CN106281606B - A kind of energy saving wear-resistant lubricating oil and its production technology and application method - Google Patents
A kind of energy saving wear-resistant lubricating oil and its production technology and application method Download PDFInfo
- Publication number
- CN106281606B CN106281606B CN201610641620.2A CN201610641620A CN106281606B CN 106281606 B CN106281606 B CN 106281606B CN 201610641620 A CN201610641620 A CN 201610641620A CN 106281606 B CN106281606 B CN 106281606B
- Authority
- CN
- China
- Prior art keywords
- lubricating oil
- energy saving
- resistant lubricating
- oil
- saving wear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of energy saving wear-resistant lubricating oil, including following raw material: benzotriazole, triphenyl phosphate, polybutadiene, chlorinated paraffin, dibutyl phthalate and two wires oil.The present invention uses simultaneously with conventional lubricantss, and the additional amount of energy saving wear-resistant lubricating oil is the 3-5% of the sum of energy saving wear-resistant lubricating oil and conventional lubricantss, 320 DEG C of lubricating oil is lower than suitable for moving interface, wherein not including brake fluid.The present invention is used for automobile, improves significantly to engine behavior, and if idling is steady, lower noise accelerates sensitive, power enhancing;Low-temperature startup performance is good, shows in winter especially prominent;Fuel combustion is complete, and tail gas is improved, environmentally protective;Reduce energy consumption 10%-38%;Engine and power-transmitting part abrasion are small, and service life extends 50% to 2 times;For other aspects: can be 1 to 2 times of service life of prolonged mechanical.
Description
Technical field
The present invention relates to a kind of energy saving wear-resistant lubricating oil and its production technologies and application method, belong to Lubricating Oil Technique neck
Domain.
Background technique
Technological lubrication oil application range is very wide, and the type of base oil is relatively more, such as straight mineral oil, hydrocarbon synthetic oil, polyethers
Synthetic oil, alkylbenzene oil, biodegradable lipid oil.When they become certain industrial lubricant, being between them cannot phase
It mutually mixes, after polyethers synthetic oil and the mixing of other industry oil, performance will be remarkably decreased.
Lubricating oil in the prior art, in the case where bearing capacity continues to increase, coefficient of friction is changed greatly, and carries energy
PD value in power is generally between 260-400kg.
Summary of the invention
The purpose of the present invention is to provide a kind of energy saving wear-resistant lubricating oil and its production technology and application method, the present invention is used
In on automobile (all engines), improve significantly to engine behavior;For other aspects, fortune can reduce
The mechanical wear of dynamic component, energy saving, big machinery are especially prominent.It can be 1 to 2 times of service life of prolonged mechanical.The present invention
Technical solution is as follows:
A kind of energy saving wear-resistant lubricating oil, including following raw material:
Benzotriazole, triphenyl phosphate, polybutadiene, chlorinated paraffin, dibutyl phthalate and two wires oil.
Further, energy saving wear-resistant lubricating oil of the present invention is made of following raw material by mass percentage:
Benzotriazole 0.1-0.5%;
Triphenyl phosphate 0.5-1.0%;
Polybutadiene 2-5%;
Chlorinated paraffin 20-30%;
Dibutyl phthalate 5-10%;
Two wires oil 53.5-72.4%.
Further, energy saving wear-resistant lubricating oil of the present invention is made of following raw material by mass percentage:
Benzotriazole 0.2-0.4%;
Triphenyl phosphate 0.6-0.8%;
Polybutadiene 2.5-4%;
Chlorinated paraffin 22-28%;
Dibutyl phthalate 6-9%;
Two wires oil 58-68%.
Further, energy saving wear-resistant lubricating oil of the present invention is made of following raw material by mass percentage:
Benzotriazole 0.3%;
Triphenyl phosphate 0.7%;
Polybutadiene 3.5%;
Chlorinated paraffin 25%;
Dibutyl phthalate 7.5%;
Two wires oil 63%.
The production technology of above-mentioned energy saving wear-resistant lubricating oil is as follows:
(1) the 60%(mass fraction of two wires oil total amount is taken first) it is added in No. 1 container, container is with blender
Rustless steel container;
(2) chlorinated paraffin, polybutadiene are weighed, successively pours into No. 1 container, is stirred;
(3) dibutyl phthalate is poured into No. 1 container, continues to stir;
(4) weigh the 10%(mass fraction of two wires oil total amount) two wires oil, be placed in No. 2 rustless steel containers, be then added
Triphenyl phosphate is stirred continuously, and after white solid object all dissolves, is poured into No. 1 container, is stirred continuously;
(5) weigh the 10%(mass fraction of two wires oil total amount) two wires oil, be placed in No. 3 rustless steel containers, be added benzene a pair of horses going side by side
Triazole is stirred continuously and is allowed to uniformly, pours into No. 1 container after solids dissolution, finally supplies exposed two wires oil, is stirred for
5 minutes to obtain the final product.
