CN106391715B - A kind of preparation process of martensitic seamless steel pipe - Google Patents
A kind of preparation process of martensitic seamless steel pipe Download PDFInfo
- Publication number
- CN106391715B CN106391715B CN201610759510.6A CN201610759510A CN106391715B CN 106391715 B CN106391715 B CN 106391715B CN 201610759510 A CN201610759510 A CN 201610759510A CN 106391715 B CN106391715 B CN 106391715B
- Authority
- CN
- China
- Prior art keywords
- steel pipe
- pipe
- temperature
- acid
- preparation process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of preparation processes of martensitic seamless steel pipe, comprise the following steps:1)Martensite steel pipe pipe centering, then into eleven punch 11;2)Pipe after perforation is made annealing treatment;3)Pickling is carried out with pickle to the pipe after annealing, then carries out phosphatization, saponification and lubricated successively;Saponification liquor used in the saponification process includes petroleum sodium sulfonate, triethanolamine, oleic acid, dodecenylsuccinic acid, benzotriazole, machinery oil;4)Pipe after lubricated is subjected to hot rolling, obtains martensite steel pipe finished product, the processing step of the ageing treatment is put into for a. steel pipe pipes in stove, and temperature rises to 45 60 DEG C, keeps the temperature 0.2 0.5h;B. in-furnace temperature is risen to 150 180 DEG C, handles 0.5 1h;C. in-furnace temperature is down to 110 120 DEG C, keeps the temperature 1 1.5h.The present invention controls the parameter in each step, the bright and clean no pit point of martensite steel pipe surface, quality is good, promotes product lumber recovery, reduces production cost by rationally setting processing step.
Description
Technical field
Preparation field more particularly to a kind of preparation process of martensitic seamless steel pipe the present invention relates to steel pipe.
Background technology
Martensitic stain less steel has good mechanical property and high-temperature oxidation resistance and corrosion resistance, so application range
It is very wide, but the preparation difficulty of martensite steel pipe is big, obtained martensite steel pipe is of poor quality, is not durable, Patent No.
The Chinese patent of CN102699103 discloses a kind of preparation method of 20CrMo steel pipes, processing step letter on October 3rd, 2012
It is short, it is beneficial to energy saving consumption, but in production process, often it is present with steel pipe internal-surface or outer surface longitudinal cracking, once
Cracking just can not carry out subsequent processing, cause the waste of steel, and martensite steel pipe obtained, hardness is very big, toughness
It is small, it is difficult to process again.For this purpose, applicant applied for a kind of horse of Application No. 2013105081890 on January 25th, 2013
The preparation method of family name's body steel pipe by the improvement to technique, solves the problems, such as the production of martensite steel pipe's production, and production cost is low,
Obtained martensite tube quality is good, and hardness is low, and toughness is high, is suitble to it is further processed.But the matter of Malpighian tube
Amount is still undesirable, and surface point is on the high side, and product fraction defective is higher.
The content of the invention
For overcome the deficiencies in the prior art, the present invention provides a kind of preparation process of martensitic seamless steel pipe, prepares
The bright and clean no pit point of martensite steel pipe surface that technique obtains, quality is good, promotes product lumber recovery, reduces production cost.
In order to reach the goal of the invention, the present invention adopts the following technical scheme that:A kind of martensitic seamless steel pipe
Preparation process comprises the following steps:1)Martensite steel pipe pipe centering, then into eleven punch 11;2)To the pipe after perforation
It is made annealing treatment;3)Pickling is carried out with pickle to the pipe after annealing, is then carried out successively at phosphatization, saponification and lubrication
Reason;Saponification liquor used in the saponification process includes petroleum sodium sulfonate, triethanolamine, oleic acid, dodecenylsuccinic acid, benzene a pair of horses going side by side three
Nitrogen azoles, machinery oil;4)By after lubricated pipe carry out hot rolling, carry out ageing treatment after cooling, obtain martensite steel pipe into
Product, the processing step of the ageing treatment are put into for a. steel pipe pipes in stove, and temperature rises to 45-60 DEG C, keeps the temperature 0.2-0.5h;b.
