CN106365683A - Foamed cement brick - Google Patents
Foamed cement brick Download PDFInfo
- Publication number
- CN106365683A CN106365683A CN201610732103.6A CN201610732103A CN106365683A CN 106365683 A CN106365683 A CN 106365683A CN 201610732103 A CN201610732103 A CN 201610732103A CN 106365683 A CN106365683 A CN 106365683A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- foamed cement
- cement brick
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a foamed cement brick. The foamed cement brick is prepared from, by weight, 22-25 parts of pulverized fuel ash, 18-20 parts of silicate cement, 5-8 parts of sodium metasilicate, 8-10 parts of tail slag, 6-8 parts of stone powder, 4-6 parts of blast furnace water granulated slag, 2-4 parts of mortar crystals, 2-3 parts of cement foaming agent and 1-1.2 parts of sodium carbonate. The foamed cement brick is formed by stirring and coagulating small foam particles and cement and has the excellent performance of low weight, heat preservation, sound insulation and fireproofness; due to the fact that the small diameter is adopted, cost is greatly reduced, and the foamed cement brick is an ideal article of nonbearing walls.
Description
Technical field
The present invention relates to construction material, especially, it is related to a kind of foam water adobe.
Background technology
The compacting relying primarily on hydraulic test in cement brick production process forms, and then needs to enter raw material before shaping
Row mix and blend, it is most important that also needing to carry out rational proportioning, so can make and become the extraordinary cement of quality
Brick.So cement brick machine use raw material widely, substantially based on construction waste and industrial waste, these can
Help our reasonable employment, the cost of production can also be reduced simultaneously.So how to select rational proportioning raw materials, make cement brick
Performance reach standard require, simultaneously reduce cost of material be industry be worth study direction.
Content of the invention
Present invention aim at providing a kind of foam water adobe, to provide a kind of light weight, insulation, fire prevention, the water of low cost
Adobe.
For achieving the above object, the present invention provides a kind of foam water adobe, is made up of the component of following parts by weight: fine coal
Grey 22-25 part, portland cement 18-20 part, sodium silicate 5-8 part, mine tailings 8-10 part, stone powder 6-8 part, blast furnace granulated slag 4-6 part,
Rock sand essence 2-4 part, cement blowing agent 2-3 part, sodium carbonate 1-2.2 part.
Further, be made up of the component of following parts by weight: 23 parts of described flyash, 19 parts of described portland cement,
6 parts of described sodium silicate, 9 parts of described mine tailings, 7 parts of described stone powder, 5 parts of described blast furnace granulated slag, 3 parts of described rock sand essence, described water
2.4 parts of cement foaming agent, 2 parts of described sodium carbonate.
The method have the advantages that
This foam water adobe is to condense with cement mixing using foam little particle to form, and has lightweight, insulation, sound insulation, fireproof
High-quality performance, and greatly reduce cost due to employing the reason of minor diameter, it is the ideal of non-load bearing wall.
Specific embodiment
Hereinafter embodiments of the invention are described in detail.
The preferred embodiments of the present invention provide a kind of foam water adobe, are made up of the component of following parts by weight: fine coal
Grey 22-25 part, portland cement 18-20 part, sodium silicate 5-8 part, mine tailings 8-10 part, stone powder 6-8 part, blast furnace granulated slag 4-6 part,
Rock sand essence 2-4 part, cement blowing agent 2-3 part, sodium carbonate 1-2.2 part.
Preferably, it is made up of the component of following parts by weight: 23 parts of described flyash, 19 parts of described portland cement, institute
State 6 parts of sodium silicate, 9 parts of described mine tailings, 7 parts of described stone powder, 5 parts of described blast furnace granulated slag, 3 parts of described rock sand essence, described cement
2.4 parts of foaming agent, 2 parts of described sodium carbonate.
This foam water adobe is to condense with cement mixing using foam little particle to form, and has lightweight, insulation, sound insulation, prevents
The high-quality performance of fire, and greatly reduce cost due to employing the reason of minor diameter, it is the ideal of non-load bearing wall.
Embodiment 1
25 parts of flyash, 18 parts of portland cement, 8 parts of sodium silicate, 8 parts of mine tailings, 6 parts of stone powder, 4 parts of blast furnace granulated slag, rock sand essence 4
Part, 3 parts of cement blowing agent, 2.2 parts of sodium carbonate, the raw mill of above-mentioned parts by weight becomes powder, after adding blender mix homogeneously,
Plus suitable quantity of water direct pressing solidifies and makes.
Embodiment 2
23 parts of flyash, 19 parts of portland cement, 6 parts of sodium silicate, 9 parts of mine tailings, 7 parts of stone powder, 5 parts of blast furnace granulated slag, rock sand essence 3
Part, 2.4 parts of cement blowing agent, 2 parts of sodium carbonate, the raw mill of above-mentioned parts by weight becomes powder, after adding blender mix homogeneously,
Plus suitable quantity of water direct pressing solidifies and makes.
Embodiment 3
22 parts of flyash, 20 parts of portland cement, 5 parts of sodium silicate, 10 parts of mine tailings, 8 parts of stone powder, 6 parts of blast furnace granulated slag, rock sand essence
2 parts, 2 parts of cement blowing agent, 1 part of sodium carbonate, the raw mill of above-mentioned parts by weight becomes powder, after adding blender mix homogeneously,
Plus suitable quantity of water direct pressing solidifies and makes.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention；Skill for this area
For art personnel, the present invention can have various modifications and variations.All within the spirit and principles in the present invention, made any repair
Change, equivalent, improvement etc., should be included within the scope of the present invention.
Claims (2)
1. a kind of foam water adobe is it is characterised in that be made up of the component of following parts by weight:
Flyash 22-25 part, portland cement 18-20 part, sodium silicate 5-8 part, mine tailings 8-10 part, stone powder 6-8 part, blast furnace water
Slag 4-6 part, rock sand essence 2-4 part, cement blowing agent 2-3 part, sodium carbonate 1-2.2 part.
2. a kind of foam water adobe according to claim 1 is it is characterised in that be made up of the component of following parts by weight:
23 parts of described flyash, 19 parts of described portland cement, 6 parts of described sodium silicate, 9 parts of described mine tailings, described stone powder 7
Part, 3 parts of 5 parts of described blast furnace granulated slag, described rock sand essence, 2.4 parts of described cement blowing agent, 2 parts of described sodium carbonate.