CN106390596A - Antibacterial PC/PP automobile air conditioner filter element and preparation method thereof - Google Patents
Antibacterial PC/PP automobile air conditioner filter element and preparation method thereof Download PDFInfo
- Publication number
- CN106390596A CN106390596A CN201610805933.7A CN201610805933A CN106390596A CN 106390596 A CN106390596 A CN 106390596A CN 201610805933 A CN201610805933 A CN 201610805933A CN 106390596 A CN106390596 A CN 106390596A
- Authority
- CN
- China
- Prior art keywords
- consumption
- weight portion
- weight
- preparation
- filter element
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antibacterial PC/PP automobile air conditioner filter element and a preparation method thereof. The preparation method comprises the following steps: 1) in the existence of X-rays, carrying out activation treatment on bentonite and shell calcination matters so as to obtain an activating agent; 2) killing out, drying and smashing Chinese herbal medicine to obtain Chinese herbal medicine powder; 3) mixing PC, PP, PUR, nano rubidium oxide, cyclodextrin, butylene terephthalate, isoquinoline, glass fiber, potassium chloroplatinate, niobium pentachloride, nano-palladium, N-phenyl maleimide, dibasic lead phosphate, barium stearate, dicyclohexylurea, the activating agent and the Chinese herbal medicine powder to obtain a mixture; and 4) carrying out curing formation on the mixture to prepare the antibacterial PC/PP automobile air conditioner filter element. The antibacterial PC/PP automobile air conditioner filter element prepared through the method has excellent mechanical property, and meanwhile has excellent antibacterial activity.
Description
Technical field
The present invention relates to air conditioning for automobiles assembly, in particular it relates to a kind of antibacterial PC/PP automobile air conditioner filter element and its preparation side
Method.
Background technology
Air conditioning for automobiles has been the requisite ingredient of existing automobile, typically mainly by compressor, electric control clutch,
Condenser, vaporizer, expansion valve, drier receiver, pipeline, condenser fan, vacuum solenoid, idling device and control system group
Become.The effect that existing air conditioning for automobiles primarily serves is as follows：(1) temperature in compartment can be controlled, air can be heated, also can be cold
But air, so that temperature control in compartment to comfortable level；(2) can dampness in air-out, dry air absorbs
Human sweat, causes more comfortable environment；(3) fresh air can be sucked, there is ventilation function；(4) may filter that air, exclude in the air
Dust and pollen.
Existing air conditioning for automobiles is mainly made up of working of plastics, and these plastic parts have excellent mechanical property, and then ensures
The absolutely empty tune of automobile has longer service life.But air conditioning for automobiles needs regularly to be carried out and safeguard, otherwise in automobile
The air in portion then can have irritating abnormal smells from the patient.The reason produce penetrating odor is led to mainly to have at 2 points：On the one hand it is that automobile is empty
Adjust remaining in each part to have substantial amounts of dust, be on the other hand due to breed bacteria above each part of air conditioning for automobiles, and then produce
Harmful abnormal smells from the patient.In these automobile components, especially automobile air conditioner filter element, this is because its contact area is maximum,
The easiest breed bacteria.
Content of the invention
It is an object of the invention to provide a kind of antibacterial PC/PP automobile air conditioner filter element and preparation method thereof, by party's legal system
The antibacterial PC/PP automobile air conditioner filter element obtaining not only has excellent mechanical property, also has excellent bacteriostasis property simultaneously；And
This preparation method step is simple, and raw material is easy to get.
