CN106398041A - Building template - Google Patents
Building template Download PDFInfo
- Publication number
- CN106398041A CN106398041A CN201610798671.6A CN201610798671A CN106398041A CN 106398041 A CN106398041 A CN 106398041A CN 201610798671 A CN201610798671 A CN 201610798671A CN 106398041 A CN106398041 A CN 106398041A
- Authority
- CN
- China
- Prior art keywords
- parts
- template
- building template
- clip
- side panel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a building template. The building template comprises a template and a template card. The template card is located below the template. The template comprises a flat plate and side panels. The side panels are located below the flat plate. The side panels are integrated with the flat plate and a square through hole is arranged in the flat plate. The top surface of the square through hole is arc. The lower end of the side panel is provided with a hook body. The hook body is integrated with the side panel. The template card is hooked by the hook body. A pushing support is arranged between the top end of the template card and the hook body. The inner side of the template card is provided with a hook-shaped groove. A bar-shaped spacing body is arranged in the hook-shaped groove. The outer side of the template card is provided with a mounting/dismounting lug. The mounting/dismounting lug is provided with a lug hole. The outer side of the template card is provided with a reinforcing rib. The building template has the advantages of simple structure, strong load-bearing ability, resource saving, low cost, convenient disassembly and corrosion resistance.
Description
Technical field
Present invention relates particularly to a kind of building template.
Background technology
Building template is a kind of temporary supporting structure, makes by design requirement, makes xoncrete structure, component by regulation
Position, physical dimension shape, and keep its tram, and bear building template deadweight and effect external loads thereon.
Building engineering shuttering material used by traditional casting cement crossbeam, column, plane generally adopts wooden template, bamboo glue
Plate and steel template.Wooden template application is earliest, but due to consuming a large amount of timber, and dismounting template easily cleaves, secondary use
Must be little to change greatly, reuse number of times at 4-6 time, not only waste the forest reserves, also higher to the proportion of goods damageds of resource.Bamboo glue
Plate access times at 2-3 time, formwork reinforcement point intensive it is necessary at 10 centimeters about, otherwise just having prominent position, and make
The template making various models is also troublesome, not only time-consuming, laborious, also waste of resource.The steel template using on the market is although save
About a large amount of timber it is possible to repeatedly use, but it also have many not as people's will in place of, its cost is high, and heavy, be subject to
Weight limits, and lifts very inconvenient in construction, when splicing block number is more, time-consuming, laborious;Again due between steel template and cement
There is certain affinity, dismounting is relatively difficult, easily produces butcher cuts to cement products surface during dismounting, affects quality;Additionally, steel
Template is also easy to corrosion, the secondary use of impact template.
At present, the low intensity of the building template of existing material preparation, does not meet the intensity requirement of use.
Content of the invention
For overcoming the problems of the prior art, the invention provides a kind of structure is simple, weight capacity is strong, both saved money
Source, low cost and convenient disassembly, corrosion resistant building template.
The technology of employing and method in order to solve the problems, such as the above-mentioned present invention are as follows:
A kind of building template, including template and template clip, described template clip is located at below template, and described template includes flat
Plate and side panel, described side panel is located at the lower section of flat board, and described side panel is arranged for integral type with flat board, inside described flat board
It is provided with square through hole, the top surface of described square through hole is set to arc, described side panel lower end is provided with crozier, described hook
Shape body and side panel are that integral type is arranged, and described template clip is linked up with hook-shaped body phase, the described top of template clip and crozier
Between be provided with pushing tow support, be provided with hook-shaped groove inside described template clip, described hook-shaped groove is internally provided with bar shaped limit body,
The outside of described template clip is provided with dismounting ear, described dismounting ear is provided with earhole, is provided with reinforcement outside described template clip
Muscle.
Further, described building template is made up of the raw material of following weight portion:Polrvinyl chloride 60-100 part, chlorinated polyethylene
Alkene 5-15 part, calcium powder 45-50 part, Pulvis Talci 10-15 part, wood powder 10-15 part, Polyethylene Glycol 3-5 part, Calcium Carbonate 1-2 part, oxidation
Tissuemat E 1.2-2 part, Ammonium persulfate. 1.2-2 part, HLD 1-2 part, polypropylene grafted butyl acrylate copolymer
16-18 part, dibenzylatiooluene 1-2 part, glass fibre 10-20 part, phenyl salicylate 1-2 part, azodicarbonamide 1-2
Part, sodium bicarbonate 1.4-2 part.
