CN106316292A - Non-bearing aerated concrete brick of plant - Google Patents
Non-bearing aerated concrete brick of plant Download PDFInfo
- Publication number
- CN106316292A CN106316292A CN201610714354.1A CN201610714354A CN106316292A CN 106316292 A CN106316292 A CN 106316292A CN 201610714354 A CN201610714354 A CN 201610714354A CN 106316292 A CN106316292 A CN 106316292A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- barite
- apatite
- blast furnace
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an non-bearing aerated concrete brick of plant comprising by weight 20- 30 parts of high titania blast furnace slag, 35- 40 parts of portland cement, 5- 8 parts of apatite, 1- 3 parts of barite, 10- 12 parts of fine sand, 3- 5 parts of isomeric alcohol ethoxylates, 2- 4 parts of acacia powder, 3- 5 parts of natrium aceticum, 2- 4 parts of inorganic aluminum salt water-proofing agent, 55- 65 parts of water and 2- 4 parts of alumina silicate fiber; the invention has low manufacturing cost and uses the environment-friendly and energy-saving raw materials, and is applicable to non-bearing field of plant.
Description
Technical field
The present invention relates to hollow brick field, particularly belong to a kind of Factory Building non-load-bearing concrete aerated bricks.
Background technology
Building block is the artificial bulk utilizing concrete, industrial waste (slag, flyash etc.) or local material to make, profile
Size is bigger than brick, has equipment simple, builds fireballing advantage by laying bricks or stones, has met wanting of wall reform in building industrialization development
Ask.Building block can be divided into solid block and building-block by face shaping.Building-block has single square hole, single circular hole and multiple rows of
Three kinds of flat hole form, the most multiple rows of flat hole is advantageous to insulation.It is individually composed by building-block or joins reinforcing bar casting concrete group
The body of wall become, as novel wall, is widely used in current building trade.Build masonry material at present and have clay
Brick, air entrained concrete brick, slag hollow brick, Refuse air brick, hollow concrete block etc., and present invention employs road waste
Brick slag, production cost is lower than other common brick, consumes the waste material on road, and it is an environmentally friendly low-carbon (LC) Building wood
Material, has obtained wide application.Along with the development of building industry, increasing to the demand of hollow brick, owing to manufacturing hollow brick
Can consume substantial amounts of resource, such as clay and cement, cost is high, does not meets resource-effective principle, does not the most adapt to society
Demand.
Summary of the invention
It is an object of the invention to provide a kind of Factory Building non-load-bearing concrete aerated bricks, cost of manufacture is low, uses raw material environmental protection
Energy-conservation, it is suitably applied the non-bearing field of Factory Building.
Technical scheme is as follows:
A kind of Factory Building non-load-bearing concrete aerated bricks, is made up of the following component of following weight portion meter: high-titanium blast furnace slag
Debris 20-30 part, portland cement 35-40 part, apatite 5-8 part, barite 1-3 part, fine sand 10-12 part, isomery alcohol polyoxy
Vinyl Ether 3-5 part, Fructus Gleditsia powder 2-4 part, sodium acetate 3-5 part, inorganic aluminate water-proof agent 2-4 part, water 55-65 part, alumina silicate fibre
2-4 part;Its preparation method comprises the steps:
(1) by high-titanium blast furnace slag debris, barite, apatite through mechanical activation comminution powder, stir by formula proportion,
It is subsequently adding the water that mass ratio is 12-15%, makes, through nodulizer, the raw material ball that particle diameter is 2-5mm, at 130-150 DEG C, be dried 2-
3h, dried raw material ball is high-temperature roasting 6-8min at 1050-1200 DEG C, obtains aggregate;
(2) aggregate is mixed with remaining water constituent with portland cement, Fructus Gleditsia powder, alumina silicate fibre, be heated to 70-80
DEG C, the persistent period is 1.2-1.6h, obtains mixture;
(3) mixture obtained in above-mentioned steps (2) is mixed with other remaining ingredients, then pour into a mould, pour
After carry out quiet stopping, cutting, at 140-150 DEG C in steam-cured still after having cut, from the pressure of normal pressure~1.3MPa, boost process
Time is 0.3~0.7h, with the steam-cured 3-4 of steam hour, by extruding and being cut into adobe.
