CN106319707A - Method for preparing pine pollen yarns - Google Patents
Method for preparing pine pollen yarns Download PDFInfo
- Publication number
- CN106319707A CN106319707A CN201610690890.2A CN201610690890A CN106319707A CN 106319707 A CN106319707 A CN 106319707A CN 201610690890 A CN201610690890 A CN 201610690890A CN 106319707 A CN106319707 A CN 106319707A
- Authority
- CN
- China
- Prior art keywords
- spinning
- weight
- pollen pini
- weight portions
- gained
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing pine pollen yarns, and relates to the technical field of spinning. The method for preparing the pine pollen yarns comprises the following steps: preparing pine pollen copper ammonia fibers; determining the pine pollen copper ammonia fibers, tencel and modal fibers as raw materials; performing coiling, cotton carding, mixing and vortex spinning. By adopting the method, pine pollen can be prepared into a yarn fabric to be worn on a body, and a new pine pollen utilization method is provided.
Description
Technical field
The present invention relates to textile technology field, the preparation method of a kind of Pollen Pini yarn.
Background technology
Pollen Pini, for pinaceae plant Pinus massoniana Lamb Pinus massoniana Lamb., Pinus tabulaeformis tabuli formis
Or belong to the dry pollen of several plants together, in addition to containing the general nutrient substance such as protein, fat, saccharide, possibly together with multiple Carr.
Vitamin, trace element, flavone, enzyme, fatty acid and coenzyme etc. more than 200 plant nutritional labeling and bioactive substance.Not only have
Promote skin cell metabolism, skin-cell aging delaying, increase skin elasticity, make the beauty treatment of the pure white ruddy fitness of skin imitate
Really, also dripping to comedo, eczema, impetigo, skin erosion, dense water, traumatic hemorrhage, diaper dermatitis etc. have well treatment
Effect.Utilization for Pollen Pini is all to be made into the Land use systems that yarn fabric wears in the way of edible at present
Do not see record.
Summary of the invention
The present invention provides the preparation method of a kind of Pollen Pini yarn, and it can solve that Pollen Pini is made yarn fabric and be through body
On provide the problem of Application way of a kind of new Pollen Pini with this.
In order to solve the problems referred to above, the technical solution adopted in the present invention is: the preparation method of this Pollen Pini yarn, including
Following steps:
A, prepare Pollen Pini CUP: the native cellulose of 85 weight portions～95 weight portions is dissolved in the dense ammonia of alkaline cupric salt
In solution, it is made into spinning liquid, then adds 1 weight portion～the Pollen Pini of 5 weight portions, 0.5 weight portion～1.5 to gained spinning liquid
The coupling agent of weight portion and 5 weight portions～the dispersant of 15 weight portions, filter after mixing, by wet spinning spinning process molding,
Obtain Pollen Pini CUP standby；
B, select materials: select Pollen Pini CUP 20 weight for fineness is a length of 36mm～40mm of 1.4dtex～1.6dtex
Part～30 weight portions, fineness is tencel 10 weight portion～20 weight portions of a length of 36mm～40mm of 1.3dtex～1.5dtex,
With Modal fibre 10 weight portion that fineness is a length of 36mm～40mm of 1.2dtex～1.4dtex～20 weight portions；
C, rolling: by the raw material in step B respectively by opening picking rolling combination machine rolling；
D, comb and parallel cotton fibers prior to spinning: by the raw material of gained comb and parallel cotton fibers prior to spinning respectively in step C；
E, mixed also: the raw material of gained in step D is carried out mixed also, including head also, two and and end also, described head and two also
Time, roller gauge is 10 × 9 × 18, and total draft multiple is 5.8～6.2, and sliver exporting speed is 240m/min～260m/min, and head is also
To be mixed into master, two and based on drawing-off；Described end and time, roller gauge is 43 × 51, and total draft multiple is 5.8～6.2,
Ribbon dry weight is 25g/5m, and cotton sliver Unevenness CV is 2.5%～3.5%, and control is also done based on drawing-off and weight bar in end；
F, raw material to step E gained carry out air vortex spinning, to obtain final product.
Coupling agent includes: HK-540, HK-550, HK-560, HK-570, HK-602, HK-792, Si-563, Si-602, A-
151, A-171, A-172, Sj-42 etc..
The silicate such as dispersant includes: lignosulfonates, alkyl glyceryl ether sulfonate, waterglass, alkali sodium tripolyphosphate,
The metal phosphate such as sodium hexameta phosphate and sodium pyrophosphate, triethyl group hexyl phosphoric acid, sodium lauryl sulphate, methyl anyl alcohol, fiber
Element derivant, polyacrylamide, guar gum, fatty acid polyethylene glycol ester etc..
Owing to have employed technique scheme, the present invention compared with prior art has the advantages that
The Pollen Pini yarn of the present invention, owing to Pollen Pini grain diameter is at 35-50 micron, can be the most uniform at fibrous inside and outer surface
Distribution, for a long time in contact skin, existing Pollen Pini beauty care, relieve inflammation or internal heat relieve internal heat, effect of tender white muscle skin, have again moisture absorption ventilative,
Characteristic comfortable and easy to wear.Provide a kind of new method utilizing Pollen Pini.
