CN106432936A - Coating coil for decorating interior wall - Google Patents
Coating coil for decorating interior wall Download PDFInfo
- Publication number
- CN106432936A CN106432936A CN201610774855.9A CN201610774855A CN106432936A CN 106432936 A CN106432936 A CN 106432936A CN 201610774855 A CN201610774855 A CN 201610774855A CN 106432936 A CN106432936 A CN 106432936A
- Authority
- CN
- China
- Prior art keywords
- fiber
- coiled material
- interior wall
- decorative coating
- polylactic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a coating coil for decorating an interior wall. The coating coil comprises an interior wall coating layer, wherein the interior wall coating layer comprises polylactic acid fiber and poplar bark fiber; the length of the polylactic acid fiber is 0.5-1mm and the diameter of the polylactic acid fiber is 0.5mm or lower; the length of the poplar bark fiber is 2-5mm and the diameter of the poplar bark fiber is 0.5mm or lower; the polylactic acid fiber and the poplar bark fiber are added into a coating for the interior wall as an antibacterial agent; the interior wall coating layer comprises the following components in parts by weight: 20-25 parts of calcite powder, 5-15 parts of zinc white powder, 15-25 parts of light calcium carbonate, 20-35 parts of heavy calcium carbonate powder, 15-25 parts of ash calcium powder, 1-5 parts of the polylactic acid fiber and 1-2 parts of the poplar bark fiber.
Description
Technical field
The present invention relates to architectural decoration coating material coiled material, more particularly to a kind of inner wall decorative coating coiled material.
Background technology
Dope for inner wall of architecture is exposed surface area the best part in building, while being also that antibacterial, funguses, mycete multiply
Main positions, and antibacterial that these are multiplied, funguses, mycete are very big to the health effect of the mankind.As people are to living quality, life
The raising of prescription living, people also gradually pay attention to this problem.Antibacterial employed in current dope for inner wall of architecture
Agent is mainly the inorganic salts such as mercury salt class, because the toxicity of its own, has certain injury to human body;Other antimicrobial technology are mainly light
Catalyst technology, there are certain requirements to environment, and relatively costly.
Chinese invention patent application 03118030.2 provides one kind《Multifunction environment-protection type nano inner wall coating and its preparation
Method》, consisting of:Pure-acrylic emulsion (or styrene-acrylic emulsion), water, sodium hexameta phosphate, dispersant, thickening agent, preservative, nanometer
ZnO, Nano-meter SiO_2 #- [2], nano-TiO #- [2], triple superphosphate, titanium dioxide, wollastonite in powder, Pulvis Talci, antifreezing agent, coalescents, stream
Flat agent, defoamer.Its preparation method be first by nano-component pretreatment, by uniform for dispersant nano-component and six inclined phosphorus
Sour sodium and dispersant are added to the water stirring, then add remaining component step by step, are uniformly dispersed, and fill gets product.
Chinese invention patent application 99117416.X is given《A kind of interior wall coating with sterilizing function》, the coating
And be made up with nano zine oxide (nano-ZnO) of filler, nontoxic, tasteless, non-stimulated to skin, and pathogenic bacteria, virus can be killed
As staphylococcus aureuses, escherichia coli, killing rate is all more than 90%.
Chinese invention patent application 03108996.8 is given《Jade interior wall coating and preparation method》, be by auxiliary agent,
Jade powder, antibacterial and water composition, antibacterial therein is saturation silver solution, has killing function to indoor unicellular mushroom.
The antibacterial for interior wall coating for being given in technique scheme, though kill multiple mycetes, go to eliminate the unusual smell with suppression
Etc. function, but the material for adding is high-tech nano material or noble metal, its complicated process of preparation, relatively costly, indirect shadow
Ring the market outlet of interior wall coating.
Dope for inner wall of architecture is exposed surface area the best part in building, while being also that antibacterial, funguses, mycete multiply
Main positions, and antibacterial that these are multiplied, funguses, mycete are very big to the health effect of the mankind.
With the raising that people were required to living quality, quality of life, people also gradually pay attention to this problem.
