CN106423770A - Process for spraying vapor by iron - Google Patents
Process for spraying vapor by iron Download PDFInfo
- Publication number
- CN106423770A CN106423770A CN201610946115.9A CN201610946115A CN106423770A CN 106423770 A CN106423770 A CN 106423770A CN 201610946115 A CN201610946115 A CN 201610946115A CN 106423770 A CN106423770 A CN 106423770A
- Authority
- CN
- China
- Prior art keywords
- iron
- spraying
- heating
- soda pop
- electrifying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a process for spraying vapor by an iron. The process comprises the following steps: (1) abrasively blasting: abrasively blasting an inner cavity of a vapor chamber of the iron and coarsening the surface of the inner cavity of the vapor chamber; (2) putting the iron after abrasively blasting onto an electrifying heating device on a rotating table and making the preparation before the electrifying heating of the iron; (3) setting the electrifying heating time according to the iron in different power; (4) electrifying and heating the iron and stopping electrifying and heating till reaching the preset time; (5) spraying: spraying the vapor onto the surface of the inner cavity of the vapor chamber, thereby forming a spraying coating. According to the process provided by the invention, the electrifying heating device with the rotating table is adopted for replacing the traditional oven for heating, so that the heating and spraying of the iron can be synchronously performed on a same station; the processing cost is greatly lowered, and the production efficiency is increased; the operation is convenient; the abrasive blasting before electrifying heating is performed, so that the adhering force of the vapor is increased and the quality after the vapor spraying is stable and reliable.
Description
Technical field
The present invention relates to iron machining field technology, refers in particular to a kind of technique of iron sprayingization soda pop.
Background technology
Vaporization water, is vaporization agent again, changes soda pop, water diffusant etc..In the call of Japan, Taiwan electric apparatus manufacture it is
Diffusant, in continent, electric apparatus manufacture is generally vaporization agent, changes soda pop, aerosol etc..For steam generation electric equipment products such as electricity
Flatiron, garment steamer, steam floor-cleaning machine etc..The effect of diffusant is exactly the heating part of the steam generation cavity in electric equipment products
Position, used as a kind of coating for producing water vapour.Diffusant or the coating of vaporization agent, as the term suggests, will exactly spray or drip in
The water of the coating is rapidly spread apart along coated surface area, the hydrone for spreading apart just can promptly absorbing cavity body heat content and by vapour
It is melted into as water vapour.Water vapour after vaporization is quick because of the increase of pressure to be sprayed from electrical equipment base plate or discharges, heating and
The object that moistening will be pressed or be cleaned.
At present, the traditional handicraft of iron bottom plate sprayingization soda pop is the temperature required for base plate is heated in oven
At once carrying out of workpiece soda pop is sprayed afterwards, not only processing cost is very high for the technique of this operation, and working (machining) efficiency is low, operates also not
Convenient, and the quality that changes after soda pop spraying is unstable.
Content of the invention
In view of this, the present invention is for the disappearance of prior art presence, and its main purpose is to provide a kind of iron sprayingization
The technique of soda pop, its can the existing change soda pop spraying coating process high processing costs of effectively solving, working (machining) efficiency be low, inconvenient operation simultaneously
And change the unstable problem of the quality after soda pop spraying.
For achieving the above object, the present invention is using as purgation technical scheme：
A kind of technique of iron sprayingization soda pop, includes following steps：
（1）Sandblasting：Sandblasting is carried out to iron vaporium inner chamber, is roughened with the surface of internal cavity to vaporium；
（2）The iron for having sprayed sand is positioned on the electrified regulation equipment of turntable, iron is carried out before electrified regulation and prepare；
（3）Iron according to different capacity carries out the setting of electrified regulation time；
（4）Electrified regulation is carried out to iron, until it reaches setting time stops electrified regulation；
（5）Spraying：Coating film is formed to surface the carrying out soda pop spraying of vaporium inner chamber.
As a kind of preferred version, the step（1）Middle sandblasting adopts 60# steel sand, and the iron for having sprayed sand is little less than 12
When.
