CN106381024B - A kind of high-voltage motor high osmosis impregnating varnish and preparation method - Google Patents
A kind of high-voltage motor high osmosis impregnating varnish and preparation method Download PDFInfo
- Publication number
- CN106381024B CN106381024B CN201610824033.7A CN201610824033A CN106381024B CN 106381024 B CN106381024 B CN 106381024B CN 201610824033 A CN201610824033 A CN 201610824033A CN 106381024 B CN106381024 B CN 106381024B
- Authority
- CN
- China
- Prior art keywords
- prepolymer
- low viscosity
- parts
- voltage motor
- epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of high-voltage motor high osmosis impregnating varnish, each ingredient including following mass fraction: 40~85 parts of low viscosity unsaturated polyester resin, 15~60 parts of low viscosity epoxy ester;The viscosity of the low viscosity unsaturated polyester resin and low viscosity epoxy ester is not more than 80s.The insulation thickness of the impregnating varnish is thinned and electric property improves instead, and overcome storage and using when be easily easily polluted by the external foreign matters and viscosity increases, insulation performance reduces, heating repeatedly very sensitive to environment temperature, impregnating resin is cooling uses, waste mass energy, reduces the disadvantages of production efficiency, viscosity is low under room temperature, good penetrability, is suitable for high-voltage motor room temperature VPI impregnation insulation process and handles.The invention also discloses the above-mentioned high-voltage motor preparation methods of high osmosis impregnating varnish, and manufacturing process is simple, and raw material are cheap and easily-available, low in cost.
Description
Technical field
The invention belongs to the technical fields more particularly to a kind of high-voltage motor high osmosis impregnating varnish of insulating materials manufacture
And preparation method.
Background technique
Currently, high-voltage motor insulated structure is mainly still using the system of non-epoxy anhydride on domestic market.Using comparing
Successfully have two big series of products: one is epoxy-ester-phenylethylenes;Another kind is polyester-imide-phenylethylene.Epoxy
Ester-phenylethylene product has many advantages, such as low viscosity, good penetrability, stable storing, excellent electric properties, but there are volatile matters
The disadvantages of height, solidification temperature are high, the time is long, energy consumption is high, low efficiency;Polyester-imide-phenylethylene product have it is heat-resist,
The advantages that curing time is relatively short, stable storing, good mechanical property, but that there is also electric property nargin is few, water resistance is slightly worse
The disadvantages of.
And external large and medium-sized vacuum pressure impregnation of high voltage motor resin is substantially representative: one by two kinds of main products
It is using US Westinghouse company and French Alstom as the polystyrene systems of the epoxy polyester acid anhydrides of representative;The second is with moral
Siemens Company of state and Mitsubishi Corporation of Japan are the non-polystyrene systems of the epoxy anhydride of representative.The styrene of epoxy polyester acid anhydrides
The feature of environmental protection of system is not good enough;The non-polystyrene systems of epoxy anhydride can achieve the thinned purpose of insulation system, i.e. insulation thickness
Be thinned and electric property will improve instead, but this kind of resin storage and in use, easily be easily polluted by the external foreign matters and viscosity increase, insulation
Reduced performance, very sensitive to environment temperature, the heating repeatedly of impregnating resin is cooling to be used, and is wasted a large amount of energy, is reduced
Production efficiency, therefore in practical applications, receive larger limitation.
Currently, the related patents of high-voltage motor insulated structure are as follows both at home and abroad:
Chinese patent CN201210483323.1 describes a kind of high-voltage motor impregnated insulating paint and preparation method thereof, adopts
With unsaturated polyester modified epoxy resin, epoxy resin, unsaturated diluent, latent curing agent, peroxide are added
Initiator, epoxide diluent and levelling agent composition;Chinese patent CN201310046980.4 describes a kind of high-voltage motor without molten
Agent impregnating resin and curing method, using heat resisting unsaturated polyester, Ben Bing E piperazine imide resin, epoxy resin, reactive diluent,
The impregnating varnish that curing agent, promotor, initiator form, feature is that high-low pressure is general, and H-C grades general;Chinese patent
CN201020243735.4 describes a kind of high-voltage motor insulated structure of ten KV levels, lacks glue using double glass cloth reinforced mediate amount epoxy
Four layers of mica paper tape half-stack package formed in main insulating layer, then with double glass cloth reinforced mediate amount epoxy dry mica paper tape half-stack package four
Layer forms outer main insulating layer, and polyester-epoxy-anhydride-styrene type impregnating resin of arranging in pairs or groups forms final high-voltage motor insulated knot
Structure.But impregnating varnish involved in above-mentioned patent, the feature of environmental protection is insufficient, and cannot achieve the purpose that insulation is thinned.
