CN106334569A - Catalyst coating formula used for electrode plate - Google Patents
Catalyst coating formula used for electrode plate Download PDFInfo
- Publication number
- CN106334569A CN106334569A CN201510406759.4A CN201510406759A CN106334569A CN 106334569 A CN106334569 A CN 106334569A CN 201510406759 A CN201510406759 A CN 201510406759A CN 106334569 A CN106334569 A CN 106334569A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- oxide
- phenol
- following components
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of a catalyst coating, and especially relates to a catalyst coating formula used for an electrode plate. The catalyst coating comprises the following components in parts by mass: 2.5-3.6 parts of copper oxide, 5-10 parts of manganese dioxide, 15-20 parts of glycol, 8-15 parts of citric acid, 3.4-5.8 parts of tin oxide, 1.8-2.9 parts of nano titanium dioxide, 10-15 parts of salicylic acid, 12-18 parts of dihydroxybenzoic acid, 4.5-6.3 parts of phenol, and 2.2-4.5 parts of aluminium triphosphate. By employing the above formula, the catalyst coating has the advantages of simple process, low cost, good purifying scope, purifying effect and sterilization effect, can effectively solve the peculiar smell problem generated by an adsorbate, and has the characteristics of environmental protection and utility.
Description
Technical field
The present invention relates to catalyst coat technical field, particularly a kind of battery lead plate catalyst coat formula.
Background technology
Chlorine is normally industrially by a solution sodium chloride or hydrochloric acid or to pass through gas phase oxidation of hydrogen chloride system
Standby.If using electrolytic method, chlorine is to produce in anode.Anode material used is by being to be used as
, there is electro-chemical activity catalyst in its surface in the titanium of electrode material.Comprise the surface layer of catalyst at this
Commonly referred to as coating.The effect of catalyst is to reduce overpotential and prevent from being formed oxygen at anode.
It will be appreciated that noble metal is under electrolysis conditions over time and from painting from the coating of prior art
It is eluted out in layer;Long-term corrosion resistance is therefore not enough.To the needs of corrosion resistance due to the fact that change
Obtain obviously.
Content of the invention
The technical problem to be solved in the invention is to provide a kind of battery lead plate catalyst coat formula.
For solving above-mentioned technical problem, a kind of battery lead plate catalyst coat formula of the present invention, according to quality
Number meter includes following components: copper oxide 2.5-3.6 part, manganese dioxide 5-10 part, ethylene glycol 15-20 part,
Citric acid 8-15 part, stannum oxide 3.4-5.8 part, nano titanium oxide 1.8-2.9 part, salicylic acid 10-15
Part, resorcylic acid 12-18 part, phenol 4.5-6.3 part, aluminium triphosphate 2.2-4.5 part.
Further, include following components: 2.5 parts of copper oxide according to mass fraction meter, 5 parts of manganese dioxide,
15 parts of ethylene glycol, 8 parts of citric acid, 3.4 parts of stannum oxide, 1.8 parts of nano titanium oxide, salicylic acid 10
Part, 12 parts of resorcylic acid, 4.5 parts of phenol, 2.2 parts of aluminium triphosphate.
Further, include following components: 3.6 parts of copper oxide according to mass fraction meter, 10 parts of manganese dioxide,
20 parts of ethylene glycol, 15 parts of citric acid, 5.8 parts of stannum oxide, 2.9 parts of nano titanium oxide, salicylic acid 15
Part, 18 parts of resorcylic acid, 6.3 parts of phenol, 4.5 parts of aluminium triphosphate.
Further, include following components: 2.9 parts of copper oxide according to mass fraction meter, 6 parts of manganese dioxide,
16 parts of ethylene glycol, 11 parts of citric acid, 4.1 parts of stannum oxide, 2.2 parts of nano titanium oxide, salicylic acid 11
Part, 15 parts of resorcylic acid, 5.2 parts of phenol, 2.8 parts of aluminium triphosphate.
Further, include following components: 3.3 parts of copper oxide according to mass fraction meter, 8 parts of manganese dioxide,
18 parts of ethylene glycol, 14 parts of citric acid, 4.6 parts of stannum oxide, 2.5 parts of nano titanium oxide, salicylic acid 13
Part, 16 parts of resorcylic acid, 5.9 parts of phenol, 3.4 parts of aluminium triphosphate.
After above-mentioned formula, the catalyst coat process is simple of the present invention, low cost, purify scope, purification
Effect and bactericidal effect more preferably, also effectively solve the Peculiar Smell of adsorbate generation, more environmentally-friendly, real
With.
