CN106318252A - Coextruded coating-type protection adhesive tape and preparation method thereof - Google Patents
Coextruded coating-type protection adhesive tape and preparation method thereof Download PDFInfo
- Publication number
- CN106318252A CN106318252A CN201610696787.9A CN201610696787A CN106318252A CN 106318252 A CN106318252 A CN 106318252A CN 201610696787 A CN201610696787 A CN 201610696787A CN 106318252 A CN106318252 A CN 106318252A
- Authority
- CN
- China
- Prior art keywords
- adhesive tape
- substrate layer
- adhesive layer
- rubber
- type protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a coextruded coating-type protection adhesive tape and a preparation method thereof. The coextruded coating-type protection adhesive tape comprises a substrate layer, an adhesion layer and a bonding layer, the substrate layer is composed of polypropylene and linear low-density polyethylene, the adhesion layer is vinyl-ethylene acetate copolymer, and the bonding layer comprises rubber and tackifying resin. The preparation method includes: (1), supplying raw materials of the adhesion layer and the substrate layer to a mould head respectively through two material ways, performing compositing, casting, film forming on the raw materials of the adhesion layer and the substrate layer through the mould head, and cooling and shaping to obtain a mother substrate; (2), diluting coating liquid, coating the coating liquid on the mother substrate to form the bonding layer, and folding and cutting into needed size. The coextruded coating-type protection adhesive tape is proper in stripping strength, free of being difficult to strip due to increasing of the stripping strength as time goes and free of causing adhesive residue on the surfaces of parts due to pressure impact in the process of rolling and punching. The preparation method is simple and low in cost and has good application prospect.
Description
Technical field
The invention belongs to auto-parts surface protection field, particularly to a kind of co-extrusion application type protection adhesive tape and system thereof
Preparation Method.
Background technology
Auto-parts produce in preparation process relate to roll-in, punching press, cross cutting, wash, etching etc. is made.Spare and accessory parts
Product, as a part for vehicle complete vehicle, requires that in processing procedure product face must not have scuffing, abrasion, watermark, mist shadow, dust etc. to lack
Fall into.Generally use common PE in current domestic conventional manufacturing process, CPP is that base material is formed by acrylic resins of painting adhesive
Thin film, as protection, is attached at product surface and prevents product surface in processing procedure from damage occur.
Require that surface protection tape has suitable peel strength as protection adhesive tape, on the one hand need to keep tolerance difference
Use the bond properties of environment, on the other hand can readily peel off when completing surface protecting function, and require not pollute
Spare and accessory parts surface, does not remain the vestige of protection adhesive tape on spare and accessory parts surface.In the bright panel of automobile, aluminum alloy surface, especially
It is strict with surface protection tape and does not pollute spare and accessory parts surface, and not because of the out-of-flatness defect such as bubble, flake in protection adhesive tape
Or folds etc. produce hollow, impression on spare and accessory parts surface, scratch or the defect such as deformation.This requirement is along with internal vapor garage
The development of industry becomes increasingly stricter, and after pasting protection adhesive tape on spare and accessory parts surface, after roll-in, punching press, spare and accessory parts wait until
Mould required form, in the case of compression shock, owing to being affected by impact etc., protection adhesive tape bears extruding, so sometimes
Cull can be produced, or owing to adhesive tape pastes residual bubble, the out-of-flatness brought because of tape surface bubble after bearing deformation
Produce tape surface sometimes damaged, in turn result in spare and accessory parts surface and produce the defects such as scuffing, impression.
It should be noted that protection adhesive tape generally supplies with web-like, tape thickness is uniform, and adhesive is evenly distributed in glue
Band inner face.Current protection adhesive tape type mainly has composite co-extruding adhesive tape, reaches glutinous by tackifying resin compound on base material and covers
Effect;Another kind is that binder resin can be divided into again acrylic resin, emulsion-type by being coated with binder resin formation on base material
Acrylic acid, rubber three types.