When the preparation present invention, benzotriazole and triphenyl phosphate are purity assay or chemical purity, polybutadiene, chlorination
Paraffin, dibutyl phthalate and two wires oil are technical pure.
Application method of the invention is as follows:
The present invention uses simultaneously with conventional lubricantss, and the additional amount of lubricating oil of the present invention is overall (present invention and conventional profit
The sum of lubrication prescription) additional amount 3-5%(mass percent).The every traveling 5000-10000km(of motor vehicle or timing) it adds once.But
It is not recommended that changing the rule of previous more oil change.
Use scope of the invention:
In addition to brake fluid, it is used in the lubricating oil that all moving interfaces are lower than 320 DEG C.Including motorcycle, automobile, wheel
The moving interface that all needs of ship, civil aircraft, machinery equipment etc. lubricate.
The lubrication mechanism of wearproof lubricant (antifriction lubricant):
Wearproof lubricant is formulated by certain active materials and the new materials such as wear-resistant, anticorrosive.When rubbing surface connects
When touch pressure is high, the sags and crests of two metal surfaces intermesh, and generate localized hyperthermia, high pressure.Work in wearproof lubricant at this time
Property element and metal interaction, form the low solid protective film of shear strength, two metal surfaces separated, this layer of solid is dynamically
Film layer and liquid dynamically lubricating film layer collective effect, can play ultimate attainment lubricating action, to reduce metal mill to the maximum extent
Damage and sintering.There is collective effect jointly due to solid dynamic film layer and liquid dynamically lubricating film layer, makes kinetic energy in sealing strip
Linear transmission under part reduces loss of the power in conversion, has reached energy-efficient optimum efficiency.
The protection mechanism of wearproof lubricant:
The presence of ultra-thin solid protective film greatly reduces the abrasion of friction surface, especially when frictional interface is in boundary
Under lubricating condition (so-called boundary lubrication refers to that frictional interface is in oil-free Frotteurism), protective effect becomes especially to show
It writes.Such as: one, it is cold-started dry friction.Since in cold start-up, oil pump also has not enough time to getting to lubricating oil into each friction portion engine
Position, makes frictional interface be in dry condition, causes being seriously worn for engine;Two, it is unexpected in the working condition of engine
When change, the oil film between frictional interface is destroyed, and keeps directly contact wear between metal serious;Three, work as indicating oven temperature of engine,
When oil ageing, lubricating status is deteriorated;Four, in-engine water condensation gas causes the corrosion of metal;Five, generation of burning flies
It rises and causes corrosion of metal.
After wearproof lubricant, all of above abrasion can be avoided.
Compared with the prior art, the present invention has the following advantages:
(1) present invention is used for automobile (all engines), improves significantly to engine behavior:
1. idling is steady, lower noise, accelerate sensitive, power enhancing.
2. low-temperature startup performance is good, show in winter especially prominent.
3. water tank temperature reduces.
4. fuel combustion is complete, tail gas is improved, environmentally protective.
5. reducing energy consumption 10%-38%, the large-scale overweight vehicle of bogie is particularly evident.
6. engine and power-transmitting part abrasion are small, service life extends 50% to 2 times.
(2) present invention is for other aspects:
The mechanical wear of reduction moving component, energy saving, big machinery are especially prominent.The service life 1 of prolonged mechanical
To 2 times.
Specific embodiment
The invention will now be further described with reference to specific embodiments, the advantages and features of the present invention will be with description and
It is apparent.But examples are merely exemplary, and it is not intended to limit the scope of the present invention in any way.Those skilled in the art answer
It should be appreciated that without departing from the spirit and scope of the invention can details to technical solution of the present invention and form repair
Change or replace, but these modifications and replacement are fallen within the protection scope of the present invention.
It is required in the embodiment of the present invention as follows:
1, raw material benzotriazole and triphenyl phosphate are purity assay or chemical purity, preferably the former, other raw materials
It is the technical pure that regular factory produces.
2, it prepares, droplet (packing container and all apparatus) must not be mixed in packaging process.
3, it should be protected from light after material storage, water proof saves.Finished product must also be kept in dark place.