Specific embodiment
A kind of battery lead plate catalyst coat formula of the present invention, includes following components according to mass fraction meter: oxygen
Change copper 2.5-3.6 part, manganese dioxide 5-10 part, ethylene glycol 15-20 part, citric acid 8-15 part, oxidation
Stannum 3.4-5.8 part, nano titanium oxide 1.8-2.9 part, salicylic acid 10-15 part, resorcylic acid 12-18
Part, phenol 4.5-6.3 part, aluminium triphosphate 2.2-4.5 part.
Embodiment one:
Include following components: 2.5 parts of copper oxide, 5 parts of manganese dioxide, ethylene glycol 15 according to mass fraction meter
Part, 8 parts of citric acid, 3.4 parts of stannum oxide, 1.8 parts of nano titanium oxide, 10 parts of salicylic acid, dihydroxy
12 parts of benzoic acid, 4.5 parts of phenol, 2.2 parts of aluminium triphosphate.
Embodiment two:
Include following components: 3.6 parts of copper oxide, 10 parts of manganese dioxide, ethylene glycol 20 according to mass fraction meter
Part, 15 parts of citric acid, 5.8 parts of stannum oxide, 2.9 parts of nano titanium oxide, 15 parts of salicylic acid, dihydroxy
18 parts of yl benzoic acid, 6.3 parts of phenol, 4.5 parts of aluminium triphosphate.
Embodiment three:
Include following components: 2.9 parts of copper oxide, 6 parts of manganese dioxide, ethylene glycol 16 according to mass fraction meter
Part, 11 parts of citric acid, 4.1 parts of stannum oxide, 2.2 parts of nano titanium oxide, 11 parts of salicylic acid, dihydroxy
15 parts of yl benzoic acid, 5.2 parts of phenol, 2.8 parts of aluminium triphosphate.
Embodiment four:
Include following components: 3.3 parts of copper oxide, 8 parts of manganese dioxide, ethylene glycol 18 according to mass fraction meter
Part, 14 parts of citric acid, 4.6 parts of stannum oxide, 2.5 parts of nano titanium oxide, 13 parts of salicylic acid, dihydroxy
16 parts of yl benzoic acid, 5.9 parts of phenol, 3.4 parts of aluminium triphosphate.
Although the foregoing describing the specific embodiment of the present invention, those skilled in the art should manage
Solution, these are merely illustrative of, and can make various changes or modifications to present embodiment, without departing from send out
Bright principle and essence, protection scope of the present invention is only limited by the claims that follow.
Claims (5)
1. a kind of battery lead plate catalyst coat formula is it is characterised in that include following components according to mass fraction meter:
Copper oxide 2.5-3.6 part, manganese dioxide 5-10 part, ethylene glycol 15-20 part, citric acid 8-15 part, oxygen
Change stannum 3.4-5.8 part, nano titanium oxide 1.8-2.9 part, salicylic acid 10-15 part, resorcylic acid
12-18 part, phenol 4.5-6.3 part, aluminium triphosphate 2.2-4.5 part.
2. according to a kind of battery lead plate described in claim 1 with catalyst coat formula it is characterised in that according to matter
Amount number meter includes following components: 2.5 parts of copper oxide, 5 parts of manganese dioxide, 15 parts of ethylene glycol, citric acid
8 parts, 3.4 parts of stannum oxide, 1.8 parts of nano titanium oxide, 10 parts of salicylic acid, 12 parts of resorcylic acid,
4.5 parts of phenol, 2.2 parts of aluminium triphosphate.
3. according to a kind of battery lead plate described in claim 1 with catalyst coat formula it is characterised in that according to matter
Amount number meter includes following components: 3.6 parts of copper oxide, 10 parts of manganese dioxide, 20 parts of ethylene glycol, Fructus Citri Limoniae
15 parts of acid, 5.8 parts of stannum oxide, 2.9 parts of nano titanium oxide, 15 parts of salicylic acid, resorcylic acid
18 parts, 6.3 parts of phenol, 4.5 parts of aluminium triphosphate.
4. according to a kind of battery lead plate described in claim 1 with catalyst coat formula it is characterised in that according to matter
Amount number meter includes following components: 2.9 parts of copper oxide, 6 parts of manganese dioxide, 16 parts of ethylene glycol, citric acid
11 parts, 4.1 parts of stannum oxide, 2.2 parts of nano titanium oxide, 11 parts of salicylic acid, resorcylic acid 15
Part, 5.2 parts of phenol, 2.8 parts of aluminium triphosphate.
5. according to a kind of battery lead plate described in claim 1 with catalyst coat formula it is characterised in that according to matter
Amount number meter includes following components: 3.3 parts of copper oxide, 8 parts of manganese dioxide, 18 parts of ethylene glycol, citric acid
14 parts, 4.6 parts of stannum oxide, 2.5 parts of nano titanium oxide, 13 parts of salicylic acid, resorcylic acid 16
Part, 5.9 parts of phenol, 3.4 parts of aluminium triphosphate.