CN106316104A - 一种紫外吸收窗用隔热玻璃 - Google Patents
一种紫外吸收窗用隔热玻璃 Download PDFInfo
- Publication number
- CN106316104A CN106316104A CN201510337709.5A CN201510337709A CN106316104A CN 106316104 A CN106316104 A CN 106316104A CN 201510337709 A CN201510337709 A CN 201510337709A CN 106316104 A CN106316104 A CN 106316104A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat insulation
- glass
- glass body
- ultraviolet absorption
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种紫外吸收窗用隔热玻璃,它包括玻璃本体,所述玻璃本体包括玻璃基材和着色剂,所述着色剂成分包括:Fe2O3为0.7~1.6wt%、CeO2为0.1~1.2wt%、TiO2为0~1.5wt%,所述玻璃本体表面设置有一层隔热层,所述隔热层由以下重量比的原料制成:丙烯酸树脂25~35份、溶剂30~40份、分散剂1~2份、防沉剂1~2份、纳米隔热填料10~20份、纤维素15~25份、附着增加剂0.5~2份。本发明一种紫外吸收窗用隔热玻璃,其隔热性能较好,能够有效阻挡太阳光,从而保证室内的阴凉,并且能够有效防止紫外线对人体的侵蚀,同时具有独特的颜色和色调。
Description
技术领域
本发明涉及一种紫外吸收窗用隔热玻璃,属于玻璃技术领域。
背景技术
玻璃是一种透明的半固体、半液体物质,在熔融时形成连续网络结构,冷却过程中 粘度逐渐增大并硬化而不结晶的硅酸盐类非金属材料。普通玻璃的主要成分是二氧化硅,它具有很高的化学稳定性、热稳定性和很好的透明度,因此被广泛应用于各个领域。目前人们广泛使用的玻璃大多为单层平板玻璃,其具有良好的透光性,但是保温隔热效果较差,不能有效阻挡室外太阳光的热量进入室内,从而导致室内温度较高,并且不能有效阻隔紫外线,过量的紫外线容易对人体造成损伤。
发明内容
本发明的目的在于克服上述不足,提供一种紫外吸收窗用隔热玻璃,其隔热性能较好,能够有效阻挡太阳光,从而保证室内的阴凉,并且能够有效防止紫外线对人体的侵蚀,同时具有独特的颜色和色调。
本发明的目的是这样实现的:一种紫外吸收窗用隔热玻璃,它包括玻璃本体,所述玻璃本体包括玻璃基材和着色剂,所述玻璃基材的成分包括SiO2、Na2O、CaO、MgO和Al2O3,所述玻璃基材成分为97%~98.8wt%,所述着色剂成分包括:Fe2O3为0.7~1.6 wt%、CeO2为0.1~1.2wt%、TiO2为0~1.5 wt%,所述玻璃本体表面设置有一层隔热层,所述隔热层由以下重量比的原料制成:丙烯酸树脂25~35份、溶剂30~40份、分散剂1~2份、防沉剂1~2份、纳米隔热填料10~20份、纤维素15~25份、附着增加剂0.5~2份。
与现有技术相比,本发明具有以下有益效果:
本发明一种紫外吸收窗用隔热玻璃,其隔热性能较好,能够有效阻挡太阳光,从而保证室内的阴凉,并且能够有效防止紫外线对人体的侵蚀,同时具有独特的颜色和色调。
具体实施方式
本发明一种紫外吸收窗用隔热玻璃,它包括玻璃本体,所述玻璃本体包括玻璃基材和着色剂,所述玻璃基材的成分包括SiO2、Na2O、CaO、MgO和Al2O3,所述玻璃基材成分为97%~98.8wt%,所述着色剂成分包括:Fe2O3为0.7~1.6 wt%、CeO2为0.1~1.2wt%、TiO2为0~1.5 wt%,所述玻璃本体表面设置有一层隔热层,所述隔热层由以下重量比的原料制成:丙烯酸树脂25~35份、溶剂30~40份、分散剂1~2份、防沉剂1~2份、纳米隔热填料10~20份、纤维素15~25份、附着增加剂0.5~2份。
Claims (1)
1.一种紫外吸收窗用隔热玻璃,其特征在于:它包括玻璃本体,所述玻璃本体包括玻璃基材和着色剂,所述玻璃基材的成分包括SiO2、Na2O、CaO、MgO和Al2O3,所述玻璃基材成分为97%~98.8wt%,所述着色剂成分包括:Fe2O3为0.7~1.6 wt%、CeO2为0.1~1.2wt%、TiO2为0~1.5 wt%,所述玻璃本体表面设置有一层隔热层,所述隔热层由以下重量比的原料制成:丙烯酸树脂25~35份、溶剂30~40份、分散剂1~2份、防沉剂1~2份、纳米隔热填料10~20份、纤维素15~25份、附着增加剂0.5~2份。