CN106282728A - 一种复合耐磨材料 - Google Patents
一种复合耐磨材料 Download PDFInfo
- Publication number
- CN106282728A CN106282728A CN201610747289.2A CN201610747289A CN106282728A CN 106282728 A CN106282728 A CN 106282728A CN 201610747289 A CN201610747289 A CN 201610747289A CN 106282728 A CN106282728 A CN 106282728A
- Authority
- CN
- China
- Prior art keywords
- parts
- abrasion resistance
- resistance material
- composite abrasion
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种复合耐磨材料,按重量份计包括:废钢25~35份、钛铁2~9份、碳化硅5~15份、水泥10~15份、碳化钨5~15份、硅钙钡6~9份和硼砂10~15份。本发明提供的一种复合耐磨材料,抗压强度、抗折强度及耐磨性能三个方面均有大幅度的提高;而且其性能稳定。
Description
技术领域
本发明涉及耐磨材料技术领域,具体是一种复合耐磨材料。
背景技术
耐磨材料经常用于涂层或硬面堆焊(hardfacing)场合,以防止下面的材料受到摩擦、冲击、摩擦磨损以及类似可能带来破坏的机械作用。耐磨涂层或硬面堆焊可以包括一层均匀的硬或耐磨材料。但是,这类材料通常昂贵,而且,其自身可能不容易形成涂层。为此,一种开发耐磨涂层的策略是将硬相加入更容易实施涂覆或者硬面堆焊工艺并且成本更有效的材料中。通常,制备有效耐磨涂层材料可能需要将大体积分数的硬相加入涂层材料中。
发明内容
本发明所要解决的技术问题是提供一种复合耐磨材料。
本发明解决上述技术问题的技术方案如下:一种复合耐磨材料,按重量份计包括:
本发明的有益效果是:本发明提供的一种复合耐磨材料,抗压强度、抗折强度及耐磨性能三个方面均有大幅度的提高;而且其性能稳定。
在上述技术方案的基础上,本发明还可以做如下改进。
优选的,按重量份计包括:
优选的,还包含有3~19重量份的含氮锰铁。
优选的,按重量份计包括:
优选的,还包含有5~10重量份的氢氧化高镍。
优选的,按重量份计包括:
具体实施方式
实施例1
一种复合耐磨材料,按重量份计包括:废钢28份、钛铁6份、碳化硅12份、水泥14份、碳化钨14份、硅钙钡8份和硼砂10份。
实施例2
一种复合耐磨材料,按重量份计包括:废钢28份、钛铁6份、碳化硅12份、水泥14份、碳化钨14份、硅钙钡8份、硼砂10份和氢氧化高镍8份。
实施例3
一种复合耐磨材料,按重量份计包括:废钢32份、钛铁8份、碳化硅14份、水泥15份、碳化钨8份、硅钙钡9份、硼砂13份和氢氧化高镍8份。
实施例4
一种复合耐磨材料,按重量份计包括:按重量份计包括:废钢35份、钛铁9份、碳化硅15份、水泥15份、碳化钨15份、硅钙钡9份、硼砂15份和含氮锰铁19份。
一种复合耐磨材料的制备方法,包括如下步骤:
(1)、将各组份,按比例配比成混合均匀的混合物;
(2)、将所述混合物置于熔炼炉内,在1450℃至1550℃的条件下,使混合物完全熔化;
(3)、出炉冷却至室温,成冷凝物。
对分别由上述四个实施例复合耐磨材料的进行检验,结果如下:
本发明提供的一种复合耐磨材料,抗压强度、抗折强度及耐磨性能三个方面均有大幅度的提高;而且其性能稳定。
本发明提供的一种复合耐磨材料,制作简单,采用的生产原料选择无毒性的,胶水的使用效果好,环保,可形成坚韧涂层,具有持久的防水性和抗静电性。
尽管上面已经示出和描述了本发明的实施例,可以理解的是,上述实施例是示例性的,不能理解为对本发明的限制,本领域的普通技术人员在本发明的范围内可以对上述实施例进行变化、修改、替换和变型。
Claims (6)
1.一种复合耐磨材料,其特征在于,按重量份计包括:
2.根据权利要求1所述一种复合耐磨材料,其特征在于,按重量份计包括:
3.根据权利要求1所述一种复合耐磨材料,其特征在于,还包含有3~19重量份的含氮锰铁。
4.根据权利要求3所述一种复合耐磨材料,其特征在于,按重量份计包括:
5.根据权利要求1所述一种复合耐磨材料,其特征在于,还包含有5~10重量份的氢氧化高镍。
6.根据权利要求5所述一种复合耐磨材料,其特征在于,按重量份计包括: