CN1063377A - The prescription of polyethylene layer of power cable - Google Patents
The prescription of polyethylene layer of power cable Download PDFInfo
- Publication number
- CN1063377A CN1063377A CN 92100311 CN92100311A CN1063377A CN 1063377 A CN1063377 A CN 1063377A CN 92100311 CN92100311 CN 92100311 CN 92100311 A CN92100311 A CN 92100311A CN 1063377 A CN1063377 A CN 1063377A
- Authority
- CN
- China
- Prior art keywords
- prescription
- power cable
- mda
- polyethylene layer
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of prescription of polyethylene layer of power cable, with the polyvinyl resin is base-material, add four (β-(3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid) pentaerythritol ester, the two stearic alcohol esters of thio-2 acid, metal deactivator, ethylene bis stearamide and calcinated argil therein; Mediate again after above-mentioned substance mixed by component, banburying, open refining, granulation, extrude, stranding promptly can be made into power cable behind the irradiation, this cable temperature resistant grade height, ageing-resistant performance be good, have excellent electric insulation and mechanical performance, is applicable to rated voltage 1kV that ambient temperature height, ampacity are big and following transmission and distribution circuit.
Description
The present invention relates to a kind of prescription of polyethylene layer of power cable, the prescription of 105 ℃ of especially a kind of heatproofs, 1kV grade irradiation cross-linked power cable insulating barrier contains polyvinyl resin and various additive.
As everyone knows, in the power supply system of specific environments such as traditional power supply system of China and high temperature, all adopt the oilpaper power cable, promptly being wrapped in conductive surface with oil-paper insulate, this power cable in use, because the oil in its oilpaper layer easily exosmoses, thereby cause that its insulation property are poor, temperature resistant grade is low, useful life is short; Therefore the domestic polyvinyl chloride full plastic power cable that gradually adopts replaces original oil paper cable.But the polyvinyl chloride full plastic power cable has limited its use because of shortcomings such as its working temperature are very low, dielectric loss angle tangent is higher, ampacity is low, easy aging, easy to crack.At present, all adopt cross-linked power cable to replace all-plastic cable both at home and abroad, cross-linking method mainly contains two kinds: chemical crosslinking and cross-linking radiation; More general at home power cable is the processes for chemically crosslinked polyethylene power cable.The power cable material that is used for chemical crosslinking as the development in 1989 of Lanzhou chemical industrial company is base-material with the hp-ldpe, add dicumyl peroxide therein as cross-linked evocating agent, add 4,4 '-thiobis (the 6-tert-butyl group-3-methyl) phenol makes power cable through chemical crosslinking, cabling process then as antioxidant; This power cable makes additive reaction incomplete because of its insulating barrier adopts chemical crosslinking, cause impurity residual, thereby its insulation property is poor; Adopt chemical crosslinking to be prone to water tree, eccentric, molten flow phenomenon in addition, thereby its electrical property and mechanical performance are relatively poor, and its process conditions are difficult to control, make it further promote to produce and be restricted.Developed the cross-linking radiation cable of 90 ℃ of rated voltage 1kV, heatproof abroad, this cable uses restricted in 105 ℃ of need heatproofs account for 80% power cable.
The objective of the invention is to provide a kind of and make that cable has the working temperature height, ampacity is big, the anti-oxidant aging ability is strong for fear of above-mentioned the deficiencies in the prior art part, the prescription of the polyethylene layer of power cable of insulation property and electrical property, better mechanical property.
Purpose of the present invention can realize by following measure:
A kind of prescription of polyethylene layer of power cable contains polyvinyl resin and various additive, is base-material with the polyvinyl resin, adds various additives therein; Its formula constituent is:
100 parts of polyvinyl resins add therein
Four (β-(3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid) pentaerythritol resin
0.2-0.5 part
The two stearic alcohol ester 0.1-0.5 parts of thio-2 acid
Metal deactivator MDA-7(Tianjin synthetic material research institute) 0.3-0.5 part
Ethylene bis stearamide 0.1-0.3 part
Calcination potter's clay 8-15 part
Purpose of the present invention also can realize by following measure:
Polyvinyl resin in the prescription is that melt index is 0.3,1.3,2.0 hp-ldpe; Pentaerythritol ester can be with 2,2 in the prescription four (β-(3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid), 4-trimethyl-1, and 2-dihyaroquinoline, three (1,2,2,6,6-pentamethyl-4-piperidyl) phosphite ester replaces, and its formula constituent is constant; The two stearic alcohol esters of thio-2 acid replace with dilauryl thiodipropionate, N-isopropyl-N '-diphenyl-para-phenylene diamine, and its formula constituent is constant; Metal deactivator MDA-7 can use MDA-2, MDA-5 to replace, and its formula constituent is constant; Ethylene bis stearamide can replace with the methylene bis stearmide, and its formula constituent is constant.
A kind of prescription of polyethylene layer of power cable, its formula constituent is:
100 parts of hp-ldpes add therein
2,2,4-trimethyl-1,2-dihyaroquinoline 0.2-0.4 part
Dilauryl thiodipropionate 0.1-0.3 part
Metal deactivator MDA-2 0.3-0.4 part
Methylene bis stearmide 0.1-0.2 part
Calcination potter's clay 8-10 part
A kind of prescription of polyethylene layer of power cable, formula constituent is:
100 parts of hp-ldpes add therein
Three (1,2,2,6,6-pentamethyl-4-piperidyl) phosphite ester 0.3-0.5 part
N-isopropyl-N '-diphenyl-para-phenylene diamine 0.35-0.5 part
Metal deactivator MDA-5 0.4-0.5 part
Ethylene bis stearic amide 0.2-0.3 part
Potter's clay 10-12 part
A kind of prescription of polyethylene layer of power cable, formula constituent is:
100 parts of hp-ldpes add therein
Three (1,2,2,6,6-pentamethyl-4-piperidyl) phosphite ester 0.2-0.5 part
Dilauryl thiodipropionate 0.1-0.5 part
Metal deactivator MDA-7 0.3-0.4 part
Ethylene bis stearic amide 0.1-0.3 part
Potter's clay 10-15 part
After a kind of prescription of polyethylene layer of power cable, the material in the prescription are pressed component and mixed, through banburying, open refining, extrude, carry out cross-linking radiation again, irradiation dose is 20-30Mrad.
The present invention has following advantage compared to existing technology:
1, be base-material with the hp-ldpe in the prescription of the present invention, add four (β-(3 therein, the 5-di-tert-butyl-hydroxy phenyl) propionic acid) pentaerythritol ester is made auxiliary antioxidant as antioxidant and the two stearic alcohol esters of thio-2 acid, the two has cooperative effect, insulating barrier heat resistanceheat resistant, oxygen, aging ability have been improved, make its tensile strength and elongation at break rate of change surpass international standard, improved heat resistance.
2, add metal deactivator MDA-7 in the prescription of the present invention, suppressed the accelerated ageing effect of copper, aluminium conductor, cause the temperature resistant grade of insulating barrier when rated voltage is 1kV, to bring up to 105 ℃ from 90 ℃ to insulating barrier.
3, after the material in the prescription of the present invention is pressed the component mixing, carry out cross-linking radiation again, phenomenons such as the molten stream of having avoided adopting chemical crosslinking to cause, off-centre, water tree, mechanical performance of products and ampacity have been improved, current capacity exceeds 1-2 cross section class, and cable allows short circuit current to exceed 2 cross section class.
5, formula constituent of the present invention is few, technology is simple, cost is low, good product performance, safe and reliable.
The present invention also will be described in further detail in conjunction with the embodiments:
Embodiment one:
Get 100 parts of polyvinyl resins, as base-material, add 0.1 part of the two stearic alcohol ester of four (β-(3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid) 0.5 part of pentaerythritol resin, thio-2 acid, metal deactivator MDA-7(Tianjin synthetic material research institute therein) 0.3 part, 0.2 part of ethylene bis stearamide, 10 parts in calcination potter's clay.
Polyvinyl resin in will filling a prescription earlier adds in the high speed kneader, adds above-mentioned substance successively by the component in the prescription then, and start blender and stir after 2 minutes, banburying 8 minutes in banbury again, the banburying temperature is that 138 ℃, banbury screw speed are 40 rev/mins; And in mill, open refining pelletizing after 2 minutes, the preceding roll temperature of mill is 100 ℃, afterwards roll temperature is 90 ℃; And then in the material adding extruder with pelletizing, on extruder, be extruded in and twisted the conductive surface that makes, after sparking test, carrying out cross-linking radiation by the speed of 20 meters of per minutes, its irradiation dose is 20Mrad, stranding then.
Embodiment two:
Get 100 parts of polyvinyl resins, as base-material, add 0.5 part of the two stearic alcohol ester of four (β-(3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid) 0.2 part of pentaerythritol resin, thio-2 acid, metal deactivator MDA-7(Tianjin synthetic material research institute therein) 0.5 part, 0.1 part of ethylene bis stearamide, 8 parts in calcination potter's clay.
With embodiment together, make power cable, its irradiation dose is 30Mrad.
Embodiment three:
Get 100 parts of hp-ldpes, add 2,2 therein, 4-trimethyl-1,0.4 part of 2-dihyaroquinoline, 0.1 part of dilauryl thiodipropionate, 0.4 part of metal deactivator MDA-2,0.1 part of methylene bis stearmide, 8 parts in calcination potter's clay.
With embodiment together, make power cable, its irradiation dose is 25Mrad.
Embodiment four:
Get 100 parts of hp-ldpes, add 2,2 therein, 4-trimethyl-1,0.2 part of 2-dihyaroquinoline, 0.3 part of dilauryl thiodipropionate, 0.3 part of metal deactivator MDA-2,0.2 part of methylene bis stearmide, 10 parts in calcination potter's clay.
With embodiment together, make power cable, its irradiation dose is 28Mrad.
