CN106351012A - Sizing process for pure cotton fabric yarn - Google Patents
Sizing process for pure cotton fabric yarn Download PDFInfo
- Publication number
- CN106351012A CN106351012A CN201610789773.1A CN201610789773A CN106351012A CN 106351012 A CN106351012 A CN 106351012A CN 201610789773 A CN201610789773 A CN 201610789773A CN 106351012 A CN106351012 A CN 106351012A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- weight
- parts
- yarn
- cotton fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a sizing process for pure cotton fabric yarn. The sizing process comprises the following steps: (1) sequentially pouring 1-2 parts by weight of paraffin, 1.8 parts by weight of polyoxyethylene nonyl phenolic ether, 0.8 part by weight of purified attapulgite, 1.1 parts by weight of hydroxy propyl cellulose and 10 parts by weight of polyving akohol into 35 parts by weight of deionized water, and uniformly stirring; (2) then sequentially pouring 2.1 parts by weight of ethylene glycol monostearate, 1.5 parts by weight of sodium sulfosuccinate, 2.3 parts by weight of gluconic acid and 1.9 parts by weight of dehydroacetic acid, and continuously stirring to be fully and uniformly mixed to prepare size; and (3) immersing yarn into the size for sizing, pressing surplus size and drying. Hairiness of yarn after sizing is appressed, the strength is obviously improved, the wear-resisting performance is good, and the holding performance of yarn is good.
Description
Technical field
The present invention relates to the slashing technique of pure cotton fabric yarn.
Background technology
The warp thread of the fabrics such as cotton, viscose glue and synthetic fibers, mostly first passes through sizing before weaving;And existing sizing slurry
The performance of liquid has much room for improvement.
Content of the invention
It is an object of the invention to provide a kind of slashing technique of pure cotton fabric yarn, its starching rear yarn line filoplume patch volt,
Strongly significant raising, excellent wear resistance, it is good that the guarantor of yarn stretches performance.
For achieving the above object, the technical scheme is that and design a kind of slashing technique of pure cotton fabric yarn, including
Following steps:
1) by 1~2 weight portion paraffin, 1.8 weight portion polyoxyethylene nonyl 2, 2-Oxydiphenol, 0.8 weight portion purification attapulgite
Clay, 1.1 weight portion hydroxypropyl celluloses, 10 weight account polyethylene alcohol put in 35 parts by weight of deionized water successively, and stirring is all
Even;
2) put into successively again 2.1 weight portion ethylene glycol monostearates, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 2.3
Weight portion gluconic acid, 1.9 weight portion dehydroacetic acids, continue stirring, uniform to being sufficiently mixed, prepared serosity;
3) yarn is immersed serosity starching, pressure goes extraction raffinate, dries.
Preferably, the slashing technique of pure cotton fabric yarn, comprises the steps:
1) 1 weight portion paraffin, 1.8 weight portion polyoxyethylene nonyl 2, 2-Oxydiphenol, 0.8 weight portion purification attapulgite are glued
Soil, 1.1 weight portion hydroxypropyl celluloses, 10 weight account polyethylene alcohol put in 35 parts by weight of deionized water successively, stir;
2) put into successively again 2.1 weight portion ethylene glycol monostearates, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 2.3
Weight portion gluconic acid, 1.9 weight portion dehydroacetic acids, continue stirring, uniform to being sufficiently mixed, prepared serosity;
3) yarn is immersed serosity starching, pressure goes extraction raffinate, dries.
Preferably, the slashing technique of pure cotton fabric yarn, comprises the steps:
1) 2 weight portion paraffin, 1.8 weight portion polyoxyethylene nonyl 2, 2-Oxydiphenol, 0.8 weight portion purification attapulgite are glued
Soil, 1.1 weight portion hydroxypropyl celluloses, 10 weight account polyethylene alcohol put in 35 parts by weight of deionized water successively, stir;
2) put into successively again 2.1 weight portion ethylene glycol monostearates, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 2.3
Weight portion gluconic acid, 1.9 weight portion dehydroacetic acids, continue stirring, uniform to being sufficiently mixed, prepared serosity;
3) yarn is immersed serosity starching, pressure goes extraction raffinate, dries.
