CN106315881A - 一种多功能反渗透阻垢剂 - Google Patents
一种多功能反渗透阻垢剂 Download PDFInfo
- Publication number
- CN106315881A CN106315881A CN201610894895.7A CN201610894895A CN106315881A CN 106315881 A CN106315881 A CN 106315881A CN 201610894895 A CN201610894895 A CN 201610894895A CN 106315881 A CN106315881 A CN 106315881A
- Authority
- CN
- China
- Prior art keywords
- reverse osmosis
- acid
- antisludging agent
- multifunctional reverse
- mass percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种多功能反渗透阻垢剂,按照质量百分比计,由以下组分制备而成:盐酸5~10%、柠檬酸10~20%、聚丙烯酸5~10%、氨基三亚甲基膦酸5~10%、水解聚马来酸酐15~20%,余量为去离子水。本发明通过以上药剂的复配,又可起到协同的作用,对系统进行有效阻垢。本发明所用原料来源广、成本低,制得的多功能反渗透阻垢剂的价格便宜,使用该阻垢剂对膜进行阻垢时,具有用量少、使用效果好、性价比极高的优点。
Description
技术领域
本发明涉及水处理技术领域,具体是一种多功能反渗透阻垢剂。
背景技术
早期由于反渗透技术的不了解,绝大部分人使用反渗透膜时,都会选用较好的水质,如地表水、地下水,这些水经过一定的预处理后,使用常规的阻垢剂(如六偏磷酸钠)即可满足反渗透膜进水要求。随着人们对反渗透系统的了解,开始将反渗透应用于相对更差的水质,如:反渗透浓水、河流水、江水甚至是中水(有机物废水、重金属废水)。
在现有技术中,虽然膜的抗污染性增强了,但是由于进水水质差、进水水量大,导致使用常规阻垢剂无法完全对系统进行有效阻垢,具体表现为:进水水质变差、系统污堵加快,进口阻垢剂虽然能起到部分阻垢效果,但由于其价格昂贵、使用量大、购买不方便等,很难在日趋发展的中国全面推广进口阻垢剂。
发明内容
本发明的目的在于提供一种低成本、用量少、效果好的多功能反渗透阻垢剂。
为实现上述目的,本发明提供如下技术方案:
一种多功能反渗透阻垢剂,按照质量百分比计,由以下组分制备而成:盐酸5~10%、柠檬酸10~20%、聚丙烯酸5~10%、氨基三亚甲基膦酸5~10%、水解聚马来酸酐15~20%,余量为去离子水。
作为本发明进一步的方案:按照质量百分比计,由以下组分制备而成:盐酸5%、柠檬酸10%、聚丙烯酸5%、氨基三亚甲基膦酸5%、水解聚马来酸酐15%,余量为去离子水。
作为本发明进一步的方案:按照质量百分比计,由以下组分制备而成:盐酸8%、柠檬酸15%、聚丙烯酸7%、氨基三亚甲基膦酸8%、水解聚马来酸酐18%,余量为去离子水。
作为本发明进一步的方案:按照质量百分比计,由以下组分制备而成:盐酸10%、柠檬酸20%、聚丙烯酸10%、氨基三亚甲基膦酸10%、水解聚马来酸酐20%,余量为去离子水。
所述的多功能反渗透阻垢剂的配制方法,具体步骤为:按上述质量百分比称取盐酸、柠檬酸、聚丙烯酸、氨基三亚甲基膦酸、水解聚马来酸酐及去离子水,充分混匀溶解后,得到。
所述的多功能反渗透阻垢剂的用量为:1~1.5ppm。
与现有技术相比,本发明的有益效果是:
本发明多功能反渗透阻垢剂的组分中:盐酸起到调节pH的作用,众所周知,pH越低,碳酸盐结垢可能性越差,因此该配方中引入了廉价的盐酸作为辅助试剂;柠檬酸主要起到的是对硫酸盐的阻垢效果,使用柠檬酸作为硫酸盐阻垢剂,其阻垢效果好,成本低;聚丙烯酸分散效果较好,可对进水中的悬浮物进行分散,当进水浊度较高时,可通过使用该分散剂有效防止悬浮物聚集及其对反渗透膜产生的污染;而氨基三亚甲基膦酸及水解聚马来酸酐则对铁、锰等金属氧化物及碳酸盐垢、硫酸盐垢均有很强的阻垢效果。
本发明通过以上药剂的复配,又可起到协同的作用,对系统进行有效阻垢。本发明所用原料来源广、成本低,制得的多功能反渗透阻垢剂的价格便宜,使用该阻垢剂对膜进行阻垢时,具有用量少、使用效果好、性价比极高的优点。
具体实施方式
下面将结合本发明实施例,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例1
本发明实施例中,一种多功能反渗透阻垢剂,按照质量百分比计,由以下组分制备而成:盐酸5%、柠檬酸10%、聚丙烯酸5%、氨基三亚甲基膦酸5%、水解聚马来酸酐15%,余量为去离子水。
所述的多功能反渗透阻垢剂的配制方法,具体步骤为:按上述质量百分比称取盐酸、柠檬酸、聚丙烯酸、氨基三亚甲基膦酸、水解聚马来酸酐及去离子水,充分混匀溶解后,得到。
实施例2
本发明实施例中,一种多功能反渗透阻垢剂,按照质量百分比计,由以下组分制备而成:盐酸8%、柠檬酸15%、聚丙烯酸7%、氨基三亚甲基膦酸8%、水解聚马来酸酐18%,余量为去离子水。
