CN106318210A - Wear resistant paint mortar and preparing method thereof - Google Patents
Wear resistant paint mortar and preparing method thereof Download PDFInfo
- Publication number
- CN106318210A CN106318210A CN201610713124.3A CN201610713124A CN106318210A CN 106318210 A CN106318210 A CN 106318210A CN 201610713124 A CN201610713124 A CN 201610713124A CN 106318210 A CN106318210 A CN 106318210A
- Authority
- CN
- China
- Prior art keywords
- powder
- parts
- wear resistant
- resistant paint
- resina toxicodendri
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention claims wear resistant paint mortar and a preparing method thereof. The wear resistant paint mortar is prepared from, by weight, 30- 40 parts of refined raw lacquer, 25- 35 parts of glass powder, 20- 25 parts of ox horn powder,15- 22 parts of pebble powder, 5- 12 parts of sand powder, 5- 8 parts of laminated rock powder, and 8- 12 parts of adhesive;The preparing procedures are as follows:(1) the preparing of mixed powder; (2) mixing. The wear resistant paint mortar adopts fungal enzyme for refining processing of raw lacquer, and the rheological property of the raw lacquer can be effectively adjusted. The produced paint mortar has strong adhesion and high hardness together with corrosion-resistant and wear-resistant.It is easy to be smeared on the wood embryo to effectively improve the hardness and strength of wood and to fill the holes as well as the gaps on the board also improves the wear resistantce of the board.
Description
Technical field
The present invention relates to lacquer painting and make field, particularly relate to a kind of wear resistant paint mortar and preparation method thereof.
Background technology
In lacquer painting manufacturing process, lacquer painting tire plate is one of basic material making lacquer painting, and lacquer painting tire plate is commonly called as painting plate,
Being the tire bone of lacquer painting, most paint plate is many with plank as tire, it is also possible to metallic plate, fibre board substitute, and tire plate need through
Stick one piece of cloth or paper on top of another cloth, scrape the paint operation such as ash, japanning process after just can use.Scraping paint ash is highly important step, because paint ash is possible not only to
Hide the eye on lacquerware carcass surface, crack, scratch etc., play the effect of filling-in defect, additionally it is possible to play enhancing paint film attachment
The effect of power, reaches laborsaving, the purpose of material-saving, and paints grieshoch and also help the processing and forming works such as follow-up polishing and scraping
Sequence, is better protected from wood deformation.Some wood embryo wooden soft, in order to improve wood embryo long-term mar proof, it is necessary to smear
Paint ash.
At present, existing paint ash is many adjusts dark grey to form with lacquer, it is also possible to adjust Gypsum Fibrosum powder with Fructus anacardii paint, synthetic lacquer.This
Generally there is the deficiency that cohesive is general in class paint ash, and composition is single, preparation section simple, and the finished product paint ash prepared is attached
Put forth effort relatively low, it is impossible to fill up eye, the gap smoothing on plank well, and this kind of paint ash wearability mostly is poor, unfavorable
Follow-up making in lacquer painting.
Summary of the invention
It is an object of the invention to provide a kind of wear resistant paint mortar and preparation method thereof, have that viscosity is big, smear conveniently, resistance to
The preferable advantage of mill property.
The purpose of the present invention is achieved through the following technical solutions:
A kind of wear resistant paint mortar, the raw material of described wear resistant paint mortar is refined Resina Toxicodendri verniciflui, glass dust, horn powder, cobblestone powder, sandstone
Powder, Herba Cladoniae verticillatae powder, binding agent, described raw materials by weight portion, refined Resina Toxicodendri verniciflui 30-40 part, glass dust 25-35 part, horn powder 20-
25 parts, cobblestone powder 15-22 part, sand powder 5-12 part, Herba Cladoniae verticillatae powder 5-8 part, binding agent 8-12 part.
Described a kind of wear resistant paint mortar, raw material presses optimum weight number, refined 35 parts of Resina Toxicodendri verniciflui, 28 parts of glass dust, horn powder
22 parts, 15 parts of cobblestone powder, sand powder 8 parts, 6 parts of Herba Cladoniae verticillatae powder, binding agent 8 parts.