As it has been described above, auto-parts surface protection tape is required for full in membrane material characteristic and manufacturing process two aspect
Foot, proposes a lot of schemes for this.As for auto-parts surface protection tape, acrylic resin type adhesive tape is excellent because of it
Weather-proof and cementability and be widely used, there is also some obvious defects, as peel strength can uprise over time, very simultaneously
To finally occurring that adhesive tape removes difficulty.In experience high temperature or impact process, easily occur that glue-line cohesional failure causes degumming,
And then pollute by protection surface.Rubber-type protection adhesive tape has and good pastes performance, all has the peel strength of various base materials
Outstanding performance, stripping performance is stable simultaneously.It addition, punching press, nipping process improve common protection adhesive tape cull as improving
Problem, it is proposed that increase adhesive cohesiveness and base material does pretreatment and increases the work of cohesive force.And then, using protection glue
After band is attached to spare and accessory parts surface, implement punching press, roll-in, water mill, cut-out processing raising protective capability.But various scheme is all respectively arranged with
The chief, does not finds not only to possess and excellent pastes performance, but also the perfect relevant protection adhesive tape meeting spare and accessory parts processing procedure.
Summary of the invention
The technical problem to be solved is to provide a kind of co-extrusion application type protection adhesive tape and preparation method thereof, this guarantor
Retaining tape overcomes because the small technology pasting out-of-flatness or cull and cause spare and accessory parts surface to produce pollution or impression is asked
Topic.
A kind of co-extrusion application type protection adhesive tape of the present invention, including substrate layer, adhesive layer and adhesive layer, described substrate layer by
Polypropylene and linear low density polyethylene composition;Described adhesive layer is ethylene-vinyl acetate copolymer;Described adhesive layer includes rubber
Glue and tackifying resin.
In described substrate layer, polyacrylic mass percent is 30-70%.
The thickness of described substrate layer is 10-25 μm.
Described polyacrylic density is 0.90-0.91g/cm3, fusing point is 167-170 DEG C, and melt index MI is 0.5-2g/
10min;The density of described linear low density polyethylene is 0.918~0.935g/cm3, fusing point is 121-127 DEG C, melt index
MI is 0.1-1.9g/10min.Owing to linear low density polyethylene has a short-side chain, simultaneously with polypropene blended after play toughness reinforcing
Effect, higher anti-stretches intensity, penetration-resistant, tear resistance and percentage elongation to make protection adhesive tape have.And acrylic resin
Need suitable fusing point, softening point, toughness, the transparency, impact strength.
Described ethylene-vinyl acetate copolymer VA content is 5%-15%, and density is 0.935-0.947g/cm3, melted finger
Number MI is 3-10g/10min, and fusing point is 60-87 DEG C.Ethylene-vinyl acetate copolymer is by ethylene and two kinds of lists of vinyl acetate
A kind of thermoplastic resin obtained by body copolymerization, its character is relevant with the content of its vinylacetate (VA), along with VA content increases,
Light transmittance raises, and the pliability of material strengthens, and adhesive property increases the most therewith, but increasing of VA group also results in resin simultaneously
The performances such as the degree of crystallinity of itself, mechanical strength, heat distortion temperature reduce.So that reach good between substrate layer and adhesive layer
Bonding be combined, suitable elastic modelling quantity and VA value are necessary.
The thickness of described adhesive layer is 10-25 μm.
Coating on female base material is needed to form adhesive layer in order to realize protection adhesive tape of the present invention.
Consisting of of described adhesive layer: be 100 parts with rubber quality part, tackifying resin 40-140 part, naphthenic oil 5-15 part,
Paraffin 1-5 part, solvent 50-100 part.
In order to reach bonding effect of the present invention, it is necessary to add tackifying resin, it is necessary that its effect is to confer to pressure sensitive adhesive
Tack and bonding force, research shows, when tackifying resin exceedes a certain amount of, then forms biphase dispersion, rubber with rubber
For continuous phase, give the cohesive strength that pressure sensitive adhesive is enough;Tackifying resin and a small amount of low molecule rubber are dispersion phase, at gluing interface
Form a viscous layer the thinnest, at External Force Acting, VISCOUS FLOW directly can occur, moisten by maxxaedium so that initial bonding strength increases
Greatly.When tackifying resin is suitable with the ratio of rubber tackifying resin can be well dispersed in rubber mutually in, at this moment initial bonding strength reaches
Maximum, performance is optimal;If resin demand is excessive, there is phase in version drastically, make resin-phase become continuous phase and rubber phase transformation
For dispersion phase, glue-line just loses initial bonding strength hydraulic performance decline.
