CN106313644A - Co-extrusion double-layer composite hose and processing method thereof - Google Patents
Co-extrusion double-layer composite hose and processing method thereof Download PDFInfo
- Publication number
- CN106313644A CN106313644A CN201510375834.5A CN201510375834A CN106313644A CN 106313644 A CN106313644 A CN 106313644A CN 201510375834 A CN201510375834 A CN 201510375834A CN 106313644 A CN106313644 A CN 106313644A
- Authority
- CN
- China
- Prior art keywords
- layer
- enhancement layer
- waterproof
- extrusion
- enhancement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a co-extrusion double-layer composite hose. The co-extrusion double-layer composite hose comprises a hose body, the hose body comprises a first reinforcing layer and a second reinforcing layer; a first waterproof layer is arranged between the first reinforcing layer and the second reinforcing layer, and a first wear-resistant layer is additionally arranged on the outer surface of the first reinforcing layer; a second waterproof layer and a second wear-resistant layer are sequentially added on the inner surface of the second reinforcing layer. The invention further discloses a processing method of the co-extrusion double-layer composite hose. The processing method comprises the following steps: weaving the first reinforcing layer and the second reinforcing layer on a circular weaving machine through a double-layer common weaving technology; subjecting the outer layers, the middle layers and the inner layers of the first reinforcing layer and the second reinforcing layer to coating by the one-time forming co-extrusion technology to form the first wear-resistant layer, the first waterproof layer and the second waterproof layer; coating the inner wall of the second waterproof layer with the second wear-resistant layer; subjecting the semi-finished product obtained in the step 3 to hole rolling and then to a hot vulcanization process so that the semi-finished products can be completely bonded to form a finished product. The pressure resistance, wear resistance and sealing performance of the hose body are improved.
Description
Technical field
The invention belongs to tubing field, relate to composite soft tube material field, particularly relate to a kind of co-extrusion
Two-layer compound flexible pipe, further relates to the processing technique of a kind of co-extrusion two-layer compound flexible pipe.
Background technology
Composite soft tube is a kind of special packing container, occupies important ground in packaging field
Position, composite soft tube is made up of multiple material multi-layer sealing structure, is still had in rugged environment
Standby preferable crack resistance and resistance to leakage, will not burst suddenly.But at existing composite soft tube
In, composite soft tube uses terylene short fiber or polyester industrial filament yarn to be woven into, liner then by rubber or
Polyurethane is made, it is impossible to be provided simultaneously with wearability and corrosion resistance, brings not to industry transmission
Just, and in the processing technique of conventional composite soft tube, technique is simple and crude, is simply penetrated by lining
In enhancement layer, and lining and enhancement layer are carried out heat cure bonding, cause composite soft tube tube wall
Thin and the most pressure, the most wear-resisting shortcoming.
It would therefore be desirable to seek a kind of new technical scheme to solve this technical problem.
Summary of the invention
It is an object of the invention to provide a kind of co-extrusion two-layer compound flexible pipe and processing technique thereof.
The technical solution used in the present invention is:
A kind of co-extrusion two-layer compound flexible pipe, including hookah bodies, hookah bodies includes the first enhancing
Layer and the second enhancement layer, be provided with the first waterproof layer between the first enhancement layer and the second enhancement layer, the
One enhancement layer outer surface has additional the first wearing layer, and the inner surface of the second enhancement layer has additional successively
Second waterproof layer and the second wearing layer.
First enhancement layer or the second enhancement layer are woven by Polyester Yarns or silk and form.
First waterproof layer and the second waterproof layer by the one in rubber, polyurethane or polrvinyl chloride or
Several make.
First wearing layer and the second wearing layer by the one in rubber, polyurethane or polrvinyl chloride or
Several make.
A kind of processing technique of co-extrusion two-layer compound flexible pipe, step one: use double-deck Co-knit
Technology knits out the first enhancement layer and the second enhancement layer on circular weaving machine;
Step 2: by the common extruding technology of one-shot forming at the first enhancement layer, the second enhancement layer
Outer layer, middle level and internal layer be coated, formed the first wearing layer, the first waterproof layer and
Second waterproof layer;
Step 3: the internal layer at the second waterproof layer is coated with the second wearing layer;
Step 4: semi-finished product step 3 obtained carry out hot vulcanization process after rolling hole again
It is allowed to bond completely, forms finished product.
The invention have the advantage that and use the first enhancement layer and the double-deck of the second enhancement layer to strengthen knot
Structure, can strengthen crushing resistance and the intensity of hookah bodies, the first enhancement layer and the second enhancement layer it
Between be provided with the first waterproof layer and the second enhancement layer internal layer is provided with the second waterproof layer, flexible pipe can be increased
The water proofing property of body and sealing;The first wearing layer it is provided with and outside the first enhancement layer
It is provided with the second wearing layer in two waterproof layers, the inside and outside wearability of hookah bodies can be increased, improve soft
Tube body quality, extends the service life of hookah bodies;
Using above-mentioned production stage, step is easy, and by carrying out heat cure again after rolling hole,
Make the first waterproof layer of being made up of one or more in rubber, polyurethane or polrvinyl chloride and
Second waterproof layer and the first wearing layer and the second wearing layer melt, and mutually bond, and strengthen
The fastness of hookah bodies.