Further, described template is made using PVC material, and PVC material neither absorbs water deformation, also not adhesive product table
Face, and impact resistance corrosion, quietly performance good it is ensured that the quality of product.
Further, it is connected by template clip between described template and template, can be by two templates by template clip
Couple together.
Further, described side panel is provided with more than one piece, is adjusted also dependent on practical situation.
Further, the arched setting of profile of described pushing tow support, is adjusted also dependent on practical situation.
Further, described building template is made up of the raw material of following weight portion:60 parts of polrvinyl chloride, chlorinated polyethylene 5
Part, 45 parts of calcium powder, 10 parts of Pulvis Talci, 10 parts of wood powder, 3 parts of Polyethylene Glycol, 1 part of Calcium Carbonate, 1.2 parts of OPE, over cure
1.2 parts of sour ammonium, 1 part of HLD, 16 parts of polypropylene grafted butyl acrylate copolymer, 1 part of dibenzylatiooluene, glass
10 parts of glass fiber, 1 part of phenyl salicylate, 1 part of azodicarbonamide, 1.4 parts of sodium bicarbonate.
Further, described building template is made up of the raw material of following weight portion:100 parts of polrvinyl chloride, chlorinated polyethylene
15 parts, 50 parts of calcium powder, 15 parts of Pulvis Talci, 15 parts of wood powder, 5 parts of Polyethylene Glycol, 2 parts of Calcium Carbonate, 2 parts of OPE, over cure
2 parts of sour ammonium, 2 parts of HLD, 18 parts of polypropylene grafted butyl acrylate copolymer, 2 parts of dibenzylatiooluene, glass
20 parts of fiber, 2 parts of phenyl salicylate, 2 parts of azodicarbonamide, 2 parts of sodium bicarbonate.
Further, described building template is made up of the raw material of following weight portion:80 parts of polrvinyl chloride, chlorinated polyethylene 10
Part, 48 parts of calcium powder, 13 parts of Pulvis Talci, 13 parts of wood powder, 4 parts of Polyethylene Glycol, 1.5 parts of Calcium Carbonate, 1.6 parts of OPE, mistake
1.6 parts of ammonium sulfate, 1.5 parts of HLD, 17 parts of polypropylene grafted butyl acrylate copolymer, dibenzylatiooluene
1.5 parts, 15 parts of glass fibre, 1.5 parts of phenyl salicylate, 1.5 parts of azodicarbonamide, 1.7 parts of sodium bicarbonate.
Beneficial effects of the present invention are:Because the upper side wall of square through hole is set to arc, and the top setting of template clip
There is pushing tow support so that the weight capacity of template strengthens, the connection between template is also more firm;Because template adopts PVC material
Material manufactures, neither water suction deformation, also not adhesive product surface, and impact resistance corrosion, quietly performance good it is ensured that the matter of product
Amount;Because the outside of template clip is provided with dismounting ear, dismounting ear is provided with earhole, and template and template clip are all using PVC material
Material manufactures, and compared with steel template, mass ratio is lighter, therefore, in that context it may be convenient to dismounting when using template, saves time, laborsaving,
Improve the efficiency of construction;There is structure simultaneously simple, cheap, can repeatedly use, can be with recycling profit
With saving a large amount of timber, being conducive to the protection to the forest reserves;Because preparation technology adopts Calcium Carbonate, Polyethylene Glycol, over cure
Prepared by the combinations of materials such as sour ammonium, can effectively improve the intensity of building template so that building template meets use intensity requirement.
Brief description
Fig. 1 is a kind of structural representation of building template of the present invention;
Fig. 2 is the structural representation of the template clip of the present invention.
Specific embodiment
With reference to embodiment, the present invention is described in further detail with accompanying drawing, but they are not to skill of the present invention
The restriction of art scheme, based on present invention teach that any conversion of being made, all falls within protection scope of the present invention.
