CN106365671A - Low-stress high-strength anti-cracking inorganic thermal-insulation board - Google Patents
Low-stress high-strength anti-cracking inorganic thermal-insulation board Download PDFInfo
- Publication number
- CN106365671A CN106365671A CN201610737250.2A CN201610737250A CN106365671A CN 106365671 A CN106365671 A CN 106365671A CN 201610737250 A CN201610737250 A CN 201610737250A CN 106365671 A CN106365671 A CN 106365671A
- Authority
- CN
- China
- Prior art keywords
- parts
- insulation board
- water
- low stress
- inorganic heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a low-stress high-strength anti-cracking inorganic thermal-insulation board. The low-stress high-strength anti-cracking inorganic thermal-insulation board comprises, by mass, 170-190 parts of cement, 30-40 parts of admixture, 3-5 parts of hydrogen peroxide, 1-3 parts of polypropylene fibers, 85-95 parts of water and 3-7 parts of an additive. A novel formula and a novel method are adopted, in this way, while it is guaranteed that the thermal-insulation board has excellent mechanical properties, thermal insulation, heat insulation, waterproofness and moisture prevention are excellent, product quality is greatly improved, cracking and water seeping of the product can be effectively avoided, excellent performance indexes of all items can still be guaranteed when the low-stress high-strength anti-cracking inorganic thermal-insulation board is used at the later period, in addition, the cost is moderate, and the preparation method is simple.
Description
Technical field
The invention belongs to heat preservation technology field is and in particular to a kind of low stress high-strength anticracking inorganic heat-insulation board.
Background technology
Insulation material can not only play the protective effect to agent structures such as body of wall, bottom surfaces, can effectively reduce simultaneously
The impact to body interior of extraneous humiture and various factors.Select suitable insulation material can not only reach heat preservation energy-saving
Purpose is moreover it is possible to lift the using effect of agent structure.Insulation material is broadly divided into organic insulation material and inorganic heat insulation material two
Kind, organic insulation material has good heat-insulating property, but its fire protecting performance does not reach standard and requires, and accordingly acts as building room
Inside holding plate is less;Although inorganic heat insulation material has good fire protecting performance, its heat-insulating property but can not meet people
Demand;And insulation material is after a long time use, and its easily cracking, infiltration the problems such as, having had a strong impact on it makes
With security and stability and heat insulation effect.
Therefore, develop a kind of insulation, flameproof effect good, and long-lived inorganic heat-insulation board is those skilled in the art
Institute's urgent need to solve the problem.
Content of the invention
For solving the above problems, the invention discloses a kind of high-strength anti-cracking thermal insulative board of low stress.
In order to achieve the above object, the following technical scheme of present invention offer:
A kind of high-strength anticracking inorganic heat-insulation board of low stress, its constituent and mass fraction shared by each composition are respectively as follows:
Cement: 170~190 parts,
Admixture: 30~40 parts,
Hydrogen peroxide: 3~5 parts,
Polypropylene fibre: 1~3 part,
Water: 85~95 parts,
Additive: 3~7 parts.
Further, its preparation method includes:
(1) take cement and water according to 2:1 mass ratio, put in agitator tank and stir, add admixture, hydrogen peroxide, poly- third
It is again stirring for uniformly after alkene fiber and additive, pre-hardening 1~2h;
(2) stand 10h after the completion of initial set, carry out the demoulding;
(3) natural curing 3~5 days after the demoulding, are shaped to blank;
(4) as needed blank is cut, obtain finished product.
The invention provides a kind of low stress cracking resistance warming plate, by cement, admixture, hydrogen peroxide, polypropylene fibre, water with
And additive composition, as material, addition admixture can carry out certain modification, reduction production cost etc. to cement;Add double
Oxygen water energy enough quickly promote cement foamed, make cement and expanded become foam cement, produce a large amount of sealed porositys inside it, have
Good heat-proof quality, density is little lightweight, has outstanding sound-proof refractory performance simultaneously, and its internal rate of closed hole is high simultaneously, water
Divide and cannot invade, have outstanding water-resistant anti-freezing effect;Also polypropylene fibre is included, itself light weight, intensity in the present invention
High, elasticity is good and has outstanding warmth retention property, mixes in the present invention, can make this while ensureing not increase own wt
Invention has outstanding anti-cracking function;Additive in the present invention equally can play certain modification, potentiation effect to the present invention
Really.
