drys, mixing, extrusion, filtration, spinning, cross air blasting, oil and winding obtains；
Wherein, color master-batch is the mixed of inorganic, organic pigment, PET/PBT master batch carrier, the LONGM2# antistatic additive of high light fastness
Compound；PET regenrated slice be bright chip, semi-dulling chips or full-dull polyester any one；Wherein, spinning temperature is 263
～280 DEG C, biphenyl temperature is 265～282 DEG C, and cooling uses cross air blasting mode, and blowing wind-warm syndrome is 20～30 DEG C, and cooling wind speed is
0.35～0.7m/s, winding speed is 2500～3300m/min.
Before this outdoor spins, coloring regeneration ATY elastomer final color regenerates with PET coloured POY fiber color and PET
On the basis of coloured POY fiber color.
Wherein, before outdoor spins, coloring regeneration ATY elastomer specification is 360～1000dt/72～384f.Wherein, main
Roller process velocity 250～600m/min, fast-selling temperature 98～150 DEG C, core filaments overfeeding 8～28%, skin silk overfeeding 16～48%,
Sizing uses the sizing of closed hot tank.
Embodiment 3：
A kind of outdoor colours the production method of regeneration ATY fiber before spinning, concretely comprise the following steps：Fine with the coloured POY of PET regeneration
Dimension is raw material, wherein, with the coloured POY fiber of PET regeneration for space-variant skin silk, with the coloured POY fiber of PET regeneration for space-variant core filaments,
The mass percent of skin silk and core filaments is 1:3～3:1, use first roller 1 and the second roller 2 to enter silk, and through fast-selling 5 hot-drawns
Stretching, then after stretching through the 3rd roller 3 and the 4th roller 4, core filaments is respectively through first roller 1 and the 3rd roller 3, and skin silk is respectively through the
Two rollers 2 and the 4th roller 4, enter air-texturing in space-variant case 6, and described air-texturing pressure is 9kgf/cm2, wherein, empty
Arranging humidifying water nozzle and air texturing nozzle in gas deformation case to carry out squirting process to fiber, then wire vent guides heat calmly through main roller 7
Carrying out thermal finalization process in molding box 8, the temperature of thermal finalization is 220 DEG C, is wound into product 10 by oil tanker 9 after finally being oiled.
Wherein, the specification of the coloured POY fiber of PET regeneration is 172～540dt/36～192f, the coloured POY fiber of PET regeneration
Preparation method be：Being raw material by PET regenrated slice and color master-batch, the addition of described color master-batch is that PET regeneration is cut
The 2.0～8.0% of piece weight, through pre-crystallized, dry, mixing, extrusion, filtration, spinning, cross air blasting cooling, oil and wind
Obtain；Wherein, color master-batch is inorganic, organic pigment, PET/PBT master batch carrier, the LONGM2# antistatic additive of high light fastness
Mixture；PET regenrated slice be bright chip, semi-dulling chips or full-dull polyester any one；Wherein, spinning temperature is
263～280 DEG C, biphenyl temperature is 265～282 DEG C, and cooling uses cross air blasting mode, and blowing wind-warm syndrome is 20～30 DEG C, cools down wind
Speed is 0.35～0.7m/s, and winding speed is 2500～3300m/min.
Before this outdoor spins, coloring regeneration ATY elastomer final color regenerates coloured POY fiber color as base with PET
Accurate.
Wherein, before outdoor spins, coloring regeneration ATY elastomer specification is 360～1000dt/72～384f.Wherein, main
Roller process velocity 250～600m/min, fast-selling temperature 98～150 DEG C, core filaments overfeeding 8～28%, skin silk overfeeding 16～48%,
Sizing uses the sizing of closed hot tank.
The above, be only presently preferred embodiments of the present invention, not does any pro forma restriction to the present invention, every depends on
According to any simple modification in the technical spirit of the present invention made above example, equivalent variations, each fall within the guarantor of the present invention
Within the scope of protecting.
Claims (3)
1. the production method of coloring regeneration ATY fiber before an outdoor spins, it is characterised in that regenerate (poly-terephthaldehyde with PET
Acid glycol ester) coloured POY fiber is raw material or with the coloured POY fiber of PET (polyethylene terephthalate) and PET again
Raw (polyethylene terephthalate) coloured POY two kinds of fibers of fiber are raw material, obtain after air-texturing and thermal finalization
Coloring before outdoor spins regenerates ATY fiber, and described air-texturing pressure is 6.8～12kgf/cm2, the temperature of thermal finalization is
200～240 DEG C.
2. the production method of coloring regeneration ATY fiber before outdoor according to claim 1 spins, it is characterised in that described
The specification of PET coloured POY fiber be 172～540dt/36～192f, the preparation method of PET coloured POY fiber is：By PET
Section and color master-batch are raw material, and the addition of described color master-batch is the 2.0～8.0% of PET coupon weight, through pre-knot
Crystalline substance, drying, mixing, extrusion, filtration, spinning, cross air blasting cooling, oil and winding obtains；Wherein, color master-batch is high Exposure to Sunlight jail
Inorganic, organic pigment, PET/PBT master batch carrier, the mixture of LONGM2# antistatic additive of degree；PET section for bright chip,
Semi-dulling chips or full-dull polyester any one；Wherein, spinning temperature is 270～285 DEG C, and biphenyl temperature is 272～285
DEG C, cooling uses cross air blasting mode, and blowing wind-warm syndrome is 18～30 DEG C, and cooling wind speed is 0.35～0.7m/s, and winding speed is
2800～3400m/min.
3. the production method of coloring regeneration ATY fiber before outdoor according to claim 1 spins, it is characterised in that described
The specification of the PET coloured POY fiber of regeneration be 172～540dt/36～192f, the preparation method of the coloured POY fiber of PET regeneration
It is：Being raw material by PET regenrated slice and color master-batch, the addition of described color master-batch is the 2.0 of PET regenrated slice weight
～8.0%, through pre-crystallized, dry, mixing, extrusion, filtration, spinning, cross air blasting cooling, oil and winding obtains；Wherein,
Masterbatch is inorganic, organic pigment, PET/PBT master batch carrier, the mixture of LONGM2# antistatic additive of high light fastness；PET
Regenrated slice be bright chip, semi-dulling chips or full-dull polyester any one；Wherein, spinning temperature is 263～280 DEG C,
Biphenyl temperature is 265～282 DEG C, and cooling uses cross air blasting mode, and blowing wind-warm syndrome is 20～30 DEG C, cooling wind speed is 0.35～
0.7m/s, winding speed is 2500～3300m/min.