As a kind of preferred version, the step（3）The middle electrified regulation time is set in 35s-99s, it is ensured that iron surface
Temperature reaches 140 DEG C -160 DEG C.
As a kind of preferred version, the step（5）Middleization soda pop and water open dilute ratio by 1:1 open dilute, coating film
Thickness is 40 μm -60 μm.
The present invention has clear advantage and beneficial effect compared with prior art, specifically, by technique scheme
Understand：
Present invention process instead of the oven heating of tradition so that the heating of iron using the electrified regulation equipment with turntable
Synchronously carry out with being sprayed on same station, greatly reduce processing cost and improve production efficiency, operation is convenient to, and
Through blasting treatment before electrified regulation, the adhesive force of increased soda pop so that change the stay in grade reliability after soda pop spraying.
Specific embodiment
The present invention discloses a kind of technique of iron sprayingization soda pop, includes following steps：
（1）Sandblasting：Sandblasting is carried out to iron vaporium inner chamber, is roughened with the surface of internal cavity to vaporium, enhancingization soda pop
The adhesive force of spraying；In the present embodiment, sandblasting adopts 60# steel sand, has sprayed the iron of sand less than 12 hours.
（2）The iron for having sprayed sand is positioned on the electrified regulation equipment of turntable, iron is carried out accurate before electrified regulation
Standby.
（3）Iron according to different capacity carries out the setting of electrified regulation time；In the present embodiment, the electrified regulation time
It is set in 35s-99s, it is ensured that iron surface temperature reaches 140 DEG C -160 DEG C, because this equipment is the operation equipment of rotary table,
Workman is in the time of spraying operation process, and the iron of other stations is synchronous in heated condition, drastically increases working (machining) efficiency.
（4）Electrified regulation is carried out to iron, until it reaches setting time stops energising, reaches the temperature of surface of the work
140 DEG C -160 DEG C, the spraying of meeting soda pop is required.
（5）Spraying：Coating film is formed to surface the carrying out soda pop spraying of vaporium inner chamber, in the present embodiment, is changed
Soda pop and water open dilute ratio by 1:1 open dilute, the thickness of coating film be.
The design focal point of the present invention is：Present invention process instead of tradition using the electrified regulation equipment with turntable
Oven heating so that the heating of iron and being sprayed on same station is synchronously carried out, and is greatly reduced processing cost and is improved life
Efficiency is produced, operation is convenient to, and through blasting treatment, the adhesive force of increased soda pop before electrified regulation so that change
Stay in grade reliability after soda pop spraying.
The above, be only presently preferred embodiments of the present invention, not the technical scope of the present invention imposed any restrictions,
Therefore any trickle amendment, equivalent variations and the modification made to above example by every technical spirit according to the present invention, all still
Belong in the range of technical solution of the present invention.
Claims (4)
1. a kind of technique of iron sprayingization soda pop, it is characterised in that：Include following steps：
（1）Sandblasting：Sandblasting is carried out to iron vaporium inner chamber, is roughened with the surface of internal cavity to vaporium；
（2）The iron for having sprayed sand is positioned on the electrified regulation equipment of turntable, iron is carried out before electrified regulation and prepare；
（3）Iron according to different capacity carries out the setting of electrified regulation time；
（4）Electrified regulation is carried out to iron, until it reaches setting time stops electrified regulation；
（5）Spraying：Coating film is formed to surface the carrying out soda pop spraying of vaporium inner chamber.
2. the technique of a kind of iron sprayingization soda pop according to claim 1, it is characterised in that：The step（1）Middle spray
Sand adopts 60# steel sand, has sprayed the iron of sand less than 12 hours.
3. the technique of a kind of iron sprayingization soda pop according to claim 1, it is characterised in that：The step（3）In lead to
The electrical heating time is set in 35s-99s, it is ensured that iron surface temperature reaches 140 DEG C -160 DEG C.
4. the technique of a kind of iron sprayingization soda pop according to claim 1, it is characterised in that：The step（5）Middleization
Soda pop and water open dilute ratio by 1:1 open dilute, the thickness of coating film be.