CN106367828A - Preparation method of badminton netting lines - Google Patents
Preparation method of badminton netting lines Download PDFInfo
- Publication number
- CN106367828A CN106367828A CN201610766115.0A CN201610766115A CN106367828A CN 106367828 A CN106367828 A CN 106367828A CN 201610766115 A CN201610766115 A CN 201610766115A CN 106367828 A CN106367828 A CN 106367828A
- Authority
- CN
- China
- Prior art keywords
- temperature
- netting twine
- polymer mix
- obtains
- mix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of badminton netting lines. The preparation method comprises the following steps that 1 material preparation is performed: 85 g of PVC resin, 22 g of polyethylene fiber, 8 g of calcium-based bentonite, 8 g of 3-diethylamine propylamine, 3 g of titanium dioxide nano powder, 2 g of sodium dodecyl benzene sulfonate, 2 g of silica nano powder, 5 g of alkylene glycol phenyl ether, 2-4 g of sulfonated lignin, 1-3 g of extinction powder, 2-4 g of antioxidant RD, 5-7 g of dimethyl silicone oil, 1-3 g of nano-zinc oxide and 120-140 g of organic solvent; 2, crushing and mixing are performed; 3, dispersion is performed; 4, centrifugation is performed; 5, extrusion is performed; 6, spinning is performed; 7, paint spraying is performed; 8, rolling is performed. The preparation method is scientific, convenient to operate, low in preparation cost, environmentally friendly and non-toxic, the properties of netting lines are comprehensively improved, and a badminton made by adopting the badminton netting lines is good in usage effect, long in service life and suitable for a wide range of promotion and is favored by consumers.
Description
Technical field
The present invention relates to sports goods technical field, more particularly, to a kind of manufacture method of racket netting twine.
Background technology
Shuttlecock is an indoor and outdoor motion taking into account.According to the number participating in, singles and doubles can be divided into, and
Emerging 3v3 rule.
Racket netting twine is the important component part of racket.Selection racket netting twine main points:
1st, badminton line has different levels in terms of ballistic properties, durable performance, ball-handling performance, vibration absorbing performance, batting feel
Zu He not be with special production technology, to meet the combination needs of dissimilar player, different racket and different play.
2nd, select typically to be selected according to the needs of your racket type, requirement, play, just on the market during plumage line
Various plumage lines from the point of view of, for amateurish competitor or yonex bg65 is first-selected.
3rd, bracing wire is also to be worthy of careful study very much it is proposed that primary player is to there being professional drawing machine, and the place of professional bracing wire master worker is gone
It is proposed that being separated using the horizontal, vertical line that yonex recommends, 4 points of your plumage lines of professional bracing wire Fa Laila tied a knot, using bat line for bracing wire
Poundage be generally: horizontal 24 pounds of doubles, perpendicular 22 pounds;Horizontal 22 pounds of singles, perpendicular 20 pounds (woman can subtract 1-2 pound), sportsman
The suitable poundage of oneself can be adjusted according to this method, this new hand is entered into the regular road played ball, be maintained at from now on ball-handling,
Lob, kill, chopping the chop, putting the actions such as net optimal batting sensation aspect all beneficial.
How the present invention is with regard to improving badminton line at aspects such as vibration absorbing performance, durable performance, ball-handling performance, batting feels
Can, a kind of manufacture method of racket netting twine is provided.
Content of the invention
For overcoming above-mentioned deficiency, the present invention provides a kind of manufacture method of racket netting twine.
The present invention takes technical scheme below to realize: a kind of manufacture method of racket netting twine, it include with
Lower step: (1) dispensing: described racket netting twine is made up of following raw material: pvc resin 85g, polyethylene fibre 22g, calcium
Base bentonite 8g, 3- diethyl amino propylamine 8g, titanic oxide nano powder 3g, dodecylbenzene sodium sulfonate 2g, silicon dioxide are received
Rice flour end 2g, two aklylene glycol phenyl ether 5g, lignosulfonate 2-4g, flatting silica 1-3g, antioxidant rd2-4g, dimethyl-silicon
Oily 5-7g, nano zine oxide 1-3g, organic solvent 120-140g;
(2) it is pulverized and mixed: a, by pvc resin, polyethylene fibre, calcium-base bentonite, 3- diethyl amino propylamine, detergent alkylate
Sodium sulfonate mixes after pulverizing respectively, obtains pre-polymer mix a;
B, two aklylene glycol phenyl ethers, lignosulfonate, flatting silica, antioxidant are pulverized respectively after mix, obtain
Pre-polymer mix b;
C, by above-mentioned pre-polymer mix a, pre-polymer mix b mix after at a temperature of 45-55 DEG C stirring 34-40min after, then
Carry out supersound process 20-22min, ultrasonic power is 800-1000w, is down to room temperature and obtains final product pre-polymer mix c at a temperature of being somebody's turn to do;
(3) disperse: by above-mentioned pre-polymer mix c, and add titanic oxide nano powder, silica nano-powders, nanometer
Zinc oxide and organic solvent adopt disc type stirring paddle (1500rpm) dispersion 42-48min at a high speed, obtain mixed liquor a;
(4) it is centrifuged: the mixed liquor a after above-mentioned dispersion is utilized centrifuge, and is dried to obtain mixture d;
(5) extrude: the mixture d after above-mentioned centrifugation is added extruder extrusion, one section of temperature of extruder is 135-137 DEG C, two
Duan Wendu is 140-144 DEG C, and three sections of temperature are 145-147 DEG C, and latter end temperature is 140-142 DEG C, obtains extrudate e;
(6) spray webbing: extrudate e is added spray webbing case and adds dimethicone to carry out wire drawing, then carry out drawing-off, the first drawing-off
Roller pressure is 0.75bar, the second drawing-off roller pressure is 2.10bar, is then dried at 65 DEG C, obtains netting twine first product;
(7) paint: electrostatic painting process spray paint is utilized to netting twine first product surface obtained above, and naturally dries in the air at 35 DEG C
Dry;Wherein, the constitutive material of described paint is: butyl titanate 52g, pan base carbon fibre 12g, natural jade powder 5g, diethyl two
Alcohol phenyl ether 2g, 1- ethanamidine base-second river -1.1- di 2 ethylhexyl phosphonic acid 3g, tetrabutyl ammonium bromide 3g, sodium carbonate 6g, stibium oxide 1g, acrylic acid
Ester emulsion 70g, arabic gum 40g and organic silicone oil 9g;
(8) rolling: be wound using take-up roll, first winding roller rotating speed is 1000-1200m/min, second winding roller rotating speed
For 1500-1600m/min, the 3rd take-up roll rotating speed is 2000-2200m/min, carries out further drawing-off, is then wound into
Volume, obtains final product a kind of racket netting twine finished product.
