CN106427100A - Antibacterial skin-friendly multilayer Chinese hemp fabric - Google Patents

Antibacterial skin-friendly multilayer Chinese hemp fabric Download PDF

Info

Publication number
CN106427100A
CN106427100A CN201610773597.2A CN201610773597A CN106427100A CN 106427100 A CN106427100 A CN 106427100A CN 201610773597 A CN201610773597 A CN 201610773597A CN 106427100 A CN106427100 A CN 106427100A
Authority
CN
China
Prior art keywords
layer
antibacterial
weight portion
fiber
flax
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610773597.2A
Other languages
Chinese (zh)
Inventor
陈念
庄浩
陶小池
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Wanjing Textile Technology Co Ltd
Original Assignee
Shanghai Wanjing Textile Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Wanjing Textile Technology Co Ltd filed Critical Shanghai Wanjing Textile Technology Co Ltd
Priority to CN201610773597.2A priority Critical patent/CN106427100A/en
Publication of CN106427100A publication Critical patent/CN106427100A/en
Pending legal-status Critical Current

Abstract

The invention provides an antibacterial skin-friendly multilayer Chinese hemp fabric, comprising a surface layer, an antibacterial layer, a flax layer and a bottom layer, wherein the surface layer is obtained by mixed weaving of regenerated cellulose fibers and pure cotton fibers; the antibacterial layer is made from carbon fibers and pure cotton fibers, and a layer of a silver series nano antimicrobial agent solution is attached to the surface of the antibacterial layer; the flax layer is obtained by mixed weaving of flax fibers, nylon fibers, glass fibers and viscose fibers; the bottom layer is obtained by weaving silk fibers, elastic fibers and terylene long fibers; and the surface layer, the antibacterial layer, the flax layer and the bottom layer are connected together by sewing. Compared with the prior art, the antibacterial skin-friendly multilayer Chinese hemp fabric provided by the invention has the following beneficial effects: the fabric has multiple functions and characteristics of moisture absorption, air permeability, comfort, heat dissipation, mildew resistance, bacteriostasis, radiation resistance, crease resistant, and no scratchiness, and can be widely applied to the fields of special military supplies, top-grade apparel, home textiles, shoe materials, automobile interiors, and industrial textiles.