Described rubber is natural rubber, butadiene-styrene rubber, Oppanol, cis-1,4-polyisoprene rubber, suitable fourth
One or more in rubber, styrene-butadiene latex;Tackifying resin is LNBR, liquid isoprene rubber, liquid second third
One or several in rubber, liquid natural rubber, liquid propene acid esters rubber, liquid polyisobutene rubber, liquid cis butadiene
Kind;Solvent is high rate of volatilization solvent acetone, ethyl acetate, oxolane, butanone, methyl acetate, medium rate of volatilization solvent
N-butyl acetate, isobutyl acetate, toluene, dimethylbenzene, pentyl acetate, low volatility solvent propylene glycol methyl ether, propylene glycol fourth
One or more in ether, dipropylene glycol methyl ether, propylene glycol monomethyl ether, Ketohexamethylene.
Described substrate layer, adhesive layer and adhesive layer are also added with the antioxygen of substrate layer raw material gross mass 0.1%-0.5%
Agent and/or the light stabilizer of substrate layer raw material gross mass 0.1%-2%.
Owing to linear low density polyethylene of the present invention, ethylene-vinyl acetate copolymer melt temperature are relatively low, and
Containing tertiary hydrogen class active hydrogen in two kinds of polymer.At heat, light or the work of oxygen during compound extruded and during normal use
Under with, the chemical bond of organic molecule ruptures, and generates active free radical and hydroperoxides.Hydroperoxides are decomposed
Reaction, also generates alkoxy free group and hydroxyl radical free radical.These free radicals can cause a series of free chain reaction, leads
Cause structure and the character generation fundamental change of organic compound, and then affect protected surface, need to add appropriate metrology
The free radical that antioxidant elimination produces, or promote the decomposition of hydroperoxides, stop the carrying out of chain reaction.
Described antioxidant is made up of primary antioxidant and auxiliary antioxidant;Wherein, primary antioxidant is aromatic amine antioxidant, is subject to
Resistance phenolic antioxidant in one or both;Auxiliary antioxidant is thioether class or organic phosphorus compound.
The mass ratio of described primary antioxidant and auxiliary anti-oxidant is 4:1-2:1.
Described aromatic amine antioxidant can be the compounds such as diphenylamines, p-phenylenediamine and dihydroquinoline and derivant thereof or
Polymer.
Described Hinered phenols antioxidant can be 2,6-di-tert-butyl-4-methy phenol, double (3,5-di-t-butyl-4-hydroxyls
Base phenyl) thioether, four (β-(3,5-di-tert-butyl-hydroxy phenyl) propanoic acid) pentaerythritol ester etc..
Described auxiliary antioxidant can be thio-2 acid dibasic acid esters, double Lauryl Alcohol ester, double ten four carbon alcohols esters, double 18
Carbon alcohol ester, three monooctyl esters, three the last of the ten Heavenly stems ester, three (Lauryl Alcohol) ester, three (16 carbon alcohol) ester, phosphorous acid esters etc..
Meanwhile, unescapable meeting in process and transportation is used to receive the radiation of ultraviolet light and then right at protection adhesive tape
Protection adhesive tape produces photoaging, decomposition, causes protection tape performance to decline, and further impact is by the quality in protection face.In order to
Such issues that overcome need to add the light stabilizer of appropriate metrology at adhesive layer and substrate layer.It can shield or absorb the energy of ultraviolet
Amount, quenching singlet oxygen and hydroperoxide decomposition is become the functions such as inert matter, make high molecular polymer in the radiation of light
Under, can get rid of or slow down photochemical reaction probability, stoping or postpone the process of photoaging, thus reach to extend high molecular polymerization
The purpose in Tetramune service life.
