CN106317987A - Environment-friendly sealant - Google Patents
Environment-friendly sealant Download PDFInfo
- Publication number
- CN106317987A CN106317987A CN201610722502.4A CN201610722502A CN106317987A CN 106317987 A CN106317987 A CN 106317987A CN 201610722502 A CN201610722502 A CN 201610722502A CN 106317987 A CN106317987 A CN 106317987A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- silicone oil
- silicate
- sodium gluconate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an environment-friendly sealant. The environment-friendly sealant is prepared from, by mass, 22-35 parts of silicate, 10-20 parts of nanocarbon spheres, 9-25 parts of acrylic acid glyceride, 7-10 parts of sodium gluconate, 1-5 parts of mildew preventive, 1-5 parts of silicone oil and 30-50 parts of absolute ethyl alcohol. The environment-friendly sealant is glossy, has rich, natural and fine colors, and can bring a good overall effect to walls and improve ornamental property. Besides, the surface of the sealant is as smooth as porcelain after solidification, the sealant can be scrubbed together with ceramic tiles and has osmosis resistance and water resistance, and ceramic tile seams can never become black in the true sense.
Description
Technical field
The present invention relates to a kind of technical field of paint preparation, in particular it relates to a kind of environmental protection joint trimming agent.
Background technology
The parlor of household, kitchen and toilet would ordinarily be encountered ceramic tile gap problem attractive in appearance black by leucismus, the most unhygienic, brick now
Seam blackening meeting breed bacteria, produces abnormal flavour, and serious harm health, this antibacterial was especially apparent in summer.This perplexs dress
A decorations industry difficult problem for many years, is captured by joint trimming agent, and it not only solves the series of problems that brickwork joint blackening is caused, also
It is greatly improved finishing class.Joint trimming agent is high-grade house fitting-up product, it is adaptable to the gaps such as ceramic tile, mosaic, stone material are beautified,
Kitchen guarding bathroom inside-corner decoration.Joint trimming agent color is various, do not absorb water, oil-stain-preventing, easy cleaning, invariant color, abrasion-resistant, intensity high, thorough
The end, changes the phenomenon that seam black mould becomes.And the most traditional joint trimming agent also exists difficulty of construction greatly, fills out discontented, easy peeling
Problem.
Summary of the invention
For above-mentioned deficiency present in prior art, the technical problem to be solved is to provide a kind of effective
Environmental protection joint trimming agent.
The technical solution adopted for the present invention to solve the technical problems is: provide a kind of environmental protection joint trimming agent, including silicate,
Nano carbon microsphere, glycerol acrylate, sodium gluconate, antifungus agent, silicone oil, dehydrated alcohol, the mass fraction of each component is: silicic acid
Salt 22-35, nano carbon microsphere 10-20, glycerol acrylate 9-25, sodium gluconate 7-10, antifungus agent 1-5, silicone oil 1-5, anhydrous
Ethanol 30-50.
As preferably, the mass fraction of the described each component of environmental protection joint trimming agent is: silicate 25, nano carbon microsphere 18, acrylic acid
Glyceride 20, sodium gluconate 7, antifungus agent 2, silicone oil 2, dehydrated alcohol 50.
As preferably, the granularity of described glycerol acrylate is 1325-1600 mesh, further preferred 1575 mesh.
Concrete preparation process: silicate, nano carbon microsphere are added in glycerol acrylate, back flow reaction 1.5 hours, cold
But to room temperature, sucking filtration, gained filtering residue obtains pressed powder after drying;Then by above-mentioned pressed powder, sodium gluconate, mildew-resistant
Agent, silicone oil mix homogeneously, be placed in container, obtains crude product after microwave heating reaction;Then in above-mentioned crude product, add water
It is sufficiently stirred for.
A kind of environmental protection joint trimming agent that the present invention relates to has gloss, and various colors is naturally fine and smooth, brings preferably to metope
Whole structure, dicoration is greatly enhanced.And after its solidification, smooth surface such as porcelain, can clean together with ceramic tile, have impervious
The most waterproof characteristic, can accomplish real ceramic tile gap " never blackening ".Detailed description of the invention
A kind of environmental protection joint trimming agent that the present invention provides, including silicate, nano carbon microsphere, glycerol acrylate, sodium gluconate, prevents
Mould dose, silicone oil, dehydrated alcohol, the mass fraction of each component is: silicate 22-35, nano carbon microsphere 10-20, glycerol acrylate
9-25, sodium gluconate 7-10, antifungus agent 1-5, silicone oil 1-5, dehydrated alcohol 30-50.
As preferably, the mass fraction of the described each component of environmental protection joint trimming agent is: silicate 25, nano carbon microsphere 18, acrylic acid
Glyceride 20, sodium gluconate 7, antifungus agent 2, silicone oil 2, dehydrated alcohol 50.
As preferably, the granularity of described glycerol acrylate is 1325-1600 mesh, further preferred 1575 mesh.
Concrete preparation process: silicate, nano carbon microsphere are added in glycerol acrylate, back flow reaction 1.5 hours, cold
But to room temperature, sucking filtration, gained filtering residue obtains pressed powder after drying;Then by above-mentioned pressed powder, sodium gluconate, mildew-resistant
Agent, silicone oil mix homogeneously, be placed in container, obtains crude product after microwave heating reaction;Then in above-mentioned crude product, add water
It is sufficiently stirred for.
Claims (4)
1. an environmental protection joint trimming agent, it is characterised in that: include silicate, nano carbon microsphere, glycerol acrylate, sodium gluconate,
Antifungus agent, silicone oil, dehydrated alcohol, the mass fraction of each component is: silicate 22-35, nano carbon microsphere 10-20, acrylic acid glycerol
Ester 9-25, sodium gluconate 7-10, antifungus agent 1-5, silicone oil 1-5, dehydrated alcohol 30-50.
Environmental protection joint trimming agent the most according to claim 1, it is characterised in that: the mass fraction of the described each component of environmental protection joint trimming agent
For: silicate 25, nano carbon microsphere 18, glycerol acrylate 20, sodium gluconate 7, antifungus agent 2, silicone oil 2, dehydrated alcohol 50.
Environmental protection joint trimming agent the most according to claim 2, it is characterised in that: the granularity of described glycerol acrylate is
1325-1600 mesh, further preferred 1575 mesh.
4. concrete preparation process: silicate, nano carbon microsphere are added in glycerol acrylate, back flow reaction 1.5 hours, cooling
To room temperature, sucking filtration, gained filtering residue obtains pressed powder after drying;Then by above-mentioned pressed powder, sodium gluconate, antifungus agent,
Silicone oil mix homogeneously, is placed in container, obtains crude product after microwave heating reaction;Then in above-mentioned crude product, water is added abundant
Stir.