CN106363988A - Micro-porous ventilated waterproof fabric and preparation method thereof - Google Patents
Micro-porous ventilated waterproof fabric and preparation method thereof Download PDFInfo
- Publication number
- CN106363988A CN106363988A CN201610973886.7A CN201610973886A CN106363988A CN 106363988 A CN106363988 A CN 106363988A CN 201610973886 A CN201610973886 A CN 201610973886A CN 106363988 A CN106363988 A CN 106363988A
- Authority
- CN
- China
- Prior art keywords
- layer
- micro
- porous
- film
- breathable waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a micro-porous ventilated waterproof fabric and a preparation method thereof. The micro-porous ventilated waterproof fabric provided by the invention comprises a fabric layer, wherein a PUR (Polyurethane Reactive) micro-porous film and a PU (Polyurethane) film are arranged at one side of the fabric layer in sequence from inside to outside; a cotton wool layer, a ramie fiber layer and a polytetrafluoroethylene micro-porous film layer are arranged on the other layer of the fabric layer in sequence from inside to outside. The micro-porous ventilated waterproof fabric provided by the invention has good waterproof, ventilation, warm-keeping and skin-friendly performance.
Description
Technical field
The present invention relates to fabric field, more particularly, to a kind of micro- porous breathable waterproof fabrics and preparation method thereof.
Background technology
Fabric is just used to make the material of clothing.As one of clothing three elements, fabric not only can annotate clothing
Style and characteristic, and direct left and right the color of clothing, the expression effect of moulding.
Patent publication No. 104562715a discloses a kind of cotton flannel printed fabric processing method, and it includes following work
Sequence: pre-treatment after machine under weaving → fabric → to cloth cover is through over-cooking drift and mercerising → by forming machine pre-setting → upper machine activity print
Washing fixation → bulking agent softening agent sizing → preshrunk → product inspection is dried → evaporated to flower.This printed fabric waterproof and breathable effect
Poor.
Content of the invention
In view of this, one aspect of the present invention provides a kind of micro- porous breathable waterproof fabrics, this micro- porous breathable waterproof fabrics
Solve the problems, such as that fabric waterproof is poor with ventilative.
For reaching this purpose, the present invention employs the following technical solutions.
A kind of micro- porous breathable waterproof fabrics, including precoat, the side of described precoat is sequentially provided with pur from the inside to the outside
Micro-porous film and pu film, another layer of described precoat is sequentially provided with velveteen layer, ramee layer and polytetrafluoroethyl-ne from the inside to the outside
Alkene microporous film layers.
Wherein, described precoat is selected from the mixing of cotton layer, chemical fiber layer, a layer of leather layer or woollen goods layer or at least two-layer
Layer.
Wherein, the thickness of described precoat is 3～8mm, for example, can be 3mm, 4mm, 5mm, 6mm, 7mm or 8mm etc., excellent
Select 6～7mm.
Wherein, the thickness of described pur micro-porous film be 0.05～0.3mm, for example can for 0.05mm, 0.06mm,
0.08mm, 0.09mm, 0.1mm, 0.2mm or 0.3mm etc., preferably 0.08～0.1mm.
Wherein, the thickness of described pu film be 0.02～0.1mm, for example can for 0.02mm, 0.03mm, 0.04mm,
0.05mm, 0.06mm, 0.08mm or 0.1mm etc., preferably 0.05～0.08mm.
Wherein, the thickness of described velveteen layer is 2～6mm, for example, can be 2mm, 3mm, 4mm, 5mm or 6mm etc., preferably 3
～5mm；
The thickness of described ramee layer is 5～8mm, for example, can be 5mm, 6mm, 7mm or 8mm etc., preferably 6～7mm.
Wherein, the thickness of described microporous teflon membran layer be 0.01～0.1mm, for example can for 0.01mm,
0.02mm, 0.04mm, 0.05mm, 0.06mm, 0.08mm or 0.1mm etc., preferably 0.02～0.05mm.
Another aspect of the present invention provides a kind of preparation method of above-mentioned micro- porous breathable waterproof fabrics.This preparation method solves
Fabric preparation process is loaded down with trivial details, the problem of complex operation.
A kind of preparation method of above-mentioned micro- porous breathable waterproof fabrics, comprises the following steps:
(1) by described pu film, pur micro-porous film, precoat, velveteen layer, ramee layer and microporous teflon membran
Layer is from top to bottom placed, and carries out hot pressing laminating, obtains composite material；
(2) described composite material, through steaming and color fixing, washing, drying, expanding sizing, is obtained micro- porous breathable waterproof surface
Material.
