CN106318572A - Leather product zipper lubricating oil - Google Patents
Leather product zipper lubricating oil Download PDFInfo
- Publication number
- CN106318572A CN106318572A CN201610653222.2A CN201610653222A CN106318572A CN 106318572 A CN106318572 A CN 106318572A CN 201610653222 A CN201610653222 A CN 201610653222A CN 106318572 A CN106318572 A CN 106318572A
- Authority
- CN
- China
- Prior art keywords
- parts
- lubricating oil
- powder
- heated
- zipper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses leather product zipper lubricating oil and relates to the technical field of leather product processing. The leather product zipper lubricating oil is prepared from, by weight, 15-20 parts of wool fat, 10-15 parts of turpentine, 10-15 parts of rice bran wax, 6-11 parts of vulcanized lard oil, 5-9 parts of microcrystalline cellulose, 4-7 parts of coal ash, 4-7 parts of glyceryl behenate, 3-6 parts of coalescing agent, 3-6 parts of polyacrylamide, 2-4 parts of sepiolite powder, 2-4 parts of behenamide, 2-4 parts of polyoxypropylene glycerol ether, 2-4 parts of hydrogenated castor oil, 1-2 parts of glycerol monolaurate and 1-2 parts of nano glue powder. The lubricating oil is bright and moderate in viscosity, and a protective film can be formed on the surfaces of zipper teeth after a zipper is coated with the lubricating oil; the protective film has excellent lubricity, waterproofness and high and low temperature resistance, rusting of the zipper teeth and deterioration of the lubricating oil are effectively avoided, and therefore normal use of the zipper is guaranteed.
Description
Technical field:
The present invention relates to leatherware processing technique field, be specifically related to a kind of leatherware slide fastener lubricating oil.
Background technology:
Slide fastener is one of main parts size of leatherware, is sewn on leatherware by sewing thread.Most leatherware slide fasteners by
Metal-toothed forms, and the phenomenon that difficulty pulls in use often occurs, particularly easily gets rusty after meeting water, and rust staining can stop chain tooth
Engagement or disengagement, thus affect the normal use of slide fastener.If replacing slide fastener, will have what slide fastener and leatherware color were not arranged in pairs or groups
Phenomenon, thus affect the aesthetic property of leatherware.For above-mentioned situation, we develop a kind of leatherware slide fastener lubricating oil, first this profit
Secondly leather will not be had a negative impact by lubricating oil, and lubricity is good, and can play the water resistance of excellence after being applied in slide fastener,
Prevent slide fastener from getting rusty after meeting water.
Summary of the invention:
The technical problem to be solved is to provide one to have excellent lubricity, water proofing property and resistant of high or low temperature
And leatherware slide fastener lubricating oil leather will not being had a negative impact.
The technical problem to be solved uses following technical scheme to realize:
A kind of leatherware slide fastener lubricating oil, is made up of the raw material of following parts by weight:
Lanoline 15-20 part, Oleum Terebinthinae 10-15 part, rice bran wax 10-15 part, sulfurized lard 6-11 part, microcrystalline Cellulose 5-
9 parts, flyash 4-7 part, Glyceryl Behenate 4-7 part, coalescents 3-6 part, polyacrylamide 3-6 part, sepiolite powder 2-4
Part, behenamide 2-4 part, polypropylene glycerol aether 2-4 part, castor oil hydrogenated 2-4 part, glycerol monolaurate 1-2 part, receive
Rice glue powder 1-2 part;
Its preparation method comprises the steps:
(1) in lanoline, add rice bran wax and castor oil hydrogenated, and be heated to 80-90 DEG C of insulation mixing 10min, then add
Enter flyash, sepiolite powder and nanometer rubber powder, continue to be heated to 110-120 DEG C of insulation mixing 5min, obtain material I;
(2) in Oleum Terebinthinae, add sulfurized lard and coalescents, at 0-5 DEG C, stand 1h after being sufficiently mixed, then at room
Temperature is lower adds Glyceryl Behenate and polyacrylamide, is then heated to 70-80 DEG C of insulation mixing 15min, obtains material II;
(3) in material I, material II, microcrystalline Cellulose, behenamide, polypropylene glycerol aether and lauric acid list are added
Glyceride, grinds and forms it into uniform mastic.
