CN106280805A - A kind of preparation technology primed in one-component thermoplastic acrylic - Google Patents
A kind of preparation technology primed in one-component thermoplastic acrylic Download PDFInfo
- Publication number
- CN106280805A CN106280805A CN201610743383.0A CN201610743383A CN106280805A CN 106280805 A CN106280805 A CN 106280805A CN 201610743383 A CN201610743383 A CN 201610743383A CN 106280805 A CN106280805 A CN 106280805A
- Authority
- CN
- China
- Prior art keywords
- butyl acetate
- efka
- thermoplastic acrylic
- levelling agent
- light stabilizers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the preparation technology primed in a kind of one-component thermoplastic acrylic, comprise the steps: A, select dispersion cylinder;B, successively input thermoplastic acrylic resin 72%~81.75%, 15% polyamide wax slurry 2%~3%, Dispers610s dispersant 0.5%~0.2%, EFKA 3600 levelling agent 0.05%~0.2%, EFKA 3033 levelling agent 0.1%~0.3%, BYK 066N defoamer 0.1%~0.3%, trimethylbenzene 3%~5%;C, startup dispersion machine, 600~800r/min dispersions 5 minutes;D, under the rotating speed of 600~800r/min, add zinc stearate 2%~3.5%, with n-butyl acetate 0.5% cleaning cylinder limit, and shovel dynamic cylinder limit;E, be uniformly dispersed to fineness≤35um with 1200~1500r/min, shut down censorship fineness qualified after, add MIBK 1%~3%, 1130 light stabilizer 0.5%~1%, 292 light stabilizers 0.5%~1%, n-butyl acetates 7.5%~10%;F, startup dispersion machine, 800~1200r/min disperse 10 minutes, release at seam and refund in dispersion cylinder no less than 2KG paint, censorship after being uniformly dispersed, and addition n-butyl acetate 0.5%~1%, tune are coated with 4 glasss of viscosity: 20s~30s/25 DEG C, prime in preparing.
Description
Technical field
The present invention relates to the preparation technology primed in a kind of one-component thermoplastic acrylic.
Background technology
Outdoor woodenware lacquer is by three layers, i.e. seal coat, halfway priming paint and finish paint is constituted, and seal coat has permeability
By force, the feature such as closed performance is excellent, be attached directly to substrate surface, substrate strength can be improved, priming paint is used for strengthening finish paint halfway
Bonding force so that the more plentiful exquisiteness of finish paint and round and smooth, the most also there is corrosion-resisting function, finish paint is the final painting of application
Layer, the lacquer painting effect presented after finishing or mopping is presented by finish paint.
But prime in currently used, it is contemplated that being applied on outdoor woodenware, its coating hardness is not high enough, wear-resisting resistance to
Draw poor-performing, therefore, it is necessary to improve and optimize.
Summary of the invention
In order to overcome above-mentioned the deficiencies in the prior art, the present invention provides the one-component that a kind of hardness scratch-proofness high, wear-resisting is good
The preparation technology primed in thermoplastic acrylic.
The technical solution adopted for the present invention to solve the technical problems is:
The preparation technology primed in a kind of one-component thermoplastic acrylic, comprises the steps:
A, select clean standard compliant dispersion cylinder;
B, successively input thermoplastic acrylic resin 72%~81.75%, 15% polyamide wax slurry 2%~3%, Dispers610s divide
Powder 0.5%~0.2%, EFKA-3600 levelling agent 0.05%~0.2%, EFKA-3033 levelling agent 0.1%~0.3%, BYK-066N
Defoamer 0.1%~0.3%, trimethylbenzene 3%~5%;
C, startup dispersion machine, 600~800r/min dispersions 5 minutes;
D, under the rotating speed of 600~800r/min, add zinc stearate 2%~3.5%, with n-butyl acetate 0.5% cleaning cylinder limit,
And shovel dynamic cylinder limit, it is ensured that not bound edge, not conglomeration;
E, be uniformly dispersed to fineness≤35um with 1200~1500r/min, shut down censorship fineness qualified after, add MIBK 1%~
3%, 1130 light stabilizer 0.5%~1%, 292 light stabilizers 0.5%~1%, n-butyl acetate 7.5%~10%;
F, startup dispersion machine, 800~1200r/min dispersions 10 minutes, release at seam and refund dispersion no less than 2KG paint
In cylinder, censorship after being uniformly dispersed, add n-butyl acetate 0.5%~1%, adjust-4 glasss of viscosity of painting: 20s~30s/25 DEG C, in preparing
Prime.