To achieve these goals, the invention provides a kind of preparation method of antibacterial PC/PP automobile air conditioner filter element, wrap
Include：
1) in the presence of X-ray, bentonite and shell calcined material are carried out activation processing to obtain activator；
2) Chinese herbal medicine is completed, is dried, pulverizing so that herbal powder is obtained；
3) by PC (Merlon), PP (polypropylene), PUR (polyurethane), nano oxidized rubidium, cyclodextrin, p-phthalic acid
Butanediol ester, isoquinolin, glass fibre, potassium chloroplatinate, Columbium pentachloride., Technique of Nano Pd, N-phenylmaleimide, two alkali formula phosphorous
Lead plumbate, barium stearate, 1,3-Dicyclohexylurea, described activator and herbal powder knead to obtain mixing thing；
4) described mixing thing curing molding is obtained described antibacterial PC/PP automobile air conditioner filter element；
Wherein, described Chinese herbal medicine be Fructus Evodiae, Radix Clematidis, Rhizoma Saururi (Herba Saururi), Semen Cassiae, Herba Patriniae, Folium Artemisiae Argyi, Cortex Magnoliae Officinalis, Fructus Foeniculi and
Radix Euphorbiae Pekinensiss.
Present invention also offers a kind of antibacterial PC/PP automobile air conditioner filter element, this antibacterial PC/PP automobile air conditioner filter element passes through upper
The method stated is prepared.
By technique scheme, the present invention first passes through and bentonite and shell calcined material is carried out activation processing and then make
Bentonite after must processing and shell calcined material have excellent activity；Then Chinese herbal medicine is completed, is dried, pulverize be obtained in
Herbal powder；Then PC, PP, PUR, nano oxidized rubidium, cyclodextrin, mutual-phenenyl two acid bromide two alcohol ester, isoquinolin, glass fibers are utilized
Dimension, potassium chloroplatinate, Columbium pentachloride., Technique of Nano Pd, N-phenylmaleimide, dibasic lead phosphite, barium stearate, dicyclohexyl
The synergism of urea, activator and herbal powder so that prepared antibacterial PC/PP automobile air conditioner filter element not only have excellent
Mechanical property, also has excellent antibiotic property simultaneously, and then ensure that the quality of automotive interior air.
Other features and advantages of the present invention will be described in detail in subsequent specific embodiment part.
Specific embodiment
Hereinafter the specific embodiment of the present invention is described in detail.It should be appreciated that it is described herein concrete
Embodiment is merely to illustrate and explains the present invention, is not limited to the present invention.
The invention provides a kind of preparation method of antibacterial PC/PP automobile air conditioner filter element, including：
1) in the presence of X-ray, bentonite and shell calcined material are carried out activation processing to obtain activator；
2) Chinese herbal medicine is completed, is dried, pulverizing so that herbal powder is obtained；
3) by PC (Merlon), PP (polypropylene), PUR (polyurethane), nano oxidized rubidium, cyclodextrin, p-phthalic acid
Butanediol ester, isoquinolin, glass fibre, potassium chloroplatinate, Columbium pentachloride., Technique of Nano Pd, N-phenylmaleimide, two alkali formula phosphorous
Lead plumbate, barium stearate, 1,3-Dicyclohexylurea, described activator and herbal powder knead to obtain mixing thing；
4) described mixing thing curing molding is obtained described antibacterial PC/PP automobile air conditioner filter element；
Wherein, described Chinese herbal medicine be Fructus Evodiae, Radix Clematidis, Rhizoma Saururi (Herba Saururi), Semen Cassiae, Herba Patriniae, Folium Artemisiae Argyi, Cortex Magnoliae Officinalis, Fructus Foeniculi and
Radix Euphorbiae Pekinensiss.
In the present invention, the actual conditions of activation processing can select in wide scope, but so that bentonite and
Shell calcined material can be able to the most fully activate it is preferable that in step 1) in, activation processing at least meets following condition：X-
The wavelength of ray is 0.5-5nm, and activation temperature is 80-95 DEG C, and soak time is 5-8h.
Step 1 in the present invention) in, the consumption of each material can select in wide scope, but so that bentonite
Can be able to the most fully activate with shell calcined material it is preferable that the weight of bentonite and shell calcined material is than for 1：0.8-
1.2.