所述的多功能反渗透阻垢剂的配制方法,具体步骤为:按上述质量百分比称取盐酸、柠檬酸、聚丙烯酸、氨基三亚甲基膦酸、水解聚马来酸酐及去离子水,充分混匀溶解后,得到。
实施例3
本发明实施例中,一种多功能反渗透阻垢剂,按照质量百分比计,由以下组分制备而成:盐酸10%、柠檬酸20%、聚丙烯酸10%、氨基三亚甲基膦酸10%、水解聚马来酸酐20%,余量为去离子水。
所述的多功能反渗透阻垢剂的配制方法,具体步骤为:按上述质量百分比称取盐酸、柠檬酸、聚丙烯酸、氨基三亚甲基膦酸、水解聚马来酸酐及去离子水,充分混匀溶解后,得到。
实施例4
本发明实施例中,一种多功能反渗透阻垢剂,按照质量百分比计,由以下组分制备而成:盐酸8%、柠檬酸14%、聚丙烯酸5%、氨基三亚甲基膦酸7%、水解聚马来酸酐16%,余量为去离子水。
所述的多功能反渗透阻垢剂的配制方法,具体步骤为:按上述质量百分比称取盐酸、柠檬酸、聚丙烯酸、氨基三亚甲基膦酸、水解聚马来酸酐及去离子水,充分混匀溶解后,得到。
实施例5
本发明实施例中,一种多功能反渗透阻垢剂,按照质量百分比计,由以下组分制备而成:盐酸10%、柠檬酸18%、聚丙烯酸7%、氨基三亚甲基膦酸9%、水解聚马来酸酐18%,余量为去离子水。
所述的多功能反渗透阻垢剂的配制方法,具体步骤为:按上述质量百分比称取盐酸、柠檬酸、聚丙烯酸、氨基三亚甲基膦酸、水解聚马来酸酐及去离子水,充分混匀溶解后,得到。
本发明的技术效果验证:
目前市场上反渗透用阻垢剂品种较多,我们选用具有代表性的欣格瑞阻垢剂和亚什兰阻垢剂进行阻垢效果对比。
取反渗透膜片上的污染物进行静态阻垢试验,实验用水水质数据分析,pH:7.3,碱度:140mg/L,钙:185mg/L,总硬度:240mg/L,自然浓缩四倍,试验温度40℃。分别按照投加量为1mg/L、2mg/L、3mg/L、4mg/L,投加实施例1~5、欣格瑞阻垢剂、亚什兰阻垢剂,搅拌处理1h,对处理后的水质溶解进行分析,各阻垢剂的阻垢效果如表1所示。
表1各阻垢剂的阻垢效果
投加浓度 | 1mg/L | 2mg/L | 3mg/L | 4mg/L |
实施例1 | 98.60% | 99.00% | 99.40% | 99.00% |
实施例2 | 99.70% | 99.86% | 99.97% | 99.63% |
实施例3 | 99.30% | 99.40% | 99.60% | 99.47% |
实施例4 | 99.10% | 99.23% | 99.15% | 99.30% |
实施例5 | 98.90% | 99.30% | 99.81% | 99.73% |
欣格瑞阻垢剂 | 95.20% | 93.99% | 96.15% | 93.37% |
亚什兰阻垢剂 | 96.20% | 96.25% | 94.30% | 92.49% |
通过以上试验分析可以得出,当投加浓度达到3mg/L时,实施例2的效果为最佳,达到了99.97%,表明其阻垢性能非常的优异;与欣格瑞阻垢剂和亚什兰阻垢剂相比,本发明多功能反渗透阻垢剂的实际阻垢效果好,且具有低成本、用量少、使用效果好、性价比极高的优点。
对于本领域技术人员而言,显然本发明不限于上述示范性实施例的细节,而且在不背离本发明的精神或基本特征的情况下,能够以其他的具体形式实现本发明。因此,无论从哪一点来看,均应将实施例看作是示范性的,而且是非限制性的,本发明的范围由所附权利要求而不是上述说明限定,因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外,应当理解,虽然本说明书按照实施方式加以描述,但并非每个实施方式仅包含一个独立的技术方案,说明书的这种叙述方式仅仅是为清楚起见,本领域技术人员应当将说明书作为一个整体,各实施例中的技术方案也可以经适当组合,形成本领域技术人员可以理解的其他实施方式。
Claims (5)
1.一种多功能反渗透阻垢剂,其特征在于,按照质量百分比计,由以下组分制备而成:盐酸5~10%、柠檬酸10~20%、聚丙烯酸5~10%、氨基三亚甲基膦酸5~10%、水解聚马来酸酐15~20%,余量为去离子水。
2.根据权利要求1所述的多功能反渗透阻垢剂,其特征在于,按照质量百分比计,由以下组分制备而成:盐酸5%、柠檬酸10%、聚丙烯酸5%、氨基三亚甲基膦酸5%、水解聚马来酸酐15%,余量为去离子水。
3.根据权利要求1所述的多功能反渗透阻垢剂,其特征在于,按照质量百分比计,由以下组分制备而成:盐酸8%、柠檬酸15%、聚丙烯酸7%、氨基三亚甲基膦酸8%、水解聚马来酸酐18%,余量为去离子水。
4.根据权利要求1所述的多功能反渗透阻垢剂,其特征在于,按照质量百分比计,由以下组分制备而成:盐酸10%、柠檬酸20%、聚丙烯酸10%、氨基三亚甲基膦酸10%、水解聚马来酸酐20%,余量为去离子水。
5.根据权利要求1~4任一所述的多功能反渗透阻垢剂的配制方法,其特征在于,具体步骤为:按上述质量百分比称取盐酸、柠檬酸、聚丙烯酸、氨基三亚甲基膦酸、水解聚马来酸酐及去离子水,充分混匀溶解后,得到。