Wherein, in described step (1) hot pressing temperature be 146～155 DEG C, for example can for 146 DEG C, 147 DEG C, 148 DEG C,
150 DEG C, 152 DEG C, 153 DEG C or 155 DEG C etc., preferably 148～152 DEG C.
Wherein, in described step (2) steaming and color fixing temperature be 120～124 DEG C, for example can for 120 DEG C, 121 DEG C, 122
DEG C, 123 DEG C or 124 DEG C etc., preferably 120～122 DEG C；Described drying temperature be 140～165 DEG C, for example can for 140 DEG C, 141
DEG C, 142 DEG C, 145 DEG C, 150 DEG C, 160 DEG C or 165 DEG C etc., preferably 145～155 DEG C；Described expanding setting temperature is 120～130
DEG C, can be for example 120 DEG C, 121 DEG C, 122 DEG C, 124 DEG C, 126 DEG C, 128 DEG C or 130 DEG C etc., preferably 122～125 DEG C.
Beneficial effects of the present invention are as follows: micro- porous breathable waterproof fabrics that the present invention provides, including precoat, described face
The side of the bed of material is sequentially provided with pur micro-porous film and pu film from the inside to the outside, and another layer of described precoat sets from the inside to the outside successively
There are velveteen layer, ramee layer and microporous teflon membran layer.Pur micro-porous film is combined with pu film so as to have anti-
Water airing function, velveteen layer has good warming and pro-skin performance, and ramee layer has excellent breathability and antibacterial anti-
Rotten performance, microporous teflon membran is a kind of pliable and tough and whippy poromerics, and porosity is high, even aperture distribution, tool
There is the characteristic of permeable watertight；The present invention micro- porous breathable waterproof fabrics there is good waterproof, ventilative, warming and pro-skin
Performance.
Brief description
Fig. 1 is the structural representation of the present invention micro- porous breathable waterproof fabrics.
Accompanying drawing indicates:
1- precoat, 2-pur micro-porous film, 3-pu film, 4- velveteen layer, 5- ramee layer, 6- politef micropore
Film layer.
Specific embodiment
To further illustrate technical scheme with reference to the accompanying drawings and examples.
Embodiment 1
Micro- porous breathable waterproof fabrics in the present embodiment, including precoat 1, the thickness of precoat 1 is 6mm, precoat 1
Side be sequentially provided with pur micro-porous film 2 and pu film 3 from the inside to the outside, the thickness of pur micro-porous film 2 is 0.06mm, pu film 3
Thickness is 0.03mm, and it is micro- that another layer of precoat 1 is sequentially provided with velveteen layer 4, ramee layer 5 and politef from the inside to the outside
Pore membrane layer 6, the thickness of velveteen layer 4 is 3mm, and the thickness of ramee layer 5 is 5mm, and the thickness of microporous teflon membran layer 6 is
0.03mm.
The preparation method of above-mentioned micro- porous breathable waterproof fabrics, comprises the following steps:
By pu film 3, pur micro-porous film 2, precoat 1, velveteen layer 4, ramee layer 5 and microporous teflon membran layer 6
From top to bottom place, carry out hot pressing laminating at a temperature of 148 DEG C, obtain composite material；
Composite material, through steaming and color fixing, washing, drying, expanding sizing, is obtained micro- porous breathable waterproof fabrics, wherein,
Steaming and color fixing temperature is 122 DEG C, and drying temperature is 145 DEG C, and expanding setting temperature is 122 DEG C.
Embodiment 2
Micro- porous breathable waterproof fabrics of the present embodiment, including precoat 1, the thickness of precoat 1 is 7mm, precoat 1
Side is sequentially provided with pur micro-porous film 2 and pu film 3 from the inside to the outside, and the thickness of pur micro-porous film 2 is 0.08mm, the thickness of pu film 3
Spend for 0.05mm, another layer of precoat 1 is sequentially provided with velveteen layer 4, ramee layer 5 and politef micropore from the inside to the outside
Film layer 6, the thickness of velveteen layer 4 is 3mm, and the thickness of ramee layer 5 is 6mm, and the thickness of microporous teflon membran layer 6 is
0.05mm, precoat 1 is selected from the mixed layer of cotton layer, chemical fiber layer, a layer of leather layer or woollen goods layer or at least two-layer.
The preparation method of above-mentioned micro- porous breathable waterproof fabrics, comprises the following steps:
By pu film 3, pur micro-porous film 2, precoat 1, velveteen layer 4, ramee layer 5 and microporous teflon membran layer 6
From top to bottom place, carry out hot pressing laminating at a temperature of 148 DEG C, obtain composite material；
Composite material, through steaming and color fixing, washing, drying, expanding sizing, is obtained micro- porous breathable waterproof fabrics, wherein,
Steaming and color fixing temperature is 122 DEG C, and drying temperature is 145 DEG C, and expanding setting temperature is 122 DEG C.
