CN106314001A - Surface figure manufacturing process for glass fiber reinforced plastics - Google Patents
Surface figure manufacturing process for glass fiber reinforced plastics Download PDFInfo
- Publication number
- CN106314001A CN106314001A CN201610718670.6A CN201610718670A CN106314001A CN 106314001 A CN106314001 A CN 106314001A CN 201610718670 A CN201610718670 A CN 201610718670A CN 106314001 A CN106314001 A CN 106314001A
- Authority
- CN
- China
- Prior art keywords
- glass
- fiberglass
- gel coating
- coating resin
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a surface figure manufacturing process for glass fiber reinforced plastics. The process includes the steps that the outer surface of the glass fiber reinforced plastics is coated with gel coat resin; non-woven fabric with figures is bonded onto the gel coat resin; the non-woven fabric can be torn off after being solidified, then glass fibers are covered, and glue is coated between the gel coat resin and the glass fibers; 90-110 g of epoxy glass paint and 40-60 g of a glass paint curing agent are evenly stirred without bubbles to be prepared into the gel coat resin; and 900-1100 g of glass fiber reinforced plastic resin, 900-1600 g of talcum powder and 10-25 g of accelerant are collected to be evenly stirred and then 10-25 g of the curing agent is added, and then the materials are evenly stirred to be made into glue. According to the surface figure manufacturing process, the non-woven fabric with figures is laid onto the surface of the gel coat resin before the gel coat resin is dried, rugged figure marks are left on the surface of the gel coat resin after the non-woven fabric is torn off, and after the glass fibers are covered again, figures on the glass fiber reinforced plastic surface can have an abundant stereoscopic impression; and therefore the attractiveness can be greatly improved, the hardness is also improved, the preparation process is simple, operation is easy and cost is low.
Description
Technical field
The present invention relates to decorative materials technology, the surface detail processing technology of a kind of fiberglass.
Background technology
Fiberglass (FRP) also referred to as GFRP, i.e. fiber-reinforced plastic, refer generally to glass fiber reinforcement unsaturated polyester,
Epoxy resin and phenolic resin as matrix resin.Make the reinforced plastics of reinforcing material with glass fibre or its goods, appellation is glass fibre
Reinforced plastics, or appellation fiberglass, note being distinguished with safety glass.Resin variety owing to being used is different, therefore has
Organic toughened glass, fiber glass epoxy, the title of phenolic fiberglass reinforced plastics.Light weight and hard, non-conductive, stable performance, mechanical strength is high, reclaims
Utilize few, corrosion-resistant.Can substitute for steel and manufacture machine parts and automobile, ship housing etc..The characteristic that fiberglass is exquisitely carved
Being loved by the people, due to smooth surface, style form is enriched changeable, but the third dimension of decorative pattern shortcoming, and therefore aesthetic degree is again
Decrease.
Summary of the invention
It is an object of the invention to provide and a kind of there is abundant third dimension, promote aesthetic degree, improve its hardness, prepared
Journey is simple, the surface detail processing technology of easily operation, low cost fiberglass, with asking of solving to propose in above-mentioned background technology
Topic.
For achieving the above object, the present invention provides following technical scheme:
The surface detail processing technology of a kind of fiberglass, comprises the following steps:
The first step, at fiberglass outer surface gel coating resin；
Second step, is bonded at figuratum non-woven fabrics on gel coating resin；
3rd step, is torn after waiting non-woven fabrics solidification, cover glass fiber the most again, gel coating resin and glass fibre it
Between coating adhesive.
As the further scheme of the present invention: in the first step, by expoxy glass paint 90-110g, glass lacquer firming agent 40-
60g, stirs and does not has bubble, is configured to gel coating resin.
As the further scheme of the present invention: in the first step, by expoxy glass paint 100g, glass lacquer firming agent 50g, stirring
Uniformly there is no bubble, be configured to gel coating resin.
As the further scheme of the present invention: in second step, described non-woven fabrics is colour camoufague cloth.