In-furnace temperature is risen to 150-180 DEG C, handles 0.5-1h;C. in-furnace temperature is down to 110-120 DEG C, keeps the temperature 1-1.5h.
Applicant has found that the outer surface pit point of steel pipe is on the high side, and such case occurs mostly in actual production
In step 3)Afterwards, in process below, these pit points can not also eliminate, in said program, by saponification
Liquid is improved, and can be effectively improved point situation, and combines the ageing treatment of segmented, and tube quality is stablized.
Preferably, the saponification liquor is by mass percentage, including petroleum sodium sulfonate 42-55%, triethanolamine 3-9%,
Oleic acid 15-20%, dodecenylsuccinic acid 1-8%, benzotriazole 15-20%, surplus are machinery oil.
Preferably, the pickle of the pickling is the mixed liquor of phosphoric acid, citric acid solution, Klorvess Liquid, it is described
The concentration of phosphoric acid is 10-15%, and the concentration of citric acid solution is 30-42%.
The pickle of said program can improve pickling effect, can the rust on fully erased pipe surface, oxide skin, and will not
Corrosive is generated, ensures the concentration of the quality, especially phosphoric acid and citric acid of steel pipe, pickling effect is influenced very big.
Preferably, phosphoric acid, citric acid, the volumetric mixture ratio of Klorvess Liquid are 3-5 in the pickle:2:1.
Preferably, the step 3)In pickling temperature for 38-45 DEG C, pickling time 20-25min.
With reference to the pickle of this programme, suitable pickling temperature can improve pickling effect, and pickling time is long to be caused
Steel pipe overpickling, the pipe surface of overpickling it is thick it is hot-tempered, color is dark, have circular pin hole when serious, easy roll banding or broken during cold rolling;Acid
Wash it is insufficient if cannot the rust on fully erased pipe surface, oxide skin, obtained steel pipe finished product resistance to corrosion is poor.
Preferably, the pipe after the hot rolling is carried out at timeliness again after thermal conduction plate and hot roll after natural cooling
Reason.
Preferably, before the phosphorating treatment, pipe is surface-treated using surface treatment liquid, the surface treatment
Liquid includes oxalic acid, glacial acetic acid.
The defects of corrosion caused by pipe pickling is uneven can be eliminated by carrying out surface treatment, be improved at phosphatization speed shortening
The time is managed, pipe is made to generate the uniform phosphate coating of compact crystallization in parkerizing process, while enhances corrosion resisting property and improves painting
Film adhesive force reduces phosphating dregs.
Preferably, the annealing carries out under vacuum, the pit of steel tube surface can be improved to a certain extent
Point defect.
Preferably, the vacuum degree of the annealing vacuum condition is at least 2 × 10-2Pa。
Preferably, the material nickel content that the thermal conduction plate uses is 5%-12%, hot roll material uses 2Cr13NiMo.
It has been found that the generation of pit point, except technologic influence, in Steel Tube Rolling, the thermal conduction plate of process
Influence is will also result in hot roll, the thermal conduction plate and hot roll used at present can cause steel bonding, and pit, shadow are generated in steel tube surface
Tube quality is rung, according to this programme, by the material of thermal conduction plate, hot roll, can solve the problems, such as this.
By implementing above-mentioned technical proposal, the present invention has following advantageous effect:The present invention is by rationally setting technique
Step controls the parameter in each step, and the bright and clean no pit point of martensite steel pipe surface, quality is good, promotes product lumber recovery, drop
Low production cost.
Specific embodiment
Below by specific embodiment, the present invention is described in further detail.
