CN106317375A - Anti-mosquito foamed polyurethane sponge cushion containing polyvinyl alcohol - Google Patents
Anti-mosquito foamed polyurethane sponge cushion containing polyvinyl alcohol Download PDFInfo
- Publication number
- CN106317375A CN106317375A CN201610684818.9A CN201610684818A CN106317375A CN 106317375 A CN106317375 A CN 106317375A CN 201610684818 A CN201610684818 A CN 201610684818A CN 106317375 A CN106317375 A CN 106317375A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyether polyol
- polyvinyl alcohol
- sponge cushion
- containing polyvinyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-mosquito foamed polyurethane sponge cushion containing polyvinyl alcohol. The sponge cushion is prepared from, by weight, 35-45 parts of microcrystalline cellulose, 140-180 parts of soybean oil, 160-200 parts of diethylene glycol, 0.13-0.27 part of potassium hydroxide, 90-100 parts of polyether polyol, 8-12 parts of a foaming agent, 1.3-1.6 parts of a foam stabilizer, 0.4-0.6 part of a catalyst, 56-68 parts of toluene diisocynate, 4-6 parts of distilled water, 4-6 parts of mint leaves, 3-4 parts of polyvinyl alcohol, 1-2 parts of stearic acid, 2-4 parts of silica sol, 0.2-0.3 part of an anti-aging agent and 1-2 parts of white oil. The prepared sponge cushion is simple in preparation process, wide in material source, excellent in performance, capable of meeting the requirements of markets and people on the sponge cushion, high in comfort, good in softness, durable in use and worthy of popularization.
Description
Technical field
The present invention relates to foam sponge technical field, particularly relate to a kind of mosquito proof polyurathamc containing polyvinyl alcohol sea
Continuous medicated cushion.
Background technology
Polyurethane low resilience urethane foam resilient foam, due to the comfort property of its excellence, has been widely used in household articles, automobile, footwear
The field such as material, medical apparatus and instruments, polyurethane rebound foam, due to the molecular structure of its uniqueness, has higher comfort property, when being subject to
During to certain pressure, polyurethane rebound foam can change shape along with pressure, makes pressure be evenly distributed, and reduces local pressure
Point, after pressure is released, its shape the most slowly returns to original state.But due to the hole-closing structure of himself, polyurethane slow rebound steeps
The permeability of foam and damping sound absorbing capabilities are poor." synthesis of soybean oil polyol and grinding of polyurethane low resilience urethane foam resilient foam performance
Studying carefully " author has been synthesized modified soybean oil by maleic anhydride and soybean oil, then with diethylene glycol and modified soybean in a literary composition
Oil reacts under the catalysis of potassium hydroxide, has synthesized soybean oil polyol.The soybean oil polyol of recycling synthesis is prepared for greatly
Oleum Glycines polyol based polyurethane low resilience urethane foam resilient foam, in article, the stretching to soybean oil polyol based polyurethanes low resilience urethane foam resilient foam is strong
The mechanical properties such as degree, elongation at break and 40% degree of compression are studied, and find that the use of soybean oil polyol can improve polyurethane
The permeability damping capacity of low resilience urethane foam resilient foam and sound absorbing capabilities, but the decline of mechanical property can be caused, propose to increase foaming
Agent water consumption or raising isocyanate index, can have higher ventilative at soybean oil polyol based polyurethanes low resilience urethane foam resilient foam
On the premise of performance, damping capacity and sound absorbing capabilities, improve its mechanical property.
Although author is by soybean oil modified thus synthesize soybean oil polyol based polyurethanes rebound foam, improve slow
The permeability of recovery sponge, damping capacity and sound absorbing capabilities, but the bad shortcoming of its bad mechanical strength, toughness reduces material
The service life of material and the comfort level of people, affect the quality of product, does not promotes expanding economy, and its slow time prepared
Playing sponge and can't fully meet the nowadays people's various demands to foam-rubber cushion, so needing further to improve, improving it
Other performances such as mechanical property, heat stability, hydrophobicity, expand application and increase the service life.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of mosquito proof foaming containing polyvinyl alcohol is poly-
Urethane sponge cushion.
