CN106283624A - The slashing technique of superfine denier nylon yarn - Google Patents
The slashing technique of superfine denier nylon yarn Download PDFInfo
- Publication number
- CN106283624A CN106283624A CN201610779859.6A CN201610779859A CN106283624A CN 106283624 A CN106283624 A CN 106283624A CN 201610779859 A CN201610779859 A CN 201610779859A CN 106283624 A CN106283624 A CN 106283624A
- Authority
- CN
- China
- Prior art keywords
- weight
- weight portion
- parts
- yarn
- serosity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the slashing technique of a kind of superfine denier nylon yarn, comprise the steps: 1) 1~2 weight portion Lenzin viscose glues, 2.1 parts by weight of formaldehyde, 1.3 weight portion hydrolyzed polyacrylonitriles, 1.4 weight portion HYDROXY PROPYL METHYLCELLULOSE, 14 parts by weight of phosphoric acid ester starch are put in 35 parts by weight of deionized water successively, stir;2) put into 2.2 parts by weight of sucrose fatty acid esters, 1.8 weight portion alkylphenol polyoxyethylene, 1.3 weight portion two nonyl certain herbaceous plants with big flowers base barium sulfonates, 2.1 weight portion mannans the most successively, continue stirring, to being sufficiently mixed uniformly, prepare serosity;3) yarn immersing serosity starching, pressure removes remaining liquid, dries.Yarn filoplume patch volt, the most significant raising after starching of the present invention, excellent wear resistance, it is good that the guarantor of yarn stretches performance.
Description
Technical field
The present invention relates to the slashing technique of superfine denier nylon yarn.
Background technology
The warp thread of the fabrics such as cotton, viscose glue and synthetic fibers, mostly first passes through sizing before weaving;And existing sizing slurry
The performance of liquid haves much room for improvement.
Summary of the invention
It is an object of the invention to provide the slashing technique of a kind of superfine denier nylon yarn, Yarn filoplume after its starching
Patch volt, the most significant raising, excellent wear resistance, it is good that the guarantor of yarn stretches performance.
For achieving the above object, the technical scheme is that and design the sizing work of a kind of superfine denier nylon yarn
Skill, comprises the steps:
1) by 1~2 weight portion Lenzin viscose glues, 2.1 parts by weight of formaldehyde, 1.3 weight portion hydrolyzed polyacrylonitriles, 1.4 weight portions
HYDROXY PROPYL METHYLCELLULOSE, 14 parts by weight of phosphoric acid ester starch put in 35 parts by weight of deionized water successively, stir;
2) 2.2 parts by weight of sucrose fatty acid esters, 1.8 weight portion alkylphenol polyoxyethylene, 1.3 weight portions are put into the most successively
Two nonyl certain herbaceous plants with big flowers base barium sulfonates, 2.1 weight portion mannans, continue stirring, to being sufficiently mixed uniformly, prepares serosity;
3) yarn immersing serosity starching, pressure removes remaining liquid, dries.
Preferably, the slashing technique of superfine denier nylon yarn, comprise the steps:
1) by 1 weight portion Lenzin viscose glue, 2.1 parts by weight of formaldehyde, 1.3 weight portion hydrolyzed polyacrylonitriles, 1.4 weight portion hydroxyls
Propyl methocel, 14 parts by weight of phosphoric acid ester starch put in 35 parts by weight of deionized water successively, stir;
2) 2.2 parts by weight of sucrose fatty acid esters, 1.8 weight portion alkylphenol polyoxyethylene, 1.3 weight portions are put into the most successively
Two nonyl certain herbaceous plants with big flowers base barium sulfonates, 2.1 weight portion mannans, continue stirring, to being sufficiently mixed uniformly, prepares serosity;
3) yarn immersing serosity starching, pressure removes remaining liquid, dries.
Preferably, the slashing technique of superfine denier nylon yarn, comprise the steps:
1) by 2 weight portion Lenzin viscose glues, 2.1 parts by weight of formaldehyde, 1.3 weight portion hydrolyzed polyacrylonitriles, 1.4 weight portion hydroxyls
Propyl methocel, 14 parts by weight of phosphoric acid ester starch put in 35 parts by weight of deionized water successively, stir;
2) 2.2 parts by weight of sucrose fatty acid esters, 1.8 weight portion alkylphenol polyoxyethylene, 1.3 weight portions are put into the most successively
Two nonyl certain herbaceous plants with big flowers base barium sulfonates, 2.1 weight portion mannans, continue stirring, to being sufficiently mixed uniformly, prepares serosity;
3) yarn immersing serosity starching, pressure removes remaining liquid, dries.