A kind of Factory Building non-load-bearing concrete aerated bricks, is made up of the following component of following weight portion meter: high-titanium blast furnace slag
Debris 25 parts, portland cement 37 parts, 6.5 parts of apatite, 2 parts of barite, fine sand 11 parts, isomeric alcohol polyethenoxy ether 4 parts, soap
3 parts of pod powder, sodium acetate 4 parts, inorganic aluminate water-proof agent 3 parts, 60 parts of water, alumina silicate fibre 3 parts.
The present invention employs the high-titanium blast furnace slag debris on road in raw material, solves high-titanium blast furnace slag debris
Stacking problem, save energy resource consumption;Owing to formula is reasonable in design, the stable physical property of aerated bricks product and bulk strength
Height, long-time use do not ftractures, not hollowing, and aging resistance, bulk strength improve further, and service life is long.
Detailed description of the invention
A kind of Factory Building non-load-bearing concrete aerated bricks, is made up of the following component of following weight portion meter: high-titanium blast furnace slag
Debris 25 parts, portland cement 37 parts, 6.5 parts of apatite, 2 parts of barite, fine sand 11 parts, isomeric alcohol polyethenoxy ether 4 parts, soap
3 parts of pod powder, sodium acetate 4 parts, inorganic aluminate water-proof agent 3 parts, 60 parts of water, alumina silicate fibre 3 parts;Its preparation method includes walking as follows
Rapid:
(1) by high-titanium blast furnace slag debris, barite, apatite through mechanical activation comminution powder, stir by formula proportion,
It is subsequently adding the water that mass ratio is 13.5%, makes, through nodulizer, the raw material ball that particle diameter is 3.5mm, at 140 DEG C, be dried 2.5h, dry
Raw material ball after dry is high-temperature roasting 7min at 1120 DEG C, obtains aggregate;
(2) aggregate is mixed with remaining water constituent with portland cement, Fructus Gleditsia powder, alumina silicate fibre, is heated to 75 DEG C,
Persistent period is 1.4h, obtains mixture;
(3) mixture obtained in above-mentioned steps (2) is mixed with other remaining ingredients, then pour into a mould, pour
After carry out quiet stopping, cutting, at 145 DEG C in steam-cured still after having cut, from the pressure of normal pressure~1.3MPa, the boost process time
For 0.5h, with steam steam-cured 3.5 hours, by extruding be cut into adobe.
The aerated bricks performance parameter of the embodiment of the present invention 1 is as follows:
Claims (2)
1. a Factory Building non-load-bearing concrete aerated bricks, it is characterised in that be made up of the following component of following weight portion meter: Gao Tai
Type blast furnace slag debris 20-30 part, portland cement 35-40 part, apatite 5-8 part, barite 1-3 part, fine sand 10-12 part, different
Structure polyoxyethylenated alcohol 3-5 part, Fructus Gleditsia powder 2-4 part, sodium acetate 3-5 part, inorganic aluminate water-proof agent 2-4 part, water 55-65 part, silicon
Acid aluminum fiber 2-4 part;Its preparation method comprises the steps:
(1) by high-titanium blast furnace slag debris, barite, apatite through mechanical activation comminution powder, stir by formula proportion, then
Adding mass ratio is the water of 12-15%, makes, through nodulizer, the raw material ball that particle diameter is 2-5mm, is dried 2-3h at 130-150 DEG C, dry
Raw material ball after dry is high-temperature roasting 6-8min at 1050-1200 DEG C, obtains aggregate;
(2) aggregate is mixed with remaining water constituent with portland cement, Fructus Gleditsia powder, alumina silicate fibre, is heated to 70-80 DEG C,
Persistent period is 1.2-1.6h, obtains mixture;
(3) mixture obtained in above-mentioned steps (2) is mixed with other remaining ingredients, then pour into a mould, pour laggard
Row quiet stops, cuts, at 140-150 DEG C in steam-cured still after having cut, from the pressure of normal pressure~1.3MPa, and the boost process time
It is 0.3~0.7h, with the steam-cured 3-4 of steam hour, by extruding and being cut into adobe.
Factory Building non-load-bearing concrete aerated bricks the most according to claim 1, it is characterised in that by under following weight portion meter
State component to form: high-titanium blast furnace slag debris 25 parts, portland cement 37 parts, 6.5 parts of apatite, 2 parts of barite, fine sand 11
Part, isomeric alcohol polyethenoxy ether 4 parts, 3 parts of Fructus Gleditsia powder, sodium acetate 4 parts, inorganic aluminate water-proof agent 3 parts, 60 parts of water, aluminium silicate fiber
Tie up 3 parts.