Further scheme as the present invention: it comprises the following steps: (1) dispensing: described racket netting twine be by with
Under raw material composition: pvc resin 85g, polyethylene fibre 22g, calcium-base bentonite 8g, 3- diethyl amino propylamine 8g, titanium dioxide
Nanometer powder 3g, dodecylbenzene sodium sulfonate 2g, silica nano-powders 2g, two aklylene glycol phenyl ether 5g, sulfonation wood
Quality 2g, flatting silica 1g, antioxidant rd2g, dimethicone 5g, nano zine oxide 1g, organic solvent 120g;
(2) it is pulverized and mixed: a, by pvc resin, polyethylene fibre, calcium-base bentonite, 3- diethyl amino propylamine, detergent alkylate
Sodium sulfonate mixes after pulverizing respectively, obtains pre-polymer mix a;
B, two aklylene glycol phenyl ethers, lignosulfonate, flatting silica, antioxidant are pulverized respectively after mix, obtain
Pre-polymer mix b;
C, above-mentioned pre-polymer mix a, pre-polymer mix b are mixed after after stirring 34min at a temperature of 45 DEG C, then in this temperature
Under carry out supersound process 20min, ultrasonic power be 800w, be down to room temperature and obtain final product pre-polymer mix c;
(3) disperse: by above-mentioned pre-polymer mix c, and add titanic oxide nano powder, silica nano-powders, nanometer
Zinc oxide and organic solvent adopt disc type stirring paddle (1500rpm) dispersion 42min at a high speed, obtain mixed liquor a;
(4) it is centrifuged: the mixed liquor a after above-mentioned dispersion is utilized centrifuge, and is dried to obtain mixture d;
(5) extrude: the mixture d after above-mentioned centrifugation is added extruder extrusion, one section of temperature of extruder is 135 DEG C, two-stage nitration temperature
Spend for 140 DEG C, three sections of temperature are 145 DEG C, and latter end temperature is 140 DEG C, obtains extrudate e;
(6) spray webbing: extrudate e is added spray webbing case and adds dimethicone to carry out wire drawing, then carry out drawing-off, the first drawing-off
Roller pressure is 0.75bar, the second drawing-off roller pressure is 2.10bar, is then dried at 65 DEG C, obtains netting twine first product;
(7) paint: electrostatic painting process spray paint is utilized to netting twine first product surface obtained above, and naturally dries in the air at 35 DEG C
Dry;Wherein, the constitutive material of described paint is: butyl titanate 52g, pan base carbon fibre 12g, natural jade powder 5g, diethyl two
Alcohol phenyl ether 2g, 1- ethanamidine base-second river -1.1- di 2 ethylhexyl phosphonic acid 3g, tetrabutyl ammonium bromide 3g, sodium carbonate 6g, stibium oxide 1g, acrylic acid
Ester emulsion 70g, arabic gum 40g and organic silicone oil 9g;
(8) rolling: be wound using take-up roll, first winding roller rotating speed is 1000m/min, second winding roller rotating speed is
1500m/min, the 3rd take-up roll rotating speed is 2000m/min, carries out further drawing-off, is then wound rolling, obtains final product one kind
Racket netting twine finished product.