Further, according to mass ratio, composition is as follows:
Thermoplastic acrylic resin 72%
15% polyamide wax slurry 3%
Dispers610s dispersant 0.2%
EFKA-360 levelling agent 0.2%
EFKA-3033 levelling agent 0.3%
BYK-066N defoamer 0.3%
Trimethylbenzene 5%
Zinc stearate 3.5%
N-butyl acetate 0.5%
MIBK 3%
1130 light stabilizer light stabilizers 1%
292 light stabilizers 1%
N-butyl acetate 10%.
Further, according to mass ratio, composition is as follows:
Thermoplastic acrylic resin 81.75%
15% polyamide wax slurry 2%
Dispers610s dispersant 0.5%
EFKA-360 levelling agent 0.05%
EFKA-3033 levelling agent 0.1%
BYK-066N defoamer 0.1%
Trimethylbenzene 2%
Zinc stearate 2%
N-butyl acetate 0.5%
MIBK 1%
1130 light stabilizer light stabilizers 0.5%
292 light stabilizers 0.5%
N-butyl acetate 9%.
Further, according to mass ratio, composition is as follows:
Thermoplastic acrylic resin 77.5%
15% polyamide wax slurry 2.5%
Dispers610s dispersant 0.4%
EFKA-360 levelling agent 0.1%
EFKA-3033 levelling agent 0.2%
BYK-066N defoamer 0.2%
Trimethylbenzene 4%
Zinc stearate 3%
N-butyl acetate 0.5%
MIBK 2%
1130 light stabilizer light stabilizers 0.8%
292 light stabilizers 0.8%
N-butyl acetate 8%.
The invention has the beneficial effects as follows: use above-mentioned technique to prime in preparing, be uniformly dispersed to fineness≤35um,
It is coated with-4 glasss of viscosity: 20s~30s/25 DEG C, have the advantages that hardness scratch-proofness high, wear-resisting is good, it is possible to preferably meet outdoor woodenware
Use.
Detailed description of the invention
Below the present invention is described in further detail.
The preparation technology primed in a kind of one-component thermoplastic acrylic of the present invention, comprises the steps:
A, select clean standard compliant dispersion cylinder;
B, successively input thermoplastic acrylic resin 72%~81.75%, 15% polyamide wax slurry 2%~3%, Dispers610s divide
Powder 0.5%~0.2%, EFKA-3600 levelling agent 0.05%~0.2%, EFKA-3033 levelling agent 0.1%~0.3%, BYK-066N
Defoamer 0.1%~0.3%, trimethylbenzene 3%~5%;
C, startup dispersion machine, 600~800r/min dispersions 5 minutes;
D, under the rotating speed of 600~800r/min, add zinc stearate 2%~3.5%, with n-butyl acetate 0.5% cleaning cylinder limit,
And shovel dynamic cylinder limit, it is ensured that not bound edge, not conglomeration;
E, be uniformly dispersed to fineness≤35um with 1200~1500r/min, shut down censorship fineness qualified after, add MIBK 1%~
3%, 1130 light stabilizer 0.5%~1%, 292 light stabilizers 0.5%~1%, n-butyl acetate 7.5%~10%;
F, startup dispersion machine, 800~1200r/min dispersions 10 minutes, release at seam and refund dispersion no less than 2KG paint
In cylinder, censorship after being uniformly dispersed, add n-butyl acetate 0.5%~1%, adjust-4 glasss of viscosity of painting: 20s~30s/25 DEG C, in preparing
Prime.
Embodiment 1:
According to mass ratio, composition is as follows:
Thermoplastic acrylic resin 72%
15% polyamide wax slurry 3%
Dispers610s dispersant 0.2%
EFKA-360 levelling agent 0.2%
EFKA-3033 levelling agent 0.3%
BYK-066N defoamer 0.3%
Trimethylbenzene 5%
Zinc stearate 3.5%
N-butyl acetate 0.5%
MIBK 3%
1130 light stabilizer light stabilizers 1%
292 light stabilizers 1%
N-butyl acetate 10%.
In step C, rotating speed is 600r/min, and in step D, rotating speed is 800r/min, and in step E, rotating speed is 1500 r/
Min, in step F, rotating speed is 1200r/min, adjusts and is coated with-4 glasss of viscosity: 30s/25 DEG C.
Embodiment 2:
According to mass ratio, composition is as follows:
Thermoplastic acrylic resin 81.75%
15% polyamide wax slurry 2%
Dispers610s dispersant 0.5%
EFKA-360 levelling agent 0.05%
EFKA-3033 levelling agent 0.1%
BYK-066N defoamer 0.1%
Trimethylbenzene 2%
Zinc stearate 2%
N-butyl acetate 0.5%
MIBK 1%
1130 light stabilizer light stabilizers 0.5%
292 light stabilizers 0.5%
N-butyl acetate 9%.
In step C, rotating speed is 800r/min, and in step D, rotating speed is 600r/min, and in step E, rotating speed is 1200 r/
Min, in step F, rotating speed is, 800r/min, adjusts and is coated with-4 glasss of viscosity: 20s/25 DEG C.
