CN106348683A - Colored nano waterproof glue - Google Patents
Colored nano waterproof glue Download PDFInfo
- Publication number
- CN106348683A CN106348683A CN201610710410.4A CN201610710410A CN106348683A CN 106348683 A CN106348683 A CN 106348683A CN 201610710410 A CN201610710410 A CN 201610710410A CN 106348683 A CN106348683 A CN 106348683A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- weight portion
- component
- prepared
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to colored nano waterproof glue. The colored nano waterproof glue is prepared through uniformly mixing and stirring an organic component A and an inorganic component B according to the ratio (in parts by weight) of 1: 2, wherein the organic component A is prepared from the following raw materials in parts by weight: 30-35 parts of acrylic emulsion, 0.3-0.4 part of antifoamer, 0.1-0.15 part of preservative agent and 28 parts of water; the inorganic component B is prepared from the following raw materials in parts by weight: 35-38 parts of silicate cement, 20-22 parts of quartz sand, 5-6 parts of heavy calcium carbonate, 5-6 parts of nano-scale diatom powder, 4-5 parts of iron oxide pigment and 0.2-0.3 part of water reducing agent.
Description
Technical field
This technology is related to the waterproof material product in the range of a kind of building, and waterproof material is widely used, to basement, kitchen
Defend, carry out water-proofing treatment outside roofing, tunnel, exterior wall, main purpose is to ensure that building body is not attacked by rainwater, subsoil water,
Make building dry, sturdy and durable.
Background technology
Current building industry is the important industry of China, and its output value is in terms of trillion.And buildings waterproof product also species is numerous
Many, its technology is also constantly brought forth new ideas change.But some buildings waterproof products existing still have its technical deficiency, have during the problem of leak
Occur.
Current waterproof system material product, has obvious waterproof effect using in initial stage and short time, but through number
The expanding with heat and contract with cold of year, common high polymer waterproof material are easily aging, and its water resistance reduces year by year, finally occur infiltration,
Leak, cause economic loss.
The commercial house is that town dweller accumulates the fixed assets of formation and important wealth for many years, and its quality directly concerns life matter
Amount, although buildings waterproof product is many, because waterproof effect and waterproof durability are bad, so provide a kind of high property of high-quality
The waterproof material of energy has important Social and economic benef@, is also a technical problem urgently to be resolved hurrily.
Content of the invention
The present invention is directed to above-mentioned technical problem, provides a kind of inorganic material strong by efficient organic waterproof material and durability
The waterproof composite material that material is constituted.
The process structure of the present invention colorful nano water-proof glue and formulation composition are constituted using the easy bi-component preserving, this pair of group
Part includes organic component a and inorganic component b.
Wherein organic component a adopts the strong high-quality acrylic emulsion of water resistance and its adds auxiliary agent composition, inorganic component b
The strong portland cement of weather-proof durability, nanoscale diatom powder and aggregate, colorant is mainly adopted to constitute, wherein, described has
Machine component and the equal environmental protection of inorganic component, nontoxic, tasteless.
Wherein, described organic component a is emulsified into liquid form by Organic Ingredientss；Described inorganic component b is by inorganic glue
The premixing thing of the solid forms such as solidifying agent, aggregate, inserts, pigment stirs and is formed.
Wherein, described organic component a is made up of following weight parts raw material: 30 ~ 35 parts of acrylic emulsion, and defoamer 0.3 ~
0.4 part, 0.1 ~ 0.15 part of preservative, 28 parts of water.Canned after above-mentioned each raw material mixing and stirring.
Wherein, described inorganic component b is made up of the raw material of following weight portion: 35 ~ 38 parts of portland cement (gellant),
20 ~ 22 parts of quartz sand (aggregate), 5 ~ 6 parts of triple superphosphate (inserts), 5 ~ 6 parts of nanoscale diatom powder (close material), iron oxide pigment 4
~ 5 parts, 0.2 ~ 0.3 part of water reducer (auxiliary agent).
Organic component a that the present invention colorful nano water-proof glue is made up of above-mentioned raw material and inorganic component b is by 1:2's
Weight portion mixing and stirring is made.It is noted that organic component a and inorganic component b weight proportion between the two is because each
Ground material slightly difference, when implementing, should could obtain optimum structure through test adjustment, its proportioning.