Accompanying drawing explanation
With detailed description of the invention, the present invention is described in further detail below in conjunction with the accompanying drawings.
Fig. 1 is the structural representation of the present invention.
Wherein: 1, hookah bodies, the 2, first enhancement layer, the 3, second enhancement layer, 4, first
Waterproof layer, the 5, first wearing layer, the 6, second waterproof layer, the 7, second wearing layer.
Detailed description of the invention
As it is shown in figure 1, a kind of co-extrusion two-layer compound flexible pipe of the present invention, including hookah bodies 1,
Hookah bodies 1 includes the first enhancement layer 2 and the second enhancement layer 3, the first enhancement layer 2 and second
Being provided with the first waterproof layer 4 between enhancement layer 3, it is resistance to that the first enhancement layer 2 outer surface has additional first
Mill layer 5, it is wear-resisting that the inner surface of the second enhancement layer 3 has additional the second waterproof layer 6 and second successively
Layer 7.
First enhancement layer 2 or the second enhancement layer 3 are woven by Polyester Yarns or silk and form.
First waterproof layer 4 and the second waterproof layer 6 are by rubber, polyurethane or polrvinyl chloride
Kind or several make.
First wearing layer 5 and the second wearing layer 7 are by rubber, polyurethane or polrvinyl chloride
Kind or several make.
A kind of processing technique of co-extrusion two-layer compound flexible pipe, step one: use double-deck Co-knit
Technology knits out the first enhancement layer 2 and the second enhancement layer 3 on circular weaving machine;
Step 2: strengthened at the first enhancement layer 2, second by the common extruding technology of one-shot forming
Outer layer, middle level and the internal layer of layer 3 are coated, and form the first wearing layer 5, first waterproof
Layer 4 and the second waterproof layer 6;
Step 3: the internal layer at the second waterproof layer 6 is coated with the second wearing layer 7;
Step 4: semi-finished product step 3 obtained carry out hot vulcanization process after rolling hole again
It is allowed to bond completely, forms finished product.
Use the first enhancement layer 2 and double layer reinforcement structure of the second enhancement layer 3, flexible pipe can be strengthened
The crushing resistance of body 1 and intensity, be provided with between the first enhancement layer 2 and the second enhancement layer 3
One waterproof layer 4 and the second enhancement layer 3 internal layer are provided with the second waterproof layer 6, can increase flexible pipe originally
The water proofing property of body 1 and sealing;Be provided with outside the first enhancement layer 2 first wearing layer 5 and
In the second waterproof layer 6, it is provided with the second wearing layer 7, the inside and outside wear-resisting of hookah bodies 1 can be increased
Property, improve hookah bodies quality, extend the service life of hookah bodies;
Using above-mentioned production stage, step is easy, and by carrying out heat cure again after rolling hole,
Make the first waterproof layer 4 being made up of one or more in rubber, polyurethane or polrvinyl chloride
Melt with the second waterproof layer 6 and the first wearing layer 5 and the second wearing layer 7, and mutually bond,
Strengthen the fastness of hookah bodies.
Above-described is only some embodiments of the present invention.For those of ordinary skill in the art
For, without departing from the concept of the premise of the invention, it is also possible to make some deformation and change
Entering, these broadly fall into the protection domain of invention (present invention).
Claims (5)
1. a co-extrusion two-layer compound flexible pipe, including hookah bodies, it is characterised in that: described flexible pipe
Body include the first enhancement layer and the second enhancement layer, described first enhancement layer and the second enhancement layer it
Between be provided with the first waterproof layer, described first enhancement layer outer surface has additional the first wearing layer, described
The inner surface of the second enhancement layer has additional the second waterproof layer and the second wearing layer successively.
A kind of co-extrusion two-layer compound flexible pipe the most according to claim 1, it is characterised in that: institute
State the first enhancement layer or the second enhancement layer to be formed by Polyester Yarns or silk braiding.
A kind of co-extrusion two-layer compound flexible pipe the most according to claim 1, it is characterised in that: institute
State the first waterproof layer and the second waterproof layer by the one in rubber, polyurethane or polrvinyl chloride or several
Plant and make.
A kind of co-extrusion two-layer compound flexible pipe the most according to claim 1, it is characterised in that: institute
State the first wearing layer and the second wearing layer by the one in rubber, polyurethane or polrvinyl chloride or several
Plant and make.
5. according to a kind of co-extrusion two-layer compound described in any one claim in claim 1-4
The processing technique of flexible pipe, it is characterised in that: step one: use double-deck Co-knit technology justifying
The first enhancement layer and the second enhancement layer is knit out on loom;
Step 2: by the common extruding technology of one-shot forming outside the first enhancement layer, the second enhancement layer
Layer, middle level and internal layer are coated, and form the first wearing layer, the first waterproof layer and second
Waterproof layer;
Step 3: the internal layer at the second waterproof layer is coated with the second wearing layer;
Step 4: semi-finished product step 3 obtained carry out hot vulcanization process again after rolling hole and are allowed to
Bond completely, form finished product.