Preferably, the slashing technique of superfine denier nylon yarn, comprise the steps:
1) by 1.2 weight portion Lenzin viscose glues, 2.1 parts by weight of formaldehyde, 1.3 weight portion hydrolyzed polyacrylonitriles, 1.4 weight portion hydroxyls
Base propyl methocel, 14 parts by weight of phosphoric acid ester starch put in 35 parts by weight of deionized water successively, stir;
2) 2.2 parts by weight of sucrose fatty acid esters, 1.8 weight portion alkylphenol polyoxyethylene, 1.3 weight portions are put into the most successively
Two nonyl certain herbaceous plants with big flowers base barium sulfonates, 2.1 weight portion mannans, continue stirring, to being sufficiently mixed uniformly, prepares serosity;
3) yarn immersing serosity starching, pressure removes remaining liquid, dries.
Advantages of the present invention and having the beneficial effects that: provide the slashing technique of a kind of superfine denier nylon yarn, on it
Yarn filoplume patch volt, the most significant raising after slurry, excellent wear resistance, it is good that the guarantor of yarn stretches performance.
Performance and the purposes of " desizing liquid " are determined by its component and proportioning, and the different component meeting in " desizing liquid "
Influencing each other, component and proportioning thereof can determine the final performance of " desizing liquid ", as the most mutually coordinated in fruit component and proportioning thereof, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, and the when of serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " desizing
Liquid " optimal component and proportioning so that multiple components combine, mutually coordinated and produce forward comprehensive effect.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Following example are only used for more
Add and clearly demonstrate technical scheme, and can not limit the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
The slashing technique of superfine denier nylon yarn, comprises the steps:
1) by 1~2 weight portion Lenzin viscose glues, 2.1 parts by weight of formaldehyde, 1.3 weight portion hydrolyzed polyacrylonitriles, 1.4 weight portions
HYDROXY PROPYL METHYLCELLULOSE, 14 parts by weight of phosphoric acid ester starch put in 35 parts by weight of deionized water successively, stir;
2) 2.2 parts by weight of sucrose fatty acid esters, 1.8 weight portion alkylphenol polyoxyethylene, 1.3 weight portions are put into the most successively
Two nonyl certain herbaceous plants with big flowers base barium sulfonates, 2.1 weight portion mannans, continue stirring, to being sufficiently mixed uniformly, prepares serosity;
3) yarn immersing serosity starching, pressure removes remaining liquid, dries.
Embodiment 2
The slashing technique of superfine denier nylon yarn, comprises the steps:
1) by 1 weight portion Lenzin viscose glue, 2.1 parts by weight of formaldehyde, 1.3 weight portion hydrolyzed polyacrylonitriles, 1.4 weight portion hydroxyls
Propyl methocel, 14 parts by weight of phosphoric acid ester starch put in 35 parts by weight of deionized water successively, stir;
2) 2.2 parts by weight of sucrose fatty acid esters, 1.8 weight portion alkylphenol polyoxyethylene, 1.3 weight portions are put into the most successively
Two nonyl certain herbaceous plants with big flowers base barium sulfonates, 2.1 weight portion mannans, continue stirring, to being sufficiently mixed uniformly, prepares serosity;
3) yarn immersing serosity starching, pressure removes remaining liquid, dries.
Embodiment 3
The slashing technique of superfine denier nylon yarn, comprises the steps:
1) by 2 weight portion Lenzin viscose glues, 2.1 parts by weight of formaldehyde, 1.3 weight portion hydrolyzed polyacrylonitriles, 1.4 weight portion hydroxyls
Propyl methocel, 14 parts by weight of phosphoric acid ester starch put in 35 parts by weight of deionized water successively, stir;
2) 2.2 parts by weight of sucrose fatty acid esters, 1.8 weight portion alkylphenol polyoxyethylene, 1.3 weight portions are put into the most successively
Two nonyl certain herbaceous plants with big flowers base barium sulfonates, 2.1 weight portion mannans, continue stirring, to being sufficiently mixed uniformly, prepares serosity;
3) yarn immersing serosity starching, pressure removes remaining liquid, dries.