Further scheme as the present invention: it comprises the following steps: (1) dispensing: described racket netting twine be by with
Under raw material composition: pvc resin 85g, polyethylene fibre 22g, calcium-base bentonite 8g, 3- diethyl amino propylamine 8g, titanium dioxide
Nanometer powder 3g, dodecylbenzene sodium sulfonate 2g, silica nano-powders 2g, two aklylene glycol phenyl ether 5g, sulfonation wood
Quality 3g, flatting silica 2g, antioxidant rd3g, dimethicone 6g, nano zine oxide 2g, organic solvent 130g;
(2) it is pulverized and mixed: a, by pvc resin, polyethylene fibre, calcium-base bentonite, 3- diethyl amino propylamine, detergent alkylate
Sodium sulfonate mixes after pulverizing respectively, obtains pre-polymer mix a;
B, two aklylene glycol phenyl ethers, lignosulfonate, flatting silica, antioxidant are pulverized respectively after mix, obtain
Pre-polymer mix b;
C, above-mentioned pre-polymer mix a, pre-polymer mix b are mixed after after stirring 37min at a temperature of 50 DEG C, then in this temperature
Under carry out supersound process 21min, ultrasonic power be 900w, be down to room temperature and obtain final product pre-polymer mix c;
(3) disperse: by above-mentioned pre-polymer mix c, and add titanic oxide nano powder, silica nano-powders, nanometer
Zinc oxide and organic solvent adopt disc type stirring paddle (1500rpm) dispersion 45min at a high speed, obtain mixed liquor a;
(4) it is centrifuged: the mixed liquor a after above-mentioned dispersion is utilized centrifuge, and is dried to obtain mixture d;
(5) extrude: the mixture d after above-mentioned centrifugation is added extruder extrusion, one section of temperature of extruder is 136 DEG C, two-stage nitration temperature
Spend for 142 DEG C, three sections of temperature are 146 DEG C, and latter end temperature is 141 DEG C, obtains extrudate e;
(6) spray webbing: extrudate e is added spray webbing case and adds dimethicone to carry out wire drawing, then carry out drawing-off, the first drawing-off
Roller pressure is 0.75bar, the second drawing-off roller pressure is 2.10bar, is then dried at 65 DEG C, obtains netting twine first product;
(7) paint: electrostatic painting process spray paint is utilized to netting twine first product surface obtained above, and naturally dries in the air at 35 DEG C
Dry;Wherein, the constitutive material of described paint is: butyl titanate 52g, pan base carbon fibre 12g, natural jade powder 5g, diethyl two
Alcohol phenyl ether 2g, 1- ethanamidine base-second river -1.1- di 2 ethylhexyl phosphonic acid 3g, tetrabutyl ammonium bromide 3g, sodium carbonate 6g, stibium oxide 1g, acrylic acid
Ester emulsion 70g, arabic gum 40g and organic silicone oil 9g;
(8) rolling: be wound using take-up roll, first winding roller rotating speed is 1100m/min, second winding roller rotating speed is
1550m/min, the 3rd take-up roll rotating speed is 2100m/min, carries out further drawing-off, is then wound rolling, obtains final product one kind
Racket netting twine finished product.
Further scheme as the present invention: it comprises the following steps: (1) dispensing: described racket netting twine be by with
Under raw material composition: pvc resin 85g, polyethylene fibre 22g, calcium-base bentonite 8g, 3- diethyl amino propylamine 8g, titanium dioxide
Nanometer powder 3g, dodecylbenzene sodium sulfonate 2g, silica nano-powders 2g, two aklylene glycol phenyl ether 5g, sulfonation wood
Quality 4g, flatting silica 3g, antioxidant rd4g, dimethicone 7g, nano zine oxide 3g, organic solvent 140g;
(2) it is pulverized and mixed: a, by pvc resin, polyethylene fibre, calcium-base bentonite, 3- diethyl amino propylamine, detergent alkylate
Sodium sulfonate mixes after pulverizing respectively, obtains pre-polymer mix a;
B, two aklylene glycol phenyl ethers, lignosulfonate, flatting silica, antioxidant are pulverized respectively after mix, obtain
Pre-polymer mix b;
C, above-mentioned pre-polymer mix a, pre-polymer mix b are mixed after after stirring 40min at a temperature of 55 DEG C, then in this temperature
Under carry out supersound process 22min, ultrasonic power be 1000w, be down to room temperature and obtain final product pre-polymer mix c;
(3) disperse: by above-mentioned pre-polymer mix c, and add titanic oxide nano powder, silica nano-powders, nanometer
Zinc oxide and organic solvent adopt disc type stirring paddle (1500rpm) dispersion 48min at a high speed, obtain mixed liquor a;
(4) it is centrifuged: the mixed liquor a after above-mentioned dispersion is utilized centrifuge, and is dried to obtain mixture d;
(5) extrude: the mixture d after above-mentioned centrifugation is added extruder extrusion, one section of temperature of extruder is 137 DEG C, two-stage nitration temperature
Spend for 144 DEG C, three sections of temperature are 147 DEG C, and latter end temperature is 142 DEG C, obtains extrudate e;
(6) spray webbing: extrudate e is added spray webbing case and adds dimethicone to carry out wire drawing, then carry out drawing-off, the first drawing-off
Roller pressure is 0.75bar, the second drawing-off roller pressure is 2.10bar, is then dried at 65 DEG C, obtains netting twine first product;
(7) paint: electrostatic painting process spray paint is utilized to netting twine first product surface obtained above, and naturally dries in the air at 35 DEG C
Dry;Wherein, the constitutive material of described paint is: butyl titanate 52g, pan base carbon fibre 12g, natural jade powder 5g, diethyl two
Alcohol phenyl ether 2g, 1- ethanamidine base-second river -1.1- di 2 ethylhexyl phosphonic acid 3g, tetrabutyl ammonium bromide 3g, sodium carbonate 6g, stibium oxide 1g, acrylic acid
Ester emulsion 70g, arabic gum 40g and organic silicone oil 9g;
(8) rolling: be wound using take-up roll, first winding roller rotating speed is 1200m/min, second winding roller rotating speed is
1600m/min, the 3rd take-up roll rotating speed is 2200m/min, carries out further drawing-off, is then wound rolling, obtains final product one kind
Racket netting twine finished product.