Step 2 in the present invention) in, the consumption of each material can select in wide scope, but so that be obtained
Antibacterial PC/PP automobile air conditioner filter element has more excellent mechanical property and anti-microbial property it is preferable that in step 2) in, with respect to
The described Fructus Evodiae of 100 weight portions, the consumption of described Radix Clematidis is 33-40 weight portion, and the consumption of described Rhizoma Saururi (Herba Saururi) is 55-62 weight
Amount part, the consumption of described Semen Cassiae is 18-23 weight portion, and the consumption of described Herba Patriniae is 28-36 weight portion, the use of described Folium Artemisiae Argyi
Measure as 70-85 weight portion, the consumption of described Cortex Magnoliae Officinalis is 9-18 weight portion, the consumption of described Fructus Foeniculi is 44-56 weight portion, described capital
The consumption of the Radix Euphorbiae Pekinensis is 20-34 weight portion.
Step 2 in the present invention) in, the actual conditions completing can select in wide scope, but so that is obtained
Antibacterial PC/PP automobile air conditioner filter element there is more excellent mechanical property and anti-microbial property it is preferable that in step 2) in, complete
For：Described Chinese herbal medicine is placed in steaming and decocting 3-8h in 95-101 DEG C of water.
Step 2 in the present invention) in, the particle diameter of herbal powder can select in wide scope, but so that system
Antibacterial PC/PP automobile air conditioner filter element there is more excellent mechanical property and anti-microbial property it is preferable that the grain of herbal powder
Footpath is 0.1-0.6mm.
Step 3 in the present invention) in, PC, PP, PUR, the concrete species of nano oxidized rubidium can be selected in wide scope
Select, but so that the antibacterial PC/PP automobile air conditioner filter element being obtained has more excellent mechanical property and anti-microbial property, preferably
Ground, the weight average molecular weight of PC is 8000-12000, and the weight average molecular weight of PP is 5000-7000, and the weight average molecular weight of PUR is
3000-5000, the particle diameter of nano oxidized rubidium is 15-25nm.
Step 3 in the present invention) in, the consumption of each material can select in wide scope, but so that be obtained
Antibacterial PC/PP automobile air conditioner filter element has more excellent mechanical property and anti-microbial property it is preferable that with respect to 100 weight portions
The consumption of PC, PP is 34-38 weight portion, and the consumption of PUR is 51-58 weight portion, and the consumption of nano oxidized rubidium is 0.2-0.9 weight
Part, the consumption of cyclodextrin is 11-17 weight portion, and the consumption of mutual-phenenyl two acid bromide two alcohol ester is 33-44 weight portion, the use of isoquinolin
Measure as 9-12 weight portion, the consumption of glass fibre is 3-8 weight portion, the consumption of potassium chloroplatinate is 0.8-1.3 weight portion, phosphoric
The consumption of niobium is 1.1-1.4 weight portion, and the consumption of Technique of Nano Pd is 0.3-0.6 weight portion, and the consumption of N-phenylmaleimide is
10-16 weight portion, the consumption of dibasic lead phosphite is 22-27 weight portion, and the consumption of barium stearate is 11-16 weight portion, two
The consumption of cyclohexyl urea is 14-28 weight portion, and the consumption of activator is 27-35 weight portion, and the consumption of herbal powder is 14-28
Weight portion.
Step 4 in the present invention) in, the concrete mode of curing molding can be the conventional solidification in any one of this area
Molding mode, such as extrusion molding, injection moulding and jet flow forming, but in view of the convenience operating it is preferable that curing molding is adopted
Carried out with the mode of cast molding；And mixing thing is incubated 2-3h in 150-160 DEG C of casting die, is subsequently cooled to 15-
35℃.
In the present invention, the preparation method of shell calcined material can be the conventional method in any one of this area, but
So that shell calcined material has more excellent activity it is preferable that in step 1) before, this preparation method also includes：By shellfish
Shell calcines 5-6h so that shell calcined material is obtained at 350-375 DEG C.
Present invention also offers a kind of antibacterial PC/PP automobile air conditioner filter element, this antibacterial PC/PP automobile air conditioner filter element passes through upper
The method stated is prepared.
Hereinafter will be described the present invention by embodiment.
