CN106435330A - High-wear-resistance fence metal material - Google Patents
High-wear-resistance fence metal material Download PDFInfo
- Publication number
- CN106435330A CN106435330A CN201610904236.7A CN201610904236A CN106435330A CN 106435330 A CN106435330 A CN 106435330A CN 201610904236 A CN201610904236 A CN 201610904236A CN 106435330 A CN106435330 A CN 106435330A
- Authority
- CN
- China
- Prior art keywords
- powder
- parts
- metal material
- silver
- silicon nitride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-wear-resistance fence metal material. The high-wear-resistance fence metal material comprises copper powder, iron powder, sulfur powder, phosphorus powder, silver-nickel-zinc powder, aluminum oxide, silicon nitride, manganese powder, molybdenum disulfide powder, graphite powder and ball-milled chromium powder; the high-wear-resistance fence metal material comprises the following components including, by mass percent, 1.5 to 6.0 parts of copper powder, 2 to 5 parts of iron powder, 1 to 6 parts of sulfur powder, 2 to 5 parts of phosphorus powder, 1 to 4 parts of silver-nickel-zinc powder, 3 to 5 parts of aluminum oxide, 1 to 6 parts of silicon nitride, 1 to 3 parts of manganese powder, 0.5 to 2.0 parts of molybdenum disulfide powder, 5 to 10 parts of graphite powder and 1 to 5 parts of ball-milled chromium powder. Through the way, the high-wear-resistance fence metal material disclosed by the invention is capable of improving the mechanical properties and practicability of the metal material, so that the metal material is compact in texture, high in quality, excellent in friction performance, relatively low in friction coefficient, small in abrasion, convenient to produce and easy to popularize.
Description
Technical field
The present invention relates to a kind of metal material, more particularly to high abrasion fence metal material.
Background technology
With life and the modernization producing, during metal material is widely used in all kinds of lives and produces, conventional gold
Belonging to material also has a lot, also occurs in that various functions in formula, to ensure that metal material has better performance, but
In implementation process, due to the imperfection of formula, the metal material function of being produced is bad, and therefore my company develops more
Have more can effect metal material formula.
Content of the invention
The invention mainly solves the technical problem of how to provide a kind of mechanical performance that can improve metal material and reality
With property so that metal material quality is tight, quality is high, has excellent frictional behaviour, coefficient of friction is relatively low, and abrasion is little,
Convenient for production it is easy to promote metal material formula.
For solving above-mentioned technical problem, one aspect of the present invention is:A kind of high abrasion fence metal is provided
Material, including:Copper powder, iron powder, sulphur powder, phosphorus powder, silver-colored nickel zinc powder, aluminum oxide, silicon nitride, manganese powder, molybdenum disulphide powder, graphite powder,
Ball milling chromium powder, described high abrasion fence metal material calculates according to mass percent, including following weight portion:Copper powder 1.5-
6.0 parts, iron powder 2-5 part, sulphur powder 1-6 part, phosphorus powder 2-5 part, silver-colored nickel zinc powder 1-4 part, aluminum oxide 3-5 part, silicon nitride 1-6 part, manganese
Powder 1-3 part, molybdenum disulphide powder 0.5-2.0 part, graphite powder 5-10 part, ball milling chromium powder 1-5 part.
In a preferred embodiment, described high abrasion fence metal material calculates according to mass percent, including with
Lower weight portion:2 parts of copper powder, 3 parts of iron powder, 2 parts of sulphur powder, 3 parts of phosphorus powder, silver-colored 2 parts of nickel zinc powder, 4 parts of aluminum oxide, 2 parts of silicon nitride, manganese powder
2 parts, 1.0 parts of molybdenum disulphide powder, 6 parts of graphite powder, 2 parts of ball milling chromium powder.
In a preferred embodiment, described high abrasion fence metal material calculates according to mass percent, including with
Lower weight portion:5.0 parts of copper powder, 4 parts of iron powder, 5 parts of sulphur powder, 4 parts of phosphorus powder, silver-colored 3 parts of nickel zinc powder, 4.5 parts of aluminum oxide, 4 parts of silicon nitride,
2 parts of manganese powder, 1.5 parts of molybdenum disulphide powder, 7 parts of graphite powder, 4 parts of ball milling chromium powder.
The invention has the beneficial effects as follows:The mechanical performance of metal material and practicality can be improved so that metal material matter
Closely, quality is high, has excellent frictional behaviour, coefficient of friction is relatively low on ground, and abrasion is little, convenient for production it is easy to promote.