4, after preparing every time, (configure next time before) necessary clear cylinder is clean, because having a small amount of solids residual after precipitating
Slag, this is normal.
A kind of energy saving wear-resistant lubricating oil of embodiment 1 and its production technology
Energy saving wear-resistant lubricating oil is made of following raw material by mass percentage:
Benzotriazole 0.3%;
Triphenyl phosphate 0.7%;
Polybutadiene 3.5%;
Chlorinated paraffin 25%;
Dibutyl phthalate 7.5%;
Two wires oil 63%.
The production technology of above-mentioned energy saving wear-resistant lubricating oil is as follows:
(1) the 60%(mass fraction of two wires oil total amount is taken first) it is added in No. 1 container, container is with blender
Rustless steel container;
(2) chlorinated paraffin, polybutadiene are weighed, successively pours into No. 1 container, is stirred;
(3) dibutyl phthalate is poured into No. 1 container, continues to stir;
(4) weigh the 10%(mass fraction of two wires oil total amount) two wires oil, be placed in No. 2 rustless steel containers, be then added
Triphenyl phosphate is stirred continuously, and after white solid object all dissolves, is poured into No. 1 container, is stirred continuously;
(5) weigh the 10%(mass fraction of two wires oil total amount) two wires oil, be placed in No. 3 rustless steel containers, be added benzene a pair of horses going side by side
Triazole is stirred continuously and is allowed to uniformly, pours into No. 1 container after solids dissolution, finally supplies exposed two wires oil, is stirred for
5 minutes to obtain the final product.
It when using energy saving wear-resistant lubricating oil manufactured in the present embodiment, is used in combination with automobile engine oil, present invention lubrication
The additional amount of oil accounts for overall 4%(mass fraction), when the every traveling 8000km of automobile, add once.It records automobile to use 3 years, row
The case where sailing 80000km is moistened so that the same money vehicle of general-utility car engine oil is used alone as control using energy saving wear-resistant of the present invention
The automobile energy consumption of lubrication prescription reduces 28%, and engine scuffing is significantly smaller.
A kind of energy saving wear-resistant lubricating oil of embodiment 2 and its production technology
Energy saving wear-resistant lubricating oil is made of following raw material by mass percentage:
Benzotriazole 0.15%;
Triphenyl phosphate 0.8%;
Polybutadiene 4%;
Chlorinated paraffin 21%;
Dibutyl phthalate 6%;
Two wires oil 68.05%.
The production technology of above-mentioned energy saving wear-resistant lubricating oil is as follows:
(1) the 60%(mass fraction of two wires oil total amount is taken first) it is added in No. 1 container, container is with blender
Rustless steel container;
(2) chlorinated paraffin, polybutadiene are weighed, successively pours into No. 1 container, is stirred;
(3) dibutyl phthalate is poured into No. 1 container, continues to stir;
(4) weigh the 10%(mass fraction of two wires oil total amount) two wires oil, be placed in No. 2 rustless steel containers, be then added
Triphenyl phosphate is stirred continuously, and after white solid object all dissolves, is poured into No. 1 container, is stirred continuously;
(5) weigh the 10%(mass fraction of two wires oil total amount) two wires oil, be placed in No. 3 rustless steel containers, be added benzene a pair of horses going side by side
Triazole is stirred continuously and is allowed to uniformly, pours into No. 1 container after solids dissolution, finally supplies exposed two wires oil, is stirred for
5 minutes to obtain the final product.
It when using energy saving wear-resistant lubricating oil manufactured in the present embodiment, is used in combination with automobile gear oil, lubricating oil of the present invention
Additional amount account for overall 3.5%(mass fraction), when the every traveling 8000km of automobile, add primary.It records automobile to use 3 years, row
The case where sailing 80000km, the same money vehicle of general-utility car gear oil is used alone as control, geared parts abrasion is significantly smaller.
A kind of energy saving wear-resistant lubricating oil of embodiment 3 and its production technology
Energy saving wear-resistant lubricating oil is made of following raw material by mass percentage:
Benzotriazole 0.45%;
Triphenyl phosphate 0.8%;
Polybutadiene 5%;
Chlorinated paraffin 28%;
Dibutyl phthalate 6%;
Two wires oil 59.75%.