Described binding agent is the one in polyvinyl acetate resin adhesive, hide glue, casein.
Described refined Resina Toxicodendri verniciflui is to be added the fungal enzyme of 3-5%, the diluent of 10-15% by Resina Toxicodendri verniciflui, through enzyme reaction, grinding, dilute
Obtain after releasing.
The preparation process of described refined Resina Toxicodendri verniciflui is as follows:
Step one: after taking Resina Toxicodendri verniciflui filtering and impurity removing, is placed in container, is gradually heating to 20-30 DEG C, is stirred continuously while intensification,
Stirring simultaneously, adds fungal enzyme, and is passed through oxygen, and under the conditions of 20-30 DEG C, constant temperature stirring reaction 5-8h, obtains Resina Toxicodendri verniciflui emulsion；
Step 2: take Resina Toxicodendri verniciflui emulsion, continues stirring under the conditions of 20-30 DEG C, and stirring is simultaneously introduced diluent, after stirring,
After grinding 1.5-2h in being placed in grinder, obtain refined Resina Toxicodendri verniciflui.
Described Resina Toxicodendri verniciflui is selected and is originated in the Guizhou natural raw lacquer of Guizhou Bijie or the hair dam natural raw lacquer of enshi.
Described diluent is the one in retinal, oleum lini, Oleum Terebinthinae.
Described a kind of wear resistant paint mortar, its preparation section is as follows:
(1) mixed powder is prepared:
A, prepare glass dust: by weight, take glass dust and be placed in crusher for crushing to 1200-1400 mesh, sieve and obtain glass
Glass powder；
B, prepare horn powder: by weight, take after Cornu Bovis seu Bubali cleans, be placed in crusher for crushing to 1000-1200 mesh, sieve
To horn powder；
C, prepare cobblestone powder: by weight, take cobblestone, after cleaning, be placed in crusher for crushing to 900-1100 mesh, mistake
Sieve obtains cobblestone powder；
D, prepare sand powder: by weight, take sandstone, after rinsing 5-10min with clear water, naturally dry, be placed in pulverizer
It is crushed to 1000-1200 mesh, sieves and obtain sand powder；
E, prepare Herba Cladoniae verticillatae powder: by weight, take Herba Cladoniae verticillatae, after cleaning, dry, be placed in crusher for crushing to 1400-
1500 mesh, sieve and obtain Herba Cladoniae verticillatae powder；
F, prepare mixed powder: by weight, take glass dust, horn powder, cobblestone powder, sand powder, Herba Cladoniae verticillatae powder, be placed in mixing
In machine, after middling speed mixing 20-30min, obtain mixed powder；
(2) mixing:
By weight, take mixed powder, be placed in blender, be stirring evenly and then adding into refined Resina Toxicodendri verniciflui, binding agent, stir 1-2h
After, get product.
Beneficial effects of the present invention: a kind of wear resistant paint mortar of the present invention, uses fungal enzyme that Resina Toxicodendri verniciflui is carried out refinement treatment,
Can effectively regulate Resina Toxicodendri verniciflui rheological characteristic, and the paint mortar produced, adhesive force is strong, and hardness is high, and also has corrosion-resistant, resistance to
Mill function, is applied on wood embryo, is smeared conveniently, and can be effectively improved hardness and the intensity of wood embryo, fills up well and comforts
Eye on flat plank, gap, and preferably improve the wearability of plank.
Glass dust has that transparency is good, hardness is high, the advantage of even particle size distribution, and good dispersion, can be with resin, oil
Other composition intermiscibilities in paint system are good, as filler, and can be effectively increased the hardness of finish paint, toughness, improve paint film
Anti scuffing performance, there is smooth interaction, the wearability of paint film can be improved.Meanwhile, horn powder, cobblestone powder, sand are additionally used
Stone powder, Herba Cladoniae verticillatae powder are arranged in pairs or groups with it, can be effectively improved hardness and the anti-wear performance of plank, improve the quality of base plate, thus ensure
The quality of finished product lacquer painting.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in further detail.