Further scheme as the present invention: the preparation method of the paint of described step (7) is: described paint is removed propylene
Pulverize after all components mixing outside acid esters emulsion, arabic gum and organic silicone oil, cross 200 mesh sieves, mix, plus
Enter acrylic acid ester emulsion, stir 60min at a temperature of 50 DEG C, stir and be cooled to room temperature, add organic silicone oil, shaking is mixed
After conjunction, soaked overnight, obtain the first mixed liquor;First mixed liquor is mixed with arabic gum, heating in water bath, to 78 DEG C, stirs
55min, then carry out supersound process 15min at such a temperature, ultrasonic power is 800w, is down to room temperature and obtains final product described paint.
In sum the method have the advantages that the present invention provides a kind of manufacture method of racket netting twine,
Preparation method science, is easy to operate, low manufacture cost, and is painted, and environment-protecting asepsis comprehensively improve each side of netting twine
Can, using the racket of present invention preparation, using effect is good, long service life, is deeply liked by consumer, particularly in absorbing
Performance, durable performance, resistance to impact, thermostability, ballistic properties, the batting aspect such as good hand touch have excellent effect it is adaptable to big
Scope is promoted.
Specific embodiment
Technological means, creation characteristic, reached purpose and effect for making the present invention realize are easy to understand, with reference to
Specific embodiment, is expanded on further the present invention.
A kind of manufacture method of racket netting twine of embodiment 1
A kind of manufacture method of racket netting twine, it comprises the following steps: (1) dispensing: described racket netting twine be by with
Under raw material composition: pvc resin 85g, polyethylene fibre 22g, calcium-base bentonite 8g, 3- diethyl amino propylamine 8g, titanium dioxide
Nanometer powder 3g, dodecylbenzene sodium sulfonate 2g, silica nano-powders 2g, two aklylene glycol phenyl ether 5g, sulfonation wood
Quality 2g, flatting silica 1g, antioxidant rd2g, dimethicone 5g, nano zine oxide 1g, organic solvent 120g;
(2) it is pulverized and mixed: a, by pvc resin, polyethylene fibre, calcium-base bentonite, 3- diethyl amino propylamine, detergent alkylate
Sodium sulfonate mixes after pulverizing respectively, obtains pre-polymer mix a;
B, two aklylene glycol phenyl ethers, lignosulfonate, flatting silica, antioxidant are pulverized respectively after mix, obtain
Pre-polymer mix b;
C, above-mentioned pre-polymer mix a, pre-polymer mix b are mixed after after stirring 34min at a temperature of 45 DEG C, then in this temperature
Under carry out supersound process 20min, ultrasonic power be 800w, be down to room temperature and obtain final product pre-polymer mix c;
(3) disperse: by above-mentioned pre-polymer mix c, and add titanic oxide nano powder, silica nano-powders, nanometer
Zinc oxide and organic solvent adopt disc type stirring paddle (1500rpm) dispersion 42min at a high speed, obtain mixed liquor a;
(4) it is centrifuged: the mixed liquor a after above-mentioned dispersion is utilized centrifuge, and is dried to obtain mixture d;
(5) extrude: the mixture d after above-mentioned centrifugation is added extruder extrusion, one section of temperature of extruder is 135 DEG C, two-stage nitration temperature
Spend for 140 DEG C, three sections of temperature are 145 DEG C, and latter end temperature is 140 DEG C, obtains extrudate e;
(6) spray webbing: extrudate e is added spray webbing case and adds dimethicone to carry out wire drawing, then carry out drawing-off, the first drawing-off
Roller pressure is 0.75bar, the second drawing-off roller pressure is 2.10bar, is then dried at 65 DEG C, obtains netting twine first product;
(7) paint: electrostatic painting process spray paint is utilized to netting twine first product surface obtained above, and naturally dries in the air at 35 DEG C
Dry;Wherein, the constitutive material of described paint is: butyl titanate 52g, pan base carbon fibre 12g, natural jade powder 5g, diethyl two
Alcohol phenyl ether 2g, 1- ethanamidine base-second river -1.1- di 2 ethylhexyl phosphonic acid 3g, tetrabutyl ammonium bromide 3g, sodium carbonate 6g, stibium oxide 1g, acrylic acid
Ester emulsion 70g, arabic gum 40g and organic silicone oil 9g;
(8) rolling: be wound using take-up roll, first winding roller rotating speed is 1000m/min, second winding roller rotating speed is
1500m/min, the 3rd take-up roll rotating speed is 2000m/min, carries out further drawing-off, is then wound rolling, obtains final product one kind
Racket netting twine finished product.