Described coalescents is made up of the raw material of following parts by weight: pentalyn 10-15 part, rosin glyceride
10-15 part, pentaerythritol stearate 7-12 part, microwax 5-8 part, spermol 5-8 part, ultra-fine tetramethylolmethane 4-6 part, rubber
Powder 3-5 part, polyvinylpyrrolidone 3-5 part, polyethylene glycol 6000 2-3 part, emulsified silicone oil 2-3 part, camellia oleosa seed powder 1-2 part, silane
Coupling agent 1-2 part;Its preparation method is: pentalyn, rosin glyceride and rubber powder are first heated to 80-90 DEG C of guarantor
Temperature mixing 10min, adds microwax, spermol and emulsified silicone oil, continues to be heated to 120-130 DEG C of insulation mixing 5min, so
After under ice-water bath with 10 DEG C/min lower the temperature, after temperature is down to 60-70 DEG C insulation mixing 10min, be eventually adding tetramethylolmethane
Stearate, ultra-fine tetramethylolmethane, polyvinylpyrrolidone, polyethylene glycol 6000, camellia oleosa seed powder and silane coupler, grind and make it
It is sufficiently mixed uniformly.
The invention has the beneficial effects as follows: the present invention, with lanoline, Oleum Terebinthinae and rice bran wax as primary raw material, is aided with multiple helping
Agent prepares leatherware slide fastener lubricating oil, and this lubricating oil is bright and modest viscosity, can form protection at chain tooth surface after being applied in slide fastener
Film, even if adhere to also to have a negative impact leather on leather simultaneously;And this protecting film have excellence lubricity,
Water proofing property and resistant of high or low temperature, effectively prevent chain tooth from getting rusty and deterioration of lubricant, thus ensures the normal use of slide fastener.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below knot
Close specific embodiment, the present invention is expanded on further.
Embodiment 1
(1) in 15 parts of lanolines, add 10 parts of rice bran waxs and 4 parts of castor oil hydrogenated, and it is mixed to be heated to 80-90 DEG C of insulation
Close 10min, add 4 parts of flyash, 3 parts of sepiolite powders and 1 part of nanometer rubber powder, continue to be heated to 110-120 DEG C of insulation mixing
5min, obtains material I;
(2) in 10 parts of Oleum Terebinthinaes, add 6 parts of sulfurized lard and 5 parts of coalescents, stand at 0-5 DEG C after being sufficiently mixed
1h, then add 4 parts of Glyceryl Behenates and 3 parts of polyacrylamides at room temperature, it is then heated to 70-80 DEG C of insulation mixing
15min, obtains material II;
(3) in material I, material II, 5 parts of microcrystalline Cellulose, 3 parts of behenamide, 2 parts of polypropylene glycerol aethers are added
With 1 part of glycerol monolaurate, grind and form it into uniform mastic.
The preparation of coalescents: first 15 parts of pentalyns, 10 parts of rosin glyceride and 3 parts of rubber powders are heated to
80-90 DEG C of insulation mixing 10min, adds 6 parts of microwaxes, 5 parts of spermols and 2 parts of emulsified silicone oils, continues to be heated to 120-130
DEG C insulation mixing 5min, then under ice-water bath with 10 DEG C/min lower the temperature, after temperature is down to 60-70 DEG C insulation mixing 10min,
It is eventually adding 10 parts of pentaerythritol stearates, 4 parts of ultra-fine tetramethylolmethanes, 5 parts of polyvinylpyrrolidones, 3 parts of Polyethylene Glycol
6000,1 part of camellia oleosa seed powder and 1 part of silane coupler, grinds and makes it be sufficiently mixed uniformly.
Embodiment 2
(1) in 20 parts of lanolines, add 10 parts of rice bran waxs and 2 parts of castor oil hydrogenated, and it is mixed to be heated to 80-90 DEG C of insulation
Close 10min, add 6 parts of flyash, 2 parts of sepiolite powders and 1 part of nanometer rubber powder, continue to be heated to 110-120 DEG C of insulation mixing
5min, obtains material I;
(2) in 10 parts of Oleum Terebinthinaes, add 6 parts of sulfurized lard and 3 parts of coalescents, stand at 0-5 DEG C after being sufficiently mixed
1h, then add 5 parts of Glyceryl Behenates and 3 parts of polyacrylamides at room temperature, it is then heated to 70-80 DEG C of insulation mixing
15min, obtains material II;
(3) in material I, material II, 8 parts of microcrystalline Cellulose, 2 parts of behenamide, 2 parts of polypropylene glycerol aethers are added
With 2 parts of glycerol monolaurate, grind and form it into uniform mastic.