Described light stabilizer can be oxybenzoic acid phenyl ester, 2-(2-hydroxy-5-methyl base phenyl) BTA,
2,4 dihydroxyl benzophenone, ESCALOL 567, Octabenzone, 2-(2-hydroxyl
The tertiary phenyl of base-3,5-two)-5-chlorination benzotriazole, single benzoic acid resorcinol, 2,2 '-thiobis (4-t-octyl phenol oxygen
Base) nickel, three (1,2,2,6,6-pempidine base) phosphite ester, 4 benzoyloxy 2,2,6,6 tetramethyl piperidine, 2,4,6-
Three (2 ' n-butoxyphenyl)-1,3,5-triazine etc..
The preparation method of a kind of application type protection adhesive tape of the present invention, comprises the steps:
(1) by Liang Liao road respectively to die head supply adhesive layer and substrate layer raw material, by die head by adhesive layer, substrate layer
Raw material is combined casting film-forming, obtains female base material through cooling and shaping;
(2) will coating fluid dilute after coat and on female base material, form adhesive layer, rolling, cut into required size and i.e. obtain co-extrusion
Application type protection adhesive tape.
Using curtain coating coextru-lamination moulding process, substrate layer tract temperature is 230-250 DEG C;Adhesive layer and adhesive layer tract
Temperature is 70-120 DEG C;In cooling and shaping, chill-roll temperature is 0-30 DEG C, and chill roll surface temperature difference is less than 0.1 DEG C.
Beneficial effect
Peel strength of the present invention is suitable, and will not As time goes on be peeling intensity and rise and be difficult to peel off, will not
Because compression shock causes spare and accessory parts surface cull in roll-in, punching press processing procedure;Preparation method is simple, low cost, has good
Application prospect.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is expanded on further.Should be understood that these embodiments are merely to illustrate the present invention
Rather than restriction the scope of the present invention.In addition, it is to be understood that after having read the content that the present invention lectures, people in the art
The present invention can be made various changes or modifications by member, and these equivalent form of values fall within the application appended claims equally and limited
Scope.
Embodiment 1
Substrate layer raw material: polypropylene and linear low density polyethylene, the most polyacrylic mass percent is 30%.Linearly
Its density of Low Density Polyethylene is 0.918g/cm3, melt index (MI) 0.1g/10min, fusing point is 121 DEG C.Acrylic resin
Density is 0.90g/cm3, fusing point is 167 DEG C, and melt index (MI) is 0.5g/10min.
Adhesive layer raw material: ethylene-vinyl acetate copolymer.VA content is 5%.Density is 0.935g/cm3, melt index
(MI) being 3g/10min, fusing point is 60 DEG C.
Adhesive layer raw material: be 100 parts with natural rubber mass parts, liquid natural rubber 40 parts, naphthenic oil 5 parts, paraffin 1
Part, 50 parts of acetone.
Antioxidant: substrate layer raw material gross mass 0.1%, mass ratio is the diphenylamines of 4:1 and double Lauryl Alcohol ester.
Light stabilizer: substrate layer raw material gross mass 0.2%, oxybenzoic acid phenyl ester.
Preparation method includes:
(1) pour substrate layer raw material into mixing kettle in proportion, arrange 50 DEG C, respectively antioxidant, light stabilizer are pressed formula
Ratio slowly pours mixing kettle into, until antioxidant and light stabilizer are absorbed by raw material completely, about 1 hour, standby.By Liang Liao road
Respectively to die head supply adhesive layer and the substrate layer raw material containing auxiliary agent, by die head by adhesive layer (10 μm), substrate layer (20 μ
M) raw material is combined casting film-forming, obtains female base material through cooling and shaping;Wherein, substrate layer tract temperature is 230 DEG C;Adhesive layer and
Adhesive layer tract temperature is 70 DEG C;In cooling and shaping, chill-roll temperature is 5 DEG C, and chill roll surface temperature difference is less than 0.1 DEG C.
(2) by proportioning raw materials preparation coating fluid (stirring 0.5 hour);Coat after coating fluid is diluted and formed on female base material
Adhesive layer, rolling, cut into required size i.e. obtain co-extrusion application type protection adhesive tape.