The beneficial effect comprise that: each component material compatibility is good, the acrylic emulsion of high-quality has strong
Resistance to water, under the enriching of nanometer diatom powder, it is close that emulsion penetrates into all of micro- space in formation a lot of to inorganic gel materials
Real waterproof system, its water-proof wire resistance to water is high, but also with the advantage that weatherability is long in the presence of inorganic body.The present invention is
It is combined by the organic material of water-tolerant and the inorganic material of good weatherability, add shades of colour and keep homochromy one with building body
Kind of waterproof material, its good waterproof performance, weather-proof persistently, multicolour optional to be consistent with building body color.
Specific embodiment
With reference to the preferred embodiment of the present invention, the invention is described in detail:
The organic component a of colorful nano water-proof glue is prepared: (1) is standby by following weight portion feeding: acrylic emulsion 30 ~ 33
Part, with 0.1 ~ 0.15 part of preservative as auxiliary agent, 2.8 ~ 3.0 parts of water is as solvent for 0.2 ~ 0.4 part of defoamer；(2) by above-mentioned heavy
Amount part, acrylic emulsion is added to the water and stirs；(3) above-mentioned weight portion defoamer is added in (2) gains and stir
Uniformly；(4) above-mentioned weight portion preservative is added and measure after stirring 15 minutes about in (3) gains, fill, storage.
The inorganic component b of colorful nano water-proof glue is prepared: (1) is standby by following weight portion feeding: 42.5# silicate
, as gellant, as aggregate, 400 5 ~ 6 parts of mesh triple superphosphate are as inserts, nano silicone for 20 ~ 22 parts of quartz sand for 35 ~ 38 parts of cement
, as close material, as colorant, 0.2 ~ 0.3 part of water reducer is as auxiliary agent for 4 ~ 5 parts of iron oxide pigment for 5 parts of algae powder；(2) by (1)
In each raw material mix and blend 3 ~ 5 minutes, be dry mixed uniformly, then measure, packaging, storage.
By the above-mentioned organic component a preparing gained and inorganic component b mixing and stirring, obtain final product.
Claims (3)
1. a kind of colorful nano water-proof glue, is made up of organic component a and inorganic component b 1:2 mixing and stirring by weight；Its
It is characterised by, described organic component a is made up of following weight parts raw material: 30 ~ 35 parts of acrylic emulsion, defoamer 0.3 ~ 0.4
Part, 0.1 ~ 0.15 part of preservative, 28 parts of water；Described inorganic component b is made up of the raw material of following weight portion: portland cement 35
~ 38 parts, 20 ~ 22 parts of quartz sand, 5 ~ 6 parts of triple superphosphate, 5 ~ 6 parts of nanoscale diatom powder, 4 ~ 5 parts of iron oxide pigment, water reducer 0.2 ~ 0.3
Part.
2. as claimed in claim 1 colorful nano water-proof glue it is characterised in that described organic component a is prepared: (1)
Standby by following weight portion feeding: 30 ~ 33 parts of acrylic emulsion, 0.2 ~ 0.4 part of defoamer and 0.1 ~ 0.15 part of conduct of preservative
Auxiliary agent, 2.8 ~ 3.0 parts of water is as solvent；(2) press above-mentioned weight portion, acrylic emulsion is added to the water and stirs；(3) will
Stir in above-mentioned weight portion defoamer addition (2) gains；(4) above-mentioned weight portion preservative is added in (3) gains
Measure after stirring 15 minutes about, fill, storage.
3. as claimed in claim 1 or 2 colorful nano water-proof glue it is characterised in that described inorganic component b is prepared:
(1) press following weight portion feeding standby:, as gellant, 20 ~ 22 parts of quartz sand is as bone for 35 ~ 38 parts of 42.5# portland cement
Material, as inserts, as close material, 4 ~ 5 parts of iron oxide pigment is as color for 5 parts of nanoscale diatom powder for 400 5 ~ 6 parts of mesh triple superphosphate
Material, 0.2 ~ 0.3 part of water reducer is as auxiliary agent；(2) by raw material mix and blend each in (1) 3 ~ 5 minutes, it is dry mixed uniformly, then measures,
Packaging, storage.