CN106433353A - Water-based half-open clear primer - Google Patents
Water-based half-open clear primer Download PDFInfo
- Publication number
- CN106433353A CN106433353A CN201610962578.4A CN201610962578A CN106433353A CN 106433353 A CN106433353 A CN 106433353A CN 201610962578 A CN201610962578 A CN 201610962578A CN 106433353 A CN106433353 A CN 106433353A
- Authority
- CN
- China
- Prior art keywords
- aqueouss
- priming paint
- open model
- semi open
- clear priming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
An embodiment of the invention discloses water-based half-open clear primer. The water-based half-open clear primer can be prepared from, in parts by weight, 65-80 parts of an acrylic emulsion, 0.4-0.6 parts of an antifoaming agent, 0.5-1 part of a dispersant, 0.1-0.2 parts of a bactericide, 0.1-0.2 parts of a pH regulator, 4-7 parts of a coalescing agent, 1-3 parts of a polishing aid, 0.4-0.7 parts of a wetting agent, 0.5-1 part of a thickener and 7-27 parts of deionized water. The clear primer has the characteristics of good pore entering performance, good wetting performance for substrates, good half-open effect, good transparency, good polishing performance and the like, and wood grains on thin, small and long wood are natural and clear and have better appearances.
Description
Technical field
The present invention relates to chemical technology field, the more particularly to a kind of clear priming paint of aqueouss semi open model.
Background technology
With rapid development of economy, and progressively enhancing of the people to environmental consciousness, the demand of environment-friendlywater-based water-based paint
Improve constantly, be especially gradually improved in current water paint performance, and most of coating base materials are imitated to the application of water paint
In the case of fruit requires that comparison is high and diversified again.
In general, the surface of the base material such as indoor all kinds of timber, articles made of bamboo, rattan articles, door and window floor, furniture is all to need to carry out
Application, to obtain different applications, and obtains preferable outward appearance.But water paint layer conventional at present is opened due to its water surface
Power is big and to enter permeability effect poor, and semi-open property effect is less than oil paint, so as to be difficult to clearly keep wood substrate original
Natural grain, and then be difficult to make wood substrate to obtain preferable natural look.
Content of the invention
Embodiments provide a kind of clear priming paint of aqueouss semi open model, the clear priming paint have good into permeability, to ground
Wettability is good, and semi-open effect is good, excellent transparency, the features such as grinability is good, it is possible to so that on the timber of the tiny length of conduit
Wood grain is naturally clear, with preferable outward appearance.
In view of this, first aspect present invention provides a kind of aqueouss semi open model clear priming paint, counts by weight, can wrap
Include：
In conjunction with the embodiment of the present invention in a first aspect, the first embodiment of first aspect in the embodiment of the present invention
In, acrylic emulsion is modified acrylic acid emulsion.
In conjunction with the embodiment of the present invention in a first aspect, or the embodiment of the present invention first aspect the first embodiment,
In second embodiment of the first aspect of the embodiment of the present invention, defoamer is that brokenly bubble polymer and/or polysiloxanes are molten
Liquid.
In conjunction with the embodiment of the present invention in a first aspect, the embodiment of the present invention first aspect the first embodiment or
Two kinds of embodiments, in the third embodiment of the first aspect of the embodiment of the present invention, dispersant be containing pigment group
High molecular weight block copolymer.
In conjunction with the embodiment of the present invention in a first aspect, the embodiment of the present invention first aspect the first embodiment to
Any one in three kinds of embodiments, in the 4th kind of embodiment of the first aspect of the embodiment of the present invention, antibacterial is
Chlormethylisothiazo,ine ketone.
In conjunction with the embodiment of the present invention in a first aspect, the embodiment of the present invention first aspect the first embodiment to
Any one in four kinds of embodiments, in the 5th kind of embodiment of the first aspect of the embodiment of the present invention, pH adjusting agent
For 2-amino-2-methyl-1-propanol.
In conjunction with the embodiment of the present invention in a first aspect, the embodiment of the present invention first aspect the first embodiment to
Any one in five kinds of embodiments, in the 6th kind of embodiment of the first aspect of the embodiment of the present invention, coalescents
For dipropylene glycol methyl ether DPM and dipropylene DPNB.