The present invention enables to the present invention in later strength not when making using the technique of initial set under low temperature stress
Become, do not degenerate, each composition performance of itself and activity in the present invention can be kept, and shrinkage factor is little, can be prevented effectively from this
Invention finished product ftractures, seeps water.
Preferably, the constituent of the present invention and mass fraction shared by each composition are respectively as follows:
Cement: 180 parts,
Admixture: 35 parts,
Hydrogen peroxide: 4 parts,
Polypropylene fibre: 1 part,
Water: 90 parts,
Additive: 4 parts.
The invention provides one group of optimal proportion, specific as follows: cement: 180 parts, admixture: 35 parts, hydrogen peroxide: 4 parts,
Polypropylene fibre: 1 part, water: 90 parts, additive: 4 parts;The finished product thermal insulation plate being obtained by above composition proportion has outstanding
Resistance to compression, anti-folding, tensile strength, the coefficient such as its water absorption, impermeability, weatherability, freeze-thawing resistant and ant wind load is all higher than phase
The like product of congruent composition.
Preferably, admixture is flyash.
In the present invention, admixture selects flyash, can greatly reduce the materials of cement, reduces manufacturing cost.
Preferably, additive is water reducer.
Water reducer in the present invention can substantially reduce unit consumption of water, improves mixture after each composition mixing in the present invention
Mobility, reduce cement consumption, reduce manufacturing cost.
Preferably, natural curing in step (3) method particularly includes: wrapped using plastic sheeting in 2h after the demoulding
Wrap up in, under the conditions of being positioned over natural temperature, and be completely covered with wet soil, continue 3~5 days.
The present invention compared with prior art, using formula and the method for novelty, is ensureing that warming plate has superior mechanical
While performance, also make it have outstanding insulation, waterproof and dampproof performance, greatly improve product quality, and also can
Be prevented effectively from the cracking of product, infiltration so as to after a procedure the phase still ensure that every outstanding performance indications, cost simultaneously
Moderate, preparation method is simple.
Specific embodiment
The technical scheme present invention being provided below with reference to specific embodiment is described in detail it should be understood that following concrete
Embodiment is only illustrative of the invention and is not intended to limit the scope of the invention.
Embodiment 1:
A kind of high-strength anticracking inorganic heat-insulation board of low stress, its constituent and mass fraction shared by each composition are respectively as follows:
Cement: 180 parts,
Flyash: 35 parts,
Hydrogen peroxide: 4 parts,
Polypropylene fibre: 1 part,
Water: 90 parts,
Water reducer: 4 parts.
Its preparation method includes:
(1) take cement and water according to 2:1 mass ratio, put in agitator tank and stir, add admixture, hydrogen peroxide, poly- third
It is again stirring for uniformly after alkene fiber and additive, pre-hardening 2h;
(2) stand 10h after the completion of initial set, carry out the demoulding;
(3) wrapped up using plastic sheeting in 2h after the demoulding, under the conditions of being positioned over natural temperature, and with wet soil, it is covered completely
Lid, continues 5 days, is shaped to blank;
(4) as needed blank is cut, obtain finished product.
Embodiment 2:
A kind of high-strength anticracking inorganic heat-insulation board of low stress, its constituent and mass fraction shared by each composition are respectively as follows:
Cement: 170 parts,
Flyash: 40 parts,
Hydrogen peroxide: 3 parts,
Polypropylene fibre: 3 parts,
Water: 85 parts,
Water reducer: 3 parts.