Embodiment 1
1) in the presence of wavelength is for the X-ray of 2.5nm, by bentonite and shell calcined material according to 1：1.0 weight are than mixed
It is incorporated at 88 DEG C and carries out activation processing 7h to obtain activator, wherein, shell calcined material is to calcine shell at 360 DEG C
It is obtained after 5.5h；
2) by Fructus Evodiae, Radix Clematidis, Rhizoma Saururi (Herba Saururi), Semen Cassiae, Herba Patriniae, Folium Artemisiae Argyi, Cortex Magnoliae Officinalis, Fructus Foeniculi and Radix Euphorbiae Pekinensiss according to 100：
38：59：21：33：75：14：49：24 weight than mixed be incorporated in 99 DEG C of water steaming and decocting 5h with carry out completing, be dried, pulverize with
Prepared particle diameter is the herbal powder of 0.5mm；
3) by PC (weight average molecular weight be 9000), PP (weight average molecular weight is 6000), PUR (weight average molecular weight is 4000),
Nano oxidized rubidium (particle diameter is 20nm), cyclodextrin, mutual-phenenyl two acid bromide two alcohol ester, isoquinolin, glass fibre, potassium chloroplatinate, five
Niobium chloride, Technique of Nano Pd, N-phenylmaleimide, dibasic lead phosphite, barium stearate, 1,3-Dicyclohexylurea, activator and in
Herbal powder is according to 100：36：55：0.7：13：38：10：5：1.1：1.3：0.5：13：25：14：22：29：21 weight is than mixed
Refining is to obtain mixing thing；
4) above-mentioned mixing thing is poured insulation 2.5h in the casting die cast from 155 DEG C, be cooled to 25 DEG C and described antibacterial is obtained
PC/PP automobile air conditioner filter element A1.
Embodiment 2
1) in the presence of wavelength is for the X-ray of 0.5nm, by bentonite and shell calcined material according to 1：0.8 weight is than mixed
It is incorporated at 80 DEG C and carries out activation processing 5h to obtain activator, wherein, shell calcined material is that shell is calcined at 350 DEG C 5h
It is obtained afterwards；
2) by Fructus Evodiae, Radix Clematidis, Rhizoma Saururi (Herba Saururi), Semen Cassiae, Herba Patriniae, Folium Artemisiae Argyi, Cortex Magnoliae Officinalis, Fructus Foeniculi and Radix Euphorbiae Pekinensiss according to 100：
33：55：18：28：70：9：44：20 weight than mixed be incorporated in 95 DEG C of water steaming and decocting 3h with carry out completing, be dried, pulverize with
Prepared particle diameter is the herbal powder of 0.1mm；
3) by PC (weight average molecular weight be 8000), PP (weight average molecular weight is 5000), PUR (weight average molecular weight is 3000),
Nano oxidized rubidium (particle diameter is 15nm), cyclodextrin, mutual-phenenyl two acid bromide two alcohol ester, isoquinolin, glass fibre, potassium chloroplatinate, five
Niobium chloride, Technique of Nano Pd, N-phenylmaleimide, dibasic lead phosphite, barium stearate, 1,3-Dicyclohexylurea, activator and in
Herbal powder is according to 100：34：51：0.2：11：33：9：3：0.8：1.1：0.3：10：22：11：14：27：14 weight is than mixing
To obtain mixing thing；
4) above-mentioned mixing thing is poured insulation 2h in the casting die cast from 150 DEG C, be cooled to 15 DEG C and described antibacterial PC/ is obtained
PP automobile air conditioner filter element A2.