Content of the invention
The technical problem to be solved in the present invention is for above not enough, provides inner wall decorative coating coiled material, the inner wall decoration
The construction of coating coiled material is rapid, with sterilizing function.
For solving above technical problem, the present invention is employed the following technical solutions:
Inner wall decorative coating coiled material, it is characterised in that:Including interior wall coating layer, the interior wall coating layer include acid fiber by polylactic and
Willow hide fiber, acid fiber by polylactic 0.5-1mm length, below diameter 0.5mm, the willow hide fiber 2-5mm length, diameter 0.5mm
Hereinafter, the acid fiber by polylactic and willow hide fiber are added in interior wall coating as antibacterial.
The following is the improvement further to technique scheme:
Interior wall coating layer includes calcite powder 20-25 part, zinc oxide powder 5-15 part, precipitated calcium carbonate 15-25 part, dry powder 20-
35 parts, sierozem power 15-25 part, acid fiber by polylactic 1-5 part, willow hide fiber 1-2 part.
Also include high polymer layer, described high polymer layer is polystyrene, polyethylene, the poly- second of metallocene
At least one in alkene, polypropylene, metallocene polypropylene, polyethylene terephthalate, polycaprolactam.
The method of inner wall decorative coating coiled material, 1)By described calcite powder, zinc oxide powder, precipitated calcium carbonate, dry powder,
Sierozem power, acid fiber by polylactic, willow hide fiber, after mix homogeneously, dispersing apparatus are added, inorganic particle is made with Chinese white interface
It is fully contacted, and dispersed;
2)By step 1)The material that obtains introduces high-speed mixer, adds grafting agent, described, 80-140 DEG C of temperature conditionss,
15-30min is reacted under 900-1500r/min stirring condition;
3)Lubricating auxiliary agent, stabilizer are added in above-mentioned high-speed mixer, in 100-140 DEG C of temperature conditionss, 900-1500r/min
5-10min is reacted under stirring condition;
4)High molecular polymer is added and is uniformly mixed in above-mentioned high-speed mixing equipment;
5)The material of above-mentioned mix homogeneously is introduced extrusion calendaring stretcher, by reactive extrursion, rolled, stretch, batching
To a kind of inner wall decorative coating coiled material.
Described grafting agent is methyl methacrylate, poly- butylacrylic acid, at least one in maleic anhydride.
Dispersing apparatus are three chamber continuous way eddy airstream refining machines.
Extrusion calendaring stretcher selects screw extruder.
The willow hide fiber is that manually grinding is formed in 90 DEG C of oven drying at low temperatures by natural Cortex Populi Davidianae.
During construction, the present invention can be attached directly on metope, measure after use in 1 year through test, antibiotic rate can reach
99%;Using in rear 1-3, antibiotic rate can reach more than 95%.
With reference to embodiment, the present invention is described in detail.
Specific embodiment
Embodiment, inner wall decorative coating coiled material, including interior wall coating layer, the interior wall coating layer include acid fiber by polylactic and
Willow hide fiber, acid fiber by polylactic 0.5-1mm length, below diameter 0.5mm, the willow hide fiber 2-5mm length, diameter 0.5mm
Hereinafter, the acid fiber by polylactic and willow hide fiber are added in interior wall coating as antibacterial.
Interior wall coating layer includes calcite powder 20-25 part, zinc oxide powder 5-15 part, precipitated calcium carbonate 15-25 part, dry powder
20-35 part, sierozem power 15-25 part, acid fiber by polylactic 1-5 part, willow hide fiber 1-2 part.
Also include high polymer layer, described high polymer layer is polystyrene, polyethylene, the poly- second of metallocene
At least one in alkene, polypropylene, metallocene polypropylene, polyethylene terephthalate, polycaprolactam.