As the further scheme of the present invention: in the 3rd step, take fiber glass resin 900-1100g, Pulvis Talci 900-
1600g, accelerator 10-25g, stir and add firming agent 10-25g afterwards, be stirred for uniformly making glue.
As the further scheme of the present invention: in the 3rd step, take fiber glass resin 1000g, Pulvis Talci 1000-1500g, rush
Enter agent 15-20g, stir and add firming agent 15-20g afterwards, be stirred for uniformly making glue.
Compared with prior art, the invention has the beneficial effects as follows:
In the present invention, gel coating resin lays figuratum non-woven fabrics on its surface, after non-woven fabrics is torn before becoming dry
The rough decorative pattern marking is left on gel coating resin surface, then after covering glass fibre, the decorative pattern of glass fiber reinforced plastic surface just tool
Having abundant third dimension, aesthetic degree is greatly improved, and also improves its hardness, preparation process simply, easily operate, low cost.
Detailed description of the invention
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under not making creative work premise, all
Belong to the scope of protection of the invention.
Embodiment 1
In the embodiment of the present invention, the surface detail processing technology of a kind of fiberglass, comprise the following steps:
The first step, at fiberglass outer surface gel coating resin；Wherein gel coating resin is by expoxy glass paint 90g, glass
Paint firming agent 40g, stirs and does not has bubble, be configured to.
Second step, is bonded at figuratum non-woven fabrics on gel coating resin.
3rd step, is torn after waiting non-woven fabrics solidification, cover glass fiber the most again, gel coating resin and glass fibre it
Between coating adhesive.Glue is to take fiber glass resin 900g, Pulvis Talci 900g, accelerator 10g, stirs and adds firming agent 10g afterwards,
It is stirred for uniformly making.
Embodiment 2
In the embodiment of the present invention, the surface detail processing technology of a kind of fiberglass, comprise the following steps:
The first step, at fiberglass outer surface gel coating resin；Wherein gel coating resin is by expoxy glass paint 110g, glass
Paint firming agent 60g, stirs and does not has bubble, be configured to.
Second step, is bonded at figuratum non-woven fabrics on gel coating resin.
3rd step, is torn after waiting non-woven fabrics solidification, cover glass fiber the most again, gel coating resin and glass fibre it
Between coating adhesive.Glue is to take fiber glass resin 1100g, Pulvis Talci 1600g, accelerator 25g, stirs and adds firming agent afterwards
25g, is stirred for uniformly making.
Embodiment 3
In the embodiment of the present invention, the surface detail processing technology of a kind of fiberglass, comprise the following steps:
The first step, at fiberglass outer surface gel coating resin；Wherein gel coating resin is by expoxy glass paint 100g, glass
Paint firming agent 50g, stirs and does not has bubble, be configured to.
Second step, is bonded at figuratum colour camoufague cloth on gel coating resin.
3rd step, is torn after waiting colour camoufague cloth solidification, cover glass fiber the most again, gel coating resin and glass fibre it
Between coating adhesive.Glue is to take fiber glass resin 1000g, Pulvis Talci 1000g, accelerator 15g, stirs and adds firming agent afterwards
15g, is stirred for uniformly making.
Embodiment 4
In the embodiment of the present invention, the surface detail processing technology of a kind of fiberglass, comprise the following steps:
The first step, at fiberglass outer surface gel coating resin；Wherein gel coating resin is by expoxy glass paint 100g, glass
Paint firming agent 50g, stirs and does not has bubble, be configured to.
Second step, is bonded at figuratum colour camoufague cloth on gel coating resin.
3rd step, is torn after waiting colour camoufague cloth solidification, cover glass fiber the most again, gel coating resin and glass fibre it
Between coating adhesive.Glue is to take fiber glass resin 1000g, Pulvis Talci 1500g, accelerator 20g, stirs and adds firming agent afterwards
20g, is stirred for uniformly making.
Embodiment 5
In the embodiment of the present invention, the surface detail processing technology of a kind of fiberglass, comprise the following steps:
The first step, at fiberglass outer surface gel coating resin；Wherein gel coating resin is by expoxy glass paint 100g, glass
Paint firming agent 50g, stirs and does not has bubble, be configured to.