The preparation of coalescents: first 12 parts of pentalyns, 10 parts of rosin glyceride and 3 parts of rubber powders are heated to
80-90 DEG C of insulation mixing 10min, adds 6 parts of microwaxes, 5 parts of spermols and 3 parts of emulsified silicone oils, continues to be heated to 120-130
DEG C insulation mixing 5min, then under ice-water bath with 10 DEG C/min lower the temperature, after temperature is down to 60-70 DEG C insulation mixing 10min,
It is eventually adding 8 parts of pentaerythritol stearates, 5 parts of ultra-fine tetramethylolmethanes, 3 parts of polyvinylpyrrolidones, 2 parts of Polyethylene Glycol
6000,2 parts of camellia oleosa seed powder and 1 part of silane coupler, grinds and makes it be sufficiently mixed uniformly.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The technology of the industry
Personnel, it should be appreciated that the present invention is not restricted to the described embodiments, simply illustrating this described in above-described embodiment and description
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these become
Change and improvement both falls within scope of the claimed invention.Claimed scope by appending claims and
Equivalent defines.
Claims (2)
1. a leatherware slide fastener lubricating oil, it is characterised in that be made up of the raw material of following parts by weight:
Lanoline 15-20 part, Oleum Terebinthinae 10-15 part, rice bran wax 10-15 part, sulfurized lard 6-11 part, microcrystalline Cellulose 5-9 part,
Flyash 4-7 part, Glyceryl Behenate 4-7 part, coalescents 3-6 part, polyacrylamide 3-6 part, sepiolite powder 2-4 part, mountain
Yu acid amide 2-4 part, polypropylene glycerol aether 2-4 part, castor oil hydrogenated 2-4 part, glycerol monolaurate 1-2 part, nanometre glue
Powder 1-2 part;
Its preparation method comprises the steps:
(1) in lanoline, add rice bran wax and castor oil hydrogenated, and be heated to 80-90 DEG C of insulation mixing 10min, add powder
Coal ash, sepiolite powder and nanometer rubber powder, continue to be heated to 110-120 DEG C of insulation mixing 5min, obtain material I;
(2) in Oleum Terebinthinae, add sulfurized lard and coalescents, at 0-5 DEG C, after being sufficiently mixed, stand 1h, more at room temperature
Add Glyceryl Behenate and polyacrylamide, be then heated to 70-80 DEG C of insulation mixing 15min, obtain material II;
(3) in material I, material II, microcrystalline Cellulose, behenamide, polypropylene glycerol aether and lauric monoglyceride are added
Ester, grinds and forms it into uniform mastic.
Leatherware slide fastener lubricating oil the most according to claim 1, it is characterised in that described coalescents is by following parts by weight
Raw material make: pentalyn 10-15 part, rosin glyceride 10-15 part, pentaerythritol stearate 7-12 part, micro-
Brilliant wax 5-8 part, spermol 5-8 part, ultra-fine tetramethylolmethane 4-6 part, rubber powder 3-5 part, polyvinylpyrrolidone 3-5 part, poly-second
Glycol 60002-3 part, emulsified silicone oil 2-3 part, camellia oleosa seed powder 1-2 part, silane coupler 1-2 part;Its preparation method is: first by Colophonium
Pentaerythritol ester, rosin glyceride and rubber powder be heated to 80-90 DEG C insulation mixing 10min, add microwax, spermol and
Emulsified silicone oil, continues to be heated to 120-130 DEG C of insulation mixing 5min, then lowers the temperature with 10 DEG C/min under ice-water bath, treat temperature
After being down to 60-70 DEG C, insulation mixing 10min, is eventually adding pentaerythritol stearate, ultra-fine tetramethylolmethane, polyvinylpyrrolidine
Ketone, polyethylene glycol 6000, camellia oleosa seed powder and silane coupler, grind and make it be sufficiently mixed uniformly.