In conjunction with the embodiment of the present invention in a first aspect, the embodiment of the present invention first aspect the first embodiment to
Any one in six kinds of embodiments, in the 7th kind of embodiment of the first aspect of the embodiment of the present invention, grinding auxiliary agent
For zinc powder.
In conjunction with the embodiment of the present invention in a first aspect, the embodiment of the present invention first aspect the first embodiment to
Any one in seven kinds of embodiments, in the 8th kind of embodiment of the first aspect of the embodiment of the present invention, wetting agent is
Organic silicon surfactant.
In conjunction with the embodiment of the present invention in a first aspect, the embodiment of the present invention first aspect the first embodiment to
Any one in eight kinds of embodiments, in the 9th kind of embodiment of the first aspect of the embodiment of the present invention, thickening agent is
Polyurethane type thickening agent and the swollen type thickeners of alkali soluble.
As can be seen from the above technical solutions, the embodiment of the present invention has advantages below：
Present embodiments provide a kind of clear priming paint of aqueouss semi open model, the clear priming paint can by acrylic emulsion, defoamer,
Dispersant, antibacterial, pH adjusting agent, coalescents, grinding auxiliary agent, wetting agent, thickening agent, deionized water are according to suitable weight
Portion rate allotment is formed, and is shown through result of the test, the clear priming paint extremely difficult enter hole base material on have preferably and enter permeability, it is possible to
So that wood grain on the timber of the tiny length of conduit is naturally clear, with preferable outward appearance, and compared with traditional paint, which is not only
Open effect is suitable, with preferable painting effect on base material, and can have more the scentless advantage of environmental protection.
Specific embodiment
Embodiments provide a kind of clear priming paint of aqueouss semi open model, the clear priming paint have good into permeability, to ground
Wettability is good, and semi-open effect is good, excellent transparency, the features such as grinability is good, it is possible to so that on the timber of the tiny length of conduit
Wood grain is naturally clear, with preferable outward appearance.
In order that those skilled in the art more fully understand the present invention program, below to the technology in the embodiment of the present invention
Scheme is clearly and completely described, it is clear that described embodiment is only the embodiment of a present invention part, rather than
Whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art are not making creative work premise
Lower obtained every other embodiment, should all belong to the scope of protection of the invention.
The invention provides a kind of clear priming paint of aqueouss semi open model, in terms of parts by weight, can include：
The clear priming paint of aqueouss semi open model that the present invention is provided can include acrylic emulsion, defoamer, dispersant, sterilization
Agent, pH adjusting agent, coalescents, grinding auxiliary agent, wetting agent, thickening agent and deionized water.The clear priming paint of aqueouss semi open model can
With without curing agent component is added, only application, simple and convenient, strong applicability need to be carried out by using front stirring.
In the present invention, acrylic emulsion is the key component of the clear priming paint of aqueouss semi open model, half-open for providing aqueouss
Put the Fundamental Physical Properties of the clear priming paint of formula and various tolerations, and with good permeability, enter permeability the features such as, preferably
, in one embodiment that the present invention is provided, acrylic emulsion can be modified acrylic acid emulsion, specifically, the modification third
Olefin(e) acid emulsion requires that particle diameter is little, transparent height, and chemical resistance is more excellent.
In the present invention, the effect of defoamer is to remove the gas that the clear priming paint of aqueouss semi open model is produced in process of production
Bubble, and the clear priming paint of aqueouss semi open model bubble for producing in construction can be suppressed, it is preferred that for providing in the present invention
In embodiment, defoamer can be brokenly bubble polymer and/or polysiloxane solution.In actual applications, brokenly bubble polymer and poly-
The collocation of both siloxane solutions can make coating froth breaking faster, and construction is less also easy to produce steam bubble, but brokenly bubble should be polymerized before allotment
Thing and polysiloxanes dissolve into row to be disperseed at a high speed, otherwise can produce, because water-based system is not single-phase, phenomenon of going rancid.
In the present invention, the effect of dispersant is to shorten the jitter time of the clear priming paint of aqueouss semi open model, improves aqueouss
The gloss of the clear priming paint of semi open model, tinting strength, tinting power and covering power, improve color developing and the toning property of the clear priming paint of aqueouss semi open model, prevent
Only flocculate, sedimentation is prevented, is conducive to the steady in a long-term of the clear priming paint of aqueouss semi open model, it is preferred that for providing in the present invention
In embodiment, dispersant can be the high molecular weight block copolymer containing pigment group.
