CN106433155A - 一种非热熔型自粘耐根穿刺防水卷材的制备方法 - Google Patents

一种非热熔型自粘耐根穿刺防水卷材的制备方法 Download PDF

Info

Publication number
CN106433155A
CN106433155A CN201510477109.9A CN201510477109A CN106433155A CN 106433155 A CN106433155 A CN 106433155A CN 201510477109 A CN201510477109 A CN 201510477109A CN 106433155 A CN106433155 A CN 106433155A
Authority
CN
China
Prior art keywords
root
rubber
preparation
type self
waterproof roll
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510477109.9A
Other languages
English (en)
Inventor
延晓平
宋正红
李会平
刘伟芹
仇立静
夏友军
李猛
李奇智
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANJIN QICAI WATERPROOF MATERIAL CO Ltd
Tianjin Rare Talent's Development In Science And Technology Co Ltd
TIANJIN QICAI WATERPROOF MATERIALS CO Ltd
Original Assignee
TIANJIN QICAI WATERPROOF MATERIAL CO Ltd
Tianjin Rare Talent's Development In Science And Technology Co Ltd
TIANJIN QICAI WATERPROOF MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN QICAI WATERPROOF MATERIAL CO Ltd, Tianjin Rare Talent's Development In Science And Technology Co Ltd, TIANJIN QICAI WATERPROOF MATERIALS CO Ltd filed Critical TIANJIN QICAI WATERPROOF MATERIAL CO Ltd
Priority to CN201510477109.9A priority Critical patent/CN106433155A/zh
Publication of CN106433155A publication Critical patent/CN106433155A/zh
Pending legal-status Critical Current

Abstract

一种非热熔型自粘耐根穿刺防水卷材的制备方法，以高分子树脂、优质沥青为基料，再添加一定量的滑石粉﹑SBS、SBR等材料，少量阻根剂以及溶剂油类。具有应力蠕变、穿刺自闭合、压敏自粘、耐物理穿刺以及快速反应粘结的技术特点与混凝土基层形成完美的防水层，从根本上改变了传统热熔型防水卷材以及物理性自粘防水卷材的技术缺陷所带来的防水隐患。通过对改性沥青体系的防根化处理，既阻根又阻茎，形成化学、物理双重阻根体系，从根本上防止了植物根尖穿透防水层，同时不影响植物的正常生长。通过对自粘卷材与耐根穿刺卷材的性能研究，融合两种卷材的优点，使得该产品的适用范围更加广泛与应用更加方便，同时减少能源的消耗。

Description

一种非热熔型自粘耐根穿刺防水卷材的制备方法
技术领域
本发明属于建筑屋面、墙面、露台、广场地坪面等的种植绿化以及堤坝、水库的防水、防根穿刺的自粘卷材。
背景技术
随着科技的发展，能源的应用越来越多，可是可再生能源很少，所以为了改善耐根穿刺防水卷材热熔法施工的能源浪费问题，开发研究了非热熔型自粘耐根穿刺防水卷材。
该产品的主要特点：具有应力蠕变、穿刺自闭合、压敏自粘、耐物理穿刺以及快速反应粘结的技术特点与混凝土基层形成完美的防水层，从根本上改变了传统热熔型防水卷材以及物理性自粘防水卷材的技术缺陷所带来的防水隐患。耐根穿刺方面：通过对改性沥青体系的防根化处理，既阻根又阻茎，形成化学、物理双重阻根体系，从根本上防止了植物根尖穿透防水层，同时不影响植物的正常生长。施工时不用粘结剂，也不须加热烤至熔化，只须撕去隔离层，即可牢固地粘结在基层上，又防根穿刺，又防水，具有双重效果。
发明内容
一种非热熔型自粘耐根穿刺防水卷材的制备方法，以高分子树脂、优质沥青为基料，再添加一定量的橡胶改性剂﹑耐高温、耐低温改性剂等材料，少量阻根剂以及填充剂等经过一定工艺流程而制得。通过对自粘卷材与耐根穿刺卷材的性能研究，融合两种卷材的优点，使得该产品的适用范围更加广泛与应用更加方便，同时减少能源的消耗。
本发明通过合理的配比，以及合理填料尺寸的选择，使材料储存稳定。
本发明的技术方案是：
一种非热熔型自粘耐根穿刺防水卷材的制备方法，其特征在于原料组成的质量百分数为：
所述的石油沥青，可以为煤焦油沥青、石油沥青和天然沥青中的一种或者几种混合，优选石油沥青。
所述的石油沥青可为常用的10号沥青和90号沥青的一种或者两种按一定比例混合使用。比例可为：0-10：10-50；优选0-8：15-42。
所述的橡胶类改性剂为：天然橡胶、合成橡胶、通用橡胶的一种或者几种混合使用，优选通用橡胶：丁苯橡胶、丁腈橡胶、硅橡胶、顺丁橡胶、异戊橡胶、乙丙橡胶、氯丁橡胶中的一种或者几种混合使用，更优选丁苯橡胶中的:苯乙烯-丁二烯-苯乙烯嵌段共聚物和苯乙烯-丁二烯二元共聚物混合使用，混合比例为：3-13：2-13。
所述的阻根剂为：化学阻根剂、物理阻根剂中的一种或者几种混合使用。
所述的耐高温改性剂为无规聚丙烯、无定型烯径共聚物中的一种或几种混合使用。
所述的耐低温改性剂为饱和烃类增塑剂，优选环烷油、芳烷油中的一种或几种混合物。
所述的填料为增强、提高尺寸稳定性、提高耐磨性、改善耐老化性能、降低体系粘度、不影响力学性能的固体填充料，一般为：碳酸钙、石墨、钛白粉、滑石粉中的一种或几种混合物，优选活性碳酸钙和活性滑石粉。
所述的非热熔型自粘耐根穿刺防水卷材可以为有胎基型或者无胎基型，胎基可以为：聚烯烃胎基、聚酯胎基、玻纤增强胎基等。
附图说明
附图是一种非热熔型自粘耐根穿刺防水卷材的制备方法的生产工艺流程图。
工艺过程：
(1)将石油沥青融化加入搅拌机，到达一定温度后加入改性物料开启搅拌器，使其分散溶解均匀。
(2)继续搅拌，加入填充物料，搅拌30min。
(3)用玻纤、化纤、麻纤和聚酯毡为基胎，经过单槽浸渍法和辊涂法浸渍和涂盖。
(4)打卷包装。
实施例1
配方
工艺过程：
(1)将10#石油沥青4份﹑90#石油沥青38份融化后加入到搅拌罐，加入环烷油7份，芳烃油11份，APAO 6份，当温度达到140℃左右时加入SBR 8份，搅拌使其溶解分散均匀，后加入SBS 6份，温度最好在180℃左右，搅拌2h。
(2)继续搅拌，阻根剂2份及滑石粉18份。
(3)用玻纤、化纤、麻纤和聚酯毡为基胎，经过单槽浸渍法和辊涂法浸渍和涂盖。
(4)打卷包装。
制得产品性能测试结果附于表1中。
实施例2
配方
工艺过程：
(1)将10#石油沥青4份﹑90#石油沥青34份融化后加入到搅拌罐，加入环烷油8份，芳烃油8份，APAO 11份，当温度达到140℃左右时加入SBR 5份，搅拌使其溶解分散均匀，后加入SBS 5份，温度最好在180℃左右，搅拌2h。
(2)继续搅拌，阻根剂6份及滑石粉19份。
(3)用玻纤、化纤、麻纤和聚酯毡为基胎，经过单槽浸渍法和辊涂法浸渍和涂盖。
(4)打卷包装。
制得产品性能测试结果附于表1中。
实施例3
配方
工艺过程：
(1)将10#石油沥青3份，90#石油沥青38份融化后加入到搅拌罐，加入环烷油10份，芳烃油11份，APAO 2份，当温度达到140℃左右时加入SBR 10份，搅拌使其溶解分散均匀，后加入SBS 10份，温度最好在180℃左右，搅拌2h。
(2)继续搅拌，阻根剂6份及滑石粉10份。
(3)用玻纤、化纤、麻纤和聚酯毡为基胎，经过单槽浸渍法和辊涂法浸渍和涂盖。
(4)打卷包装。
制得产品性能测试结果附于表1中。
表1 非热熔型自粘耐根穿刺防水卷材性能指标
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，通过本发明专利延伸拓展而直接或者间接应用的到技术领域，均属于本发明专利保护范围。