The production technology of above-mentioned energy saving wear-resistant lubricating oil is as follows:
(1) the 60%(mass fraction of two wires oil total amount is taken first) it is added in No. 1 container, container is with blender
Rustless steel container;
(2) chlorinated paraffin, polybutadiene are weighed, successively pours into No. 1 container, is stirred;
(3) dibutyl phthalate is poured into No. 1 container, continues to stir;
(4) weigh the 10%(mass fraction of two wires oil total amount) two wires oil, be placed in No. 2 rustless steel containers, be then added
Triphenyl phosphate is stirred continuously, and after white solid object all dissolves, is poured into No. 1 container, is stirred continuously;
(5) weigh the 10%(mass fraction of two wires oil total amount) two wires oil, be placed in No. 3 rustless steel containers, be added benzene a pair of horses going side by side
Triazole is stirred continuously and is allowed to uniformly, pours into No. 1 container after solids dissolution, finally supplies exposed two wires oil, is stirred for
5 minutes to obtain the final product.
It when using energy saving wear-resistant lubricating oil manufactured in the present embodiment, is used in combination with large-scale grinding machine gear oil, present invention profit
The additional amount of lubricating oil accounts for overall 3%(mass fraction).When grinding machine uses 6 months, the same model of ordinary gear oil is used alone
Grinding machine is control, and using the grinding machine of energy saving wear-resistant lubricant of the present invention, moving component abrasion is significantly smaller.
Test example 1
Energy saving wear-resistant lubricating oil of the present invention is through the Chinese Lanzhou Ke Yuan Chemical Physics research institute, national lubriation material product quality
Supervision Test Center detection and analysis show:
PD value in lubricating oil bearing capacity of the present invention are as follows: 7840N(800kg), it is the maximum value of national examination criteria, so
And in maximum value, still there is not sintering phenomenon.
Coefficient of friction (600rpm, 75 DEG C) numerical value are as follows:
98N——0.101
196N——0.910
294N——0.100
392N——0.106
490N——0.119
588N——0.125
686N——0.126
784N——0.125
882N——0.119
980N——0.116
Testing result shows the stability of coefficient of friction of the present invention.In the case where bearing capacity continues to increase, friction system
Number is well below lubricating oil in the prior art.
In addition, lubricating oil PD value is between 260-400kg in the prior art.Bearing capacity reaches 980N(100kg) when, friction
Coefficient is higher than 0.5 or more.
Claims (8)
1. a kind of energy saving wear-resistant lubricating oil, which is characterized in that energy saving wear-resistant lubricating oil is by following raw material by mass percentage
Composition:
2. energy saving wear-resistant lubricating oil according to claim 1, which is characterized in that the energy saving wear-resistant lubricating oil by pressing below
The raw material of mass percentage forms:
3. energy saving wear-resistant lubricating oil according to claim 2, which is characterized in that the energy saving wear-resistant lubricating oil by pressing below
The raw material of mass percentage forms:
4. the production technology of energy saving wear-resistant lubricating oil as described in claim any one of 1-3, the specific steps are as follows:
(1) the 60% of two wires oil total amount is taken to be added in No. 1 container first, container is the rustless steel container with blender;
(2) chlorinated paraffin, polybutadiene are weighed, successively pours into No. 1 container, is stirred;
(3) dibutyl phthalate is poured into No. 1 container, continues to stir;
(4) the 10% two wires oil for weighing two wires oil total amount, is placed in No. 2 rustless steel containers, triphenyl phosphate is then added, no
Disconnected stirring, after white solid object all dissolves, pours into No. 1 container, is stirred continuously;
(5) the 10% two wires oil for weighing two wires oil total amount, is placed in No. 3 rustless steel containers, benzotriazole is added, constantly stirs
It mixes and is allowed to uniformly, poured into No. 1 container after solids dissolution, finally supply exposed two wires oil, be stirred for 5 minutes to obtain the final product.
5. production technology according to claim 4, which is characterized in that the benzotriazole and triphenyl phosphate are analysis
Purity or chemical purity, polybutadiene, chlorinated paraffin, dibutyl phthalate and two wires oil are technical pure.
6. the application method of energy saving wear-resistant lubricating oil as described in claim any one of 1-3, the energy saving wear-resistant lubricating oil and often
Rule lubricant uses simultaneously, and the additional amount of energy saving wear-resistant lubricating oil is energy saving wear-resistant lubricating oil and conventional profit by mass percentage
The 3-5% of the sum of lubrication prescription.
7. energy saving wear-resistant lubricating oil is lower than 320 DEG C of lubricating oil for moving interface as described in claim any one of 1-3,
It does not wherein include brake fluid.
8. energy saving wear-resistant lubricating oil is used for motorcycle, automobile, steamer, civil aircraft, machine as described in claim any one of 1-3
Moving interface in equipment.