Description

A kind of antibacterial pro-skin multilayer Chinese flax fabric
Technical field
The present invention is a kind of antibacterial pro-skin multilayer Chinese flax fabric, belongs to Chinese flax fabric field.
Background technology
With the raising day by day of living standard, people increasingly pay close attention to living environment, working environment and the health of self. In order to adapt to and improving living environment and the working environment of people, improving quality of life and the quality of life of people, people are more next More pay close attention to the health-care effect of daily necessities.
Occur in that antibiotic facing material in the market, but these fabric narrow antimicrobial spectrum, water-wash resistance difference, Durability of antimicrobial effect and Snugness of fit all can not reach demand.
And with growth in the living standard, garment material role is not only warming, also impart a lot of new Function, as ventilative, soft etc., one or both compound garment material generally a lot of can meet above-mentioned functions, as cotton and Terylene, silk and cotton etc., but cotton and silk price is more and more expensive, fades out for manufacturing garment material, and cost occupies height Under not, accordingly, it would be desirable to a kind of new, that can meet above-mentioned functions and low-cost composite material replaces.
Content of the invention
The deficiency existing for prior art, it is an object of the present invention to provide a kind of antibacterial pro-skin multilayer Chinese flax fabric, to solve The problem certainly proposing in above-mentioned background technology, the present invention designs ingenious, improves the market competitiveness.
To achieve these goals, the present invention is to realize by the following technical solutions：A kind of antibacterial pro-skin multilayer Chinese Flax fabric, including top layer, antibiotic layer, flax layer and bottom, described top layer is mixed by regenerated celulose fibre and pure cotton fiber Prevent from forming；Described antibiotic layer is made by carbon fiber and pure cotton fiber, and the surface of described antibiotic layer is received with one layer of silver system Nano antibacterial agent solution；Described flax layer is formed by flax fiber, nylon fiber, glass fibre and viscose fiber mixed weaving, Wherein flax fiber 50-70 weight portion, nylon fiber 10-20 weight portion, glass fibre 5-10 weight portion, viscose fiber 15-20 Weight portion；Described bottom is formed by weaving by cocoon fiber, elastomer and terylene long fibre；Described top layer, antibiotic layer, flax Layer and bottom link together by way of sewing up.
Further, described regenerated celulose fibre is a kind of viscose chitin fibre.
Further, when making antibiotic layer, first carbon fiber and pure cotton fiber are fabricated to semi-finished product cloth, then will Silver system nano antibacterial agent is pulverized in pulverizer, is ground into the silver system nano antibacterial agent powder that size is 300 mesh, then in stirring Add the water of certain part by weight in container, in the case that environment temperature is 24-28 ° of C, pour the silver system nanometer of certain part by weight into Anti-bacterial powders, then stirs 30-50min, forms silver system nano-antibacterial water slurry, then take semi-finished product cloth and be placed on a level Platform on, be poured on silver system nano-antibacterial water slurry on semi-finished product cloth uniformly, then strike off with scraper plate, in environment temperature be In the case of 24-28 ° of C, naturally place 2-3h, form antibiotic layer.
Further, in mixed solution, the weight portion of described water is between 60-80 weight portion, and described silver system nanometer resists The weight portion of microbial inoculum powder is between 20-40 weight portion.
Further, the mixed solution of every 100 weight portions contains water 73 weight portion, the mixed solution of every 100 weight portions In contain silver system nano antibacterial agent powder 27 weight portion.
Further, the antibiotic layer of every 100 weight portions contains flax fiber 60 weight portion, every 100 weight portions antibacterial Contain nylon fiber 15 weight portion in Ceng, the antibiotic layer of every 100 weight portions contains glass fibre 10 weight portion, every 100 weight The antibiotic layer of part contains viscose fiber 15 weight portion.
Further, in bottom, terylene long fibre is selected to make parallel, always as warp, cocoon fiber and elastomer Warp：9000, using 23# reed 3 denting, upper machine reed width is 180cm, upper machine filling density 54 piece/centimetre；Use 16 Heald frame one, along wearing, uses 16*16 alternative construction intertexture rule, floats long alternately change by longitude and latitude, forms bottom.
Beneficial effects of the present invention：The one antibacterial pro-skin multilayer Chinese flax fabric of the present invention, hemp fabric has moisture absorption, thoroughly Gas, pleasant, heat radiation, mildew-resistant, antibacterial, radioresistance, crease-resistant and without the multi-functional and feature such as scratchy, can be widely applied to extraordinary army Need the fields such as articles for use, high-grade dress ornament, home textile, footwear material, automotive trim, and fabrics for industrial use.
Viscose chitin fibre is to mix with cellulose with chitin, shitosan to be made by conventional wet spinning process Fiber.It has biologically active, biological degradability and biocompatibility, has excellent moisture-absorbing moisture-keeping function.Use chitin Fiber takes the function of deodorizing with cotton blended fabric, has vast potential for future development in terms of clothes decoration application and development.
Brief description