Embodiment 1
Refering to shown in 1, a kind of building template, including template 1 and template clip 2, described template clip 2 is located at below template 1, institute
State template 1 and include flat board 3 and side panel 4, described side panel 4 is located at the lower section of flat board 3, described side panel 4 and flat board 3 are one
Body formula is arranged, and described flat board 3 is internally provided with square through hole 7, and the top surface of described square through hole 7 is set to arc, described side
Plate 4 lower end is provided with crozier 5, and described crozier 5 and side panel 4 are integral type setting, described template clip 2 and crozier 5 phase
Hook, is provided with pushing tow support 6, is provided with hook-type inside described template clip 2 between the top of described template clip 2 and crozier 5
Groove 8, described hook-shaped groove 8 is internally provided with bar shaped limit body 11, and the outside of described template clip 2 is provided with dismounting ear 9, described dismounting
Earhole 10 is provided with ear 9, outside described template clip 2, is provided with reinforcement 12.
Described building template is made up of the raw material of following weight portion:60 parts of polrvinyl chloride, 5 parts of chlorinated polyethylene, calcium powder 45
Part, 10 parts of Pulvis Talci, 10 parts of wood powder, 3 parts of Polyethylene Glycol, 1 part of Calcium Carbonate, 1.2 parts of OPE, 1.2 parts of Ammonium persulfate.,
1 part of HLD, 16 parts of polypropylene grafted butyl acrylate copolymer, 1 part of dibenzylatiooluene, glass fibre 10
Part, 1 part of phenyl salicylate, 1 part of azodicarbonamide, 1.4 parts of sodium bicarbonate.
Described template 1 is made using PVC material, and PVC material neither absorbs water deformation, also not adhesive product surface, and resistance to punching
Hit corrosion, quietly performance good it is ensured that the quality of product.
It is connected by template clip between described template 1 and template 1, two templates can be connected by template clip
Come.
Described side panel 4 is provided with more than one piece, is adjusted also dependent on practical situation.
The arched setting of profile of described pushing tow support 6, is adjusted also dependent on practical situation.
Wherein, the preparation method of building board is as follows:
1) 10 parts of glass fibre is put into fire 1min in 420 DEG C DEG C of heating furnace, standby;
2) by step 1) 10 parts of glass fibre after fire is put into containing mass concentration is 1% silane coupler and quality is dense
Spend and put into 120 DEG C of DEG C of drying in convection oven after taking-up in 1 hour for soaking in the aqueous solution of 0.5% thermoplastic film formers, standby;
3) 10 parts of Pulvis Talci is put into mass concentration and stir 15min in blender for 1% silane coupler aqueous solution, standby
With;
4) batch mixer is warming up to 90 DEG C, adds 45 parts of calcium powder, 10 parts of wood powder, then sequentially add chlorinated polyethylene 60
Part, 10 parts of Pulvis Talci, 3 parts of Polyethylene Glycol, 1 part of Calcium Carbonate, 1.2 parts of OPE, 1.2 parts of Ammonium persulfate., resinousness chlorine
1 part of fourth glue, 16 parts of polypropylene grafted butyl acrylate copolymer, 1 part of dibenzylatiooluene, 10 parts of glass fibre, azo two
0.6 part of Methanamide, 1.4 parts of sodium bicarbonate, 1 part of phenyl salicylate, it is gradually heating to 140 DEG C, carry out mixing 10min, be cooled to
30 DEG C, standby;
5) will be placed in double screw extruder after compound, extrusion plasticizing agglutination material, standby;
6) by gluey material traction to compression molding forming machine mould, it is pressed into sheet material, cooled, sizing forms building template,
?.
Embodiment 2
Refering to shown in 1, a kind of building template, including template 1 and template clip 2, described template clip 2 is located at below template 1, institute
State template 1 and include flat board 3 and side panel 4, described side panel 4 is located at the lower section of flat board 3, described side panel 4 and flat board 3 are one
Body formula is arranged, and described flat board 3 is internally provided with square through hole 7, and the top surface of described square through hole 7 is set to arc, described side
Plate 4 lower end is provided with crozier 5, and described crozier 5 and side panel 4 are integral type setting, described template clip 2 and crozier 5 phase
Hook, is provided with pushing tow support 6, is provided with hook-type inside described template clip 2 between the top of described template clip 2 and crozier 5
Groove 8, described hook-shaped groove 8 is internally provided with bar shaped limit body 11, and the outside of described template clip 2 is provided with dismounting ear 9, described dismounting
Earhole 10 is provided with ear 9, outside described template clip 2, is provided with reinforcement 12.