(3) performance test:
Embodiment 2
Substrate layer raw material: polypropylene and linear low density polyethylene, the most polyacrylic mass percent is 50%.Linearly
Its density of Low Density Polyethylene is 0.921g/cm3, melt index (MI) 0.5g/10min, fusing point is 124 DEG C.Acrylic resin
Density is 0.91g/cm3, fusing point is 168 DEG C, and melt index (MI) is 1g/10min.
Adhesive layer raw material: ethylene-vinyl acetate copolymer.VA content is 10%.Density is 0.940g/cm3, melt index
(MI) being 6g/10min, fusing point is 70 DEG C.
Adhesive layer raw material: be 100 parts with natural rubber mass parts, liquid natural rubber 40 parts, naphthenic oil 5 parts, paraffin 1
Part, 50 parts of acetone.
Antioxidant: substrate layer raw material gross mass 0.5%, mass ratio is p-phenylenediamine and three monooctyl esters of 2:1.
Light stabilizer: substrate layer raw material gross mass 0.5%, three (1,2,2,6,6-pempidine base) phosphite ester.
Preparation method includes:
(1) pour substrate layer raw material into mixing kettle in proportion, arrange 50 DEG C, respectively antioxidant, light stabilizer are pressed formula
Ratio slowly pours mixing kettle into, until antioxidant and light stabilizer are absorbed by raw material completely, about 1 hour, standby.By Liang Liao road
Respectively to die head supply adhesive layer and substrate layer raw material, by die head, adhesive layer (15 μm), substrate layer (25 μm) raw material are combined
Casting film-forming, obtains female base material through cooling and shaping;Wherein, substrate layer tract temperature is 240 DEG C;Adhesive layer and adhesive layer tract
Temperature is 90 DEG C;In cooling and shaping, chill-roll temperature is 10 DEG C, and chill roll surface temperature difference is less than 0.1 DEG C.
(2) by proportioning raw materials preparation coating fluid (stirring 0.5 hour);Coat after coating fluid is diluted and formed on female base material
Adhesive layer, rolling, cut into required size i.e. obtain co-extrusion application type protection adhesive tape.
(3) performance test:
Embodiment 3
Substrate layer raw material: polypropylene and linear low density polyethylene, the most polyacrylic mass percent is 70%.Linearly
Its density of Low Density Polyethylene is 0.935g/cm3, melt index (MI) 1.8g/10min, fusing point is 126 DEG C.Acrylic resin
Density is 0.90g/cm3, fusing point is 170 DEG C, and melt index (MI) is 2g/10min.
Adhesive layer raw material: ethylene-vinyl acetate copolymer.VA content is 15%.Density is 0.947g/cm3, melt index
(MI) being 10g/10min, fusing point is 85 DEG C.
Adhesive layer raw material: be 100 parts with butadiene rubber mass parts, liquid cis butadiene 50 parts, naphthenic oil 15 parts, paraffin 5
Part, oxolane 100 parts.
Antioxidant: substrate layer raw material gross mass 0.3%, mass ratio is the 2 of 3:1,6-di-tert-butyl-4-methy phenol and
Thio-2 acid dibasic acid esters.
Light stabilizer: substrate layer raw material gross mass 1%, 2-(2-hydroxyl-3, the tertiary phenyl of 5-bis-)-5-chlorination benzo three
Azoles.
Preparation method includes:
(1) pour substrate layer raw material into mixing kettle in proportion, arrange 50 DEG C, respectively antioxidant, light stabilizer are pressed formula
Ratio slowly pours mixing kettle into, until antioxidant and light stabilizer are absorbed by raw material completely, about 1 hour, standby.By Liang Liao road
Respectively to die head supply adhesive layer and substrate layer raw material, by die head, adhesive layer (25 μm), substrate layer (35 μm) raw material are combined
Casting film-forming, obtains female base material through cooling and shaping;Wherein, substrate layer tract temperature is 250 DEG C;Adhesive layer and adhesive layer tract
Temperature is 120 DEG C;In cooling and shaping, chill-roll temperature is 15 DEG C, and chill roll surface temperature difference is less than 0.1 DEG C.