By reading the detailed description made non-limiting example with reference to the following drawings, the further feature of the present invention, Objects and advantages will become more apparent upon：
Fig. 1 is the structural representation of a kind of antibacterial pro-skin multilayer Chinese flax fabric of the present invention；
In figure：1-top layer, 2-antibiotic layer, 3-flax layer, 4-bottom.
Detailed description of the invention
For make the present invention realize technological means, creation characteristic, reach purpose and be easy to understand with effect, below in conjunction with Detailed description of the invention, is expanded on further the present invention.
Referring to Fig. 1, the present invention provides a kind of technical scheme：A kind of antibacterial pro-skin multilayer Chinese flax fabric, including top layer is the 1st, Antibiotic layer the 2nd, flax layer 3 and bottom 4, top layer 1 is prevented from forming by regenerated celulose fibre and pure cotton fiber mixing；Antibiotic layer 2 Being made by carbon fiber and pure cotton fiber, the surface of antibiotic layer 2 has one layer of silver system nano-antibacterial agent solution；Flax layer 3 by Flax fiber, nylon fiber, glass fibre and viscose fiber mixed weaving form, wherein flax fiber 50-70 weight portion, Buddhist nun Dragon fiber 10-20 weight portion, glass fibre 5-10 weight portion, viscose fiber 15-20 weight portion；Bottom 4 is by cocoon fiber, elasticity Fiber and terylene long fibre are formed by weaving；Top layer the 1st, antibiotic layer the 2nd, flax layer 3 and bottom 4 are connected to by way of sewing up Together.
Regenerated celulose fibre is a kind of viscose chitin fibre, and viscose chitin fibre is to gather with chitin, shell Sugar mixes the fiber made by conventional wet spinning process with cellulose.It has biologically active, biological degradability and biofacies Capacitive, has excellent moisture-absorbing moisture-keeping function.Chitin fiber and cotton blended fabric is used to take the function of deodorizing, in health care Apparel applications exploitation aspect has vast potential for future development.
When making antibiotic layer 2, first carbon fiber and pure cotton fiber are fabricated to semi-finished product cloth, then by silver system nanometer Antiseptic is pulverized in pulverizer, is ground into the silver system nano antibacterial agent powder that size is 300 mesh, then adds in stirring container Enter the water of certain part by weight, in the case that environment temperature is 24-28 ° of C, pour the silver system nano antibacterial agent powder of certain part by weight into End, then stirs 30-50min, forms silver system nano-antibacterial water slurry, then take semi-finished product cloth and be placed on the platform of a level On, it is poured on silver system nano-antibacterial water slurry on semi-finished product cloth uniformly, then strikes off with scraper plate, be 24-28 ° in environment temperature In the case of C, naturally place 2-3h, form antibiotic layer 2.
In mixed solution, the weight portion of water is between 60-80 weight portion, and the weight portion of silver system nano antibacterial agent powder exists Between 20-40 weight portion.
The mixed solution of every 100 weight portions contains water 73 weight portion, containing silver system in the mixed solution of every 100 weight portions Nano antibacterial agent powder 27 weight portion.
The antibiotic layer 2 of every 100 weight portions contains flax fiber 60 weight portion, the antibiotic layer 2 of every 100 weight portions contains Nylon fiber 15 weight portion, contains glass fibre 10 weight portion, every 100 weight portions antibacterial in the antibiotic layer 2 of every 100 weight portions Layer 2 contains viscose fiber 15 weight portion.
In bottom 4, selecting terylene long fibre as warp, cocoon fiber and elastomer make parallel, total warp：9000 Root, uses 23# reed 3 denting, and upper machine reed width is 180cm, upper machine filling density 54 piece/centimetre；Use 16 heald frames one suitable Wear, use 16*16 alternative construction intertexture rule, float long alternately change by longitude and latitude, form bottom 4.
The one antibacterial pro-skin multilayer Chinese flax fabric of the present invention, hemp fabric has moisture absorption, ventilative, pleasant, heat radiation, anti- Mould, antibacterial, radioresistance, crease-resistant and without the multi-functional and feature such as scratchy, can be widely applied to extraordinary military supplies articles for use, high-grade clothes Decorations, home textile, footwear material, automotive trim, and the field such as fabrics for industrial use.
The general principle of the present invention and principal character and advantages of the present invention are more than shown and described, for this area skill For art personnel, it is clear that the invention is not restricted to the details of above-mentioned one exemplary embodiment, and without departing substantially from the present invention spirit or In the case of essential characteristic, the present invention can be realized in other specific forms.Therefore, no matter from the point of view of which point, all should be by Embodiment regards exemplary as, and is nonrestrictive, the scope of the present invention by claims rather than on state Bright restriction, it is intended that include all changes falling in the implication of equivalency and scope of claim in the present invention In.Any reference in claim should be considered as limiting involved claim.
Although moreover, it will be appreciated that this specification is been described by according to embodiment, but not each embodiment only wraps Containing an independent technical scheme, this narrating mode of specification is only that for clarity sake those skilled in the art should Using specification as an entirety, the technical scheme in each embodiment also can form those skilled in the art through appropriately combined May be appreciated other embodiments.