Embodiment 3
1) in the presence of wavelength is for the X-ray of 5nm, by bentonite and shell calcined material according to 1：1.2 weight are than mixing
And carry out activation processing 8h at 95 DEG C to obtain activator, wherein, shell calcined material is to calcine after 6h shell at 375 DEG C
Prepared；
2) by Fructus Evodiae, Radix Clematidis, Rhizoma Saururi (Herba Saururi), Semen Cassiae, Herba Patriniae, Folium Artemisiae Argyi, Cortex Magnoliae Officinalis, Fructus Foeniculi and Radix Euphorbiae Pekinensiss according to 100：
40：62：23：36：85：18：56：34 weight is than the mixed steaming and decocting 8h that is incorporated in 101 DEG C of water to carry out completing, be dried, pulverize
So that particle diameter herbal powder as 0.6mm is obtained；
3) by PC (weight average molecular weight be 12000), PP (weight average molecular weight is 7000), PUR (weight average molecular weight is 5000),
Nano oxidized rubidium (particle diameter is 25nm), cyclodextrin, mutual-phenenyl two acid bromide two alcohol ester, isoquinolin, glass fibre, potassium chloroplatinate, five
Niobium chloride, Technique of Nano Pd, N-phenylmaleimide, dibasic lead phosphite, barium stearate, 1,3-Dicyclohexylurea, activator and in
Herbal powder is according to 100：38：58：0.9：17：44：12：8：1.3：1.4：0.6：16：27：16：28：35：28 weight is than mixed
Refining is to obtain mixing thing；
4) above-mentioned mixing thing is poured insulation 3h in the casting die cast from 160 DEG C, be cooled to 35 DEG C and described antibacterial PC/ is obtained
PP automobile air conditioner filter element A3.
Comparative example 1
Method according to embodiment 1 carries out automobile air conditioner filter element B1, except for the difference that, step 1 are obtained) in do not carry out at activation
Reason.
Comparative example 2
Method according to embodiment 1 carries out automobile air conditioner filter element B2, except for the difference that, step 1 are obtained) in not using swelling
Soil.
Comparative example 3
Method according to embodiment 1 carries out automobile air conditioner filter element B3, except for the difference that, step 1 are obtained) in do not forged using shell
Burn thing.
Comparative example 4
Method according to embodiment 1 carries out automobile air conditioner filter element B4, except for the difference that, step 3 are obtained) in not using activation
Agent.
Comparative example 4
Method according to embodiment 1 carries out automobile air conditioner filter element B4, except for the difference that, step 3 are obtained) in not using Chinese herbal medicine
Powder.
Detection example 1
Above-mentioned prepared automobile air conditioner filter element is carried out notch impact strength detected, pass through GB15981-1995 simultaneously
Described in method above-mentioned automobile air conditioner filter element is carried out with the detection of antibiotic rate, concrete outcome is shown in Table 1.
Table 1
| Notch impact strength/MPa | Antibiotic rate/% | |
| A1 | 54.8 | 98 |
| A2 | 54.9 | 97 |
| A3 | 54.7 | 99 |
| B1 | 38.3 | 70 |
| B2 | 37.7 | 72 |
| B3 | 36.6 | 74 |
| B4 | 34.1 | 77 |
| B5 | 34.0 | 57 |
By above-described embodiment, comparative example and detection example, the automobile air conditioner filter element that the present invention provides not only has excellent
Different mechanical property, also has excellent anti-microbial property.
The preferred embodiment of the present invention described in detail above, but, the present invention is not limited in above-mentioned embodiment
Detail, in the range of the technology design of the present invention, multiple simple variant can be carried out to technical scheme, this
A little simple variant belong to protection scope of the present invention.
It is further to note that each particular technique feature described in above-mentioned specific embodiment, in not lance
In the case of shield, can be combined by any suitable means, in order to avoid unnecessary repetition, the present invention to various can
The compound mode of energy no longer separately illustrates.
Additionally, combination in any can also be carried out between the various different embodiment of the present invention, as long as it is without prejudice to this
The thought of invention, it equally should be considered as content disclosed in this invention.
Claims (10)
1. a kind of preparation method of antibacterial PC/PP automobile air conditioner filter element is it is characterised in that include：
1) in the presence of X-ray, bentonite and shell calcined material are carried out activation processing to obtain activator；
2) Chinese herbal medicine is completed, is dried, pulverizing so that herbal powder is obtained；
3) by PC (Merlon), PP (polypropylene), PUR (polyurethane), nano oxidized rubidium, cyclodextrin, p-phthalic acid fourth two
Alcohol ester, isoquinolin, glass fibre, potassium chloroplatinate, Columbium pentachloride., Technique of Nano Pd, N-phenylmaleimide, two alkali formula phosphorous acid
Lead, barium stearate, 1,3-Dicyclohexylurea, described activator and herbal powder knead to obtain mixing thing；
4) described mixing thing curing molding is obtained described antibacterial PC/PP automobile air conditioner filter element；
Wherein, described Chinese herbal medicine is that Fructus Evodiae, Radix Clematidis, Rhizoma Saururi (Herba Saururi), Semen Cassiae, Herba Patriniae, Folium Artemisiae Argyi, Cortex Magnoliae Officinalis, Fructus Foeniculi and capital are big
Halberd.