Second step, is bonded at figuratum colour camoufague cloth on gel coating resin.
3rd step, is torn after waiting colour camoufague cloth solidification, cover glass fiber the most again, gel coating resin and glass fibre it
Between coating adhesive.Glue is to take fiber glass resin 1000g, Pulvis Talci 1200g, accelerator 18g, stirs and adds firming agent afterwards
18g, is stirred for uniformly making.
Embodiment 6
In the embodiment of the present invention, the surface detail processing technology of a kind of fiberglass, comprise the following steps:
The first step, at fiberglass outer surface gel coating resin；Wherein gel coating resin is by expoxy glass paint 95g, glass
Paint firming agent 45g, stirs and does not has bubble, be configured to.
Second step, is bonded at figuratum non-woven fabrics on gel coating resin.
3rd step, is torn after waiting non-woven fabrics solidification, cover glass fiber the most again, gel coating resin and glass fibre it
Between coating adhesive.Glue is to take fiber glass resin 900g, Pulvis Talci 1100g, accelerator 12g, stirs and adds firming agent afterwards
12g, is stirred for uniformly making.
Embodiment 7
In the embodiment of the present invention, the surface detail processing technology of a kind of fiberglass, comprise the following steps:
The first step, at fiberglass outer surface gel coating resin；Wherein gel coating resin is by expoxy glass paint 105g, glass
Paint firming agent 55g, stirs and does not has bubble, be configured to.
Second step, is bonded at figuratum non-woven fabrics on gel coating resin.
3rd step, is torn after waiting non-woven fabrics solidification, cover glass fiber the most again, gel coating resin and glass fibre it
Between coating adhesive.Glue is to take fiber glass resin 1050g, Pulvis Talci 1400g, accelerator 22g, stirs and adds firming agent afterwards
22g, is stirred for uniformly making.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of the spirit or essential attributes of the present invention, it is possible to realize the present invention in other specific forms.Therefore, no matter
From the point of view of which point, all should regard embodiment as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all by fall in the implication of equivalency and scope of claim
Change is included in the present invention.
Although moreover, it will be appreciated that this specification is been described by according to embodiment, but the most each embodiment only wraps
Containing an independent technical scheme, this narrating mode of description is only that for clarity sake those skilled in the art should
Description can also be formed those skilled in the art through appropriately combined as an entirety, the technical scheme in each embodiment
May be appreciated other embodiments.
Claims (6)
1. the surface detail processing technology of a fiberglass, it is characterised in that comprise the following steps:
The first step, at fiberglass outer surface gel coating resin；
Second step, is bonded at figuratum non-woven fabrics on gel coating resin；
3rd step, is torn after waiting non-woven fabrics solidification, cover glass fiber the most again, is coated with between gel coating resin and glass fibre
Cover glue.
The surface detail processing technology of fiberglass the most according to claim 1, it is characterised in that in the first step, by epoxy
Glass lacquer 90-110g, glass lacquer firming agent 40-60g, stir and do not have bubble, be configured to gel coating resin.
The surface detail processing technology of fiberglass the most according to claim 2, it is characterised in that in the first step, by epoxy
Glass lacquer 100g, glass lacquer firming agent 50g, stir and do not have bubble, be configured to gel coating resin.
The surface detail processing technology of fiberglass the most according to claim 1, it is characterised in that in second step, described nothing
Spinning cloth is colour camoufague cloth.
The surface detail processing technology of fiberglass the most according to claim 1, it is characterised in that in the 3rd step, take glass
Steel resin 900-1100g, Pulvis Talci 900-1600g, accelerator 10-25g, stir and add firming agent 10-25g afterwards, then
Stir and make glue.
The surface detail processing technology of fiberglass the most according to claim 5, it is characterised in that in the 3rd step, take glass
Steel resin 1000g, Pulvis Talci 1000-1500g, accelerator 15-20g, stir and add firming agent 15-20g afterwards, be stirred for
Uniformly make glue.