Described building template is made up of the raw material of following weight portion:100 parts of polrvinyl chloride, 15 parts of chlorinated polyethylene, calcium powder
50 parts, 15 parts of Pulvis Talci, 15 parts of wood powder, 5 parts of Polyethylene Glycol, 2 parts of Calcium Carbonate, 2 parts of OPE, 2 parts of Ammonium persulfate., tree
2 parts of lipid neoprene, 18 parts of polypropylene grafted butyl acrylate copolymer, 2 parts of dibenzylatiooluene, 20 parts of glass fibre,
2 parts of phenyl salicylate, 2 parts of azodicarbonamide, 2 parts of sodium bicarbonate.
Described template 1 is made using PVC material, and PVC material neither absorbs water deformation, also not adhesive product surface, and resistance to punching
Hit corrosion, quietly performance good it is ensured that the quality of product.
It is connected by template clip between described template 1 and template 1, two templates can be connected by template clip
Come.
Described side panel 4 is provided with more than one piece, is adjusted also dependent on practical situation.
The arched setting of profile of described pushing tow support 6, is adjusted also dependent on practical situation.
Wherein, the preparation method of building board is as follows:
1) 20 parts of glass fibre is put into fire 3min in 580 DEG C of heating furnace, standby;
2) by step 1) 20 parts of glass fibre after fire is put into containing mass concentration is 1% silane coupler and quality is dense
Spend and put into 150 DEG C of drying in convection oven after 1-2 hour is taken out for soaking in the aqueous solution of 0.5% thermoplastic film formers, standby;
3) 15 parts of Pulvis Talci is put into mass concentration and stir 15min in blender for 1% silane coupler aqueous solution, standby
With;
4) batch mixer is warming up to 90 DEG C, adds 50 parts of calcium powder, 15 parts of wood powder, then sequentially add chlorinated polyethylene 100
Part, 15 parts of Pulvis Talci, 5 parts of Polyethylene Glycol, 2 parts of Calcium Carbonate, 2 parts of OPE, 2 parts of Ammonium persulfate., HLD 2
Part, 18 parts of polypropylene grafted butyl acrylate copolymer, 2 parts of dibenzylatiooluene, 20 parts of glass fibre, azodicarbonamide
1 part, 2 parts of sodium bicarbonate, 2 parts of phenyl salicylate, it is gradually heating to 140 DEG C, carry out mixing 20min, be cooled to 45 DEG C, standby;
5) will be placed in double screw extruder after compound, extrusion plasticizing agglutination material, standby;
6) by gluey material traction to compression molding forming machine mould, it is pressed into sheet material, cooled, sizing forms building template,
?.
Embodiment 3
Refering to shown in 1, a kind of building template, including template 1 and template clip 2, described template clip 2 is located at below template 1, institute
State template 1 and include flat board 3 and side panel 4, described side panel 4 is located at the lower section of flat board 3, described side panel 4 and flat board 3 are one
Body formula is arranged, and described flat board 3 is internally provided with square through hole 7, and the top surface of described square through hole 7 is set to arc, described side
Plate 4 lower end is provided with crozier 5, and described crozier 5 and side panel 4 are integral type setting, described template clip 2 and crozier 5 phase
Hook, is provided with pushing tow support 6, is provided with hook-type inside described template clip 2 between the top of described template clip 2 and crozier 5
Groove 8, described hook-shaped groove 8 is internally provided with bar shaped limit body 11, and the outside of described template clip 2 is provided with dismounting ear 9, described dismounting
Earhole 10 is provided with ear 9, outside described template clip 2, is provided with reinforcement 12.