Embodiment 4
The slashing technique of superfine denier nylon yarn, comprises the steps:
1) by 1.2 weight portion Lenzin viscose glues, 2.1 parts by weight of formaldehyde, 1.3 weight portion hydrolyzed polyacrylonitriles, 1.4 weight portion hydroxyls
Base propyl methocel, 14 parts by weight of phosphoric acid ester starch put in 35 parts by weight of deionized water successively, stir;
2) 2.2 parts by weight of sucrose fatty acid esters, 1.8 weight portion alkylphenol polyoxyethylene, 1.3 weight portions are put into the most successively
Two nonyl certain herbaceous plants with big flowers base barium sulfonates, 2.1 weight portion mannans, continue stirring, to being sufficiently mixed uniformly, prepares serosity;
3) yarn immersing serosity starching, pressure removes remaining liquid, dries.
Yarn filoplume patch volt, the most significant raising after the various embodiments described above starching, excellent wear resistance, it is good that the guarantor of yarn stretches performance.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvements and modifications, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. the slashing technique of superfine denier nylon yarn, it is characterised in that comprise the steps:
1) by 1~2 weight portion Lenzin viscose glues, 2.1 parts by weight of formaldehyde, 1.3 weight portion hydrolyzed polyacrylonitriles, 1.4 weight portion hydroxyls
Propyl methocel, 14 parts by weight of phosphoric acid ester starch put in 35 parts by weight of deionized water successively, stir;
2) 2.2 parts by weight of sucrose fatty acid esters, 1.8 weight portion alkylphenol polyoxyethylene, 1.3 weight portion two nonyls are put into the most successively
Certain herbaceous plants with big flowers base barium sulfonate, 2.1 weight portion mannans, continue stirring, to being sufficiently mixed uniformly, prepares serosity;
3) yarn immersing serosity starching, pressure removes remaining liquid, dries.
The slashing technique of superfine denier nylon yarn the most according to claim 1, it is characterised in that include walking as follows
Rapid:
1) by 1 weight portion Lenzin viscose glue, 2.1 parts by weight of formaldehyde, 1.3 weight portion hydrolyzed polyacrylonitriles, 1.4 weight portion hydroxypropyls
Methylcellulose, 14 parts by weight of phosphoric acid ester starch put in 35 parts by weight of deionized water successively, stir;
2) 2.2 parts by weight of sucrose fatty acid esters, 1.8 weight portion alkylphenol polyoxyethylene, 1.3 weight portion two nonyls are put into the most successively
Certain herbaceous plants with big flowers base barium sulfonate, 2.1 weight portion mannans, continue stirring, to being sufficiently mixed uniformly, prepares serosity;
3) yarn immersing serosity starching, pressure removes remaining liquid, dries.
The slashing technique of superfine denier nylon yarn the most according to claim 1, it is characterised in that include walking as follows
Rapid:
1) by 2 weight portion Lenzin viscose glues, 2.1 parts by weight of formaldehyde, 1.3 weight portion hydrolyzed polyacrylonitriles, 1.4 weight portion hydroxypropyls
Methylcellulose, 14 parts by weight of phosphoric acid ester starch put in 35 parts by weight of deionized water successively, stir;
2) 2.2 parts by weight of sucrose fatty acid esters, 1.8 weight portion alkylphenol polyoxyethylene, 1.3 weight portion two nonyls are put into the most successively
Certain herbaceous plants with big flowers base barium sulfonate, 2.1 weight portion mannans, continue stirring, to being sufficiently mixed uniformly, prepares serosity;
3) yarn immersing serosity starching, pressure removes remaining liquid, dries.
The slashing technique of superfine denier nylon yarn the most according to claim 1, it is characterised in that include walking as follows
Rapid:
1) by 1.2 weight portion Lenzin viscose glues, 2.1 parts by weight of formaldehyde, 1.3 weight portion hydrolyzed polyacrylonitriles, 1.4 weight portion hydroxyls third
Ylmethyl cellulose, 14 parts by weight of phosphoric acid ester starch put in 35 parts by weight of deionized water successively, stir;
2) 2.2 parts by weight of sucrose fatty acid esters, 1.8 weight portion alkylphenol polyoxyethylene, 1.3 weight portion two nonyls are put into the most successively
Certain herbaceous plants with big flowers base barium sulfonate, 2.1 weight portion mannans, continue stirring, to being sufficiently mixed uniformly, prepares serosity;
3) yarn immersing serosity starching, pressure removes remaining liquid, dries.