A kind of manufacture method of racket netting twine of embodiment 2
A kind of manufacture method of racket netting twine, it comprises the following steps: (1) dispensing: described racket netting twine be by with
Under raw material composition: pvc resin 85g, polyethylene fibre 22g, calcium-base bentonite 8g, 3- diethyl amino propylamine 8g, titanium dioxide
Nanometer powder 3g, dodecylbenzene sodium sulfonate 2g, silica nano-powders 2g, two aklylene glycol phenyl ether 5g, sulfonation wood
Quality 3g, flatting silica 2g, antioxidant rd3g, dimethicone 6g, nano zine oxide 2g, organic solvent 130g;
(2) it is pulverized and mixed: a, by pvc resin, polyethylene fibre, calcium-base bentonite, 3- diethyl amino propylamine, detergent alkylate
Sodium sulfonate mixes after pulverizing respectively, obtains pre-polymer mix a;
B, two aklylene glycol phenyl ethers, lignosulfonate, flatting silica, antioxidant are pulverized respectively after mix, obtain
Pre-polymer mix b;
C, above-mentioned pre-polymer mix a, pre-polymer mix b are mixed after after stirring 37min at a temperature of 50 DEG C, then in this temperature
Under carry out supersound process 21min, ultrasonic power be 900w, be down to room temperature and obtain final product pre-polymer mix c;
(3) disperse: by above-mentioned pre-polymer mix c, and add titanic oxide nano powder, silica nano-powders, nanometer
Zinc oxide and organic solvent adopt disc type stirring paddle (1500rpm) dispersion 45min at a high speed, obtain mixed liquor a;
(4) it is centrifuged: the mixed liquor a after above-mentioned dispersion is utilized centrifuge, and is dried to obtain mixture d;
(5) extrude: the mixture d after above-mentioned centrifugation is added extruder extrusion, one section of temperature of extruder is 136 DEG C, two-stage nitration temperature
Spend for 142 DEG C, three sections of temperature are 146 DEG C, and latter end temperature is 141 DEG C, obtains extrudate e;
(6) spray webbing: extrudate e is added spray webbing case and adds dimethicone to carry out wire drawing, then carry out drawing-off, the first drawing-off
Roller pressure is 0.75bar, the second drawing-off roller pressure is 2.10bar, is then dried at 65 DEG C, obtains netting twine first product;
(7) paint: electrostatic painting process spray paint is utilized to netting twine first product surface obtained above, and naturally dries in the air at 35 DEG C
Dry;Wherein, the constitutive material of described paint is: butyl titanate 52g, pan base carbon fibre 12g, natural jade powder 5g, diethyl two
Alcohol phenyl ether 2g, 1- ethanamidine base-second river -1.1- di 2 ethylhexyl phosphonic acid 3g, tetrabutyl ammonium bromide 3g, sodium carbonate 6g, stibium oxide 1g, acrylic acid
Ester emulsion 70g, arabic gum 40g and organic silicone oil 9g;
(8) rolling: be wound using take-up roll, first winding roller rotating speed is 1100m/min, second winding roller rotating speed is
1550m/min, the 3rd take-up roll rotating speed is 2100m/min, carries out further drawing-off, is then wound rolling, obtains final product one kind
Racket netting twine finished product.
A kind of manufacture method of racket netting twine of embodiment 3
A kind of manufacture method of racket netting twine, it comprises the following steps: (1) dispensing: described racket netting twine be by with
Under raw material composition: pvc resin 85g, polyethylene fibre 22g, calcium-base bentonite 8g, 3- diethyl amino propylamine 8g, titanium dioxide
Nanometer powder 3g, dodecylbenzene sodium sulfonate 2g, silica nano-powders 2g, two aklylene glycol phenyl ether 5g, sulfonation wood
Quality 4g, flatting silica 3g, antioxidant rd4g, dimethicone 7g, nano zine oxide 3g, organic solvent 140g;
(2) it is pulverized and mixed: a, by pvc resin, polyethylene fibre, calcium-base bentonite, 3- diethyl amino propylamine, detergent alkylate
Sodium sulfonate mixes after pulverizing respectively, obtains pre-polymer mix a;
B, two aklylene glycol phenyl ethers, lignosulfonate, flatting silica, antioxidant are pulverized respectively after mix, obtain
Pre-polymer mix b;
C, above-mentioned pre-polymer mix a, pre-polymer mix b are mixed after after stirring 40min at a temperature of 55 DEG C, then in this temperature
Under carry out supersound process 22min, ultrasonic power be 1000w, be down to room temperature and obtain final product pre-polymer mix c;
(3) disperse: by above-mentioned pre-polymer mix c, and add titanic oxide nano powder, silica nano-powders, nanometer
Zinc oxide and organic solvent adopt disc type stirring paddle (1500rpm) dispersion 48min at a high speed, obtain mixed liquor a;
(4) it is centrifuged: the mixed liquor a after above-mentioned dispersion is utilized centrifuge, and is dried to obtain mixture d;
(5) extrude: the mixture d after above-mentioned centrifugation is added extruder extrusion, one section of temperature of extruder is 137 DEG C, two-stage nitration temperature
Spend for 144 DEG C, three sections of temperature are 147 DEG C, and latter end temperature is 142 DEG C, obtains extrudate e;
(6) spray webbing: extrudate e is added spray webbing case and adds dimethicone to carry out wire drawing, then carry out drawing-off, the first drawing-off
Roller pressure is 0.75bar, the second drawing-off roller pressure is 2.10bar, is then dried at 65 DEG C, obtains netting twine first product;
(7) paint: electrostatic painting process spray paint is utilized to netting twine first product surface obtained above, and naturally dries in the air at 35 DEG C
Dry;Wherein, the constitutive material of described paint is: butyl titanate 52g, pan base carbon fibre 12g, natural jade powder 5g, diethyl two
Alcohol phenyl ether 2g, 1- ethanamidine base-second river -1.1- di 2 ethylhexyl phosphonic acid 3g, tetrabutyl ammonium bromide 3g, sodium carbonate 6g, stibium oxide 1g, acrylic acid
Ester emulsion 70g, arabic gum 40g and organic silicone oil 9g;
(8) rolling: be wound using take-up roll, first winding roller rotating speed is 1200m/min, second winding roller rotating speed is
1600m/min, the 3rd take-up roll rotating speed is 2200m/min, carries out further drawing-off, is then wound rolling, obtains final product one kind
Racket netting twine finished product.