(2) by proportioning raw materials preparation coating fluid (stirring 0.5 hour);Coat after coating fluid is diluted and formed on female base material
Adhesive layer, rolling, cut into required size i.e. obtain co-extrusion application type protection adhesive tape.
(3) performance test:
Claims (10)
1. a co-extrusion application type protection adhesive tape, including substrate layer, adhesive layer and adhesive layer, it is characterised in that: described substrate layer
It is made up of polypropylene and linear low density polyethylene;Described adhesive layer is ethylene-vinyl acetate copolymer;Described adhesive layer includes
Rubber and tackifying resin.
A kind of co-extrusion application type protection adhesive tape the most according to claim 1, it is characterised in that: polypropylene in described substrate layer
Mass percent be 30-70%.
A kind of co-extrusion application type protection adhesive tape the most according to claim 1, it is characterised in that: described polyacrylic density is
0.90-0.91g/cm3, fusing point is 167-170 DEG C, and melt index MI is 0.5-2g/10min;Described linear low density polyethylene
Density be 0.918~0.935g/cm3, fusing point is 121-127 DEG C, and melt index MI is 0.1-1.9g/10min.
A kind of co-extrusion application type protection adhesive tape the most according to claim 1, it is characterised in that: described ethene-vinyl acetate
Copolymer VA content is 5%-15%, and density is 0.935-0.947g/cm3, melt index MI is 3-10g/10min, and fusing point is
60-87℃。
A kind of co-extrusion application type protection adhesive tape the most according to claim 1, it is characterised in that: the composition of described adhesive layer
For: it is 100 parts with rubber quality part, tackifying resin 40-140 part, naphthenic oil 5-15 part, paraffin 1-5 part, solvent 50-100 part.
A kind of co-extrusion application type protection adhesive tape the most according to claim 5, it is characterised in that: described rubber is natural rubber
One or several in glue, butadiene-styrene rubber, Oppanol, cis-1,4-polyisoprene rubber, butadiene rubber, styrene-butadiene latex
Kind;Tackifying resin is LNBR, liquid isoprene rubber, Liquid Ethylene Propylene Methylene, liquid natural rubber, liquid propene
One or more in acid esters rubber, liquid polyisobutene rubber, liquid cis butadiene;Solvent is acetone, ethyl acetate, tetrahydrochysene
Furan, butanone, methyl acetate, n-butyl acetate, isobutyl acetate, toluene, dimethylbenzene, pentyl acetate, propylene glycol monomethyl ether, the third two
One or more in alcohol butyl ether, dipropylene glycol methyl ether, propylene glycol monomethyl ether, Ketohexamethylene.
A kind of co-extrusion application type protection adhesive tape the most according to claim 1, it is characterised in that: described substrate layer, adhesive layer
With antioxidant and/or the substrate layer raw material gross mass being also added with substrate layer raw material gross mass 0.1%-0.5% in adhesive layer
The light stabilizer of 0.1%-2%.
A kind of co-extrusion application type protection adhesive tape the most according to claim 7, it is characterised in that: described antioxidant is by main antioxygen
Agent and auxiliary antioxidant composition;Wherein, the one during primary antioxidant is aromatic amine antioxidant, Hinered phenols antioxidant or two
Kind.
9. a preparation method for co-extrusion application type as claimed in claim 1 protection adhesive tape, comprises the steps:
(1) by Liang Liao road respectively to die head supply adhesive layer and substrate layer raw material, by die head by adhesive layer, substrate layer raw material
Compound casting film-forming, obtains female base material through cooling and shaping;
(2) will coating fluid dilute after coat and on female base material, form adhesive layer, rolling, cut into required size and i.e. obtain co-extrusion coating
Type protection adhesive tape.
The preparation method of a kind of co-extrusion application type the most according to claim 9 protection adhesive tape, it is characterised in that: substrate layer
Tract temperature is 230-250 DEG C;Adhesive layer and adhesive layer tract temperature are 70-120 DEG C;In cooling and shaping, chill-roll temperature is 0-
30 DEG C, chill roll surface temperature difference is less than 0.1 DEG C.