Described building template is made up of the raw material of following weight portion:80 parts of polrvinyl chloride, 10 parts of chlorinated polyethylene, calcium powder 48
Part, 13 parts of Pulvis Talci, 13 parts of wood powder, 4 parts of Polyethylene Glycol, 1.5 parts of Calcium Carbonate, 1.6 parts of OPE, Ammonium persulfate. 1.6
Part, 1.5 parts of HLD, 17 parts of polypropylene grafted butyl acrylate copolymer, 1.5 parts of dibenzylatiooluene, glass
15 parts of fiber, 1.5 parts of phenyl salicylate, 1.5 parts of azodicarbonamide, 1.7 parts of sodium bicarbonate.
Described template 1 is made using PVC material, and PVC material neither absorbs water deformation, also not adhesive product surface, and resistance to punching
Hit corrosion, quietly performance good it is ensured that the quality of product.
It is connected by template clip between described template 1 and template 1, two templates can be connected by template clip
Come.
Described side panel 4 is provided with more than one piece, is adjusted also dependent on practical situation.
The arched setting of profile of described pushing tow support 6, is adjusted also dependent on practical situation.
Wherein, the preparation method of building board is as follows:
1) 15 parts of glass fibre is put into fire 2min in 500 DEG C of heating furnace, standby;
2) by step 1) the glass fibre 10-20 part after fire is put into containing mass concentration is 1% silane coupler and matter
Measure to soak in the aqueous solution that concentration is 0.5% thermoplastic film formers and put into 135 DEG C of drying in convection oven after 1-2 hour is taken out,
Standby;
3) 13 parts of Pulvis Talci is put into mass concentration and stir 15min in blender for 1% silane coupler aqueous solution, standby
With;
4) batch mixer is warming up to 90 DEG C, adds 48 parts of calcium powder, 13 parts of wood powder, then sequentially add chlorinated polyethylene 80
Part, 13 parts of Pulvis Talci, 4 parts of Polyethylene Glycol, 1.5 parts of Calcium Carbonate, 1.6 parts of OPE, 1.6 parts of Ammonium persulfate., resinousness
1.5 parts of neoprene, 17 parts of polypropylene grafted butyl acrylate copolymer, 1.5 parts of dibenzylatiooluene, 15 parts of glass fibre,
0.8 part of azodicarbonamide, 1.7 parts of sodium bicarbonate, 1.5 parts of phenyl salicylate, it is gradually heating to 140 DEG C, mixed
15min, is cooled to 40 DEG C, standby;
5) will be placed in double screw extruder after compound, extrusion plasticizing agglutination material, standby;
6) by gluey material traction to compression molding forming machine mould, it is pressed into sheet material, cooled, sizing forms building template,
?.
Experimental example:
Experimental subject:Experimental group selects a kind of 50 pieces of building template of the present invention, and matched group is from building of commonly using on the market
Build 50 pieces of sheet material;
Experimental period:Experimental period is 2 months;
Experimental technique:Carry out the bending strength experiment of equal extent respectively, and impact test;
Criterion:
Invalid:Gross distortion and infringement phenomenon occur;
Effectively:Gross distortion or infringement phenomenon occur;
Effective:No deform, harmless phenomenon;
Experimental subject | Invalid | Effectively | Effective |
Experimental group | 5 | 10 | 35 |
Matched group | 25 | 20 | 5 |
Beneficial effects of the present invention are:Because the upper side wall of square through hole is set to arc, and the top setting of template clip
There is pushing tow support so that the weight capacity of template strengthens, the connection between template is also more firm;Because template adopts PVC material
Material manufactures, neither water suction deformation, also not adhesive product surface, and impact resistance corrosion, quietly performance good it is ensured that the matter of product
Amount;Because the outside of template clip is provided with dismounting ear, dismounting ear is provided with earhole, and template and template clip are all using PVC material
Material manufactures, and compared with steel template, mass ratio is lighter, therefore, in that context it may be convenient to dismounting when using template, saves time, laborsaving,
Improve the efficiency of construction;There is structure simultaneously simple, cheap, can repeatedly use, can be with recycling profit
With saving a large amount of timber, being conducive to the protection to the forest reserves;Because preparation technology adopts Calcium Carbonate, Polyethylene Glycol, over cure
Prepared by the combinations of materials such as sour ammonium, can effectively improve the intensity of building template so that building template meets use intensity requirement.