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment one:
The preparation method of a kind of Pollen Pini yarn is as follows:
A, prepare Pollen Pini CUP: in the copper-bath of 5%, add the sodium hydroxide solution of 10%, obtain Copper hydrate
Precipitation, outwells supernatant, dissolves the Copper hydrate precipitation obtained with strong aqua ammonia, it is thus achieved that the copper ammon solution of higher concentration, takes 85 kg
Cotton fiber is dissolved in copper ammon solution, is made into spinning liquid；Then to gained spinning liquid add 1kg Pollen Pini, 0.2kg HK-540,
0.3kg HK-550,1kg alkyl glycerol ether sulfonic acid, 2kg sodium lauryl sulphate and 2kg fatty acid polyethylene glycol ester, after mixing
Filtering, wherein filtering accuracy is≤50 μm, routinely the molding of wet spinning spinning process, obtains Pollen Pini CUP standby；
B, select materials: select Pollen Pini CUP 20 weight for fineness is a length of 36mm～40mm of 1.4dtex～1.6dtex
Part, fineness is tencel 10 weight portion of a length of 36mm～40mm of 1.3dtex～1.5dtex, and fineness be 1.2dtex～
Modal fibre 10 weight portion of a length of 36mm～40mm of 1.4dtex；
C, rolling: by the raw material in step B respectively by opening picking rolling combination machine rolling；
D, comb and parallel cotton fibers prior to spinning: by the raw material of gained comb and parallel cotton fibers prior to spinning respectively in step C；
E, mixed also: the raw material of gained in step D is carried out mixed also, including head also, two and and end also, described head and two also
Time, roller gauge is 10 × 9 × 18, and total draft multiple is 5.8～6.2, and sliver exporting speed is 240m/min～260m/min, and head is also
To be mixed into master, two and based on drawing-off；Described end and time, roller gauge is 43 × 51, and total draft multiple is 5.8～6.2,
Ribbon dry weight is 25g/5m, and cotton sliver Unevenness CV is 2.5%～3.5%, and control is also done based on drawing-off and weight bar in end；
F, raw material to step E gained carry out air vortex spinning, airflow temperature-control at 20 DEG C ~ 30 DEG C, relative humidity controls 60 ~
70, spinning speed is 340r/min, and total draft (TDR) is 211, and dominant draft (MDR) is 30, and feeding ratio is 0.96, curling ratio
Being 1.015, BR inception rate is 100%.
Obtain the Pollen Pini yarn of the present invention.
Embodiment two:
The preparation method of a kind of Pollen Pini yarn is as follows:
A, prepare Pollen Pini CUP: in the copper-bath of 5%, add the sodium hydroxide solution of 10%, obtain Copper hydrate
Precipitation, outwells supernatant, dissolves the Copper hydrate precipitation obtained with strong aqua ammonia, it is thus achieved that the copper ammon solution of higher concentration, takes 95 kg
Flaxen fiber is dissolved in copper ammon solution, is made into spinning liquid；Then to gained spinning liquid add 5kg Pollen Pini, 0.5kg HK-570,
0.2kg Si-563,0.3kg A-171,3kg methyl anyl alcohol, 3kg polyacrylamide, 3kg sodium lauryl sulphate, 3kg polypropylene
Amide and 3kg fatty acid polyethylene glycol ester, filter after mixing, and wherein filtering accuracy is≤50 μm, routinely wet spinning spray webbing
Technological forming, obtains Pollen Pini CUP standby；
B, select materials: select Pollen Pini CUP 30 weight for fineness is a length of 36mm～40mm of 1.4dtex～1.6dtex
Part, fineness is tencel 20 weight portion of a length of 36mm～40mm of 1.3dtex～1.5dtex, and fineness be 1.2dtex～
Modal fibre 20 weight portion of a length of 36mm～40mm of 1.4dtex；
Remaining step is with embodiment one.
Claims (1)
1. the preparation method of a Pollen Pini yarn, it is characterised in that comprise the following steps:
A, prepare Pollen Pini CUP: the native cellulose of 85 weight portions～95 weight portions is dissolved in the dense ammonia of alkaline cupric salt
In solution, it is made into spinning liquid, then adds 1 weight portion～the Pollen Pini of 5 weight portions, 0.5 weight portion～1.5 to gained spinning liquid
The coupling agent of weight portion and 5 weight portions～the dispersant of 15 weight portions, filter after mixing, by wet spinning spinning process molding,
Obtain Pollen Pini CUP standby；
B, select materials: select Pollen Pini CUP 20 weight for fineness is a length of 36mm～40mm of 1.4dtex～1.6dtex
Part～30 weight portions, fineness is tencel 10 weight portion～20 weight portions of a length of 36mm～40mm of 1.3dtex～1.5dtex,
With Modal fibre 10 weight portion that fineness is a length of 36mm～40mm of 1.2dtex～1.4dtex～20 weight portions；
C, rolling: by the raw material in step B respectively by opening picking rolling combination machine rolling；
D, comb and parallel cotton fibers prior to spinning: by the raw material of gained comb and parallel cotton fibers prior to spinning respectively in step C；
E, mixed also: the raw material of gained in step D is carried out mixed also, including head also, two and and end also, described head and two also
Time, roller gauge is 10 × 9 × 18, and total draft multiple is 5.8～6.2, and sliver exporting speed is 240m/min～260m/min, and head is also
To be mixed into master, two and based on drawing-off；Described end and time, roller gauge is 43 × 51, and total draft multiple is 5.8～6.2,
Ribbon dry weight is 25g/5m, and cotton sliver Unevenness CV is 2.5%～3.5%, and control is also done based on drawing-off and weight bar in end；
F, air vortex spinning: the raw material of step E gained is carried out air vortex spinning, to obtain final product.