CN106318290A - Heat-resistant waterproof adhesive for shoes - Google Patents
Heat-resistant waterproof adhesive for shoes Download PDFInfo
- Publication number
- CN106318290A CN106318290A CN201610696555.3A CN201610696555A CN106318290A CN 106318290 A CN106318290 A CN 106318290A CN 201610696555 A CN201610696555 A CN 201610696555A CN 106318290 A CN106318290 A CN 106318290A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsion
- heat
- modified
- footwear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a heat-resistant waterproof adhesive for shoes. The heat-resistant waterproof adhesive comprises, by weight, 20-50 parts of modified acrylate emulsion, 5-15 parts of polyvinyl acetate emulsion, 2-8 parts of natural latex, 3-5 parts of styrene-butadiene latex, 1-4 parts of neoprene latex, 1-4 parts of polyacrylamide, 3-5 parts of phenolic resin, 2-6 parts of polyurethane, 1-4 parts of polyvinyl butyral, 2-5 parts of carboxymethylcellulose, 2-5 parts of organosilicon boron, 3-6 parts of nano silica, 4-8 parts of organic bentonite, 5-8 parts of light calcium carbonate, 4-9 parts of white clay, 2-5 parts of modified curing agent, 3-6 parts of silane coupling agent KH-550, 1-4 parts of promoter DMP-30, 2-5 parts of polyether polyol and 2-5 parts of antioxidant. The heat-resistant waterproof adhesive has excellent heat-resistant and waterproof performance.
Description
Technical field
The present invention relates to a kind of adhesive, particularly relate to a kind of heat-resisting moisture-proof adhesive of footwear.
Background technology
China is footwear manufacturing country, country of consumption and exported country maximum in the world, footwear annual production tens pairs, accounts for complete
More than the 50% of sneakers production.About more than 20 hundred million pairs, domestic annual consumption footwear, have exceeded the U.S. and have occupied first place in the world.Domestic existing
Family more than 20,000 of footwear enterprise, produced footwear 80% are above rubber adhesive shoes, and footwear glue consumption reaches more than 20 ten thousand tons.The use of adhesive is significantly
Improve the production efficiency of shoe-making industry.
Heat-resisting and the water resistance of the adhesive that existing shoe-making field uses cannot meet the demand of reality, therefore needs badly and sets
A kind of footwear of meter solve demand of the prior art with heat-resisting moisture-proof adhesive.
Summary of the invention
For solving technical problem present in background technology, the present invention proposes a kind of heat-resisting moisture-proof adhesive of footwear, has
Excellent heat-resisting and water resistance.
The heat-resisting moisture-proof adhesive of a kind of footwear that the present invention proposes, its raw material includes by weight: modification acrylate breast
Liquid 20-50 part, polyvinyl acetate emulsion 5-15 part, natural emulsion 2-8 part, styrene-butadiene latex 3-5 part, polychloroprene latex 1-4 part, poly-
Acrylamide 1-4 part, phenolic resin 3-5 part, polyurethane 2-6 part, polyvinyl butyral resin 1-4 part, carboxymethyl cellulose 2-5
Part, organic silicon-boron 2-5 part, nano silicon 3-6 part, organobentonite 4-8 part, precipitated calcium carbonate 5-8 part, white clay 4-9
Part, modified firming agent 2-5 part, silane resin acceptor kh-550 3-6 part, altax P-30 1-4 part, polyether polyol 2-5 part,
Antioxidant 1010 2-5 part.
Preferably, the raw material of modified acrylate emulsion includes by weight: dodecylbenzene sodium sulfonate 8-16 part, OP-
10 6-12 parts, epoxy resin 12-24 part, butyl acrylate 2-5 part, methyl methacrylate 1-4 part, acrylic acid 3-5 part, mistake
Ammonium sulfate 2-6 part, sodium bicarbonate 3-9 part, deionized water 5-15 part.
Preferably, modified acrylate emulsion is prepared by following technique: by dodecylbenzene sodium sulfonate, OP-10, ring
Epoxy resins, butyl acrylate, methyl methacrylate, acrylic acid and deionized water mix homogeneously, in 12000-14000r/min
Emulsion dispersion 25-35min, obtains emulsion, then adds Ammonium persulfate. and sodium bicarbonate mix homogeneously in emulsion, heats up
To 75-85 DEG C, it is incubated 1-3h, is cooled to room temperature, filter and backward filtrate adds triethanolamine regulation pH to 7.0-8.0, obtain
Modified acrylate emulsion.