The method of inner wall decorative coating coiled material, 1)By described calcite powder, zinc oxide powder, precipitated calcium carbonate, dry powder,
Sierozem power, acid fiber by polylactic, willow hide fiber, after mix homogeneously, dispersing apparatus are added, inorganic particle is made with Chinese white interface
It is fully contacted, and dispersed;
2)By step 1)The material that obtains introduces high-speed mixer, adds grafting agent, described, 80-140 DEG C of temperature conditionss,
15-30min is reacted under 900-1500r/min stirring condition;
3)Lubricating auxiliary agent, stabilizer are added in above-mentioned high-speed mixer, in 100-140 DEG C of temperature conditionss, 900-1500r/min
5-10min is reacted under stirring condition;
4)High molecular polymer is added and is uniformly mixed in above-mentioned high-speed mixing equipment;
5)The material of above-mentioned mix homogeneously is introduced extrusion calendaring stretcher, by reactive extrursion, rolled, stretch, batching
To a kind of inner wall decorative coating coiled material.
Described grafting agent is methyl methacrylate, poly- butylacrylic acid, at least one in maleic anhydride.
Dispersing apparatus are three chamber continuous way eddy airstream refining machines.
Extrusion calendaring stretcher selects screw extruder.
The willow hide fiber is that manually grinding is formed in 90 DEG C of oven drying at low temperatures by natural Cortex Populi Davidianae.
During construction, the present invention can be attached directly on metope, measure after use in 1 year through test, antibiotic rate can reach
99%;Using in rear 1-3, antibiotic rate can reach more than 95%.
Claims (7)
1. inner wall decorative coating coiled material, it is characterised in that:Including interior wall coating layer, the interior wall coating layer includes acid fiber by polylactic
With willow hide fiber, acid fiber by polylactic 0.5-1mm length, below diameter 0.5mm, the willow hide fiber 2-5mm length, diameter
Below 0.5mm, the acid fiber by polylactic and willow hide fiber are added in interior wall coating as antibacterial.
2. inner wall decorative coating coiled material according to claim 1, it is characterised in that:Interior wall coating layer includes calcite powder
20-25 part, zinc oxide powder 5-15 part, precipitated calcium carbonate 15-25 part, dry powder 20-35 part, sierozem power 15-25 part, acid fiber by polylactic
1-5 part, willow hide fiber 1-2 part.
3. inner wall decorative coating coiled material according to claim 2, it is characterised in that:Also include high polymer layer, institute
High polymer layer is stated for polystyrene, polyethylene, metallocene PE, polypropylene, metallocene polypropylene, poly- terephthaldehyde
At least one in sour second diester, polycaprolactam.
4. the method for preparing the inner wall decorative coating coiled material described in claim 3, it is characterised in that:
1)By described calcite powder, zinc oxide powder, precipitated calcium carbonate, dry powder, sierozem power, acid fiber by polylactic, Cortex Populi Davidianae fibre
Dimension, after mix homogeneously, is added dispersing apparatus, so that inorganic particle is fully contacted with Chinese white interface, and dispersed;
2)By step 1)The material that obtains introduces high-speed mixer, adds grafting agent, described, 80-140 DEG C of temperature conditionss,
15-30min is reacted under 900-1500r/min stirring condition;
3)Lubricating auxiliary agent, stabilizer are added in above-mentioned high-speed mixer, in 100-140 DEG C of temperature conditionss, 900-1500r/min
5-10min is reacted under stirring condition;
4)High molecular polymer is added and is uniformly mixed in above-mentioned high-speed mixing equipment;
5)The material of above-mentioned mix homogeneously is introduced extrusion calendaring stretcher, by reactive extrursion, rolled, stretch, batching
To a kind of inner wall decorative coating coiled material.
5. the method for inner wall decorative coating coiled material as claimed in claim 4, it is characterised in that described grafting agent be
At least one in e pioic acid methyl ester, poly- butylacrylic acid, maleic anhydride.
6. the method for preparing inner wall decorative coating coiled material as claimed in claim 5, it is characterised in that:Dispersing apparatus are that three chambeies are continuous
Formula eddy airstream refining machine.
7. the method for preparing inner wall decorative coating coiled material as claimed in claim 6, it is characterised in that:Extrusion calendaring stretcher is selected
Use screw extruder.