The present invention is achieved by the following technical solutions:
A kind of mosquito proof polyurathamc sponge cushion containing polyvinyl alcohol, is made up of the raw material of following weight portion: crystallite
Cellulose 35-45, soybean oil 140-180, diethylene glycol 160-200, potassium hydroxide 0.13-0.27, polyether polyol 90-110, send out
Infusion 8-12, foam stabiliser 1.3-1.6, catalyst 0.4-0.6, toluene di-isocyanate(TDI) 56-68, distilled water 4-6, mentha leave
4-6, polyvinyl alcohol 3-4, stearic acid 1-2, Ludox 2-4, age resister 0.2-0.3, white oil 1-2.
Described a kind of mosquito proof polyurathamc sponge cushion containing polyvinyl alcohol, is made up of step in detail below:
(1) the microcrystalline Cellulose dry toluene of 6-8 times amount is disperseed, be added to after being uniformly dispersed in there-necked flask, make with nitrogen
For protective gas, heating in water bath liter high-temperature, to 80-90 DEG C, drips octadecylisocyanate, wherein octadecyl Carbimide.
Ester and microcrystalline Cellulose mix according to mass ratio 1:5, mechanic whirl-nett reaction 2-4h, and reaction uses the cable-styled reflux extraction of acetone after terminating
24-30h, takes out post-drying standby to constant weight;
(2) product that in four-hole boiling flask prepared by addition soybean oil and step (1), with nitrogen as protective gas, exists afterwards
Both are thoroughly mixed uniformly by 160-180 DEG C, then are placed in heating mantle by four-hole boiling flask, add diethylene glycol and hydroxide
Potassium, rises high-temperature and reacts 3-4h to 200-220 DEG C, and washing purifies, separatory removes unreacted impurity, standby after drying;
(3) dry after clean for mentha leave surface clean, be placed in grinder and be ground into fine powder, polyvinyl alcohol is added to 4-5 times amount
Distilled water in, rise high-temperature stir to being uniformly dissolved, then mentha leave powder, stearic acid and Ludox are added to polyvinyl alcohol molten
In liquid, in-6 DEG C of lyophilizations after ultrasonic disperse is uniform, time 2-3h, takes out post-drying standby;
(4) product, polyether polyol and other surplus materialss mixing in addition to toluene di-isocyanate(TDI) prepared by step (2),
At room temperature stir with the rotating speed of 3000 revs/min, be stirring evenly and then adding into product prepared by step (3), be subsequently adding first
Pour into rapidly in foam box after phenylene diisocyanate stirring 4-6S, remove from casing after 15-20min and get final product.
Described a kind of mosquito proof polyurathamc sponge cushion containing polyvinyl alcohol, described polyether polyol is by polyether polyols
Alcohol 1, polyether polyol 2, polyether polyol 3 precentagewise content 10%-30%, 10%-20%, 20%-50% respectively mix, poly-
Ethoxylated polyhydric alcohol 1 is the hydroxyl value trifunctional polyether polyol at 50-100, and polyether polyol 2 is the hydroxyl value two senses at 35-80
Reunion ethoxylated polyhydric alcohol, polyether polyol 3 is the hydroxyl value trifunctional polyether polyol at 250-280.