Embodiment 1
A kind of wear resistant paint mortar, the raw material of described wear resistant paint mortar is refined Resina Toxicodendri verniciflui, glass dust, horn powder, cobblestone powder, sandstone
Powder, Herba Cladoniae verticillatae powder, binding agent, described raw materials by weight portion, refined Resina Toxicodendri verniciflui 30-40 part, glass dust 25-35 part, horn powder 20-
25 parts, cobblestone powder 15-22 part, sand powder 5-12 part, Herba Cladoniae verticillatae powder 5-8 part, binding agent 8-12 part.
Embodiment 2
Described a kind of wear resistant paint mortar, raw material presses optimum weight number, refined 35 parts of Resina Toxicodendri verniciflui, 28 parts of glass dust, horn powder 22 parts,
15 parts of cobblestone powder, sand powder 8 parts, 6 parts of Herba Cladoniae verticillatae powder, binding agent 8 parts.
Embodiment 3
Described binding agent is the one in polyvinyl acetate resin adhesive, hide glue, casein.
Embodiment 4
Described refined Resina Toxicodendri verniciflui is to be added the fungal enzyme of 3-5%, the diluent of 10-15% by Resina Toxicodendri verniciflui, after enzyme reaction, grinding, dilute
Obtain.
Embodiment 5
The preparation process of described refined Resina Toxicodendri verniciflui is as follows:
Step one: after taking Resina Toxicodendri verniciflui filtering and impurity removing, is placed in container, is gradually heating to 20-30 DEG C, is stirred continuously while intensification,
Stirring simultaneously, adds fungal enzyme, and is passed through oxygen, and under the conditions of 20-30 DEG C, constant temperature stirring reaction 5-8h, obtains Resina Toxicodendri verniciflui emulsion；
Step 2: take Resina Toxicodendri verniciflui emulsion, continues stirring under the conditions of 20-30 DEG C, and stirring is simultaneously introduced diluent, after stirring,
After grinding 1.5-2h in being placed in grinder, obtain refined Resina Toxicodendri verniciflui.
Embodiment 6
Described Resina Toxicodendri verniciflui is selected and is originated in the Guizhou natural raw lacquer of Guizhou Bijie or the hair dam natural raw lacquer of enshi.
Embodiment 7
Described diluent is the one in retinal, oleum lini, Oleum Terebinthinae.
Embodiment 8
Described a kind of wear resistant paint mortar, its preparation section is as follows:
(1) mixed powder is prepared:
A, prepare glass dust: by weight, take glass dust and be placed in crusher for crushing to 1200-1400 mesh, sieve and obtain glass
Glass powder；
B, prepare horn powder: by weight, take after Cornu Bovis seu Bubali cleans, be placed in crusher for crushing to 1000-1200 mesh, sieve
To horn powder；
C, prepare cobblestone powder: by weight, take cobblestone, after cleaning, be placed in crusher for crushing to 900-1100 mesh, mistake
Sieve obtains cobblestone powder；
D, prepare sand powder: by weight, take sandstone, after rinsing 5-10min with clear water, naturally dry, be placed in pulverizer
It is crushed to 1000-1200 mesh, sieves and obtain sand powder；
E, prepare Herba Cladoniae verticillatae powder: by weight, take Herba Cladoniae verticillatae, after cleaning, dry, be placed in crusher for crushing to 1400-
1500 mesh, sieve and obtain Herba Cladoniae verticillatae powder；
F, prepare mixed powder: by weight, take glass dust, horn powder, cobblestone powder, sand powder, Herba Cladoniae verticillatae powder, be placed in mixing
In machine, after middling speed mixing 20-30min, obtain mixed powder；
(2) mixing:
By weight, take mixed powder, be placed in blender, be stirring evenly and then adding into refined Resina Toxicodendri verniciflui, binding agent, stir 1-2h
After, get product.