Chinese patent CN201210566052.6 describes high voltage motor stator major insulation ultra-thin insulated technique, using ring
Three layers of oxygen polyester film dry mica half-stack package form insulation system, the epoxy anhydride with epoxy anhydride solvent-free immersion paint
Although system has achieved the purpose that insulation is thinned, is energy-saving, but the stable storing sexual deviation of epoxy anhydride system, causes to insulate
Service life is difficult to be expected.
Chinese patent CN201410771173.3 describes high-voltage motor stator coil insulation system and its dipping and solidification
Technique, using organosilicon solvent-free dip varnish with four layers of half-stack package of Kapton glass cloth dry mica paper tape form it is exhausted
Edge structure, for temperature resistant grade up to 220 grades, the organosilicon systems high temperature resistant grade is high and insulation life is long but at high cost, and bakes temperature
Degree is high, and application range receives limitation.
It can be seen that research and develop it is a kind of not only can with reduction insulation structure, improve electric property, but also can overcome that viscosity is big, temperature
The high environment-friendly type high osmosis high-voltage motor insulating impregnating varnish of susceptibility, has a very important significance the art.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the shortcomings of to mention in background above technology and defect, provide one
Kind high-voltage motor high osmosis impregnating varnish and preparation method.
In order to solve the above technical problems, technical solution proposed by the present invention are as follows:
A kind of high-voltage motor high osmosis impregnating varnish, each ingredient including following mass fraction:
40~85 parts of low viscosity unsaturated polyester resin,
15~60 parts of low viscosity epoxy ester;
The viscosity of the low viscosity unsaturated polyester resin and low viscosity epoxy ester is not more than 80s.
Above-mentioned high-voltage motor high osmosis impregnating varnish, it is preferred that the low viscosity unsaturated polyester resin is by cis-butenedioic anhydride
10~25 parts, 5~15 parts of monounsaturated dicarboxylic acid, 10~30 parts of dihydric alcohol, 0~10 part of polyalcohol and 10~25 parts of monohydric alcohol press quality
Number mixing, after esterification, by mass fraction plus 0.005~0.5 part of stabilizer, 0.5~1.5 part of initiator and crosslinking
It 3~20 parts of agent, is made after mixing evenly.The viscosity for the low viscosity unsaturated polyester resin that the present invention uses is not more than 80s, passes through
The viscosity of unsaturated polyester resin is controlled to realize low viscosity, the viscosity is lower, therefore has good permeability, does not need to make
With any diluent components, it is only necessary to the crosslinking agent of appropriate mix, when the high osmosis impregnating varnish being prepared into is used for high-voltage motor
When, it needs to carry out high temperature baked and cured, crosslinking agent is reacted with unsaturated bond in unsaturated polyester resin in the curing process, is formed
Stable reticular structure, this solidification process VOC free discharge, achievees the purpose that environmental emission reduction;In addition acid anhydrides or acidity is not used
Promotor, therefore the storage stability of system is good, to temperature-insensitive.
Preferably, the monounsaturated dicarboxylic acid includes M-phthalic acid, succinic acid, glutaric acid, succinic acid, adipic acid, certain herbaceous plants with big flowers two
One or more of acid and dimer (fatty acid) yl;The dihydric alcohol includes neopentyl glycol, ethylene glycol, propylene glycol, butanediol and one
One or more of diglycol ethylene;The polyalcohol includes one of match gram, glycerine and trimethylolethane or several
Kind;The monohydric alcohol include imidohydrine, n-butanol, isobutanol, neopentyl alcohol, in n-octyl alcohol and isooctanol and glycol monoethyl ether
It is one or more of.
Preferably, the stabilizer include 1,4-benzoquinone, hydroquinone, p-tert-Butylcatechol, methylnaphthohydroquinone, to hydroxyl
One or more of methyl phenyl ethers anisole, 2- tert-butyl hydroquinone and 2,5 di tert butyl hydroquinone.
