CN104745977A - High temperature heat-resisting die steel - Google Patents
High temperature heat-resisting die steel Download PDFInfo
- Publication number
- CN104745977A CN104745977A CN201310734395.3A CN201310734395A CN104745977A CN 104745977 A CN104745977 A CN 104745977A CN 201310734395 A CN201310734395 A CN 201310734395A CN 104745977 A CN104745977 A CN 104745977A
- Authority
- CN
- China
- Prior art keywords
- die steel
- temperature heat
- high temperature
- resisting die
- glass fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses high temperature heat-resisting die steel which comprises the following ingredients by weight, 0.3-0.35% of carbon, 0.02-0.2% of silicon, 0.25-0.3% of aluminium, 0.09-0.12% of glass fibre, 0.5-1.2% of bamboo charcoal, 0.3-0.5% of manganese, 0.01-0.03% of platinum and the balance iron. The high temperature heat-resisting die steel has beneficial effects of scientific and reasonable ingredients, stable performance, long service life, good toughness, high strength and strong high temperature resistance.
Description
Technical field
The present invention relates to a kind of high-temperature heat-resistance die steel.
Background technology
At present, die steel material realizes one of the modern basis of production and core technology, and its developmental level is the leading indicator of the national production level height of measurement one.Hot-work die steel generally operates under suitable complex work condition, and the performance requriements for die steel material is also quite strict.And the hot-work die steel of domestic production, the tropism such as grade of steel is lower, and homogeneity of structure is poor, and the mould synthetic performance examination produced is lower, seriously limits work-ing life.
Therefore, for solving the problem, spy provides a kind of new technical scheme to satisfy the demands.
Summary of the invention
The invention provides a kind of high-temperature heat-resistance die steel.
The technical solution used in the present invention is:
A kind of high-temperature heat-resistance die steel, comprises the component composition of following weight percent:
Carbon 0.3-0.35%;
Silicon 0.02-0.2%;
Aluminium 0.25-0.3%;
Glass fibre 0.09-0.12%;
Bamboo charcoal 0.5-1.2%;
Manganese 0.3-0.5%;
Platinum 0.01-0.03%;
Surplus is iron.
The antimony that weight percent is 0.16-1.3% can also be added.
The invention has the beneficial effects as follows: this kind of high-temperature heat-resistance die steel component is scientific and reasonable, stable performance, long service life, and good toughness, intensity is high, and high-temperature resistant result is strong.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment only for explaining the present invention, does not form limiting the scope of the present invention.
Embodiment 1
A kind of high-temperature heat-resistance die steel, comprises the component composition of following weight percent:
Carbon 0.3%;
Silicon 0.02%;
Aluminium 0.25%;
Glass fibre 0.09%;
Bamboo charcoal 0.5%;
Manganese 0.3%;
Platinum 0.01%;
Antimony 0.16%;
Surplus is iron.
Embodiment 2
A kind of high-temperature heat-resistance die steel, comprises the component composition of following weight percent:
Carbon 0.32%;
Silicon 0.15%;
Aluminium 0.27%;
Glass fibre 0.1%;
Bamboo charcoal 0.8%;
Manganese 0.4%;
Platinum 0.02%;
Surplus is iron.
Embodiment 3
A kind of high-temperature heat-resistance die steel, comprises the component composition of following weight percent:
Carbon 0.35%;
Silicon 0.2%;
Aluminium 0.3%;
Glass fibre 0.12%;
Bamboo charcoal 1.2%;
Manganese 0.5%;
Platinum 0.03%;
Glass fibre 1.3%;
Surplus is iron.
The invention has the beneficial effects as follows: this kind of high-temperature heat-resistance die steel component is scientific and reasonable, stable performance, long service life, and good toughness, intensity is high, and high-temperature resistant result is strong.
The above is only preferred embodiment of the present invention, is not restriction the present invention being made to any other form, and any amendment done according to technical spirit of the present invention or equivalent variations, still belong to the present invention's scope required for protection.
Claims (2)
1. a high-temperature heat-resistance die steel, is characterized in that: the component composition comprising following weight percent:
Carbon 0.3-0.35%;
Silicon 0.02-0.2%;
Aluminium 0.25-0.3%;
Glass fibre 0.09-0.12%;
Bamboo charcoal 0.5-1.2%;
Manganese 0.3-0.5%;
Platinum 0.01-0.03%;
Surplus is iron.
2. a kind of high-temperature heat-resistance die steel according to claim 1, is characterized in that: can also add the antimony that weight percent is 0.16-1.3%.