The invention have the advantage that vegetable oil based polyalcohol is a kind of potential Biodegradable material, with the high score of synthesis
Sub-material is compared, and can effectively alleviate problem of environmental pollution, the present invention at the discarded rear degradable or Partial digestion of goods
Utilize cellulose concentration advantage little, degradable modified high-molecular synthetic material, but the mechanical property of cellulosic material is the highest,
Poor mechanical property and the most high thermally-stabilised application that governs, the present invention uses octadecylisocyanate graft modification crystallite
Cellulose improves its hot strength, heat stability and wearability, then with it to soybean oil modified, obtains the soybean oil of excellent performance
Polyhydric alcohol, environmental protection, then by soybean oil polyol and unclassified stores synthesis of polyurethane foam sponge, there is dredging of excellence
Water, damp, the performance such as breathe freely, also improve intensity and the mechanical property of sponge, also utilize mentha leave refreshment, pure and fresh refrigerant
Advantage be added in sponge, traditional be directly added into the formation that can affect polyurethane abscess, and easily reunite and block hole
Being formed, be unfavorable for foaming, the present invention uses at mentha leave Surface coating polyvinyl alcohol, improves its caking property and rich in a large amount of hydroxyls
Base, easily forms preferable crosslinking do not affect the formation of polyurethane abscess with polyether polyol, and also improve polyurethane sea
Continuous resistance to water, wearability etc., sponge preparation technology prepared by the present invention is simple, and material source is extensive, function admirable, it is possible to meet
The market people requirement to sponge cushion, comfortableness is high, and flexibility is good, durable in use, is worthy to be popularized.
Detailed description of the invention
A kind of mosquito proof polyurathamc sponge cushion containing polyvinyl alcohol, is prepared by the raw material of following weight portion (kilogram)
Make: microcrystalline Cellulose 35, soybean oil 140, diethylene glycol 160, potassium hydroxide 0.13, polyether polyol 90, foaming agent 8, foam
Stabilizer 1.3, catalyst 0.4, toluene di-isocyanate(TDI) 56, distilled water 4, mentha leave 4, polyvinyl alcohol 3, stearic acid 1, Ludox
2, age resister 0.2, white oil 1.
Described a kind of mosquito proof polyurathamc sponge cushion containing polyvinyl alcohol, is made up of step in detail below:
(1) the microcrystalline Cellulose dry toluene of 6 times amount is disperseed, be added to after being uniformly dispersed in there-necked flask, use nitrogen conduct
Protective gas, heating in water bath rises high-temperature to 80 DEG C, drips octadecylisocyanate, wherein octadecylisocyanate and micro-
Crystalline cellulose mixes according to mass ratio 1:5, mechanic whirl-nett reaction 2h, and reaction uses acetone cable-styled reflux extraction 24h after terminating, and takes out
Post-drying is standby to constant weight;
(2) product that in four-hole boiling flask prepared by addition soybean oil and step (1), with nitrogen as protective gas, afterwards 160
DEG C both are thoroughly mixed uniformly, then four-hole boiling flask is placed in heating mantle, add diethylene glycol and potassium hydroxide, rise high temperature
Spending to 200 DEG C of reaction 3h, washing purifies, separatory removes unreacted impurity, standby after drying;
(3) dry after clean for mentha leave surface clean, be placed in grinder and be ground into fine powder, polyvinyl alcohol is added to 4 times amount
In distilled water, rise high-temperature and stir to being uniformly dissolved, then mentha leave powder, stearic acid and Ludox are added to poly-vinyl alcohol solution
In, in a DEG C lyophilization after ultrasonic disperse is uniform, time 2h, takes out post-drying standby;
(4) product, polyether polyol and other surplus materialss mixing in addition to toluene di-isocyanate(TDI) prepared by step (2),
At room temperature stir with the rotating speed of 3000 revs/min, be stirring evenly and then adding into product prepared by step (3), be subsequently adding first
Pour into rapidly in foam box after phenylene diisocyanate stirring 4S, remove from casing after 15min and get final product.