Embodiment 1:
A kind of preparation process of martensitic seamless steel pipe, comprises the following steps:1)Martensite steel pipe pipe punching footpath is
15mm, depth are the centre bore of 10mm, and punching top then is preheated to 800 DEG C, are carried out under conditions of temperature is 1000 DEG C
Perforation;2)Pipe after perforation is introduced into annealing furnace and is made annealing treatment;3)Pipe after annealing is aligned, Ran Houyong
Pickle is 38 DEG C of pickling 20min in temperature, and pickle is phosphoric acid, citric acid solution, the mixed liquor of Klorvess Liquid, and volume is mixed
Composition and division in a proportion is 3:2:1, wherein, the concentration of phosphoric acid is 10%, and the concentration of citric acid is 30%;With after high pressure water washing pickling after pickling
Steel pipe, then carry out phosphorating treatment 25min, treatment temperature be 55 DEG C, handle with water by steel tube surface phosphating solution rinse do
Only, then carry out saponification process, saponification liquor by mass percentage, including petroleum sodium sulfonate 42%, triethanolamine 3%, oleic acid
15%th, dodecenylsuccinic acid 1%, benzotriazole 15%, surplus are machinery oil;Glass dust lubricated is used after saponification process;
4)Pipe is subjected to hot rolling, ageing treatment is carried out after cooling, obtains martensite steel pipe finished product, the processing step of the ageing treatment
It is put into for a. steel pipe pipes in stove, temperature rises to 60 DEG C, keeps the temperature 0.5h;B. in-furnace temperature is risen to 180 DEG C, handles 1h;C. will
In-furnace temperature is down to 120 DEG C, keeps the temperature 1.5h.
Embodiment 2:
A kind of preparation process of martensitic seamless steel pipe, comprises the following steps:1)Martensite steel pipe pipe punching footpath is
15mm, depth are the centre bore of 10mm, and punching top then is preheated to 800 DEG C, are carried out under conditions of temperature is 1000 DEG C
Perforation;2)Pipe after perforation is introduced into annealing furnace and carries out vacuum annealing process, vacuum degree is 2 × 10-2Pa;3)After annealing
Pipe aligned, then with pickle temperature be 45 DEG C of pickling 25min, pickle for phosphoric acid, citric acid solution, chlorination
The mixed liquor of potassium solution, volumetric mixture ratio 5:2:1, wherein, the concentration of phosphoric acid is 15%, and the concentration of citric acid is 42%;Pickling
The steel pipe after high pressure water washing pickling is used afterwards, and then pipe surface is surface-treated, and surface treatment liquid includes oxalic acid, ice vinegar
Acid then carries out phosphorating treatment 20min, and treatment temperature is 50 DEG C, has handled and has been rinsed well steel tube surface phosphating solution with water, has connect
Carry out saponification process, saponification liquor by mass percentage, including petroleum sodium sulfonate 55%, triethanolamine 9%, oleic acid 20%, 12
Alkenyl succinic acid 8%, benzotriazole 20%, surplus are machinery oil;Glass dust lubricated is used after saponification process;4)By pipe
Hot rolling is carried out, ageing treatment is carried out after cooling, obtains martensite steel pipe finished product, the processing step of the ageing treatment is a. steel pipes
Pipe is put into stove, and temperature rises to 45 DEG C, keeps the temperature 0.2h;B. in-furnace temperature is risen to 150 DEG C, handles 0.5h;It c. will be warm in stove
Degree is down to 110 DEG C, keeps the temperature 1h.
