CN106318098A - Purple light curable water paint with good adhesive force - Google Patents
Purple light curable water paint with good adhesive force Download PDFInfo
- Publication number
- CN106318098A CN106318098A CN201610650281.4A CN201610650281A CN106318098A CN 106318098 A CN106318098 A CN 106318098A CN 201610650281 A CN201610650281 A CN 201610650281A CN 106318098 A CN106318098 A CN 106318098A
- Authority
- CN
- China
- Prior art keywords
- parts
- adhesive force
- purple light
- water
- photosensitizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a purple light curable water paint with good adhesive force which comprises, by weight, 60-65 parts of water photosensitive resin, 15-20 parts of photosensitizer, 10-15 parts of purified water, 5-8 parts of thickener, 10-15 parts of pigment; the water photosensitive resin is the photosensitive resin mixed by the materials of novolac epoxy resin, acrylic acid and maleic anhydride. The photosensitizer is the benzophenone. Through the process mentioned above the invention can enhance the adhesive force of the purple light curable water paint on the metal surface. The paint layer is thin and can be easily cleaned. The adhesion is excellent.
Description
Technical field
The present invention relates to UV curable waterborne coatings field, particularly relate to the good purple light curable water-borne of a kind of adhesive force and be coated with
Material.
Background technology
The application of UV curable waterborne coatings is the most not yet fully apparent from, and its exploitation application is still in the primary stage.
Being currently known, it can be used as plastic varnish, over print varnish, photopolymer galley, screen printing ink, intaglio plate and lithographic plate
How printing-ink, metallic paint etc., when coating the product of metal material, reduce coating layer thickness, improves coating at metal watch
The adhesive force in face, is a problem needing research.
Summary of the invention
The technical problem that present invention mainly solves is to provide the purple light solidified aqueous coating that a kind of adhesive force is good, it is possible to increase
Purple light solidified aqueous coating is at the adhesive force of metal surface, and coating is very thin, easy to clean, and firmness is good.
For solving above-mentioned technical problem, the technical scheme that the present invention uses is: provide the purple light that a kind of adhesive force is good
Solidified aqueous coating, it is characterised in that be to be grouped into by the one-tenth of following masses number, including: Water-soluble product 60-65
Part, photosensitizer 15-20 part, pure water 10-15 part, thickening agent 5-8 part, colorant 10-15 part;Described Water-soluble product is phenol
Formaldehyde epoxy resin, acrylic acid and maleic anhydride are the ultraviolet curable resin of Material synthesis, and described photosensitizer is benzophenone.
In a preferred embodiment of the present invention, the purple light solidified aqueous coating that described adhesive force is good, is by following masses
The one-tenth of number is grouped into, including: Water-soluble product 60 parts, photosensitizer 15 parts, pure water 10 parts, thickening agent 5 parts, colorant
10 parts.
In a preferred embodiment of the present invention, the purple light solidified aqueous coating that described adhesive force is good, is by following masses
The one-tenth of number is grouped into, including: Water-soluble product 63 parts, photosensitizer 17 parts, pure water 12 parts, thickening agent 6 parts, colorant
13 parts.
In a preferred embodiment of the present invention, the purple light solidified aqueous coating that described adhesive force is good, is by following masses
The one-tenth of number is grouped into, including: Water-soluble product 65 parts, photosensitizer 20 parts, pure water 15 parts, thickening agent 8 parts, colorant
15 parts.
The invention has the beneficial effects as follows: the present invention can improve the purple light solidified aqueous coating adhesive force in metal surface,
Coating is very thin, easy to clean, and firmness is good.
Detailed description of the invention
Below presently preferred embodiments of the present invention is described in detail so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that thus protection scope of the present invention is made apparent clear and definite defining.
The embodiment of the present invention includes:
Embodiment 1:
The purple light solidified aqueous coating that adhesive force is good, is to be grouped into by the one-tenth of following masses number, including: the photosensitive tree of water solublity
60 parts of fat, photosensitizer 15 parts, pure water 10 parts, thickening agent 5 parts, 10 parts of colorant.
Embodiment 2:
The purple light solidified aqueous coating that adhesive force is good, is to be grouped into by the one-tenth of following masses number, including: the photosensitive tree of water solublity
63 parts of fat, photosensitizer 17 parts, pure water 12 parts, thickening agent 6 parts, 13 parts of colorant.
Embodiment 3:
The purple light solidified aqueous coating that adhesive force is good, is to be grouped into by the one-tenth of following masses number, including: the photosensitive tree of water solublity
65 parts of fat, photosensitizer 20 parts, pure water 15 parts, thickening agent 8 parts, 15 parts of colorant.
The purple light solidified aqueous coating that described adhesive force is good, is to be prepared by the following step: by Water-soluble product
With photosensitizer mix homogeneously, Infrared Heating to 65 DEG C, pour pure water into, be heated to 89 DEG C, pour thickening agent and colorant into, mixing,
Keep 5 minutes, be cooled to room temperature, by obtaining finished product coating after ultraviolet irradiation 5 minutes.
The present invention can improve the purple light solidified aqueous coating adhesive force in metal surface, and coating is very thin, easy to clean, jail
Soundness is good.
The foregoing is only embodiments of the invention, not thereby limit the scope of the claims of the present invention, every utilize this
Equivalent structure or equivalence flow process that bright description is made convert, or are directly or indirectly used in other relevant technology necks
Territory, is the most in like manner included in the scope of patent protection of the present invention.
Claims (4)
1. the purple light solidified aqueous coating that an adhesive force is good, it is characterised in that be to be grouped into by the one-tenth of following masses number,
Including: Water-soluble product 60-65 part, photosensitizer 15-20 part, pure water 10-15 part, thickening agent 5-8 part, colorant 10-15
Part;Described Water-soluble product be novolac epoxy resin, acrylic acid and maleic anhydride be the ultraviolet curable resin of Material synthesis, institute
Stating photosensitizer is benzophenone.
The purple light solidified aqueous coating that adhesive force the most according to claim 1 is good, it is characterised in that be by following masses part
The one-tenth of number is grouped into, including: Water-soluble product 60 parts, photosensitizer 15 parts, pure water 10 parts, thickening agent 5 parts, colorant 10
Part.
The purple light solidified aqueous coating that adhesive force the most according to claim 1 is good, it is characterised in that be by following masses part
The one-tenth of number is grouped into, including: Water-soluble product 63 parts, photosensitizer 17 parts, pure water 12 parts, thickening agent 6 parts, colorant 13
Part.
The purple light solidified aqueous coating that adhesive force the most according to claim 1 is good, it is characterised in that be by following masses part
The one-tenth of number is grouped into, including: Water-soluble product 65 parts, photosensitizer 20 parts, pure water 15 parts, thickening agent 8 parts, colorant 15
Part.