Preferably, the initiator include cumyl peroxide, 2,5- dimethyl -2,5- bis- (tert-butyl peroxides) oneself
One or more of alkane, peroxidized t-butyl perbenzoate and benzoyl peroxide.
Preferably, the crosslinking agent includes neopentylglycol diacrylate or its prepolymer, propoxylation (2) neopentyl glycol
Diacrylate or its prepolymer, ethoxylated bisphenol A diacrylate or its prepolymer, ethoxylated bisphenol A dimethacrylate
Ester or its prepolymer, tri (propylene glycol) diacrylate or its prepolymer, 1,6 hexanediol diacrylate or its prepolymer,
Trimethylolpropane trimethacrylate or its prepolymer, 1,4 butanediol diacrylate or its prepolymer, pentaerythrite 4 third
Olefin(e) acid or its prepolymer, pentaerythritol triacrylate or its prepolymer, isobornyl acrylate or its prepolymer, propylene oxide
Ester or its prepolymer, ethoxylation ring alcohol acrylate or its prepolymer, two propylene olefin(e) acid ester of diethylene glycol phthalate or
One or more of its prepolymer, diallyphthalate acid esters or its prepolymer.
Preferably, the low viscosity epoxy ester is mixed by low viscosity epoxy resin and cis-butenedioic anhydride by quality proportioning 1:0.1~1,
Through esterification, it is made after the dissolution of epoxy-ester curing agent is then added;The low viscosity epoxy resin is viscosity no more than 80s's
Epoxy resin;The quality proportioning of the low viscosity epoxy ester and epoxy-ester curing agent is 1:0.01~0.06.Of the invention is low viscous
It spends epoxy-ester and uses suitable esterification ratio (mass ratio of low viscosity epoxy resin and cis-butenedioic anhydride), make the low viscosity ring being prepared
Oxygen ester has preferable viscosity and storage stability, and has excellent performance, and has good compatibility with unsaturated polyester resin, multiple
It is had excellent performance after matching.
Preferably, the epoxy-ester curing agent include zinc Isoocatanoate, aluminium acetylacetonate, zinc acetylacetonate, chromium acetylacetonate,
One or more of calcium acetylacetonate and acetylacetone cobalt.
High-voltage motor of the invention high osmosis impregnating varnish can achieve the thinned purpose of insulation system, i.e. insulation is thick
It spends and is thinned and electric property will improve instead, and overcome storage and in use, be easily easily polluted by the external foreign matters and viscosity increase, insulating properties
It can reduce, the cooling use of heating repeatedly very sensitive to environment temperature, impregnating resin, waste a large amount of energy, reduce life
The disadvantages of producing efficiency, viscosity is low under room temperature, good penetrability, and VPI dipping lacquer process can carry out at normal temperature, without in advance to paint into
Row heating, is able to achieve low temperature fast curing, energy conservation and environmental protection, high production efficiency, be a kind of good penetrability, without heating cooling repeatedly,
VOC free discharge, electric property intensity is high, dielectric loss is low, water resistance is good, storage stability is excellent, low in cost and Storage period
With long-lived product, be suitable for high-voltage motor room temperature VPI impregnation insulation process handle, be particularly suitable for 6kv, 10kv,
The whole leaching VPI of 10.5kv high-voltage motor is also used in the F-H class B insulation processing of common mesolow motor.
Based on a total technical concept, the present invention also provides a kind of preparation sides of high-voltage motor high osmosis impregnating varnish
Method includes the following steps:
(1) cis-butenedioic anhydride, monounsaturated dicarboxylic acid, dihydric alcohol, polyalcohol and monohydric alcohol are warming up to 170~215 DEG C after mixing,
Esterification is carried out, is vacuumized, stabilizer is added after being cooled to 160~180 DEG C and is uniformly mixed, then naturally cools to 30~50
DEG C, it is eventually adding initiator and crosslinking agent and is uniformly mixed to get the low viscosity unsaturated polyester resin is arrived;
(2) low viscosity epoxy resin and cis-butenedioic anhydride are warming up to 100~150 DEG C after mixing, through esterification, ring is added
Oxygen ester curing agent dissolves to arrive the low viscosity epoxy ester;
(3) by the low viscosity unsaturated polyester resin obtained after step (1) and the low viscosity epoxy ester obtained after step (2)
It is stirred evenly after mixing to get high-voltage motor high osmosis impregnating varnish is arrived.