Its preparation method includes:
(1) take cement and water according to 2:1 mass ratio, put in agitator tank and stir, add admixture, hydrogen peroxide, poly- third
It is again stirring for uniformly after alkene fiber and additive, pre-hardening 1h;
(2) stand 10h after the completion of initial set, carry out the demoulding;
(3) wrapped up using plastic sheeting in 2h after the demoulding, under the conditions of being positioned over natural temperature, and with wet soil, it is covered completely
Lid, continues 4 days, is shaped to blank;
(4) as needed blank is cut, obtain finished product.
Embodiment 3:
A kind of high-strength anticracking inorganic heat-insulation board of low stress, its constituent and mass fraction shared by each composition are respectively as follows:
Cement: 190 parts,
Flyash: 30 parts,
Hydrogen peroxide: 5 parts,
Polypropylene fibre: 3 parts,
Water: 95 parts,
Water reducer: 7 parts.
Its preparation method includes:
(1) take cement and water according to 2:1 mass ratio, put in agitator tank and stir, add admixture, hydrogen peroxide, poly- third
It is again stirring for uniformly after alkene fiber and additive, pre-hardening 1h;
(2) stand 10h after the completion of initial set, carry out the demoulding;
(3) wrapped up using plastic sheeting in 2h after the demoulding, under the conditions of being positioned over natural temperature, and with wet soil, it is covered completely
Lid, continues 3 days, is shaped to blank;
(4) as needed blank is cut, obtain finished product.
Warming plate composition proportion by three above embodiment provide and method being obtained respectively is incubated
Heat-insulated rush test, fire-proof and water-proof test, and mechanical strength test, the optimum proportioning optimum that embodiment 1 provides is outstanding, embodiment
3 secondly, and embodiment 2 is slightly poorer to embodiment 3, but compared with existing warming plate, its performance parameter is also obviously improved.
Last it should be noted that above example is only in order to illustrate technical scheme and non-limiting technical side
Case, it will be understood by those within the art that, those are modified to technical scheme or equivalent, and
Objective without departing from the technical program and scope, all should cover in the middle of scope of the presently claimed invention.
Claims (6)
1. a kind of high-strength anticracking inorganic heat-insulation board of low stress it is characterised in that: its constituent and mass parts shared by each composition
Several cement that are respectively as follows:: 170~190 parts,
Admixture: 30~40 parts,
Hydrogen peroxide: 3~5 parts,
Polypropylene fibre: 1~3 part,
Water: 85~95 parts,
Additive: 3~7 parts.
2. a kind of high-strength anticracking inorganic heat-insulation board of low stress according to claim 1 it is characterised in that: its preparation method bag
Include: (1) takes cement and water according to 2:1 mass ratio, puts in agitator tank and stirs, add admixture, hydrogen peroxide, polypropylene
It is again stirring for uniformly after fiber and additive, pre-hardening 1~2h;
(2) stand 10h after the completion of initial set, carry out the demoulding;
(3) natural curing 3~5 days after the demoulding, are shaped to blank;
(4) as needed blank is cut, obtain finished product.
3. a kind of high-strength anticracking inorganic heat-insulation board of low stress according to claim 1 it is characterised in that: its constituent with
And mass fraction shared by each composition is respectively as follows:
Cement: 180 parts,
Admixture: 35 parts,
Hydrogen peroxide: 4 parts,
Polypropylene fibre: 1 part,
Water: 90 parts,
Additive: 4 parts.
4. a kind of high-strength anticracking inorganic heat-insulation board of low stress according to claim 1 it is characterised in that: described admixture is
Flyash.
5. a kind of high-strength anticracking inorganic heat-insulation board of low stress according to claim 1 it is characterised in that: described additive is
Water reducer.
6. a kind of high-strength anticracking inorganic heat-insulation board of low stress according to claim 2 it is characterised in that: described step (3)
Middle natural curing method particularly includes: wrapped up using plastic sheeting in 2h after the demoulding, under the conditions of being positioned over natural temperature, and
It is completely covered with wet soil, continued 3~5 days.