Claims (7)

1. an antibacterial pro-skin multilayer Chinese flax fabric, including top layer, antibiotic layer, flax layer and bottom, it is characterised in that：Described Top layer is prevented from forming by regenerated celulose fibre and pure cotton fiber mixing；
Described antibiotic layer is made by carbon fiber and pure cotton fiber, and the surface of described antibiotic layer has one layer of silver system nano-antibacterial Agent solution；
Described flax layer is formed by flax fiber, nylon fiber, glass fibre and viscose fiber mixed weaving, and wherein flax is fine Dimension 50-70 weight portion, nylon fiber 10-20 weight portion, glass fibre 5-10 weight portion, viscose fiber 15-20 weight portion；
Described bottom is formed by weaving by cocoon fiber, elastomer and terylene long fibre；
Described top layer, antibiotic layer, flax layer and bottom link together by way of sewing up.
2. one according to claim 1 antibacterial pro-skin multilayer Chinese flax fabric, it is characterised in that：Described regenerated cellulose is fine Dimension is a kind of viscose chitin fibre.
3. one according to claim 1 antibacterial pro-skin multilayer Chinese flax fabric, it is characterised in that：When making antibiotic layer, First carbon fiber and pure cotton fiber are fabricated to semi-finished product cloth, then silver system nano antibacterial agent are pulverized in pulverizer, powder It is broken into the silver system nano antibacterial agent powder that size is 300 mesh, in stirring container, then add the water of certain part by weight, at environment In the case that temperature is 24-28 ° of C, pours the silver system nano antibacterial agent powder of certain part by weight into, then stir 30-50min, shape Become silver system nano-antibacterial water slurry, then take semi-finished product cloth and be placed on the platform of a level, uniformly by silver system nano-antibacterial Water slurry is poured on semi-finished product cloth, then strikes off with scraper plate, in the case that environment temperature is 24-28 ° of C, naturally places 2-3h, Form antibiotic layer.
4. one according to claim 2 antibacterial pro-skin multilayer Chinese flax fabric, it is characterised in that：In mixed solution, institute State the weight portion of water between 60-80 weight portion, the weight portion of described silver system nano antibacterial agent powder 20-40 weight portion it Between.
5. one according to claim 4 antibacterial pro-skin multilayer Chinese flax fabric, it is characterised in that：Mixing of every 100 weight portions Close and solution contains water 73 weight portion, the mixed solution of every 100 weight portions contains silver system nano antibacterial agent powder 27 weight portion.
6. one according to claim 1 antibacterial pro-skin multilayer Chinese flax fabric, it is characterised in that：Resisting of every 100 weight portions Bacterium layer contains flax fiber 60 weight portion, the antibiotic layer of every 100 weight portions contains nylon fiber 15 weight portion, every 100 weights The antibiotic layer of amount part contains glass fibre 10 weight portion, the antibiotic layer of every 100 weight portions contains viscose fiber 15 weight portion.
7. one according to claim 1 antibacterial pro-skin multilayer Chinese flax fabric, it is characterised in that：In bottom, selection is washed Synthetic fibre long fibre is as warp, and cocoon fiber and elastomer make parallel, total warp：9000, use 23# reed 3 denting, Upper machine reed width is 180cm, upper machine filling density 54 piece/centimetre；Use 16 heald frames one along wearing, use 16*16 alternative construction to hand over Knit rule, float long alternately change by longitude and latitude, form bottom.
CN201610773597.2A 2016-08-31 2016-08-31 Antibacterial skin-friendly multilayer Chinese hemp fabric Pending CN106427100A (en)