CN106280840A - Anti-corrosion of metal layer - Google Patents
Anti-corrosion of metal layer Download PDFInfo
- Publication number
- CN106280840A CN106280840A CN201610714109.0A CN201610714109A CN106280840A CN 106280840 A CN106280840 A CN 106280840A CN 201610714109 A CN201610714109 A CN 201610714109A CN 106280840 A CN106280840 A CN 106280840A
- Authority
- CN
- China
- Prior art keywords
- corrosion
- methyl
- metal layer
- oxopentyl
- poly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-corrosion of metal layer, it is made up of the composition of following weight parts: poly-N-[2-(2-methyl-4-oxopentyl) 20 32, amino resins 8 10, glycerol 34,2 methyl 1,3 propylene glycol 24, ethylenediamine tetramethylene fork Alendronate 23, alkoxide nonyl phenol acrylate 59, firming agent 28, levelling agent 3.5 5.The invention have the advantages that anticorrosive coat is to high comprehensive performances such as matrix adhesive force, anti-corrosive properties, adhesive force; it is entirely capable of substituting sandblasting, the Pretreatment Technology Before Finishing of ball blast; the most pretreated steel surface got rusty is provided permanent efficient protection; significantly extend the service life of anticorrosion finish paint, and corrosion-proof coating process (can with the brush key to exercises coat) is simpler, efficient, economy, environmental protection.
Description
Technical field
The present invention relates to technical field of coatings, especially a kind of anti-corrosion of metal layer.
Background technology
Coating is to be coated in be protected or decorated body surface, and can form the thinnest of firm attachment with coated article
Film, it is common that based on resin or oil or emulsion, adds or without pigment, filler, adds corresponding additive, use organic solvent
Or the thick liquid that water is formulated.China's more authoritative " coating process " book of coating circle is defined such that " coating is
A kind of material, this material can be coated in object surface by different construction technologies, and formation adhesion is firm, it is certain strong to have
Degree, continuous print solid film.The film common name film so formed, also known as paint film or coating."
Within 2012, Coating Industry in Our Country realizes more than 1858 scales of the gross output value 2729.76 hundred million yuan, increases by 7.5% on a year-on-year basis, and coating produces
Amount creates the highest again 12,720,000 tons, and China is still the Coating Market that the growth generally acknowledged in the whole world is on the largest scale.But it is 2012, right by country
Real Estate Regulation affects, and China's Coating Market feels more pressure, cost increase, dog-eat-dog, recessed market, industry environmental protection upgrading.
Being continued descending impact by macroeconomic, Coating Market is cold incomparable, under huge cost pressure, and paint industry structure liter
Level, competitive advantage is made in enterprise's high-efficiency and low-cost running becomes problem demanding prompt solution.
Summary of the invention
The present invention is directed to the deficiencies in the prior art, propose a kind of anti-corrosion of metal layer, form ingenious, favorable anti-corrosion effect.
In order to realize foregoing invention purpose, the present invention provides techniques below scheme: a kind of anti-corrosion of metal layer, by following weight
Part composition constitute: poly-N-[2-(2-methyl-4-oxopentyl) 20-32, amino resins 8-10, glycerol 3-4,2-methyl isophthalic acid, 3-the third two
Alcohol 2-4, ethylenediamine tetramethylene fork Alendronate 2-3, alkoxide nonyl phenol acrylate 5-9, firming agent 2-8, levelling agent
3.5-5。
Further, the weight portion of each composition is: poly-N-[2-(2-methyl-4-oxopentyl) 26, amino resins 9, glycerol 3.4,2-
Methyl isophthalic acid, 3-propylene glycol 3, ethylenediamine tetramethylene fork Alendronate 2.3, alkoxide nonyl phenol acrylate 7, firming agent 5,
Levelling agent 4.6.
Compared with prior art, the invention have the advantages that anticorrosive coat is to matrix adhesive force, anti-corrosive properties, adhesive force etc.
High comprehensive performance, is entirely capable of substituting sandblasting, the Pretreatment Technology Before Finishing of ball blast, to the most pretreated iron and steel got rusty
Surface with durable is protected efficiently, significantly extends the service life of anticorrosion finish paint, and corrosion-proof coating process (
Can coat with the brush key to exercises) simpler, efficient, economy, environmental protection.
Detailed description of the invention
Describing the present invention below in conjunction with embodiment, the description of this part is only exemplary and explanatory, no
Reply protection scope of the present invention has any restriction effect.
Embodiment 1
A kind of anti-corrosion of metal layer, is made up of the composition of following weight parts: poly-N-[2-(2-methyl-4-oxopentyl) 26, amino resins 9, glycerol
3.4,2-methyl isophthalic acid, 3-propylene glycol 3, ethylenediamine tetramethylene are pitched Alendronate 2.3, alkoxide nonyl phenol acrylate 7, are consolidated
Agent 5, levelling agent 4.6.
Embodiment 2
A kind of anti-corrosion of metal layer, is made up of the composition of following weight parts: poly-N-[2-(2-methyl-4-oxopentyl) 20, amino resins 10, the third three
Alcohol 3,2-methyl isophthalic acid, 3-propylene glycol 4, ethylenediamine tetramethylene fork Alendronate 2, alkoxide nonyl phenol acrylate 9, solidification
Agent 2, levelling agent 5.
Embodiment 3
A kind of anti-corrosion of metal layer, is made up of the composition of following weight parts: poly-N-[2-(2-methyl-4-oxopentyl) 32, amino resins 8, the third three
Alcohol 4,2-methyl isophthalic acid, 3-propylene glycol 2, ethylenediamine tetramethylene fork Alendronate 3, alkoxide nonyl phenol acrylate 5, solidification
Agent 8, levelling agent 3.5.
Concrete technical specification is shown in Table:
The above is only the preferred embodiment of the present invention, it is noted that come for those skilled in the art
Saying, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications also should be regarded as
Protection scope of the present invention.
Claims (2)
1. an anti-corrosion of metal layer, it is characterised in that: it is made up of the composition of following weight parts: poly-N-[2-(2-methyl-4-oxopentyl) 20-32,
Amino resins 8-10, glycerol 3-4,2-methyl isophthalic acid, 3-propylene glycol 2-4, ethylenediamine tetramethylene fork Alendronate 2-3, alcoxyl
Change nonyl phenol acrylate 5-9, firming agent 2-8, levelling agent 3.5-5.
2. anti-corrosion of metal layer as claimed in claim 1, it is characterised in that: the weight portion of each composition is: poly-N-[2-(2-methyl-4-oxopentyl)
26, amino resins 9, glycerol 3.4,2-methyl isophthalic acid, 3-propylene glycol 3, ethylenediamine tetramethylene fork Alendronate 2.3, alkoxide
Nonyl phenol acrylate 7, firming agent 5, levelling agent 4.6.