Above-mentioned preparation method, it is preferred that the time vacuumized be 30~120min, the pressure vacuumized be-
0.099~-0.0999MPa.
Compared with prior art, the invention has the benefit that
1, high-voltage motor of the invention high osmosis impregnating varnish can achieve the thinned purpose of insulation system, that is, insulate
Thickness be thinned and electric property improves instead, and overcome storage and using when be easily easily polluted by the external foreign matters and viscosity increase, insulating properties
It can reduce, the cooling use of heating repeatedly very sensitive to environment temperature, impregnating resin, waste mass energy, reduce production effect
The disadvantages of rate, viscosity is low under room temperature, good penetrability, and VPI dipping lacquer process can carry out at normal temperature, without adding in advance to paint
Heat, is able to achieve low-temperature fast-curing, energy conservation and environmental protection, high production efficiency, is a kind of good penetrability, without heating cooling, nothing repeatedly
VOC emission, electric property intensity are high, dielectric loss is low, water resistance is good, storage stability is excellent, low in cost and Storage period with
Long-lived product, be suitable for high-voltage motor room temperature VPI impregnation insulation process handle, be particularly suitable for 6kv, 10kv,
The whole leaching VPI of 10.5kv high-voltage motor is also used in the F-H class B insulation processing of common mesolow motor.
2, high-voltage motor of the invention high osmosis impregnating varnish, after low resin mica tape solidification, insulation system
Uniformly, inside is without air cleft, and overall structure is closely knit, and good electric property, dielectric loss is low, and performance is close to pure epoxy anhydride system high pressure
Impregnating varnish.
3, the high-voltage motor of the present invention preparation method of high osmosis impregnating varnish, manufacturing process is simple, and raw material are cheaply easy
, it is low in cost.
Specific embodiment
To facilitate the understanding of the present invention, the present invention is done below in conjunction with preferred embodiment and more comprehensively, is meticulously described,
But protection scope of the present invention is not limited to following specific embodiments.
Unless otherwise defined, all technical terms used hereinafter are generally understood meaning phase with those skilled in the art
Together.Technical term used herein is intended merely to the purpose of description specific embodiment, and it is of the invention to be not intended to limitation
Protection scope.
Unless otherwise specified, various raw material, reagent, the instrument and equipment etc. used in the present invention can pass through city
Field is commercially available or can be prepared by existing method.
Embodiment 1:
A kind of environmentally friendly insulating impregnating varnish of high-voltage motor of the invention, each ingredient including following mass fraction: viscosity is not
70 parts of low viscosity unsaturated polyester resin greater than 80s, viscosity are not more than 30 parts of low viscosity epoxy ester of 80s;Preparation method
Include the following steps (following number is mass fraction):
(1) by 17.5 parts of cis-butenedioic anhydrides, 10.5 parts of sebacic acid, 24.5 parts of neopentyl glycols, 3.5 parts match gram and 10.5 parts of n-butanols,
After being gradually warming up to 190 DEG C of progress esterifications after mixing, acid value is reduced to 35mgKOH/g, with the pressure of -0.099MPa
60min is vacuumized, is cooled to 170~175 DEG C;Then 0.07 part of 1,4-benzoquinone is added to be uniformly mixed, naturally cools to 40 DEG C, finally
0.53 part of cumyl peroxide, 5 parts of neopentylglycol diacrylates is added, is uniformly mixed to get the low viscosity insatiable hunger is arrived
And polyester resin;
(2) low viscosity epoxy resin by 24 parts of viscosity no more than 80s gradually heats up after mixing with 3.48 parts of cis-butenedioic anhydrides
To 120~130 DEG C, heat preservation carries out esterification 3h, and 0.42 part of aluminium acetylacetonate is added and is uniformly dissolved to obtain homemade low viscosity
Epoxy-ester;
(3) the low viscosity unsaturated polyester (UP) tree being prepared after step (1) is added by quality proportioning 70:30 in mixing kettle
The low viscosity epoxy ester being prepared after rouge and step (2), obtains high-voltage motor high osmosis of the invention after mixing evenly
Impregnating varnish.
The correlated performance for the high-voltage motor insulating impregnating varnish that test the present embodiment is prepared, viscosity 40s have
Good permeability, can normal temperature dipping high-voltage motor;Temperature classification is H grade, solidifies at (155 ± 5) DEG C and needs 8h, fugitive constituent
It is 0.2%, hot (155 DEG C) adhesion strength 32N, (155 DEG C) of hot medium consumption factor are 1.5%.