In the present invention, the effect of antibacterial is to suppress the life of microorganism and antibacterial in the clear priming paint of aqueouss semi open model
Long, not only the clear priming paint of the aqueouss semi open model of storage in protection fill tank, also protects shape after the clear priming paint construction of aqueouss semi open model
The paint film for becoming is not caused the qualitative change for being applied product by microorganism and bacteria effect, enhances the clear priming paint of aqueouss semi open model
Stability, it is preferred that in one embodiment that the present invention is provided, antibacterial is chlormethylisothiazo,ine ketone, due to the sterilization
Agent does not contain formaldehyde, reduces penetrating odor, is also beneficial to environmental protection.
In the present invention, the effect of pH adjusting agent is to improve the storage stability of the clear priming paint of aqueouss semi open model, freeze proof
Melting property, improves system viscosity, it is preferred that in one embodiment that the present invention is provided, pH adjusting agent can be 2- amino -2- first
Base -1- propanol.
In the present invention, the effect of coalescents is to reduce minimum film formation temperature and the glass of the clear priming paint of aqueouss semi open model
Glass state conversion temperature, promotes emulsion colloidal to merge, it is preferred that in one embodiment that the present invention is provided, coalescents are permissible
For dipropylene glycol methyl ether DPM and dipropylene DPNB.
In the present invention, the effect of grinding auxiliary agent is to improve the grinability of the clear priming paint of aqueouss semi open model, it is preferred that
In one embodiment that the present invention is provided, grinding auxiliary agent can be zinc powder.
In the present invention, the effect of wetting agent is to reduce the surface tension of the clear paint base system of aqueouss semi open model so that
The clear priming paint of aqueouss semi open model is more easy to moistening, is more easy to spread in the coated side of ground, obtains excellent ground moistening and enter hole
Property, and unstable bubble, it is preferred that in one embodiment that the present invention is provided, wetting agent can be organic silicon surfactant.
In the present invention, the effect of thickening agent is to make the clear priming paint thickening of aqueouss semi open model, the clear bottom of aqueouss semi open model
Paint occurs sagging phenomenon in construction, and can give the excellent mechanical performance of the clear priming paint of aqueouss semi open model and store stable
Property, it is preferred that in one embodiment that the present invention is provided, thickening agent can be polyurethane type and alkali swelling species thickening
Agent, in the case of the transparency of the clear paint base system of aqueouss semi open model is not affected, can function well as thickening effect, and right
The raising for entering permeability performance of the clear priming paint of aqueouss semi open model is very helpful.
In the present invention, the effect of deionized water is to play dilution allotment effect, it is preferred that for providing in the present invention
In individual embodiment, deionized water can be industrial deionized water, be conducive to improving the storage of the clear priming paint of aqueouss semi open model
Stability.
It is understood that acrylic emulsion in the present embodiment, defoamer, dispersant, antibacterial, pH adjusting agent, becoming
Film auxiliary agent, grinding auxiliary agent, wetting agent, thickening agent and deionized water except the preferred content of described above, in actual applications,
Can also be and other materials are adopted, as long as enabling the performance of the clear priming paint of aqueouss semi open model to reach consistent or more excellent effect
, specifically do not limit herein.
Specifically, in actual applications, after the formula for determining the clear priming paint of aqueouss semi open model, following making can be adopted
Method is prepared：
1st, acrylic emulsion is added in tank body, and is stirred with 600 turns per minute of speed, in whipping process
In, appropriate defoamer, dispersant, antibacterial, pH adjustment, grinding auxiliary agent and thickening agent can be added to be mixed, afterwards
With 1200 turns per minute of speed, mixture can be disperseed 20 minutes.After dispersion terminates, it is possible to use mixture seen by scraper plate
Fineness, if fineness is less than 35 microns, and phenomenon of not going rancid, you can qualified with the fineness that judges mixture.
2nd, after fineness is qualified, 800 turns per minute can be down to the mixing speed of blender, and adds during stirring
Enter appropriate remaining material, i.e. coalescents and wetting agent, after disperseing 15 minutes, profit be able to will be mixed with appropriate deionized water
Compound is adjusted and sticks to suitable scope, obtains preparing the clear priming paint of the aqueouss semi open model for completing.