Preferably, modified firming agent is prepared by following technique: by the mixing of thiourea, diethylenetriamine and sodium chloride all
Even, it is passed through nitrogen, then oil bath is heated to 110-150 DEG C, is incubated 20-40min, is then cooled to 50-60 DEG C, is incubated 0.5-
1.5h, is then cooled to room temperature and obtains modified firming agent.
Preferably, in the preparation technology of modified firming agent, the mol ratio of thiourea, diethylenetriamine and sodium chloride is 0.5-
1.5:1-3:2-5.
Preferably, its raw material includes by weight: modified acrylate emulsion 25-45 part, polyvinyl acetate emulsion 8-
12 parts, natural emulsion 3-7 part, styrene-butadiene latex 3.5-4.5 part, polychloroprene latex 2-3 part, polyacrylamide 2-3 part, phenolic resin
3.5-4.5 part, polyurethane 3-5 part, polyvinyl butyral resin 2-3 part, carboxymethyl cellulose 3-4 part, organic silicon-boron 3-4 part, receive
Rice silicon dioxide 4-5 part, organobentonite 5-7 part, precipitated calcium carbonate 6-7 part, white clay 5-8 part, modified firming agent 3-4 part,
Silane resin acceptor kh-550 4-5 part, altax P-30 2-3 part, polyether polyol 3-4 part, antioxidant 1010 3-4 part.
Preferably, its raw material includes by weight: modified acrylate emulsion 35 parts, polyvinyl acetate emulsion 10 parts,
Natural emulsion 5 parts, styrene-butadiene latex 4 parts, polychloroprene latex 2.5 parts, polyacrylamide 2.5 parts, 4 parts of phenolic resin, polyurethane 4 parts,
Polyvinyl butyral resin 2.5 parts, carboxymethyl cellulose 3.5 parts, organic silicon-boron 3.5 parts, nano silicon 4.5 parts, organic bentonite
6 parts of profit soil, precipitated calcium carbonate 6.5 parts, white clay 6.5 parts, modified firming agent 3.5 parts, silane resin acceptor kh-550 4.5 parts, rush
Enter agent DMP-302.5 part, polyether polyol 3.5 parts, antioxidant 1010 3.5 parts.
The preparation method of the present invention is as follows: by modified acrylate emulsion, polyvinyl acetate emulsion, natural emulsion, fourth
Benzene latex, polychloroprene latex, polyacrylamide, phenolic resin, polyurethane, polyvinyl butyral resin, carboxymethyl cellulose, organosilicon
Boron, nano silicon, organobentonite, precipitated calcium carbonate, white clay, modified firming agent, silane resin acceptor kh-550, promotion
Agent DMP-30, polyether polyol and antioxidant 1010 mix homogeneously, the speed in 1200r/min stirs 30min and obtains footwear use
Heat-resisting moisture-proof adhesive.
The heat-resisting moisture-proof adhesive of a kind of footwear of the present invention, its raw material includes modified acrylate emulsion, polyvinyl acetate
Ester emulsion, natural emulsion, styrene-butadiene latex, polychloroprene latex, polyacrylamide, phenolic resin, polyurethane, polyvinyl butyral resin,
Carboxymethyl cellulose, organic silicon-boron, nano silicon, organobentonite, precipitated calcium carbonate, white clay, modified firming agent, silicon
Alkane coupling agent KH-550, altax P-30, polyether polyol and antioxidant 1010.With modified acrylate emulsion it is wherein
Major ingredient, auxiliary add polyvinyl acetate emulsion, natural emulsion, styrene-butadiene latex, polychloroprene latex, polyacrylamide, phenolic resin,
Polyurethane and the reinforcement material that polyvinyl butyral resin is major ingredient, by the proportioning of conservative control Yu major ingredient, impart footwear of the present invention
Stick with glue the heat-resisting water resistance that agent is excellent.The carboxymethyl cellulose of interpolation, organic silicon-boron, nano silicon, organic swelling
Soil, precipitated calcium carbonate and white clay are filler, impart the toughness that adhesive for shoes of the present invention is excellent, heat-resisting and water resistance
Good.The silane resin acceptor kh-550 added carries out effective graft modification to filler so that be connected more between filler with major ingredient
Add, impart the waterproof heat resistant performance that adhesive for shoes of the present invention is excellent.Add altax P-30, polyether polyol and
Antioxidant 1010, as auxiliary agent, imparts the combination property that adhesive for shoes of the present invention is excellent.The footwear that the present invention prepares
Stick with glue agent and there is the heat-resisting and water resistance of excellence.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in detail, it should be appreciated that embodiment is served only for this is described
Bright rather than be used for limiting the invention, any made on the basis of the present invention amendment, equivalent etc. is all at this
In bright protection domain.