Embodiment 3:
According to mass ratio, composition is as follows:
Thermoplastic acrylic resin 77.5%
15% polyamide wax slurry 2.5%
Dispers610s dispersant 0.4%
EFKA-360 levelling agent 0.1%
EFKA-3033 levelling agent 0.2%
BYK-066N defoamer 0.2%
Trimethylbenzene 4%
Zinc stearate 3%
N-butyl acetate 0.5%
MIBK 2%
1130 light stabilizer light stabilizers 0.8%
292 light stabilizers 0.8%
N-butyl acetate 8%.
In step C, rotating speed is 700r/min, and in step D, rotating speed is 700r/min, and in step E, rotating speed is 1400 r/
Min, in step F, rotating speed is 1000r/min, adjusts and is coated with-4 glasss of viscosity: 25s/25 DEG C.
Use above-mentioned technique to prime in preparing, be uniformly dispersed to fineness≤35um, be coated with-4 glasss of viscosity: 20s~30s/
25 DEG C, have the advantages that hardness scratch-proofness high, wear-resisting is good, it is possible to preferably meet the use of outdoor woodenware.
The above, the simply better embodiment of the present invention, but the present invention is not limited to above-described embodiment, as long as
It reaches the technique effect of the present invention with any same or similar means, all should fall under the scope of the present invention.
Claims (4)
1. the preparation technology primed in an one-component thermoplastic acrylic, it is characterised in that comprise the steps:
A, select clean standard compliant dispersion cylinder;
B, successively input thermoplastic acrylic resin 72%~81.75%, 15% polyamide wax slurry 2%~3%, Dispers610s divide
Powder 0.5%~0.2%, EFKA-3600 levelling agent 0.05%~0.2%, EFKA-3033 levelling agent 0.1%~0.3%, BYK-066N
Defoamer 0.1%~0.3%, trimethylbenzene 3%~5%;
C, startup dispersion machine, 600~800r/min dispersions 5 minutes;
D, under the rotating speed of 600~800r/min, add zinc stearate 2%~3.5%, with n-butyl acetate 0.5% cleaning cylinder limit,
And shovel dynamic cylinder limit, it is ensured that not bound edge, not conglomeration;
E, be uniformly dispersed to fineness≤35um with 1200~1500r/min, shut down censorship fineness qualified after, add MIBK 1%~
3%, 1130 light stabilizer 0.5%~1%, 292 light stabilizers 0.5%~1%, n-butyl acetate 7.5%~10%;
F, startup dispersion machine, 800~1200r/min dispersions 10 minutes, release at seam and refund dispersion no less than 2KG paint
In cylinder, censorship after being uniformly dispersed, add n-butyl acetate 0.5%~1%, adjust-4 glasss of viscosity of painting: 20s~30s/25 DEG C, in preparing
Prime.
The preparation technology primed in a kind of one-component thermoplastic acrylic the most according to claim 1, it is characterised in that:
According to mass ratio, composition is as follows:
Thermoplastic acrylic resin 72%
15% polyamide wax slurry 3%
Dispers610s dispersant 0.2%
EFKA-360 levelling agent 0.2%
EFKA-3033 levelling agent 0.3%
BYK-066N defoamer 0.3%
Trimethylbenzene 5%
Zinc stearate 3.5%
N-butyl acetate 0.5%
MIBK 3%
1130 light stabilizer light stabilizers 1%
292 light stabilizers 1%
N-butyl acetate 10%.
The preparation technology primed in a kind of one-component thermoplastic acrylic the most according to claim 1, it is characterised in that:
According to mass ratio, composition is as follows:
Thermoplastic acrylic resin 81.75%
15% polyamide wax slurry 2%
Dispers610s dispersant 0.5%
EFKA-360 levelling agent 0.05%
EFKA-3033 levelling agent 0.1%
BYK-066N defoamer 0.1%
Trimethylbenzene 2%
Zinc stearate 2%
N-butyl acetate 0.5%
MIBK 1%
1130 light stabilizer light stabilizers 0.5%
292 light stabilizers 0.5%
N-butyl acetate 9%.
The preparation technology primed in a kind of one-component thermoplastic acrylic the most according to claim 1, it is characterised in that:
According to mass ratio, composition is as follows:
Thermoplastic acrylic resin 77.5%
15% polyamide wax slurry 2.5%
Dispers610s dispersant 0.4%
EFKA-360 levelling agent 0.1%
EFKA-3033 levelling agent 0.2%
BYK-066N defoamer 0.2%
Trimethylbenzene 4%
Zinc stearate 3%
N-butyl acetate 0.5%
MIBK 2%
1130 light stabilizer light stabilizers 0.8%
292 light stabilizers 0.8%
N-butyl acetate 8%.