In the present embodiment, after the clear priming paint of prepared aqueouss semi open model, can be to the clear priming paint of aqueouss semi open model on ground
Carry out plate observation is sprayed, detect corresponding performance.
The embodiment of the present invention is reasonably combined with construction technology by setting about from formula, can obtain semi-open effect good
The clear priming paint of aqueouss semi open model, by this clear priming paint of aqueouss semi open model with commercially available typically open clear priming paint in such as black walnut
Painting effect contrast is done on wood, as a result shows that the clear priming paint of aqueouss semi open model is substantially better than in terms of permeability is entered typically open
Clear priming paint, and the disadvantage such as pin-free substantially, and compared with traditional paint, which opens effect quite, and have than traditional paint more
The scentless advantage of environmental protection.
For the sake of becoming apparent from, it is described in detail below by following examples, wherein, acrylic emulsion is purchased from DSM
(China) company limited, product grade is190；Defoamer is purchased from Bi Ke chemistry, and product grade is BYK-024；
Dispersant is purchased from Bi Ke chemistry, and product grade is BYK-190；PH adjusting agent is purchased from DOW Chemical, and product grade is AMP-95；Kill
Microbial inoculum is purchased from Clariant chemical industry (China) company limited of the U.S., and product grade is CI-15HS；Grinding auxiliary agent is purchased from U.S.'s Milliken
Company, product grade is TP-200；Polyurethane type thickening agent is purchased from the modest chemistry of moral, and product grade is Rheolate299, alkali soluble
Swollen type thickeners are purchased from ROHM AND HAAS, and product grade is ASE-60；Coalescents are purchased from DOW Chemical, the use of DPNB and DPM
Amount ratio is 1:1；Wetting agent is purchased from Bi Ke chemistry, and product grade is BYK-349；Deionized water is voluntarily produced for factory.
Embodiment 1
Get the raw materials ready：The acrylic emulsion of 70 weight portions, the defoamer of 0.5 weight portion, the dispersant of 0.5 weight portion, 0.2 weight
Part pH adjusting agent, the antibacterial of 0.1 weight portion, the grinding auxiliary agent of 2 weight portions, type thickeners that the alkali soluble of 0.5 weight portion is swollen,
The coalescents of 5 weight portions, the wetting agent of 0.5 weight portion, the polyurethane type thickening agent of 0.2 weight portion, 20.5 weight portions
Deionized water.
The clear priming paint of aqueouss semi open model will be made by above-mentioned provided preparation method with the formula proportion of above-mentioned weight portion
Afterwards, with general open clear priming paint, performance comparison can be done, it is possible to open for Masonia in ground with nitrate paint
Contrast on effect is put, the order of corresponding construction technology can be：Material pre-treatment (as material is polished or the process of material wood grain), bottom
Color, head degree, dry polishing, water glaze, the clear priming paint of aqueouss semi open model, dry polishing, the clear priming paint of aqueouss semi open model, drying
Color, finish paint are repaiied in polishing, face, and wherein, it is red that background color can apply exhibition occasion ZW74100 aqueouss background color to repair color base material, Zhan Chen ZW71100 aqueouss
The mixture that color essence, Zhan Chen ZW71200 aqueouss yellow essence, Zhan Chen ZW71300 aqueous black accurate adjustment are made into, head degree can apply exhibition occasion
ZW40251 aqueous wooden ware transparent priming, water glaze can apply exhibition occasion ZW76015 aqueous wooden ware glaze host, Zhan Chen
ZW74213 aqueous wooden ware glaze black slurry, Zhan Chen ZW74313 aqueous wooden ware glaze yellow pulp, Zhan Chen ZW74413 Waterborne wood
The mixture that the red slurry of device glaze is deployed into, face is repaiied color and exhibition occasion water ZW74005 aqueous wooden ware can be applied to repair color base material, Zhan Chen
ZW75204 aqueous wooden ware black essence, Zhan Chen ZW75304 aqueous wooden ware yellow essence, the redness accurate adjustment of Zhan Chen ZW75404 aqueous wooden ware are joined
The mixture for becoming, finish paint can apply exhibition occasion ZW51025 five points of mute finish paints of aqueous wooden ware, in actual contrast, can be coated with this reality
General open clear priming paint or nitrate paint is replaced with the processing step for applying the clear priming paint of the aqueouss semi open model in example.Through right
Than as a result showing：In terms of priming paint enters permeability, the clear priming paint of aqueouss semi open model in the present embodiment is had relatively as nitrate paint
Good enter permeability effect, the wood grain of Masonia has a clear, transparent phenomenon such as good, pin-free of nature, and general opens
The plate face for putting the clear priming paint institute application of formula has many pin holes, and priming paint enter that permeability is not good, there is no priming paint inside the conduit of ground, especially
Which is inadequate to relatively deep longer Catheter wetting ability.