Further scheme as the present invention: the preparation method of the paint of described step (7) is: described paint is removed propylene
Pulverize after all components mixing outside acid esters emulsion, arabic gum and organic silicone oil, cross 200 mesh sieves, mix, plus
Enter acrylic acid ester emulsion, stir 60min at a temperature of 50 DEG C, stir and be cooled to room temperature, add organic silicone oil, shaking is mixed
After conjunction, soaked overnight, obtain the first mixed liquor;First mixed liquor is mixed with arabic gum, heating in water bath, to 78 DEG C, stirs
55min, then carry out supersound process 15min at such a temperature, ultrasonic power is 800w, is down to room temperature and obtains final product described paint.
Comparative example 1
Racket netting twine on the market.
Using the racket netting twine of embodiment 1-3 preparation and the racket netting twine system on the market of comparative example 1
Make racket, the netting twine poundage of use is: horizontal 24 pounds, perpendicular 22 pounds;Feather prepared by embodiment of the present invention 1-3, comparative example 1
Racket supplies 400 athletes and uses, and is randomly divided into 4 groups, every group of 100 people, wherein male 200 people, women 200 people.
Detection project: ballistic properties, durable performance, resistance to impact, thermostability, vibration absorbing performance, batting good hand touch etc..
Testing result: as shown in table 1.
Table 1 is the main performance testing results of the racket of the netting twine preparation using embodiment 1-3, comparative example 1
Detection project | Embodiment 1/ people | Embodiment 2/ people | Embodiment 3/ people | Comparative example 1/ people |
Ballistic properties are good | 98 | 96 | 93 | 81 |
Durable performance is good | 91 | 92 | 89 | 57 |
Resistance to impact is good | 85 | 90 | 82 | 62 |
Heat-resist | 91 | 95 | 96 | 72 |
Vibration absorbing performance is good | 83 | 81 | 78 | 64 |
Batting good hand touch | 93 | 94 | 91 | 86 |
As known from Table 1, it is all remarkably higher than comparative example 1 market using the racket netting twine various aspects of performance of embodiment 1-3 preparation
The racket twisted-pair production racket of upper sale, is liked by consumer deeply.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of the spirit or essential attributes of the present invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.
Moreover, it will be appreciated that although this specification is been described by according to embodiment, not each embodiment only wraps
Containing an independent technical scheme, only for clarity, those skilled in the art should for this narrating mode of description
Using description as an entirety, the technical scheme in each embodiment can also form those skilled in the art through appropriately combined
Understandable other embodiment.
Claims (5)
1. a kind of manufacture method of racket netting twine is it is characterised in that it comprises the following steps: (1) dispensing: described shuttlecock
Catgut string is made up of following raw material: pvc resin 85g, polyethylene fibre 22g, calcium-base bentonite 8g, 3- diethyl amino propylamine
8g, titanic oxide nano powder 3g, dodecylbenzene sodium sulfonate 2g, silica nano-powders 2g, two aklylene glycol phenyl
Ether 5g, lignosulfonate 2-4g, flatting silica 1-3g, antioxidant rd2-4g, dimethicone 5-7g, nano zine oxide 1-3g, have
Machine solvent 120-140g;
(2) it is pulverized and mixed: a, by pvc resin, polyethylene fibre, calcium-base bentonite, 3- diethyl amino propylamine, detergent alkylate
Sodium sulfonate mixes after pulverizing respectively, obtains pre-polymer mix a;
B, two aklylene glycol phenyl ethers, lignosulfonate, flatting silica, antioxidant are pulverized respectively after mix, obtain
Pre-polymer mix b;
C, by above-mentioned pre-polymer mix a, pre-polymer mix b mix after at a temperature of 45-55 DEG C stirring 34-40min after, then
Carry out supersound process 20-22min, ultrasonic power is 800-1000w, is down to room temperature and obtains final product pre-polymer mix c at a temperature of being somebody's turn to do;
(3) disperse: by above-mentioned pre-polymer mix c, and add titanic oxide nano powder, silica nano-powders, nanometer
Zinc oxide and organic solvent adopt disc type stirring paddle (1500rpm) dispersion 42-48min at a high speed, obtain mixed liquor a;
(4) it is centrifuged: the mixed liquor a after above-mentioned dispersion is utilized centrifuge, and is dried to obtain mixture d;
(5) extrude: the mixture d after above-mentioned centrifugation is added extruder extrusion, one section of temperature of extruder is 135-137 DEG C, two
Duan Wendu is 140-144 DEG C, and three sections of temperature are 145-147 DEG C, and latter end temperature is 140-142 DEG C, obtains extrudate e;
(6) spray webbing: extrudate e is added spray webbing case and adds dimethicone to carry out wire drawing, then carry out drawing-off, the first drawing-off
Roller pressure is 0.75bar, the second drawing-off roller pressure is 2.10bar, is then dried at 65 DEG C, obtains netting twine first product;
(7) paint: electrostatic painting process spray paint is utilized to netting twine first product surface obtained above, and naturally dries in the air at 35 DEG C
Dry;Wherein, the constitutive material of described paint is: butyl titanate 52g, pan base carbon fibre 12g, natural jade powder 5g, diethyl two
Alcohol phenyl ether 2g, 1- ethanamidine base-second river -1.1- di 2 ethylhexyl phosphonic acid 3g, tetrabutyl ammonium bromide 3g, sodium carbonate 6g, stibium oxide 1g, acrylic acid
Ester emulsion 70g, arabic gum 40g and organic silicone oil 9g;
(8) rolling: be wound using take-up roll, first winding roller rotating speed is 1000-1200m/min, second winding roller rotating speed
For 1500-1600m/min, the 3rd take-up roll rotating speed is 2000-2200m/min, carries out further drawing-off, is then wound into
Volume, obtains final product a kind of racket netting twine finished product.