Embodiment 2:
A kind of environmentally friendly insulating impregnating varnish of high-voltage motor of the invention, each ingredient including following mass fraction: viscosity is not
75 parts of low viscosity unsaturated polyester resin greater than 80s, viscosity are not more than 25 parts of low viscosity epoxy ester of 80s;Preparation method
Include the following steps (following number is mass fraction):
(1) by 13.5 parts of cis-butenedioic anhydrides, 9 parts of adipic acids, 18.75 parts of ethylene glycol, 7.5 parts of matches gram and 18.75 parts of ethylene glycol list first
Ether, after being gradually warming up to 200 DEG C of progress esterifications after mixing, acid value is reduced to 40mgKOH/g, with -0.0999MPa's
Pressure vacuumizes 30min, is cooled to 170~175 DEG C;Then 0.075 part of 1,4-benzoquinone is added to be uniformly mixed, naturally cools to 50
DEG C, it is eventually adding 0.675 part of cumyl peroxide, 6.75 parts of 1,4-butanediol diacrylates, is uniformly mixed to get institute is arrived
State low viscosity unsaturated polyester resin;
(2) low viscosity epoxy resin by 20.5 parts of viscosity no more than 80s is gradually warming up to after mixing with 4 parts of cis-butenedioic anhydrides
140~150 DEG C, heat preservation carries out esterification 3h, and 0.5 part of zinc Isoocatanoate is added and is uniformly dissolved to obtain self-control low viscosity epoxy ester;
(3) the low viscosity unsaturated polyester (UP) tree being prepared after step (1) is added by quality proportioning 75:25 in mixing kettle
The low viscosity epoxy ester being prepared after rouge and step (2), obtains high-voltage motor high osmosis of the invention after mixing evenly
Impregnating varnish.
The correlated performance of high-voltage motor insulating impregnating varnish manufactured in the present embodiment is tested, viscosity 40s has good
Permeability, can normal temperature dipping high-voltage motor;Temperature classification is H grade, solidifies at (155 ± 5) DEG C and needs 7h, fugitive constituent is
0.3%, hot (155 DEG C) adhesion strength 30N, (155 DEG C) of hot medium consumption factor are 1.2%.
Embodiment 3:
A kind of environmentally friendly insulating impregnating varnish of high-voltage motor of the invention, each ingredient including following mass fraction: viscosity is not
65 parts of low viscosity unsaturated polyester resin greater than 80s, viscosity are not more than 35 parts of low viscosity epoxy ester of 80s;Preparation method
Include the following steps (following number is mass fraction):
(1) by 13 parts of cis-butenedioic anhydrides, 10 parts of M-phthalic acids, 15 parts of neopentyl glycols, 8 parts of glycerine and 15 parts of imidohydrines, mixing
After being gradually warming up to 175 DEG C of progress esterifications after uniformly, acid value is reduced to 40mgKOH/g, is taken out with the pressure of -0.099MPa true
Empty 120min is cooled to 160~165 DEG C;Then 0.06 part of hydroquinone is added to be uniformly mixed, naturally cools to 30 DEG C, finally
Bis- (tert-butyl peroxide) hexanes of 0.6 part of 2,5- dimethyl -2,5-, 5 parts of ethoxylated bisphenol A dimethylacrylates is added, mixes
Close uniformly to get arrive the low viscosity unsaturated polyester resin;
(2) low viscosity epoxy resin by 29.4 parts of viscosity no more than 80s gradually heats up after mixing with 3.1 parts of cis-butenedioic anhydrides
To 100~110 DEG C, insulation reaction 3h, 0.84 part of aluminium acetylacetonate is added and is uniformly dissolved to obtain self-control low viscosity epoxy ester;
(3) the low viscosity unsaturated polyester (UP) tree being prepared after step (1) is added by quality proportioning 65:35 in mixing kettle
The low viscosity epoxy ester being prepared after rouge and step (2), obtains high-voltage motor high osmosis of the invention after mixing evenly
Impregnating varnish.
The correlated performance of high-voltage motor insulating impregnating varnish manufactured in the present embodiment is tested, viscosity 45s has good
Permeability, can normal temperature dipping high-voltage motor;Temperature classification is H grade, solidifies at (155 ± 5) DEG C and needs 6h, fugitive constituent is
0.1%, hot (155 DEG C) adhesion strength 33N, (155 DEG C) of hot medium consumption factor are 1.0%.