Claims (9)

1.一种非热熔型自粘耐根穿刺防水卷材的制备方法，其特征在于原料组成的质量份数为：
。
2.根据权利要求1所述的一种非热熔型自粘耐根穿刺防水卷材的制备方法，其特征在于:所述的石油沥青，为10号沥青和90号沥青的一种或者两种按一定比例混合使用，比例可为：0-10：10-50；优选0-8：15-42。
3.根据权利要求1所述的一种非热熔型自粘耐根穿刺防水卷材的制备方法，其特征在于：所述的橡胶类改性剂为：天然橡胶、合成橡胶、通用橡胶的一种或者几种混合使用；优选通用橡胶：丁苯橡胶、丁腈橡胶、硅橡胶、顺丁橡胶、异戊橡胶、乙丙橡胶、氯丁橡胶中的一种或者几种混合使用，更优选丁苯橡胶中的SBS和SBR橡胶混合使用，混合比例为：3-13：2-13。
4.根据权利要求1所述的一种非热熔型自粘耐根穿刺防水卷材的制备方法，其特征在于：阻根剂为：化学阻根剂、物理阻根剂中的一种或者几种混合使用。
5.根据权利要求1所述的一种非热熔型自粘耐根穿刺防水卷材的制备方法，其特征在于：耐高温改性剂为无规聚丙烯、无定型烯径共聚物中的一种或几种混合使用。
6.根据权利要求1所述的一种非热熔型自粘耐根穿刺防水卷材的制备方法，其特征在于：耐低温改性剂为饱和烃类增塑剂，优选环烷油、芳烷油中的一种或几种混合物。
7.根据权利要求1所述的一种非热熔型自粘耐根穿刺防水卷材的制备方法，其特征在于：填料为增强、提高尺寸稳定性、提高耐磨性、改善耐老化性能、降低体系粘度、不影响力学性能的固体填充料，一般为：碳酸钙、石墨、钛白粉、滑石粉中的一种或几种混合物，优选活性碳酸钙或活性滑石粉。
8.根据权利要求1所述的一种非热熔型自粘耐根穿刺防水卷材的制备方法，其特征在于：所述的非热熔型自粘耐根穿刺防水卷材可以为有胎基型或者无胎基型，胎基可以为：聚烯烃胎基、聚酯胎基、玻纤增强胎基。
9.根据权利要求1所述的一种非热熔型自粘耐根穿刺防水卷材的制备方法，其特征在于：所述的加工工艺为：原材料经过自动计量进入搅拌系统，后经研磨机后，进入快速搅拌机进行快速搅拌，自动打入自粘胶搅拌储罐，经自粘料胶布装置、自粘卷材成型机组、在此与面膜、边膜复合成型，后经冷却机组、展平装置、缓冲装置、打卷包装。
CN201510477109.9A 2015-08-05 2015-08-05 一种非热熔型自粘耐根穿刺防水卷材的制备方法 Pending CN106433155A (zh)