The above, the only specific embodiment of the present invention, but protection scope of the present invention is not limited thereto, and any
The change or replacement expected without creative work, all should be included within the scope of the present invention, therefore, the present invention's
Protection domain should be defined by the protection domain that claims are limited.
Claims (9)
1. a kind of building template it is characterised in that:Including template and template clip, described template clip is located at below template, described mould
Plate includes flat board and side panel, and described side panel is located at the lower section of flat board, and described side panel is arranged for integral type with flat board, institute
State flat board and be internally provided with square through hole, the top surface of described square through hole is set to arc, described side panel lower end is provided with hook
Shape body, described crozier and side panel are that integral type is arranged, and described template clip is linked up with hook-shaped body phase, the top of described template clip
It is provided with pushing tow support between end and crozier, be provided with hook-shaped groove inside described template clip, described hook-shaped groove is internally provided with
Bar shaped limit body, the outside of described template clip is provided with dismounting ear, described dismounting ear is provided with earhole, outside described template clip
It is provided with reinforcement.
2. building template according to claim 1 it is characterised in that:Described building template is by the raw material system of following weight portion
Become:Polrvinyl chloride 60-100 part, chlorinated polyethylene 5-15 part, calcium powder 45-50 part, Pulvis Talci 10-15 part, wood powder 10-15 part, poly-
Ethylene glycol 3-5 part, Calcium Carbonate 1-2 part, OPE 1.2-2 part, Ammonium persulfate. 1.2-2 part, HLD 1-2
Part, polypropylene grafted butyl acrylate copolymer 16-18 part, dibenzylatiooluene 1-2 part, glass fibre 10-20 part, bigcatkin willow
Acid phenenyl ester 1-2 part, azodicarbonamide 1-2 part, sodium bicarbonate 1.4-2 part.
3. building template according to claim 1 it is characterised in that:Described template is made using PVC material.
4. building template according to claim 1 it is characterised in that:It is connected by template clip between described template and template
Connect.
5. building template according to claim 1 it is characterised in that:Described side panel is provided with more than one piece.
6. building template according to claim 1 it is characterised in that:The arched setting of profile of described pushing tow support.
7. building template according to claim 1 it is characterised in that:Described building template is by the raw material system of following weight portion
Become:60 parts of polrvinyl chloride, 5 parts of chlorinated polyethylene, 45 parts of calcium powder, 10 parts of Pulvis Talci, 10 parts of wood powder, 3 parts of Polyethylene Glycol, Calcium Carbonate
1 part, 1.2 parts of OPE, 1.2 parts of Ammonium persulfate., 1 part of HLD, polypropylene grafted butyl acrylate copolymerization
16 parts of thing, 1 part of dibenzylatiooluene, 10 parts of glass fibre, 1 part of phenyl salicylate, 1 part of azodicarbonamide, sodium bicarbonate
1.4 part.
8. building template according to claim 1 it is characterised in that:Described building template is by the raw material system of following weight portion
Become:100 parts of polrvinyl chloride, 15 parts of chlorinated polyethylene, 50 parts of calcium powder, 15 parts of Pulvis Talci, 15 parts of wood powder, 5 parts of Polyethylene Glycol, carbonic acid
2 parts of calcium, 2 parts of OPE, 2 parts of Ammonium persulfate., 2 parts of HLD, polypropylene grafted butyl acrylate copolymer
18 parts, 2 parts of dibenzylatiooluene, 20 parts of glass fibre, 2 parts of phenyl salicylate, 2 parts of azodicarbonamide, sodium bicarbonate 2
Part.
9. building template according to claim 1 it is characterised in that:Described building template is by the raw material system of following weight portion
Become:80 parts of polrvinyl chloride, 10 parts of chlorinated polyethylene, 48 parts of calcium powder, 13 parts of Pulvis Talci, 13 parts of wood powder, 4 parts of Polyethylene Glycol, carbonic acid
1.5 parts of calcium, 1.6 parts of OPE, 1.6 parts of Ammonium persulfate., 1.5 parts of HLD, polypropylene grafted acrylic acid fourth
17 parts of ester copolymer, 1.5 parts of dibenzylatiooluene, 15 parts of glass fibre, 1.5 parts of phenyl salicylate, azodicarbonamide 1.5
Part, 1.7 parts of sodium bicarbonate.