Claims (6)
1. a kind of high-voltage motor preparation method of high osmosis impregnating varnish, includes the following steps:
(1) by 10~25 parts of cis-butenedioic anhydride, 5~15 parts of monounsaturated dicarboxylic acid, 10~30 parts of dihydric alcohol, 0~10 part of polyalcohol and monohydric alcohol
10~25 parts are warming up to 170~215 DEG C by mass fraction after mixing, carry out esterification, with -0.099~-
The pressure of 0.0999MPa vacuumizes 30~120min, after being cooled to 160~180 DEG C by mass fraction be added stabilizer 0.005~
0.5 part is uniformly mixed, then naturally cools to 30~50 DEG C, and 0.5~1.5 part of initiator and crosslinking agent finally is added by mass fraction
3~20 parts and the uniformly mixed low viscosity unsaturated polyester resin to get to viscosity no more than 80s;
(2) low viscosity epoxy resin and cis-butenedioic anhydride are warming up to 100~150 DEG C by quality proportioning 1:0.1~1 after mixing, warp
It is molten that epoxy-ester curing agent is added by the quality proportioning 1:0.01~0.06 of low viscosity epoxy ester and epoxy-ester curing agent in esterification
Solution is to get the low viscosity epoxy ester for being not more than 80s to viscosity;
(3) by the low viscosity unsaturated polyester resin obtained after step (1) and the low viscosity epoxy ester obtained after step (2) by low
It stirs evenly after 40~85 mass parts of viscosity unsaturated polyester resin and the mixing of 15~60 mass parts of low viscosity epoxy ester to get arriving
High-voltage motor high osmosis impregnating varnish.
2. preparation method according to claim 1, which is characterized in that in the step (1), monounsaturated dicarboxylic acid includes isophthalic
One or more of dioctyl phthalate, succinic acid, glutaric acid, adipic acid and sebacic acid;The dihydric alcohol includes neopentyl glycol, second two
One or more of alcohol, propylene glycol, butanediol and diglycol;The polyalcohol includes match gram, glycerine and three hydroxyls
One or more of methyl ethane;The monohydric alcohol includes imidohydrine, n-butanol, isobutanol, neopentyl alcohol, n-octyl alcohol and different pungent
One or more of pure and mild glycol monoethyl ether.
3. preparation method according to claim 1, which is characterized in that in the step (1), the stabilizer includes to benzene
Quinone, hydroquinone, p-tert-Butylcatechol, methylnaphthohydroquinone, bis- uncle of p-hydroxyanisole, 2- tert-butyl hydroquinone and 2,5-
One or more of butylhydroquinone.
4. preparation method according to claim 1, which is characterized in that in the step (1), the initiator includes peroxide
Change diisopropylbenzene (DIPB), bis- (tert-butyl peroxide) hexanes of 2,5- dimethyl -2,5-, peroxidized t-butyl perbenzoate and benzoyl peroxide first
One or more of acyl.
5. preparation method according to claim 1, which is characterized in that in the step (1), the crosslinking agent includes new penta
Omega-diol diacrylate or its prepolymer, ethoxylated bisphenol A diacrylate or its prepolymer, ethoxylated bisphenol A dimethyl propylene
Olefin(e) acid ester or its prepolymer, tri (propylene glycol) diacrylate or its prepolymer, 1,6 hexanediol diacrylate or its is pre-
Polymers, trimethylolpropane trimethacrylate or its prepolymer, 1,4 butanediol diacrylate or its prepolymer, pentaerythrite
Tetrapropylene acid or its prepolymer, pentaerythritol triacrylate or its prepolymer, isobornyl acrylate or its prepolymer, epoxy
Acrylic ester or its prepolymer, ethoxylation ring alcohol acrylate or its prepolymer, diethylene glycol phthalate diacrylate
Or one or more of its prepolymer, diallyphthalate acid esters or its prepolymer.
6. preparation method according to claim 1, which is characterized in that in the step (2), the epoxy-ester curing agent packet
Include one of zinc Isoocatanoate, aluminium acetylacetonate, zinc acetylacetonate, chromium acetylacetonate, calcium acetylacetonate and acetylacetone cobalt or
It is several.