Embodiment 3
Micro- porous breathable waterproof fabrics of the present embodiment, including precoat 1, the thickness of precoat 1 is 7mm, precoat 1
Side is sequentially provided with pur micro-porous film 2 and pu film 3 from the inside to the outside, and the thickness of pur micro-porous film 2 is 0.1mm, the thickness of pu film 3
For 0.08mm, another layer of precoat 1 is sequentially provided with velveteen layer 4, ramee layer 5 and microporous teflon membran from the inside to the outside
Layer 6, the thickness of velveteen layer 4 is 5mm, and the thickness of ramee layer 5 is 7mm, and the thickness of microporous teflon membran layer 6 is
0.1mm, precoat 1 is selected from the mixed layer of cotton layer, chemical fiber layer, a layer of leather layer or woollen goods layer or at least two-layer.
The preparation method of above-mentioned micro- porous breathable waterproof fabrics, comprises the following steps:
By pu film 3, pur micro-porous film 2, precoat 1, velveteen layer 4, ramee layer 5 and microporous teflon membran layer 6
From top to bottom place, carry out hot pressing laminating at a temperature of 148 DEG C, obtain composite material；
Composite material, through steaming and color fixing, washing, drying, expanding sizing, is obtained micro- porous breathable waterproof fabrics, wherein,
Steaming and color fixing temperature is 124 DEG C, and drying temperature is 165 DEG C, and expanding setting temperature is 130 DEG C.
Applicant states, the present invention illustrates detailed construction feature and the construction party of the present invention by above-described embodiment
Method, but the invention is not limited in above-mentioned detailed construction feature and construction method, that is, do not mean that the present invention has to rely on
State detailed construction feature and construction method could be implemented.Person of ordinary skill in the field is it will be clearly understood that to the present invention's
Any improvement, the equivalence replacement to part selected by the present invention and the increase of accessory, the selection of concrete mode etc., all fall
Within the scope of protection scope of the present invention and disclosure.
Claims (10)
1. a kind of micro- porous breathable waterproof fabrics are it is characterised in that include precoat (1), the side of described precoat (1) is by interior
To being sequentially provided with outward pur micro-porous film (2) and pu film (3), another layer of described precoat (1) is sequentially provided with velveteen from the inside to the outside
Layer (4), ramee layer (5) and microporous teflon membran layer (6).
2. micro- porous breathable waterproof fabrics according to claim 1 are it is characterised in that described precoat (1) is selected from cotton
One layer of layer, chemical fiber layer, leather layer or woollen goods layer or the mixed layer of at least two-layer.
3. micro- porous breathable waterproof fabrics according to claim 1 are it is characterised in that the thickness of described precoat (1) is 3
～8mm, preferably 6～7mm.
4. micro- porous breathable waterproof fabrics according to claim 1 are it is characterised in that the thickness of described pur micro-porous film (2)
Spend for 0.05～0.3mm, preferably 0.08～0.1mm.
5. micro- porous breathable waterproof fabrics according to claim 1 are it is characterised in that the thickness of described pu film (3) is
0.02～0.1mm, preferably 0.05～0.08mm.
6. micro- porous breathable waterproof fabrics according to claim 1 are it is characterised in that the thickness of described velveteen layer (4) is 2
～6mm, preferably 3～5mm；
The thickness of described ramee layer (5) is 5～8mm, preferably 6～7mm.
7. micro- porous breathable waterproof fabrics according to claim 1 are it is characterised in that described microporous teflon membran layer
(6) thickness is 0.01～0.1mm, preferably 0.02～0.05mm.
8. a kind of arbitrary described micro- porous breathable waterproof fabrics of claim 1～7 preparation method it is characterised in that include with
Lower step:
(1) by described pu film (3), pur micro-porous film (2), precoat (1), velveteen layer (4), ramee layer (5) and polytetrafluoro
Ethylene microporous film layers (6) are from top to bottom placed, and carry out hot pressing laminating, obtain composite material；
(2) described composite material, through steaming and color fixing, washing, drying, expanding sizing, is obtained micro- porous breathable waterproof fabrics.
9. preparation method according to claim 8 it is characterised in that in described step (1) hot pressing temperature be 146～155
DEG C, preferably 148～152 DEG C.
10. preparation method according to claim 8 it is characterised in that in described step (2) steaming and color fixing temperature be 120
～124 DEG C, preferably 120～122 DEG C；Described drying temperature is 140～165 DEG C, preferably 145～155 DEG C；Described expanding sizing temperature
Spend for 120～130 DEG C, preferably 122～125 DEG C.