2. preparation method according to claim 1, wherein, in step 1) in, described activation processing at least meets following bar
Part：The wavelength of described X-ray is 0.5-5nm, and activation temperature is 80-95 DEG C, and soak time is 5-8h.
3. preparation method according to claim 1 and 2, wherein, in step 1) in, described bentonite and shell calcined material
Weight is than for 1：0.8-1.2.
4. preparation method according to claim 3, wherein, in step 2) in, with respect to the described Wu Zhu of 100 weight portions
Cornel, the consumption of described Radix Clematidis is 33-40 weight portion, and the consumption of described Rhizoma Saururi (Herba Saururi) is 55-62 weight portion, the use of described Semen Cassiae
Measure as 18-23 weight portion, the consumption of described Herba Patriniae is 28-36 weight portion, the consumption of described Folium Artemisiae Argyi is 70-85 weight portion, institute
The consumption stating Cortex Magnoliae Officinalis is 9-18 weight portion, and the consumption of described Fructus Foeniculi is 44-56 weight portion, and the consumption of described Radix Euphorbiae Pekinensiss is 20-34
Weight portion.
5. preparation method according to claim 4, wherein, in step 2) in, described complete for：Described Chinese herbal medicine is placed in
Steaming and decocting 3-8h in 95-101 DEG C of water；
Preferably, the particle diameter of described herbal powder is 0.1-0.6mm.
6. the preparation method according to claim 4 or 5, wherein, in step 3) in, the weight average molecular weight of described PC is
The weight average molecular weight of 8000-12000, described PP is 5000-7000, and the weight average molecular weight of described PUR is 3000-5000, described
The particle diameter of nano oxidized rubidium is 15-25nm.
7. preparation method according to claim 6, wherein, in step 3) in, with respect to the PC of 100 weight portions, described PP
Consumption be 34-38 weight portion, the consumption of described PUR is 51-58 weight portion, and the consumption of described nano oxidized rubidium is 0.2-0.9
Weight portion, the consumption of described cyclodextrin is 11-17 weight portion, and the consumption of described mutual-phenenyl two acid bromide two alcohol ester is 33-44 weight
Part, the consumption of described isoquinolin is 9-12 weight portion, and the consumption of described glass fibre is 3-8 weight portion, described potassium chloroplatinate
Consumption is 0.8-1.3 weight portion, and the consumption of described Columbium pentachloride. is 1.1-1.4 weight portion, and the consumption of described Technique of Nano Pd is 0.3-
0.6 weight portion, the consumption of described N-phenylmaleimide is 10-16 weight portion, and the consumption of described dibasic lead phosphite is
22-27 weight portion, the consumption of described barium stearate is 11-16 weight portion, and the consumption of described 1,3-Dicyclohexylurea is 14-28 weight
Part, the consumption of described activator is 27-35 weight portion, and the consumption of described herbal powder is 14-28 weight portion.
8. preparation method according to claim 7, wherein, in step 4) in, described curing molding adopts cast molding
Mode is carried out；And described mixing thing is incubated 2-3h in 150-160 DEG C of casting die, is subsequently cooled to 15-35 DEG C.
9. the preparation method according to claim 7 or 8, wherein, in step 1) before, described preparation method also includes：Will
Shell calcines 5-6h so that described shell calcined material is obtained at 350-375 DEG C.
10. a kind of antibacterial PC/PP automobile air conditioner filter element is it is characterised in that described antibacterial PC/PP automobile air conditioner filter element passes through right
The method described in any one in 1-9 is required to be prepared.