Described a kind of mosquito proof polyurathamc sponge cushion containing polyvinyl alcohol, described polyether polyol is by polyether polyols
Alcohol 1, polyether polyol 2, polyether polyol 3 precentagewise content 10%%, 10%%, 20%% respectively mixes, polyether polyol 1
For hydroxyl value 50 trifunctional polyether polyol, polyether polyol 2 be hydroxyl value 35 two functional group's polyether polyol, polyethers
Polyhydric alcohol 3 be hydroxyl value 250 trifunctional polyether polyol.
Preparing polyurethane foam sponge according to the step of embodiment, and it is carried out performance test, result is as follows:
Hot strength (kPa): 118;Tensile elongation (%): 98;Tearing strength (N/cm): 13.3;Rebound degree (%): 8.5;
CLD40% (kPa): 2.47.
Claims (3)
1. the mosquito proof polyurathamc sponge cushion containing polyvinyl alcohol, it is characterised in that by the raw material of following weight portion
Preparation is made: microcrystalline Cellulose 35-45, soybean oil 140-180, diethylene glycol 160-200, potassium hydroxide 0.13-0.27, polyethers are many
Unit alcohol 90-110, foaming agent 8-12, foam stabiliser 1.3-1.6, catalyst 0.4-0.6, toluene di-isocyanate(TDI) 56-68, steaming
Distilled water 4-6, mentha leave 4-6, polyvinyl alcohol 3-4, stearic acid 1-2, Ludox 2-4, age resister 0.2-0.3, white oil 1-2.
A kind of mosquito proof polyurathamc sponge cushion containing polyvinyl alcohol, it is characterised in that by
Step is made in detail below:
(1) the microcrystalline Cellulose dry toluene of 6-8 times amount is disperseed, be added to after being uniformly dispersed in there-necked flask, make with nitrogen
For protective gas, heating in water bath liter high-temperature, to 80-90 DEG C, drips octadecylisocyanate, wherein octadecyl Carbimide.
Ester and microcrystalline Cellulose mix according to mass ratio 1:5, mechanic whirl-nett reaction 2-4h, and reaction uses the cable-styled reflux extraction of acetone after terminating
24-30h, takes out post-drying standby to constant weight;
(2) product that in four-hole boiling flask prepared by addition soybean oil and step (1), with nitrogen as protective gas, exists afterwards
Both are thoroughly mixed uniformly by 160-180 DEG C, then are placed in heating mantle by four-hole boiling flask, add diethylene glycol and hydroxide
Potassium, rises high-temperature and reacts 3-4h to 200-220 DEG C, and washing purifies, separatory removes unreacted impurity, standby after drying;
(3) dry after clean for mentha leave surface clean, be placed in grinder and be ground into fine powder, polyvinyl alcohol is added to 4-5 times amount
Distilled water in, rise high-temperature stir to being uniformly dissolved, then mentha leave powder, stearic acid and Ludox are added to polyvinyl alcohol molten
In liquid, in-6 DEG C of lyophilizations after ultrasonic disperse is uniform, time 2-3h, takes out post-drying standby;
(4) product, polyether polyol and other surplus materialss mixing in addition to toluene di-isocyanate(TDI) prepared by step (2),
At room temperature stir with the rotating speed of 3000 revs/min, be stirring evenly and then adding into product prepared by step (3), be subsequently adding first
Pour into rapidly in foam box after phenylene diisocyanate stirring 4-6S, remove from casing after 15-20min and get final product.
3. according to the mosquito proof polyurathamc sponge cushion containing polyvinyl alcohol a kind of described in claim 1-2, it is characterised in that
Described polyether polyol by polyether polyol 1, polyether polyol 2, polyether polyol 3 respectively precentagewise content 10%-30%,
10%-20%, 20%-50% mix, and polyether polyol 1 is the hydroxyl value trifunctional polyether polyol at 50-100, and polyethers is many
Unit's alcohol 2 is the hydroxyl value two functional group's polyether polyol at 35-80, and polyether polyol 3 is that hydroxyl value is reunited at the trifunctional of 250-280
Ethoxylated polyhydric alcohol.