CN106433189A - Green-brown corn stalk dye and production method thereof - Google Patents
Green-brown corn stalk dye and production method thereof Download PDFInfo
- Publication number
- CN106433189A CN106433189A CN201510482470.0A CN201510482470A CN106433189A CN 106433189 A CN106433189 A CN 106433189A CN 201510482470 A CN201510482470 A CN 201510482470A CN 106433189 A CN106433189 A CN 106433189A
- Authority
- CN
- China
- Prior art keywords
- corn straw
- oak
- parts
- green brown
- alumen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a green-brown corn stalk dye and a production method thereof. The dye adopts corn stalks, willow tree leaves, oak wood, red bayberry, lotus, alum, an iron ion compound solution and mineral water as main raw materials. The main process flow of the production method comprises material selection, material cutting, immersion, hot boiling, dyeing and dye fixation. The dye is made of pure plants, has the delicate fragrance emitted by the plants, and also has the advantages of no chemical substances in the making process, no harms to human bodies, wide sources of raw materials, short processing process route, and easiness in processing and manufacturing.
Description
Technical field:
The present invention relates to a kind of vegetable colour, more particularly to a kind of green brown corn straw dyestuff and its production method.
Background technology:
Industrial art refers to that daily living article, after art up process, is allowed to the product with strong aesthetic value.
As physical product, it reflects certain era, necessarily social material and culture the level of production to industrial art works;As intellectual product, its visual image, such as moulding, color, decoration, embody the aesthetic conceptions of certain era again.
Industrial art is generally divided into two big class:First, daily technique, that is, through the life utility of decorative processing, such as some dyeing and weaving technique, ceramic process, furniture arts etc.;2nd, furnishings technique, that is, specialize in the stuff of appreciation, such as some ivory carvings, jade carving, decorative painting etc..
It is suitable for and combines with aesthetic, be industrial art essence, primary feature.The taste of workmanship is also restricted by technology category characteristic simultaneously.The aesthetic value of all kinds of artwares just sees whether the feature of this kind of artware is perfectly played to a certain extent.
Straw patchwork is an ingredient of industrial art, but in the prior art, the primary raw material Wheat Straw making straw patchwork is dyed carmine method many kinds, but most dyestuffs are chemical dye, the carmetta dyeing is not pure, easily fades, not only not environmentally, some dyes even can produce toxic gas during dye system, threatens the health of human body.
Content of the invention:
It is an object of the invention to provide a kind of pure natural, pollution-free, environmental protection, the green brown corn straw dyestuff being configured to pure natural plant that the person is had no toxic side effect and its production method.
The object of the present invention is achieved like this.It is to be made up of the raw material that following weight is joined, corn straw
25-50
Part, Folium Pterocaryae
15-30
Part, oak
10-22
Part, Fructus Myricae rubrae
7-18
Part, Flos Nelumbinis
5-15
Part, Alumen
5-15
Part, ferric ion compounds solution
5-15
Part, mineral water
30-80
Part.
The preparation present invention green brown corn straw dyestuff preferred weight ratio range is that the weight proportion of wherein various raw materials is, corn straw
25-40
Part, Folium Pterocaryae
15-25
Part, oak
10-16
Part, Fructus Myricae rubrae
7-13
Part, Flos Nelumbinis
5-10
Part, Alumen
5-10
Part, ferric ion compounds solution
5-10
Part, mineral water
30-70
Part.
The best weight ratio scope of the preparation present invention green brown corn straw dyestuff is that the weight proportion of wherein various raw materials is, corn straw
33
Part, Folium Pterocaryae
20
Part, oak
13
Part, Fructus Myricae rubrae
10
Part, Flos Nelumbinis
8
Part, Alumen
7
Part, ferric ion compounds solution
7
Part, mineral water
60
Part.