In detailed description of the invention, the weight portion of modified acrylate emulsion can be 20 parts, 25 parts, 30 parts, 35 parts, 40
Part, 45 parts, 50 parts;The weight portion of polyvinyl acetate emulsion can be 5 parts, 6 parts, 7 parts, 8 parts, 9 parts, 10 parts, 11 parts, 12
Part, 13 parts, 14 parts, 15 parts;The weight portion of natural emulsion can be 2 parts, 3 parts, 4 parts, 5 parts, 6 parts, 7 parts, 8 parts;Styrene-butadiene latex
Weight portion can be 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts;The weight portion of polychloroprene latex can be 1 part, 1.5 parts, 2 parts, 2.5
Part, 3 parts, 3.5 parts, 4 parts;The weight portion of polyacrylamide can be 1 part, 1.5 parts, 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts;Phenol
The weight portion of urea formaldehyde can be 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts;The weight portion of polyurethane can be 2 parts, 3 parts, 4 parts, 5
Part, 6 parts;The weight portion of polyvinyl butyral resin can be 1 part, 1.5 parts, 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts;Carboxymethyl is fine
The weight portion of dimension element can be 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts;The weight portion of organic silicon-boron can be 2
Part, 2.5 parts, 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts;The weight portion of nano silicon can be 3 parts, 3.5 parts, 4 parts, 4.5
Part, 5 parts, 5.5 parts, 6 parts;Bentonite weight portion can be 4 parts, 5 parts, 6 parts, 7 parts, 8 parts;The weight of precipitated calcium carbonate
Part can be 5 parts, 5.5 parts, 6 parts, 6.5 parts, 7 parts, 7.5 parts, 8 parts;The weight portion of white clay can be 4 parts, 4.5 parts, 5 parts,
5.5 parts, 6 parts, 6.5 parts, 7 parts, 7.5 parts, 8 parts, 8.5 parts, 9 parts;The weight portion of modified firming agent can be 2 parts, 2.5 parts, 3
Part, 3.5 parts, 4 parts, 4.5 parts, 5 parts;The weight portion of silane resin acceptor kh-550 can be 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts,
5.5 parts, 6 parts;The weight portion of altax P-30 can be 1 part, 1.5 parts, 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts;Polyethers is many
The weight portion of unit's alcohol can be 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts;The weight portion of antioxidant 1010 is permissible
It it is 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts.
Embodiment 1
The heat-resisting moisture-proof adhesive of a kind of footwear that the present invention proposes, its raw material includes by weight: modification acrylate breast
Liquid 35 parts, polyvinyl acetate emulsion 10 parts, natural emulsion 5 parts, styrene-butadiene latex 4 parts, polychloroprene latex 2.5 parts, polyacrylamide
2.5 parts, 4 parts of phenolic resin, polyurethane 4 parts, polyvinyl butyral resin 2.5 parts, carboxymethyl cellulose 3.5 parts, organic silicon-boron 3.5
Part, nano silicon 4.5 parts, organobentonite 6 parts, precipitated calcium carbonate 6.5 parts, white clay 6.5 parts, modified firming agent 3.5
Part, silane resin acceptor kh-550 4.5 parts, altax P-30 2.5 parts, polyether polyol 3.5 parts, antioxidant 1010 3.5
Part.