Further, to the clear priming paint of aqueouss semi open model in the present embodiment according to water paint performance standard GB/T23999-
2009《Indoor decorating water-borne wood coating》And GB24410-2009《Indoor decorating is harmful with water-borne wood coating
Material is limited the quantity》Detected, measured data result is as follows：
Table 1
Embodiment 2
Get the raw materials ready：The acrylic emulsion of 80 weight portions, the defoamer of 0.6 weight portion, the dispersant of 0.5 weight portion, 0.2 weight
Part pH adjusting agent, the antibacterial of 0.1 weight portion, the grinding auxiliary agent of 2 weight portions, type thickeners that the alkali soluble of 0.5 weight portion is swollen,
The coalescents of 6 weight portions, the wetting agent of 0.7 weight portion, the polyurethane type thickening agent of 0.4 weight portion, 9 weight portions go from
Sub- water.
The formula of above weight portion is made after the clear priming paint of aqueouss semi open model by above-mentioned provided preparation method, permissible
Performance comparison being done with general open clear priming paint, it is possible to open effect pair is done in ground for Masonia with nitrate paint
More identical with the content described in embodiment 1 than, the order of corresponding construction technology and construction effect, here is omitted.
Further, it is also possible to the clear priming paint of aqueouss semi open model in the present embodiment according to water paint performance standard GB/
T23999-2009《Indoor decorating water-borne wood coating》And GB24410-2009《Indoor decorating aqueous wooden ware
Coating limits of harmful substances》Measured data is as follows：
Table 2
Those skilled in the art can be understood that, for convenience and simplicity of description, the system of foregoing description,
Device and the specific work process of unit, may be referred to the corresponding process in preceding method embodiment, will not be described here.
The above, above example only in order to technical scheme to be described, rather than a limitation；Although with reference to front
State embodiment to be described in detail the present invention, it will be understood by those within the art that：Which still can be to front
State the technical scheme described in each embodiment to modify, or equivalent is carried out to which part technical characteristic；And these
Modification or replacement, do not make the essence of appropriate technical solution depart from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (10)
1. the clear priming paint of a kind of aqueouss semi open model, it is characterised in that count by weight, including：
2. the clear priming paint of aqueouss semi open model according to claim 1, it is characterised in that the acrylic emulsion is modified third
Olefin(e) acid emulsion.
3. the clear priming paint of aqueouss semi open model according to claim 1 and 2, it is characterised in that the defoamer is poly- for brokenly bubble
Compound and/or polysiloxane solution.
4. the clear priming paint of aqueouss semi open model according to claim 1 and 2, it is characterised in that the dispersant be containing pigment
The high molecular weight block copolymer of group.
5. the clear priming paint of aqueouss semi open model according to claim 1 and 2, it is characterised in that the antibacterial be
Isothiazolone.
6. the clear priming paint of aqueouss semi open model according to claim 1 and 2, it is characterised in that the pH adjusting agent be
Base -2- methyl isophthalic acid-propanol.
7. the clear priming paint of aqueouss semi open model according to claim 1 and 2, it is characterised in that the coalescents be
Glycol methyl ether DPM and dipropylene DPNB.
8. the clear priming paint of aqueouss semi open model according to claim 1 and 2, it is characterised in that the grinding auxiliary agent be.
9. the clear priming paint of aqueouss semi open model according to claim 1 and 2, it is characterised in that the wetting agent be
Surfactant.
10. the clear priming paint of aqueouss semi open model according to claim 1 and 2, it is characterised in that the thickening agent be
Type thickeners and the swollen type thickeners of alkali soluble.