CN106366953A - 一种耐高温环保胶水 - Google Patents
一种耐高温环保胶水 Download PDFInfo
- Publication number
- CN106366953A CN106366953A CN201610748074.2A CN201610748074A CN106366953A CN 106366953 A CN106366953 A CN 106366953A CN 201610748074 A CN201610748074 A CN 201610748074A CN 106366953 A CN106366953 A CN 106366953A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- resistant environment
- glue
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种耐高温环保胶水,按重量份计包括:醋酸乙烯乳液50~70份、聚乙烯醇2~9份、木质素10~20份、二氧化硅8~20份、丙烯酸丁酯5~20份、骨胶聚羧酸系高性能减水剂6~10份和淀粉2~6份。本发明耐高温,不易脱落,粘结力强,经济环保,使用周期长。
Description
技术领域
本发明涉及精细化工技术领域液体燃料,具体是一种耐高温环保胶水。
背景技术
胶水涂在两个物体之间,当胶水中的水分消失后,胶水中的高分子体就依靠相互间的拉力,将两个物体紧紧的结合在一起,才能发挥粘接作用,物体的粘接,就是靠胶水中的高分子体间的拉力来实现的。当胶水处在高温环境中时,其粘结力受温度的影响而降低,致使其脱落,使用性受到很大影响。
发明内容
本发明所要解决的技术问题是提供一种耐高温环保胶水。
本发明解决上述技术问题的技术方案如下:一种耐高温环保胶水,按重量份计包括:
本发明的有益效果是:本发明耐高温,不易脱落,粘结力强,经济环保,使用周期长。
在上述技术方案的基础上,本发明还可以做如下改进。
优选的,按重量份计包括:
优选的,还包含有3~19重量份的钛白粉。
优选的,按重量份计包括:
优选的,所述醋酸乙烯乳液的浓度≥99.99%。
具体实施方式
实施例1
一种耐高温环保胶水,按重量份计包括:醋酸乙烯乳液70份、聚乙烯醇6份、木质素15份、二氧化硅15份、丙烯酸丁酯15份、聚羧酸系高性能减水剂8份和淀粉4份。
将各原料依次加入反应釜中,搅拌10分钟,充分混合均匀即可。
实施例2
一种耐高温环保胶水,按重量份计包括:醋酸乙烯乳液60份、聚乙烯醇7份、木质素11份、二氧化硅12份、丙烯酸丁酯13份、聚羧酸系高性能减水剂8份和淀粉3份。
将各原料依次加入反应釜中,搅拌10分钟,充分混合均匀即可。
实施例3
一种耐高温环保胶水,醋酸乙烯乳液70份、聚乙烯醇6份、木质素15份、二氧化硅15份、丙烯酸丁酯15份、聚羧酸系高性能减水剂8份、淀粉4份和钛白粉15份。
将各原料依次加入反应釜中,搅拌10分钟,充分混合均匀即可。
实施例4
一种耐高温环保胶水,按重量份计包括:醋酸乙烯乳液60份、聚乙烯醇7份、木质素11份、二氧化硅12份、丙烯酸丁酯13份、聚羧酸系高性能减水剂8份、淀粉3份和钛白粉10份。
将各原料依次加入反应釜中,搅拌10分钟,充分混合均匀即可。
对上述实施例4的高温环保胶水进行检验,结果如下:
实施例一 | 实施例一 | 实施例一 | 实施例一 | |
40° | 未融化 | 未融化 | 未融化 | 未融化 |
50° | 未融化 | 未融化 | 未融化 | 未融化 |
60° | 未融化 | 未融化 | 未融化 | 未融化 |
70° | 融化 | 未融化 | 未融化 | 融化 |
80° | 融化 | 融化 | 融化 | 融化 |
本发明耐高温,不易脱落,粘结力强,经济环保,使用周期长。
尽管上面已经示出和描述了本发明的实施例,可以理解的是,上述实施例是示例性的,不能理解为对本发明的限制,本领域的普通技术人员在本发明的范围内可以对上述实施例进行变化、修改、替换和变型。
Claims (5)
1.一种耐高温环保胶水,其特征在于,按重量份计包括:
2.根据权利要求1所述一种耐高温环保胶水,其特征在于,按重量份计包括:
3.根据权利要求1所述一种耐高温环保胶水,其特征在于,还包含有3~19重量份的钛白粉。
4.根据权利要求3所述一种耐高温环保胶水,其特征在于,按重量份计包括:
5.根据权利要求1所述一种耐高温环保胶水,其特征在于,所述醋酸乙烯乳液的浓度≥99.99%。