Specific embodiment
The enforcement it is clear that described will be clearly and completely described to the technical scheme in the embodiment of the present invention below
Example is only a part of embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, this area is common
All other embodiment that technical staff is obtained under the premise of not making creative work, broadly falls into the model of present invention protection
Enclose.
There is provided a kind of high abrasion fence metal material in one particular embodiment of the present invention, described high abrasion fence
Metal material includes:Copper powder, iron powder, sulphur powder, phosphorus powder, silver-colored nickel zinc powder, aluminum oxide, silicon nitride, manganese powder, molybdenum disulphide powder, graphite
Powder, ball milling chromium powder, described high abrasion fence metal material calculates according to mass percent, including following weight portion:Copper powder
1.5-6.0 part, iron powder 2-5 part, sulphur powder 1-6 part, phosphorus powder 2-5 part, silver-colored nickel zinc powder 1-4 part, aluminum oxide 3-5 part, silicon nitride 1-6
Part, manganese powder 1-3 part, molybdenum disulphide powder 0.5-2.0 part, graphite powder 5-10 part, ball milling chromium powder 1-5 part.
Embodiment 1:Described high abrasion fence metal material calculates according to mass percent, including following weight portion:Copper
2 parts of powder, 3 parts of iron powder, 2 parts of sulphur powder, 3 parts of phosphorus powder, silver-colored 2 parts of nickel zinc powder, 4 parts of aluminum oxide, 2 parts of silicon nitride, 2 parts of manganese powder, curing
1.0 parts of molybdenum powder, 6 parts of graphite powder, 2 parts of ball milling chromium powder.
Embodiment 2:Described high abrasion fence metal material calculates according to mass percent, including following weight portion:Copper
5.0 parts of powder, 4 parts of iron powder, 5 parts of sulphur powder, 4 parts of phosphorus powder, silver-colored 3 parts of nickel zinc powder, 4.5 parts of aluminum oxide, 4 parts of silicon nitride, 2 parts of manganese powder, two
1.5 parts of molybdenum powder of sulfuration, 7 parts of graphite powder, 4 parts of ball milling chromium powder.
Therefore, the present invention has advantages below:The mechanical performance of metal material and practicality can be improved so that metal material
Closely, quality is high, has excellent frictional behaviour, coefficient of friction is relatively low for material quality, and abrasion is little, convenient for production it is easy to push away
Extensively.
The foregoing is only embodiments of the invention, not thereby limit the present invention the scope of the claims, every using this
Equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in the technology neck of other correlations
Domain, is included within the scope of the present invention.
Claims (3)
1. a kind of high abrasion fence metal material is it is characterised in that include:Copper powder, iron powder, sulphur powder, phosphorus powder, silver-colored nickel zinc powder, oxygen
Change aluminium, silicon nitride, manganese powder, molybdenum disulphide powder, graphite powder, ball milling chromium powder, described high abrasion fence metal material is according to quality
Percentage calculates, including following weight portion:Copper powder 1.5-6.0 part, iron powder 2-5 part, sulphur powder 1-6 part, phosphorus powder 2-5 part, silver-colored nickel zinc
Powder 1-4 part, aluminum oxide 3-5 part, silicon nitride 1-6 part, manganese powder 1-3 part, molybdenum disulphide powder 0.5-2.0 part, graphite powder 5-10 part, ball
Mill chromium powder 1-5 part.
2. high abrasion fence metal material according to claim 1 is it is characterised in that described high abrasion fence metal material
Material calculates according to mass percent, including following weight portion:2 parts of copper powder, 3 parts of iron powder, 2 parts of sulphur powder, 3 parts of phosphorus powder, silver-colored nickel zinc powder 2
Part, 4 parts of aluminum oxide, 2 parts of silicon nitride, 2 parts of manganese powder, 1.0 parts of molybdenum disulphide powder, 6 parts of graphite powder, 2 parts of ball milling chromium powder.
3. high abrasion fence metal material according to claim 1 is it is characterised in that described high abrasion fence metal material
Material calculates according to mass percent, including following weight portion:5.0 parts of copper powder, 4 parts of iron powder, 5 parts of sulphur powder, 4 parts of phosphorus powder, silver-colored nickel zinc
3 parts of powder, 4.5 parts of aluminum oxide, 4 parts of silicon nitride, 2 parts of manganese powder, 1.5 parts of molybdenum disulphide powder, 7 parts of graphite powder, 4 parts of ball milling chromium powder.