Embodiment 2
The heat-resisting moisture-proof adhesive of a kind of footwear that the present invention proposes, its raw material includes by weight: modification acrylate breast
Liquid 20 parts, polyvinyl acetate emulsion 15 parts, natural emulsion 2 parts, styrene-butadiene latex 5 parts, polychloroprene latex 1 part, polyacrylamide 4
Part, 3 parts of phenolic resin, polyurethane 6 parts, polyvinyl butyral resin 1 part, carboxymethyl cellulose 5 parts, organic silicon-boron 2 parts, nanometer two
Silicon oxide 6 parts, organobentonite 4 parts, precipitated calcium carbonate 8 parts, white clay 4 parts, modified firming agent 5 parts, silane coupler KH-
550 3 parts, altax P-30 4 parts, polyether polyol 2 parts, antioxidant 1010 5 parts.
Modified acrylate emulsion is prepared by following technique: by weight by 8 parts of dodecylbenzene sodium sulfonate, 12 parts
OP-10,12 parts of epoxy resin, 5 parts of butyl acrylate, 1 part of methyl methacrylate, 5 parts of acrylic acid and 5 parts of deionized water mixing
Uniformly, in 14000r/min emulsion dispersion 25min, obtain emulsion, in emulsion, then add 6 parts of Ammonium persulfate .s and 3 parts
Sodium bicarbonate mix homogeneously, is warming up to 85 DEG C, is incubated 1h, is cooled to room temperature, filters and adds triethanolamine regulation in backward filtrate
PH to 8.0, obtains modified acrylate emulsion.
Modified firming agent is prepared by following technique: by molar part by 0.5 part of thiourea, 3 parts of diethylenetriamines and 2 parts of chlorine
Changing sodium mix homogeneously, be passed through nitrogen, then oil bath is heated to 150 DEG C, is incubated 20min, is then cooled to 60 DEG C, is incubated 0.5h,
It is then cooled to room temperature and obtains modified firming agent.
Embodiment 3
The heat-resisting moisture-proof adhesive of a kind of footwear that the present invention proposes, its raw material includes by weight: modification acrylate breast
Liquid 50 parts, polyvinyl acetate emulsion 5 parts, natural emulsion 8 parts, styrene-butadiene latex 3 parts, polychloroprene latex 4 parts, polyacrylamide 1 part,
5 parts of phenolic resin, polyurethane 2 parts, polyvinyl butyral resin 4 parts, carboxymethyl cellulose 2 parts, organic silicon-boron 5 parts, nano-silica
SiClx 3 parts, organobentonite 8 parts, precipitated calcium carbonate 5 parts, white clay 9 parts, modified firming agent 2 parts, silane resin acceptor kh-550
6 parts, altax P-30 1 part, polyether polyol 5 parts, antioxidant 1010 2 parts.
Modified acrylate emulsion is prepared by following technique: by weight by 16 parts of dodecylbenzene sodium sulfonate, 6 parts
OP-10,24 parts of epoxy resin, 2 parts of butyl acrylate, 4 parts of methyl methacrylates, 3 parts of acrylic acid and 15 parts of deionized waters mix
Close uniformly, in 12000r/min emulsion dispersion 35min, obtain emulsion, in emulsion, then add 2 parts of Ammonium persulfate .s and 9
Part sodium bicarbonate mix homogeneously, is warming up to 75 DEG C, is incubated 3h, is cooled to room temperature, filters and adds triethanolamine tune in backward filtrate
Joint pH to 7.0, obtains modified acrylate emulsion.
Modified firming agent is prepared by following technique: by molar part by 1.5 parts of thiourea, 1 part of diethylenetriamine and 5 parts of chlorine
Changing sodium mix homogeneously, be passed through nitrogen, then oil bath is heated to 110 DEG C, is incubated 40min, is then cooled to 50 DEG C, is incubated 1.5h,
It is then cooled to room temperature and obtains modified firming agent.