Embodiment five:
Get 100 parts of hp-ldpes, add three (1,2,2 therein, 6,6-pentamethyl-4-piperidyl) 0.5 part of phosphite ester, N-isopropyl-N '-0.35 part of diphenyl-para-phenylene diamine, 0.5 part of metal deactivator MDA-5,0.2 part of ethylene bis stearic amide, 10 parts in potter's clay.
With embodiment together, make power cable, its irradiation dose is 26Mrad.
Embodiment six:
Get 100 parts of hp-ldpes, add three (1,2,2 therein, 6,6-pentamethyl-4-piperidyl) 0.3 part of phosphite ester, N-isopropyl-N '-0.5 part of diphenyl-para-phenylene diamine, 0.4 part of metal deactivator MDA-5,0.3 part of ethylene bis stearic amide, 12 parts in potter's clay.
With embodiment together, make power cable, its irradiation dose is 29Mrad.
Embodiment seven:
Get 100 parts of hp-ldpes, add three (1,2,2 therein, 6,6-pentamethyl-4-piperidyl) 0.4 part of phosphite ester, 0.3 part of dilauryl thiodipropionate, 0.3 part of metal deactivator MDA-7,0.2 part of ethylene bis stearic amide, 12 parts in potter's clay.
With embodiment together, make power cable, its irradiation dose is 22Mrad.
Embodiment eight:
Get 100 parts of hp-ldpes, add three (1,2,2 therein, 6,6-pentamethyl-4-piperidyl) 0.2 part of phosphite ester, 0.5 part of dilauryl thiodipropionate, 0.4 part of metal deactivator MDA-7,0.1 part of ethylene bis stearic amide, 15 parts in potter's clay.
With embodiment together, make power cable, its irradiation dose is 24Mrad.
Claims (7)
1, a kind of prescription of polyethylene layer of power cable contains polyvinyl resin and various additive, it is characterized in that with the polyvinyl resin being base-material, adds various additives therein; Its formula constituent is:
100 parts of polyvinyl resins add therein
Four [β-(3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester 0.2-0.5 part
The two stearic alcohol ester 0.1-0.5 parts of thio-2 acid
Metal deactivator MDA-7 (Tianjin synthetic material research institute) 0.3-0.5 part
Ethylene bis stearamide 0.1-0.3 part
Calcinated argil 8-15 part
2, the prescription of polyethylene layer of power cable as claimed in claim 1, the polyvinyl resin in it is characterized in that filling a prescription are that melt index is 0.3,1.3,2.0 hp-ldpe.
3, the prescription of polyethylene layer of power cable as claimed in claim 1, four (β-(3 in it is characterized in that filling a prescription, the 5-di-tert-butyl-hydroxy phenyl) propionic acid) pentaerythritol ester can be with 2,2,4-trimethyl-1,2-dihyaroquinoline, three (1,2,2,6,6-pentamethyl-4-piperidyl) phosphite ester replaces, and its formula constituent is constant; The two stearic alcohol esters of thio-2 acid can use dilauryl thiodipropionate, N-isopropyl-N '-diphenyl-para-phenylene diamine to replace, and its formula constituent is constant; Metal deactivator MDA-7 can use MDA-2, MDA-5 to replace, and its formula constituent is constant; Ethylene bis stearamide can replace with the methylene bis stearmide, and its formula constituent is constant.
4, the prescription of polyethylene layer of power cable as claimed in claim 1 is characterized in that formula constituent is:
100 parts of hp-ldpes add therein
2,2,4-trimethyl-1,2-dihyaroquinoline 0.2-0.4 part
Thio-2 acid two laurate 0.1-0.3 parts
Metal deactivator MDA-2 0.3-0.4 part
Methylene bis stearmide 0.1-0.2 part
Calcination potter's clay 8-10 part
5, the prescription of polyethylene layer of power cable as claimed in claim 1 is characterized in that formula constituent is:
100 parts of hp-ldpes add therein
Three (1,2,2,6,6-pentamethyl-4-piperidyl) phosphite ester 0.3-0.5 part
N-isopropyl-N '-diphenyl-para-phenylene diamine 0.35-0.5 part
Metal deactivator MDA-5 0.4-0.5 part
Ethylene bis stearic amide 0.2-0.3 part
Potter's clay 10-12 part
6, the prescription of polyethylene layer of power cable as claimed in claim 1 is characterized in that formula constituent is:
100 parts of hp-ldpes add therein
Three (1,2,2,6,6-pentamethyl-4-piperidyl) phosphite ester 0.2-0.5 part
Dilauryl thiodipropionate 0.1-0.5 part
Metal deactivator MDA-7 0.3-0.4 part
Ethylene bis stearic amide 0.1-0.3 part
Potter's clay 10-15 part
7, after the prescription of polyethylene layer of power cable as claimed in claim 1, the material in it is characterized in that filling a prescription mix by component, through banburying, open refining, extrude, carry out cross-linking radiation again, irradiation dose is 20-30Mrad.