Preferably, the slashing technique of pure cotton fabric yarn, comprises the steps:
1) 1.2 weight portion paraffin, 1.8 weight portion polyoxyethylene nonyl 2, 2-Oxydiphenol, 0.8 weight portion purification attapulgite are glued
Soil, 1.1 weight portion hydroxypropyl celluloses, 10 weight account polyethylene alcohol put in 35 parts by weight of deionized water successively, stir;
2) put into successively again 2.1 weight portion ethylene glycol monostearates, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 2.3
Weight portion gluconic acid, 1.9 weight portion dehydroacetic acids, continue stirring, uniform to being sufficiently mixed, prepared serosity;
3) yarn is immersed serosity starching, pressure goes extraction raffinate, dries.
Advantages of the present invention and having the beneficial effects that: a kind of slashing technique of pure cotton fabric yarn, its starching rear yarn are provided
Line filoplume patch volt, strongly significant raising, excellent wear resistance, it is good that the guarantor of yarn stretches performance.
The performance of " desizing liquid " and purposes are determined by its component and proportioning, and the different component meeting in " desizing liquid "
Influence each other, component and its proportioning can determine the final performance of " desizing liquid ", such as fruit component and its proportioning be not mutually coordinated, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, when serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " desizing
The optimal component of liquid " and proportioning so that multiple component combine, mutually coordinated and produce positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
The slashing technique of pure cotton fabric yarn, comprises the steps:
1) by 1~2 weight portion paraffin, 1.8 weight portion polyoxyethylene nonyl 2, 2-Oxydiphenol, 0.8 weight portion purification attapulgite
Clay, 1.1 weight portion hydroxypropyl celluloses, 10 weight account polyethylene alcohol put in 35 parts by weight of deionized water successively, and stirring is all
Even;
2) put into successively again 2.1 weight portion ethylene glycol monostearates, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 2.3
Weight portion gluconic acid, 1.9 weight portion dehydroacetic acids, continue stirring, uniform to being sufficiently mixed, prepared serosity;
3) yarn is immersed serosity starching, pressure goes extraction raffinate, dries.
Embodiment 2
The slashing technique of pure cotton fabric yarn, comprises the steps:
1) 1 weight portion paraffin, 1.8 weight portion polyoxyethylene nonyl 2, 2-Oxydiphenol, 0.8 weight portion purification attapulgite are glued
Soil, 1.1 weight portion hydroxypropyl celluloses, 10 weight account polyethylene alcohol put in 35 parts by weight of deionized water successively, stir;
2) put into successively again 2.1 weight portion ethylene glycol monostearates, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 2.3
Weight portion gluconic acid, 1.9 weight portion dehydroacetic acids, continue stirring, uniform to being sufficiently mixed, prepared serosity;
3) yarn is immersed serosity starching, pressure goes extraction raffinate, dries.
Embodiment 3
The slashing technique of pure cotton fabric yarn, comprises the steps:
1) 2 weight portion paraffin, 1.8 weight portion polyoxyethylene nonyl 2, 2-Oxydiphenol, 0.8 weight portion purification attapulgite are glued
Soil, 1.1 weight portion hydroxypropyl celluloses, 10 weight account polyethylene alcohol put in 35 parts by weight of deionized water successively, stir;
2) put into successively again 2.1 weight portion ethylene glycol monostearates, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 2.3
Weight portion gluconic acid, 1.9 weight portion dehydroacetic acids, continue stirring, uniform to being sufficiently mixed, prepared serosity;
3) yarn is immersed serosity starching, pressure goes extraction raffinate, dries.