Embodiment 4
The heat-resisting moisture-proof adhesive of a kind of footwear that the present invention proposes, its raw material includes by weight: modification acrylate breast
Liquid 25 parts, polyvinyl acetate emulsion 12 parts, natural emulsion 3 parts, styrene-butadiene latex 4.5 parts, polychloroprene latex 2 parts, polyacrylamide 3
Part, 3.5 parts of phenolic resin, polyurethane 5 parts, polyvinyl butyral resin 2 parts, carboxymethyl cellulose 4 parts, organic silicon-boron 3 parts, nanometer
Silicon dioxide 5 parts, organobentonite 5 parts, precipitated calcium carbonate 7 parts, white clay 5 parts, modified firming agent 4 parts, silane coupler KH-
550 4 parts, altax P-30 3 parts, polyether polyol 3 parts, antioxidant 1010 4 parts.
Modified acrylate emulsion is prepared by following technique: by weight by 9 parts of dodecylbenzene sodium sulfonate, 11 parts
OP-10,14 parts of epoxy resin, 4 parts of butyl acrylate, 2 parts of methyl methacrylates, 4.5 parts of acrylic acid and 8 parts of deionized waters mix
Close uniformly, in 13500r/min emulsion dispersion 28min, obtain emulsion, in emulsion, then add 5 parts of Ammonium persulfate .s and 4
Part sodium bicarbonate mix homogeneously, is warming up to 82 DEG C, is incubated 1.5h, is cooled to room temperature, filters addition triethanolamine in backward filtrate
Regulation pH to 7.8, obtains modified acrylate emulsion.
Modified firming agent is prepared by following technique: by molar part by 0.8 part of thiourea, 2.5 parts of diethylenetriamines and 3 parts
Sodium chloride mix homogeneously, is passed through nitrogen, and then oil bath is heated to 140 DEG C, is incubated 25min, is then cooled to 58 DEG C, insulation
0.8h, is then cooled to room temperature and obtains modified firming agent.
Embodiment 5
The heat-resisting moisture-proof adhesive of a kind of footwear that the present invention proposes, its raw material includes by weight: modification acrylate breast
Liquid 45 parts, polyvinyl acetate emulsion 8 parts, natural emulsion 7 parts, styrene-butadiene latex 3.5 parts, polychloroprene latex 3 parts, polyacrylamide 2
Part, 4.5 parts of phenolic resin, polyurethane 3 parts, polyvinyl butyral resin 3 parts, carboxymethyl cellulose 3 parts, organic silicon-boron 4 parts, nanometer
Silicon dioxide 4 parts, organobentonite 7 parts, precipitated calcium carbonate 6 parts, white clay 8 parts, modified firming agent 3 parts, silane coupler KH-
550 5 parts, altax P-30 2 parts, polyether polyol 4 parts, antioxidant 1010 3 parts.
Modified acrylate emulsion is prepared by following technique: by weight by 15 parts of dodecylbenzene sodium sulfonate, 7 parts
OP-10,22 parts of epoxy resin, 3 parts of butyl acrylate, 3 parts of methyl methacrylates, 3.5 parts of acrylic acid and 12 parts of deionized waters
Mix homogeneously, in 12500r/min emulsion dispersion 32min, obtains emulsion, then add in emulsion 3 parts of Ammonium persulfate .s and
8 parts of sodium bicarbonate mix homogeneously, are warming up to 78 DEG C, are incubated 2.5h, are cooled to room temperature, filter addition triethanolamine in backward filtrate
Regulation pH to 7.2, obtains modified acrylate emulsion.
Modified firming agent is prepared by following technique: by molar part by 1.2 parts of thiourea, 1.5 parts of diethylenetriamines and 4 parts
Sodium chloride mix homogeneously, is passed through nitrogen, and then oil bath is heated to 120 DEG C, is incubated 35min, is then cooled to 52 DEG C, insulation
1.2h, is then cooled to room temperature and obtains modified firming agent.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention is not limited thereto,
Any those familiar with the art in the technical scope that the invention discloses, according to technical scheme and
Inventive concept equivalent or change in addition, all should contain within protection scope of the present invention.
Claims (7)
1. the heat-resisting moisture-proof adhesive of footwear, it is characterised in that its raw material includes by weight: modified acrylate emulsion
20-50 part, polyvinyl acetate emulsion 5-15 part, natural emulsion 2-8 part, styrene-butadiene latex 3-5 part, polychloroprene latex 1-4 part, poly-third
Acrylamide 1-4 part, phenolic resin 3-5 part, polyurethane 2-6 part, polyvinyl butyral resin 1-4 part, carboxymethyl cellulose 2-5 part,
Organic silicon-boron 2-5 part, nano silicon 3-6 part, organobentonite 4-8 part, precipitated calcium carbonate 5-8 part, white clay 4-9 part,
Modified firming agent 2-5 part, silane resin acceptor kh-550 3-6 part, altax P-30 1-4 part, polyether polyol 2-5 part, anti-
Oxidant 1010 2-5 part.