Above-mentioned each component is made the production method of the present invention green brown corn straw dyestuff, technical process is:Sorting, blank, immersion, heat are boiled, dye, fixation, and concrete operation method follow these steps to successively:
A
, sorting, press raw material weight proportioning of soup processed, choose the corn straw that is completely dried, remove other branch, go the
1
Section is with finally
1
Section, leaves and takes mid portion, selects that to meet the Folium Pterocaryae of national health and quality standard, oak, Fructus Myricae rubrae, Flos Nelumbinis, Alumen, ferric ion compounds solution, mineral water standby;
B
, blank, corn straw knife is longitudinally cut open, remove the interior flesh part of the inside, retain outside straw partly standby;By the raw material selected Folium Pterocaryae, oak, Fructus Myricae rubrae, Flos Nelumbinis, be cut into respectively block standby;
C
, soak, by selected raw material be placed in equipped with the storage tank of mineral water soak, temperature be room
20
℃
-25
DEG C, the time
2
-
4
Hour;
D
, heat boil, salt and water be placed in iron pan heating, water temp. heating arrives
40
°, put into Alumen, persistently overheating to water temperature be
70
°, put into the Folium Pterocaryae after immersion, oak, Fructus Myricae rubrae, Flos Nelumbinis, and be stirred continuously, put into ferric ion compounds solution, steaming and decocting
2-3
Hour, cook green brown pigmentation solution;
E
, dyeing, extract the pigment solution that goes out of steaming and decocting, put in pottery, put into the corn straw after immersion, and steaming and decocting
1-2
Hour, period is stirred continuously, and makes corn straw fully absorb green brown pigmentation, level dyeing;
F
, fixation, by dyeing after corn straw pull out, standing
30
Minute, put in clear water
5-10
Minute, take out after drifting out loose colour, be put into and be dried at shady and cool ventilation, obtain a kind of corn straw dyestuff of green brown.
It is an advantage of the current invention that:
1
, select raw material, scientific formulation, color is pure;
2
, product made by pure plant, there is the delicate fragrance that plant distributes in itself, without any chemical substance in manufacturing process, no any injury to human body;
3
, raw material sources extensively, plus process line is short, and product easy processing manufactures.
Specific embodiment
With reference to specific embodiment, the present invention is further illustrated:
Embodiment
1
:
Preparing the present invention green brown corn straw dyestuff weight proportion scope is:Corn straw
25-50
Part, Folium Pterocaryae
15-30
Part, oak
10-22
Part, Fructus Myricae rubrae
7-18
Part, Flos Nelumbinis
5-15
Part, Alumen
5-15
Part, ferric ion compounds solution
5-15
Part, mineral water
30-80
Part.
Embodiment
2
:
Preparing the present invention green brown corn straw dyestuff preferred weight ratio range is:Corn straw
25-40
Part, Folium Pterocaryae
15-25
Part, oak
10-16
Part, Fructus Myricae rubrae
7-13
Part, Flos Nelumbinis
5-10
Part, Alumen
5-10
Part, ferric ion compounds solution
5-10
Part, mineral water
30-70
Part.
Embodiment
3
:
Preparing the present invention green brown corn straw dyestuff best weight ratio scope is:Corn straw
33
Part, Folium Pterocaryae
20
Part, oak
13
Part, Fructus Myricae rubrae
10
Part, Flos Nelumbinis
8
Part, Alumen
7
Part, ferric ion compounds solution
7
Part, mineral water
60
Part.