Embodiment 3:
A kind of preparation process of martensitic seamless steel pipe, comprises the following steps:1)Martensite steel pipe pipe punching footpath is
15mm, depth are the centre bore of 10mm, and punching top then is preheated to 800 DEG C, are carried out under conditions of temperature is 1000 DEG C
Perforation;2)Pipe after perforation is introduced into annealing furnace and carries out vacuum annealing process, vacuum degree is 3 × 10-2Pa;3)After annealing
Pipe aligned, then with pickle temperature be 38 DEG C of pickling 25min, pickle for phosphoric acid, citric acid solution, chlorination
The mixed liquor of potassium solution, volumetric mixture ratio 3:2:1, wherein, the concentration of phosphoric acid is 15%, and the concentration of citric acid is 30%;Pickling
The steel pipe after high pressure water washing pickling is used afterwards, and then pipe surface is surface-treated, and surface treatment liquid includes oxalic acid, ice vinegar
Acid then carries out phosphorating treatment 20min, and treatment temperature is 50 DEG C, has handled and has been rinsed well steel tube surface phosphating solution with water, has connect
Carry out saponification process, saponification liquor by mass percentage, including petroleum sodium sulfonate 55%, triethanolamine 3%, oleic acid 20%, 12
Alkenyl succinic acid 1%, benzotriazole 20%, surplus are machinery oil;Glass dust lubricated is used after saponification process;4)By pipe
Hot rolling is carried out, by thermal conduction plate and hot roll, ageing treatment is carried out after natural cooling, obtains martensite steel pipe finished product, the heat
The material nickel content that guide plate uses is 5%-12%, and the present embodiment selects 8%, and hot roll material uses 2Cr13NiMo;The timeliness
The processing step of processing is put into for a. steel pipe pipes in stove, and temperature rises to 60 DEG C, keeps the temperature 0.2h;B. in-furnace temperature is risen to 180
DEG C, handle 0.5h;C. in-furnace temperature is down to 120 DEG C, keeps the temperature 1h.
Claims (6)
1. a kind of preparation process of martensitic seamless steel pipe, which is characterized in that comprise the following steps:1)Martensite steel pipe pipe is beaten
Centre bore, then into eleven punch 11;2)Pipe after perforation is made annealing treatment;3)Pipe after annealing is carried out with pickle
Then pickling carries out phosphatization, saponification and lubricated successively;Saponification liquor used in the saponification process include petroleum sodium sulfonate,
Triethanolamine, oleic acid, dodecenylsuccinic acid, benzotriazole, machinery oil;4)Pipe after lubricated is subjected to hot rolling,
Ageing treatment is carried out after cooling, obtains martensite steel pipe finished product, the processing step of the ageing treatment is put into for a. steel pipe pipes
In stove, temperature rises to 45-60 DEG C, keeps the temperature 0.2-0.5h;B. in-furnace temperature is risen to 150-180 DEG C, handles 0.5-1h;C. by stove
Interior temperature is down to 110-120 DEG C, keeps the temperature 1-1.5h;
The saponification liquor by mass percentage, including petroleum sodium sulfonate 42-55%, triethanolamine 3-9%, oleic acid 15-20%, ten
Dialkylene succinic acid 1-8%, benzotriazole 15-20%, surplus are machinery oil;
The pickle of the pickling is the mixed liquor of phosphoric acid, citric acid solution, Klorvess Liquid, and the concentration of the phosphoric acid is
10-15%, the concentration of citric acid solution is 30-42%;
Pipe after the hot rolling carries out ageing treatment again after thermal conduction plate and hot roll after natural cooling;
For the material nickel content that the thermal conduction plate uses for 5%-12%, hot roll material uses 2Cr13NiMo.
A kind of 2. preparation process of martensitic seamless steel pipe according to claim 1, which is characterized in that phosphorus in the pickle
Acid, citric acid, the volumetric mixture ratio of Klorvess Liquid are 3-5:2:1.
A kind of 3. preparation process of martensitic seamless steel pipe according to claim 1, which is characterized in that the step 3)In
Pickling temperature is 38-45 DEG C, pickling time 20-25min.
A kind of 4. preparation process of martensitic seamless steel pipe according to claim 1, which is characterized in that the phosphorating treatment
Before, pipe is surface-treated using surface treatment liquid, the surface treatment liquid includes oxalic acid, glacial acetic acid.
5. a kind of preparation process of martensitic seamless steel pipe according to claim 1, which is characterized in that the annealing exists
It is carried out under vacuum condition.
6. a kind of preparation process of martensitic seamless steel pipe according to claim 5, which is characterized in that the annealing is true
The vacuum degree of empty condition is at least 2 × 10-2Pa。