The heat-resisting moisture-proof adhesive of footwear the most according to claim 1, it is characterised in that the raw material of modified acrylate emulsion
Include by weight: dodecylbenzene sodium sulfonate 8-16 part, OP-10 6-12 part, epoxy resin 12-24 part, butyl acrylate 2-
5 parts, methyl methacrylate 1-4 part, acrylic acid 3-5 part, Ammonium persulfate. 2-6 part, sodium bicarbonate 3-9 part, deionized water 5-15
Part.
The heat-resisting moisture-proof adhesive of footwear the most according to claim 1 and 2, it is characterised in that modified acrylate emulsion is pressed
Following technique is prepared: by dodecylbenzene sodium sulfonate, OP-10, epoxy resin, butyl acrylate, methyl methacrylate,
Acrylic acid and deionized water mix homogeneously, in 12000-14000r/min emulsion dispersion 25-35min, obtain emulsion, then to
Emulsion adds Ammonium persulfate. and sodium bicarbonate mix homogeneously, is warming up to 75-85 DEG C, be incubated 1-3h, be cooled to room temperature, filter
Backward filtrate adds triethanolamine regulation pH to 7.0-8.0, obtains modified acrylate emulsion.
4. according to the heat-resisting moisture-proof adhesive of footwear described in any one of claim 1-3, it is characterised in that modified firming agent is by such as
Lower technique is prepared: by thiourea, diethylenetriamine and sodium chloride mix homogeneously, being passed through nitrogen, then oil bath is heated to 110-
150 DEG C, be incubated 20-40min, be then cooled to 50-60 DEG C, be incubated 0.5-1.5h, be then cooled to room temperature obtain modified solidified
Agent.
5. according to the heat-resisting moisture-proof adhesive of footwear described in any one of claim 1-4, it is characterised in that the system of modified firming agent
In standby technique, the mol ratio of thiourea, diethylenetriamine and sodium chloride is 0.5-1.5:1-3:2-5.
6. according to the heat-resisting moisture-proof adhesive of footwear described in any one of claim 1-5, it is characterised in that its raw material is by weight
Including: modified acrylate emulsion 25-45 part, polyvinyl acetate emulsion 8-12 part, natural emulsion 3-7 part, styrene-butadiene latex
3.5-4.5 part, polychloroprene latex 2-3 part, polyacrylamide 2-3 part, phenolic resin 3.5-4.5 part, polyurethane 3-5 part, polyethylene
Butyral 2-3 part, carboxymethyl cellulose 3-4 part, organic silicon-boron 3-4 part, nano silicon 4-5 part, organobentonite 5-7
Part, precipitated calcium carbonate 6-7 part, white clay 5-8 part, modified firming agent 3-4 part, silane resin acceptor kh-550 4-5 part, accelerator
DMP-30 2-3 part, polyether polyol 3-4 part, antioxidant 1010 3-4 part.
7. according to the heat-resisting moisture-proof adhesive of footwear described in any one of claim 1-6, it is characterised in that its raw material is by weight
Including: modified acrylate emulsion 35 parts, polyvinyl acetate emulsion 10 parts, natural emulsion 5 parts, styrene-butadiene latex 4 parts, neoprene
Breast 2.5 parts, polyacrylamide 2.5 parts, 4 parts of phenolic resin, polyurethane 4 parts, polyvinyl butyral resin 2.5 parts, carboxymethyl cellulose
Element 3.5 parts, organic silicon-boron 3.5 parts, nano silicon 4.5 parts, organobentonite 6 parts, precipitated calcium carbonate 6.5 parts, white clay
6.5 parts, modified firming agent 3.5 parts, silane resin acceptor kh-550 4.5 parts, altax P-30 2.5 parts, polyether polyol 3.5
Part, antioxidant 1010 3.5 parts.