2. a kind of racket netting twine according to claim 1 preparation method it is characterised in that: it includes following step
Rapid: (1) dispensing: described racket netting twine is made up of following raw material: pvc resin 85g, polyethylene fibre 22g, calcio are swollen
Native 8g, 3- diethyl amino propylamine 8g of profit, titanic oxide nano powder 3g, dodecylbenzene sodium sulfonate 2g, silica nanometer powder
Last 2g, two aklylene glycol phenyl ether 5g, lignosulfonate 2g, flatting silica 1g, antioxidant rd2g, dimethicone 5g, nanometer
Zinc oxide 1g, organic solvent 120g;
(2) it is pulverized and mixed: a, by pvc resin, polyethylene fibre, calcium-base bentonite, 3- diethyl amino propylamine, detergent alkylate
Sodium sulfonate mixes after pulverizing respectively, obtains pre-polymer mix a;
B, two aklylene glycol phenyl ethers, lignosulfonate, flatting silica, antioxidant are pulverized respectively after mix, obtain
Pre-polymer mix b;
C, above-mentioned pre-polymer mix a, pre-polymer mix b are mixed after after stirring 34min at a temperature of 45 DEG C, then in this temperature
Under carry out supersound process 20min, ultrasonic power be 800w, be down to room temperature and obtain final product pre-polymer mix c;
(3) disperse: by above-mentioned pre-polymer mix c, and add titanic oxide nano powder, silica nano-powders, nanometer
Zinc oxide and organic solvent adopt disc type stirring paddle (1500rpm) dispersion 42min at a high speed, obtain mixed liquor a;
(4) it is centrifuged: the mixed liquor a after above-mentioned dispersion is utilized centrifuge, and is dried to obtain mixture d;
(5) extrude: the mixture d after above-mentioned centrifugation is added extruder extrusion, one section of temperature of extruder is 135 DEG C, two-stage nitration temperature
Spend for 140 DEG C, three sections of temperature are 145 DEG C, and latter end temperature is 140 DEG C, obtains extrudate e;
(6) spray webbing: extrudate e is added spray webbing case and adds dimethicone to carry out wire drawing, then carry out drawing-off, the first drawing-off
Roller pressure is 0.75bar, the second drawing-off roller pressure is 2.10bar, is then dried at 65 DEG C, obtains netting twine first product;
(7) paint: electrostatic painting process spray paint is utilized to netting twine first product surface obtained above, and naturally dries in the air at 35 DEG C
Dry;Wherein, the constitutive material of described paint is: butyl titanate 52g, pan base carbon fibre 12g, natural jade powder 5g, diethyl two
Alcohol phenyl ether 2g, 1- ethanamidine base-second river -1.1- di 2 ethylhexyl phosphonic acid 3g, tetrabutyl ammonium bromide 3g, sodium carbonate 6g, stibium oxide 1g, acrylic acid
Ester emulsion 70g, arabic gum 40g and organic silicone oil 9g;
(8) rolling: be wound using take-up roll, first winding roller rotating speed is 1000m/min, second winding roller rotating speed is
1500m/min, the 3rd take-up roll rotating speed is 2000m/min, carries out further drawing-off, is then wound rolling, obtains final product one kind
Racket netting twine finished product.
3. a kind of racket netting twine according to claim 1 preparation method it is characterised in that: it includes following step
Rapid: (1) dispensing: described racket netting twine is made up of following raw material: pvc resin 85g, polyethylene fibre 22g, calcio are swollen
Native 8g, 3- diethyl amino propylamine 8g of profit, titanic oxide nano powder 3g, dodecylbenzene sodium sulfonate 2g, silica nanometer powder
Last 2g, two aklylene glycol phenyl ether 5g, lignosulfonate 3g, flatting silica 2g, antioxidant rd3g, dimethicone 6g, nanometer
Zinc oxide 2g, organic solvent 130g;
(2) it is pulverized and mixed: a, by pvc resin, polyethylene fibre, calcium-base bentonite, 3- diethyl amino propylamine, detergent alkylate
Sodium sulfonate mixes after pulverizing respectively, obtains pre-polymer mix a;
B, two aklylene glycol phenyl ethers, lignosulfonate, flatting silica, antioxidant are pulverized respectively after mix, obtain
Pre-polymer mix b;
C, above-mentioned pre-polymer mix a, pre-polymer mix b are mixed after after stirring 37min at a temperature of 50 DEG C, then in this temperature
Under carry out supersound process 21min, ultrasonic power be 900w, be down to room temperature and obtain final product pre-polymer mix c;
(3) disperse: by above-mentioned pre-polymer mix c, and add titanic oxide nano powder, silica nano-powders, nanometer
Zinc oxide and organic solvent adopt disc type stirring paddle (1500rpm) dispersion 45min at a high speed, obtain mixed liquor a;
(4) it is centrifuged: the mixed liquor a after above-mentioned dispersion is utilized centrifuge, and is dried to obtain mixture d;
(5) extrude: the mixture d after above-mentioned centrifugation is added extruder extrusion, one section of temperature of extruder is 136 DEG C, two-stage nitration temperature
Spend for 142 DEG C, three sections of temperature are 146 DEG C, and latter end temperature is 141 DEG C, obtains extrudate e;
(6) spray webbing: extrudate e is added spray webbing case and adds dimethicone to carry out wire drawing, then carry out drawing-off, the first drawing-off
Roller pressure is 0.75bar, the second drawing-off roller pressure is 2.10bar, is then dried at 65 DEG C, obtains netting twine first product;
(7) paint: electrostatic painting process spray paint is utilized to netting twine first product surface obtained above, and naturally dries in the air at 35 DEG C
Dry;Wherein, the constitutive material of described paint is: butyl titanate 52g, pan base carbon fibre 12g, natural jade powder 5g, diethyl two
Alcohol phenyl ether 2g, 1- ethanamidine base-second river -1.1- di 2 ethylhexyl phosphonic acid 3g, tetrabutyl ammonium bromide 3g, sodium carbonate 6g, stibium oxide 1g, acrylic acid
Ester emulsion 70g, arabic gum 40g and organic silicone oil 9g;
(8) rolling: be wound using take-up roll, first winding roller rotating speed is 1100m/min, second winding roller rotating speed is
1550m/min, the 3rd take-up roll rotating speed is 2100m/min, carries out further drawing-off, is then wound rolling, obtains final product one kind
Racket netting twine finished product.