Claims (8)
1. a wear resistant paint mortar, it is characterised in that: the raw material of described wear resistant paint mortar is refined Resina Toxicodendri verniciflui, glass dust, horn powder,
Cobblestone powder, sand powder, Herba Cladoniae verticillatae powder, binding agent, described raw materials by weight portion, refined Resina Toxicodendri verniciflui 30-40 part, glass dust 25-
35 parts, horn powder 20-25 part, cobblestone powder 15-22 part, sand powder 5-12 part, Herba Cladoniae verticillatae powder 5-8 part, binding agent 8-12 part.
A kind of wear resistant paint mortar, it is characterised in that: raw material presses optimum weight number, refined Resina Toxicodendri verniciflui
35 parts, 28 parts of glass dust, horn powder 22 parts, 15 parts of cobblestone powder, sand powder 8 parts, 6 parts of Herba Cladoniae verticillatae powder, binding agent 8 parts.
3. according to wear resistant paint mortar a kind of described in claim 1-2 any one, it is characterised in that: described binding agent is poly-acetic acid
One in vinyl glue, hide glue, casein.
4. according to wear resistant paint mortar a kind of described in claim 1-2 any one, it is characterised in that: described refined Resina Toxicodendri verniciflui is by giving birth to
Paint add the fungal enzyme of 3-5%, the diluent of 10-15%, through enzyme reaction, grind, dilute after obtain.
A kind of wear resistant paint mortar, it is characterised in that: the preparation process of described refined Resina Toxicodendri verniciflui is as follows:
Step one: after taking Resina Toxicodendri verniciflui filtering and impurity removing, is placed in container, is gradually heating to 20-30 DEG C, is stirred continuously while intensification,
Stirring simultaneously, adds fungal enzyme, and is passed through oxygen, and under the conditions of 20-30 DEG C, constant temperature stirring reaction 5-8h, obtains Resina Toxicodendri verniciflui emulsion；
Step 2: take Resina Toxicodendri verniciflui emulsion, continues stirring under the conditions of 20-30 DEG C, and stirring is simultaneously introduced diluent, after stirring,
After grinding 1.5-2h in being placed in grinder, obtain refined Resina Toxicodendri verniciflui.
6. according to wear resistant paint mortar a kind of described in claim 4-5 any one, it is characterised in that: the selection of described Resina Toxicodendri verniciflui is originated in expensive
The Guizhou natural raw lacquer of state Bijie or the hair dam natural raw lacquer of enshi.
7. according to wear resistant paint mortar a kind of described in claim 4-5 any one, it is characterised in that: described diluent is Colophonium
One in oil, oleum lini, Oleum Terebinthinae.
8. according to wear resistant paint mortar a kind of described in claim 1-7 any one, it is characterised in that: its preparation section is as follows:
(1) mixed powder is prepared:
A, prepare glass dust: by weight, take glass dust and be placed in crusher for crushing to 1200-1400 mesh, sieve and obtain glass
Glass powder；
B, prepare horn powder: by weight, take after Cornu Bovis seu Bubali cleans, be placed in crusher for crushing to 1000-1200 mesh, sieve
To horn powder；
C, prepare cobblestone powder: by weight, take cobblestone, after cleaning, be placed in crusher for crushing to 900-1100 mesh, mistake
Sieve obtains cobblestone powder；
D, prepare sand powder: by weight, take sandstone, after rinsing 5-10min with clear water, naturally dry, be placed in pulverizer
It is crushed to 1000-1200 mesh, sieves and obtain sand powder；
E, prepare Herba Cladoniae verticillatae powder: by weight, take Herba Cladoniae verticillatae, after cleaning, dry, be placed in crusher for crushing to 1400-
1500 mesh, sieve and obtain Herba Cladoniae verticillatae powder；
F, prepare mixed powder: by weight, take glass dust, horn powder, cobblestone powder, sand powder, Herba Cladoniae verticillatae powder, be placed in mixing
In machine, after middling speed mixing 20-30min, obtain mixed powder；
(2) mixing:
By weight, take mixed powder, be placed in blender, be stirring evenly and then adding into refined Resina Toxicodendri verniciflui, binding agent, stir 1-2h
After, get product.