Embodiment 4
The slashing technique of pure cotton fabric yarn, comprises the steps:
1) 1.2 weight portion paraffin, 1.8 weight portion polyoxyethylene nonyl 2, 2-Oxydiphenol, 0.8 weight portion purification attapulgite are glued
Soil, 1.1 weight portion hydroxypropyl celluloses, 10 weight account polyethylene alcohol put in 35 parts by weight of deionized water successively, stir;
2) put into successively again 2.1 weight portion ethylene glycol monostearates, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 2.3
Weight portion gluconic acid, 1.9 weight portion dehydroacetic acids, continue stirring, uniform to being sufficiently mixed, prepared serosity;
3) yarn is immersed serosity starching, pressure goes extraction raffinate, dries.
Yarn filoplume patch volt, strongly significant raising, excellent wear resistance after the various embodiments described above starching, it is good that the guarantor of yarn stretches performance.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. the slashing technique of pure cotton fabric yarn is it is characterised in that comprise the steps:
1) by 1~2 weight portion paraffin, 1.8 weight portion polyoxyethylene nonyl 2, 2-Oxydiphenol, 0.8 weight portion purification attapulgite clay,
1.1 weight portion hydroxypropyl celluloses, 10 weight account polyethylene alcohol put in 35 parts by weight of deionized water successively, stir;
2) 2.1 weight portion ethylene glycol monostearates, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 2.3 weight are put into again successively
Part gluconic acid, 1.9 weight portion dehydroacetic acids, continue stirring, uniform to being sufficiently mixed, prepared serosity;
3) yarn is immersed serosity starching, pressure goes extraction raffinate, dries.
2. the slashing technique of pure cotton fabric yarn according to claim 1 is it is characterised in that comprise the steps:
1) by 1 weight portion paraffin, 1.8 weight portion polyoxyethylene nonyl 2, 2-Oxydiphenol, 0.8 weight portion purification attapulgite clay, 1.1
Weight portion hydroxypropyl cellulose, 10 weight account polyethylene alcohol put in 35 parts by weight of deionized water successively, stir;
2) 2.1 weight portion ethylene glycol monostearates, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 2.3 weight are put into again successively
Part gluconic acid, 1.9 weight portion dehydroacetic acids, continue stirring, uniform to being sufficiently mixed, prepared serosity;
3) yarn is immersed serosity starching, pressure goes extraction raffinate, dries.
3. the slashing technique of pure cotton fabric yarn according to claim 1 is it is characterised in that comprise the steps:
1) by 2 weight portion paraffin, 1.8 weight portion polyoxyethylene nonyl 2, 2-Oxydiphenol, 0.8 weight portion purification attapulgite clay, 1.1
Weight portion hydroxypropyl cellulose, 10 weight account polyethylene alcohol put in 35 parts by weight of deionized water successively, stir;
2) 2.1 weight portion ethylene glycol monostearates, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 2.3 weight are put into again successively
Part gluconic acid, 1.9 weight portion dehydroacetic acids, continue stirring, uniform to being sufficiently mixed, prepared serosity;
3) yarn is immersed serosity starching, pressure goes extraction raffinate, dries.
4. the slashing technique of pure cotton fabric yarn according to claim 1 is it is characterised in that comprise the steps:
1) by 1.2 weight portion paraffin, 1.8 weight portion polyoxyethylene nonyl 2, 2-Oxydiphenol, 0.8 weight portion purification attapulgite clay,
1.1 weight portion hydroxypropyl celluloses, 10 weight account polyethylene alcohol put in 35 parts by weight of deionized water successively, stir;
2) 2.1 weight portion ethylene glycol monostearates, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 2.3 weight are put into again successively
Part gluconic acid, 1.9 weight portion dehydroacetic acids, continue stirring, uniform to being sufficiently mixed, prepared serosity;
3) yarn is immersed serosity starching, pressure goes extraction raffinate, dries.