4. a kind of racket netting twine according to claim 1 preparation method it is characterised in that: it includes following step
Rapid: (1) dispensing: described racket netting twine is made up of following raw material: pvc resin 85g, polyethylene fibre 22g, calcio are swollen
Native 8g, 3- diethyl amino propylamine 8g of profit, titanic oxide nano powder 3g, dodecylbenzene sodium sulfonate 2g, silica nanometer powder
Last 2g, two aklylene glycol phenyl ether 5g, lignosulfonate 4g, flatting silica 3g, antioxidant rd4g, dimethicone 7g, nanometer
Zinc oxide 3g, organic solvent 140g;
(2) it is pulverized and mixed: a, by pvc resin, polyethylene fibre, calcium-base bentonite, 3- diethyl amino propylamine, detergent alkylate
Sodium sulfonate mixes after pulverizing respectively, obtains pre-polymer mix a;
B, two aklylene glycol phenyl ethers, lignosulfonate, flatting silica, antioxidant are pulverized respectively after mix, obtain
Pre-polymer mix b;
C, above-mentioned pre-polymer mix a, pre-polymer mix b are mixed after after stirring 40min at a temperature of 55 DEG C, then in this temperature
Under carry out supersound process 22min, ultrasonic power be 1000w, be down to room temperature and obtain final product pre-polymer mix c;
(3) disperse: by above-mentioned pre-polymer mix c, and add titanic oxide nano powder, silica nano-powders, nanometer
Zinc oxide and organic solvent adopt disc type stirring paddle (1500rpm) dispersion 48min at a high speed, obtain mixed liquor a;
(4) it is centrifuged: the mixed liquor a after above-mentioned dispersion is utilized centrifuge, and is dried to obtain mixture d;
(5) extrude: the mixture d after above-mentioned centrifugation is added extruder extrusion, one section of temperature of extruder is 137 DEG C, two-stage nitration temperature
Spend for 144 DEG C, three sections of temperature are 147 DEG C, and latter end temperature is 142 DEG C, obtains extrudate e;
(6) spray webbing: extrudate e is added spray webbing case and adds dimethicone to carry out wire drawing, then carry out drawing-off, the first drawing-off
Roller pressure is 0.75bar, the second drawing-off roller pressure is 2.10bar, is then dried at 65 DEG C, obtains netting twine first product;
(7) paint: electrostatic painting process spray paint is utilized to netting twine first product surface obtained above, and naturally dries in the air at 35 DEG C
Dry;Wherein, the constitutive material of described paint is: butyl titanate 52g, pan base carbon fibre 12g, natural jade powder 5g, diethyl two
Alcohol phenyl ether 2g, 1- ethanamidine base-second river -1.1- di 2 ethylhexyl phosphonic acid 3g, tetrabutyl ammonium bromide 3g, sodium carbonate 6g, stibium oxide 1g, acrylic acid
Ester emulsion 70g, arabic gum 40g and organic silicone oil 9g;
(8) rolling: be wound using take-up roll, first winding roller rotating speed is 1200m/min, second winding roller rotating speed is
1600m/min, the 3rd take-up roll rotating speed is 2200m/min, carries out further drawing-off, is then wound rolling, obtains final product one kind
Racket netting twine finished product.
5. a kind of racket netting twine according to claim 1 preparation method it is characterised in that: described step (7)
The preparation method of paint is: by all components in addition to acrylic acid ester emulsion, arabic gum and organic silicone oil for the described paint
Pulverize after mixing, cross 200 mesh sieves, mix, add acrylic acid ester emulsion, stir 60min, stirring at a temperature of 50 DEG C
Uniformly it is cooled to room temperature, add organic silicone oil, after shaking mixing, soaked overnight, obtain the first mixed liquor;By the first mixed liquor with
Arabic gum mixes, and heating in water bath, to 78 DEG C, stirs 55min, then carries out supersound process 15min, ultrasonic power at such a temperature
For 800w, it is down to room temperature and obtains final product described paint.