Above-mentioned each component is made the production method of the present invention green brown corn straw dyestuff, technical process is:Sorting, blank, immersion, heat are boiled, dye, fixation, and concrete operation method follow these steps to successively:
A
, sorting, press raw material weight proportioning of soup processed, choose the corn straw that is completely dried, remove other branch, go the
1
Section is with finally
1
Section, leaves and takes mid portion, selects that to meet the Folium Pterocaryae of national health and quality standard, oak, Fructus Myricae rubrae, Flos Nelumbinis, Alumen, ferric ion compounds solution, mineral water standby;
B
, blank, corn straw knife is longitudinally cut open, remove the interior flesh part of the inside, retain outside straw partly standby;By the raw material selected Folium Pterocaryae, oak, Fructus Myricae rubrae, Flos Nelumbinis, be cut into respectively block standby;
C
, soak, by selected raw material be placed in equipped with the storage tank of mineral water soak, temperature be room
20
℃
-25
DEG C, the time
2
-
4
Hour;
D
, heat boil, salt and water be placed in iron pan heating, water temp. heating arrives
40
°, put into Alumen, persistently overheating to water temperature be
70
°, put into the Folium Pterocaryae after immersion, oak, Fructus Myricae rubrae, Flos Nelumbinis, and be stirred continuously, put into ferric ion compounds solution, steaming and decocting
2-3
Hour, cook green brown pigmentation solution;
E
, dyeing, extract the pigment solution that goes out of steaming and decocting, put in pottery, put into the corn straw after immersion, and steaming and decocting
1-2
Hour, period is stirred continuously, and makes corn straw fully absorb green brown pigmentation, level dyeing;
F
, fixation, by dyeing after corn straw pull out, standing
30
Minute, put in clear water
5-10
Minute, take out after drifting out loose colour, be put into and be dried at shady and cool ventilation, obtain a kind of corn straw dyestuff of green brown.
Claims (4)
1. a kind of green brown corn straw dyestuff it is characterised in that:It is to be made up of the raw material of following weight proportioning, corn straw 25-50 part, Folium Pterocaryae 15-30 part, oak 10-22 part, Fructus Myricae rubrae 7-18 part, Flos Nelumbinis 5-15 part, Alumen 5-15 part, ferric ion compounds solution 5-15 part, mineral water 30-80 part.
2. a kind of green brown corn straw dyestuff it is characterised in that:The weight proportion of wherein various raw materials is, corn straw 25-40 part, Folium Pterocaryae 15-25 part, oak 10-16 part, Fructus Myricae rubrae 7-13 part, Flos Nelumbinis 5-10 part, Alumen 5-10 part, ferric ion compounds solution 5-10 part, mineral water 30-70 part.
3. a kind of green brown corn straw dyestuff it is characterised in that:The weight proportion of wherein various raw materials is, 33 parts of corn straw, 20 parts of Folium Pterocaryae, 13 parts of oak, 10 parts of Fructus Myricae rubrae, 8 parts of Flos Nelumbinis, 7 parts of Alumen, 7 parts of ferric ion compounds solution, 60 parts of mineral water.
4. a kind of production method preparing green brown corn straw dyestuff according to claim 3 it is characterised in that:Technical process is:Sorting, blank, immersion, heat are boiled, dye, fixation, and concrete operation method follow these steps to successively:A, sorting, press raw material weight proportioning of soup processed, choose the corn straw being completely dried, remove other branch, remove Section 1 and last 1 section, leave and take mid portion, select that to meet the Folium Pterocaryae of national health and quality standard, oak, Fructus Myricae rubrae, Flos Nelumbinis, Alumen, ferric ion compounds solution, mineral water standby;B, blank, corn straw knife is longitudinally cut open, removes the interior flesh part of the inside, retain outside straw partly standby;By the raw material selected Folium Pterocaryae, oak, Fructus Myricae rubrae, Flos Nelumbinis, be cut into respectively block standby;C, immersion, by selected raw material be placed in equipped with the storage tank of mineral water soak, temperature be 20 DEG C -25 DEG C of room, time 2-4 hour;D, heat are boiled, salt and water are placed on heating in iron pan, and water temp. heating, to 40 °, puts into Alumen, persistently overheating to water temperature be 70 °, put into the Folium Pterocaryae after immersion, oak, Fructus Myricae rubrae, Flos Nelumbinis, and be stirred continuously, put into ferric ion compounds solution, steaming and decocting 2-3 hour, cook green brown pigmentation solution;The pigment solution that E, dyeing, extraction steaming and decocting go out, puts in pottery, puts into the corn straw after immersion, and steaming and decocting 1-2 hour, and period is stirred continuously, and makes corn straw fully absorb green brown pigmentation, level dyeing;F, fixation, the corn straw after dyeing is pulled out, stand 30 minutes, put into 5-10 minute in clear water, drift out and take out after loose colour, be put into and be dried at shady and cool ventilation, obtain a kind of corn straw dyestuff of green brown.