CN106280702A - A kind of noble metal preparation of silk screen printing - Google Patents
A kind of noble metal preparation of silk screen printing Download PDFInfo
- Publication number
- CN106280702A CN106280702A CN201610668957.2A CN201610668957A CN106280702A CN 106280702 A CN106280702 A CN 106280702A CN 201610668957 A CN201610668957 A CN 201610668957A CN 106280702 A CN106280702 A CN 106280702A
- Authority
- CN
- China
- Prior art keywords
- noble metal
- screen printing
- silk screen
- preparation
- metal preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the noble metal preparation of a kind of silk screen printing, it carries out noble metal decoration at substrate surface, and described base material includes pottery, glass or porcelain, and described decorating method uses direct silk screen printing or indirect screen printing.The invention provides long shelf-life, adhesive force is good, and has the noble metal preparation of cracking resistance and good rheological performance, solves the technological deficiency of existing existence.
Description
Technical field
The invention belongs to printing technology, be specifically related to the noble metal preparation of a kind of silk screen printing.
Background technology
For producing noble metal decoration on decoration, the base material that can fire, typically contain one or more gold, silver, rhodium,
Bismuth, aluminum, silicon and other base metal resinate, its printing quality is that the adhesive system consisted of resin compound improves
's.Adhesive system has the biggest relation, current binding agent shelf-life to shelf-life and the printing quality of noble metal preparation
Too short, easily become viscous or thinning.
Summary of the invention
It is an object of the invention to provide a kind of long shelf-life, adhesive force is good, and has cracking resistance and good rheological performance
Noble metal preparation, solves the technological deficiency of existing existence.
The noble metal preparation of a kind of silk screen printing, carries out noble metal decoration at substrate surface, described base material include pottery,
Glass or porcelain, described decorating method uses direct silk screen printing or indirect screen printing.
Described decoration formula includes precious metal material, binding agent, thixotropic agent, solvent and defoamer, and its proportioning is as follows: your gold
Belong to material 22-30 part, binding agent 20-45 part, thixotropic agent 0.1-3 part, solvent 30-45 part and defoamer 0.5-2 part.
Described precious metal material uses mercaptan gold/palladium/platinum or noble metal organic compound.
Described noble metal organic compound employing industrialization organic precious metal compounds, employing isooctyl acid silver/rhodium/bismuth/chromium/
Aluminum/silicon.
Described binding agent uses plasticizing methacrylic resin.
Described thixotropic agent is the mixture of castor oil hydrogenated, polyamide wax, polyureas.
The regulation ratio of described thixotropic agent is castor oil hydrogenated: polyamide wax: polyureas=1:0.3-0.5:0.1-0.4.
Described solvent uses Ketohexamethylene, naphthane or ketone.
Its preparation process is as follows:
Step 1, weighs raw material on request；
Step 2, heats mix and blend by binding agent, precious metal material and solvent, until stirring, heating-up temperature is 60-70
DEG C, mixing speed is 1000-2000r/min, and mixing time is 10-15min；
Step 3, by adding thixotropic agent under the conditions of constant temperature 60 DEG C, naturally cools to room temperature after stirring, mixing speed is 1500-
2000r/min, mixing time is 5-9min；
Step 4, i.e. can get final products after stirring at normal temperature 1-2min.
Compared with prior art, the method have the advantages that
1, preparation method of the present invention can obtain by being directly or indirectly printed onto on glass, pottery or the porcelain base material that can fire
Decorative effect is honorable, without the noble metal decoration of cracking.
2, the present invention provides a kind of long shelf-life, and adhesive force is good, and has the noble metal of cracking resistance and good rheological performance
Preparation, solves the technological deficiency of existing existence.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described further:
Embodiment 1
The noble metal preparation of a kind of silk screen printing, carries out noble metal decoration at substrate surface, and described base material includes pottery, described
Decorating method uses direct silk screen printing.
Described decoration formula includes precious metal material, binding agent, thixotropic agent, solvent and defoamer, and its proportioning is as follows: your gold
Belong to material 22 parts, binding agent 20 parts, thixotropic agent 0.1 part, solvent 30 parts and defoamer 0.5 part.
Described precious metal material uses mercaptan
Described binding agent uses plasticizing methacrylic resin.
Described thixotropic agent is the mixture of castor oil hydrogenated, polyamide wax, polyureas.
The regulation ratio of described thixotropic agent is castor oil hydrogenated: polyamide wax: polyureas=1:0.3:0.1.
Described solvent uses Ketohexamethylene.
Its preparation process is as follows:
Step 1, weighs raw material on request；
Step 2, heats mix and blend by binding agent, precious metal material and solvent, until stirring, heating-up temperature is 60 DEG C,
Mixing speed is 1000r/min, and mixing time is 10min；
Step 3, by adding thixotropic agent under the conditions of constant temperature 60 DEG C, naturally cools to room temperature after stirring, mixing speed is
1500r/min, mixing time is 5min；
Step 4, i.e. can get final products after stirring at normal temperature 1min.
Embodiment 2
The noble metal preparation of a kind of silk screen printing, carries out noble metal decoration at substrate surface, and described base material includes glass, described
Decorating method uses direct silk screen printing or indirect screen printing.
Described decoration formula includes precious metal material, binding agent, thixotropic agent, solvent and defoamer, and its proportioning is as follows: your gold
Belong to material 30 parts, binding agent 45 parts, thixotropic agent 3 parts, solvent 45 parts and defoamer 2 parts.
Described precious metal material uses mercaptan palladium.
Described binding agent uses plasticizing methacrylic resin.
Described thixotropic agent is the mixture of castor oil hydrogenated, polyamide wax, polyureas.
The regulation ratio of described thixotropic agent is castor oil hydrogenated: polyamide wax: polyureas=1:0.5:0.4.
Described solvent uses naphthane.
Its preparation process is as follows:
Step 1, weighs raw material on request；
Step 2, heats mix and blend by binding agent, precious metal material and solvent, until stirring, heating-up temperature is 70 DEG C,
Mixing speed is 2000r/min, and mixing time is 15min；
Step 3, by adding thixotropic agent under the conditions of constant temperature 60 DEG C, naturally cools to room temperature after stirring, mixing speed is
2000r/min, mixing time is 9min；
Step 4, i.e. can get final products after stirring at normal temperature 2min.
Embodiment 3
The noble metal preparation of a kind of silk screen printing, carries out noble metal decoration at substrate surface, and described base material includes pottery, glass
Or porcelain, described decorating method uses direct silk screen printing or indirect screen printing.
Described decoration formula includes precious metal material, binding agent, thixotropic agent, solvent and defoamer, and its proportioning is as follows: your gold
Belong to material 26 parts, binding agent 37 parts, thixotropic agent 1.5 parts, solvent 28 parts and defoamer 1.4 parts.
Described noble metal organic compound uses industrialization organic precious metal compounds, uses isooctyl acid silver.
Described binding agent uses plasticizing methacrylic resin.
Described thixotropic agent is the mixture of castor oil hydrogenated, polyamide wax, polyureas.
The regulation ratio of described thixotropic agent is castor oil hydrogenated: polyamide wax: polyureas=1:0.4:0.3.
Acetone adopted by described solvent.
Its preparation process is as follows:
Step 1, weighs raw material on request；
Step 2, heats mix and blend by binding agent, precious metal material and solvent, until stirring, heating-up temperature is 65 DEG C,
Mixing speed is 1500r/min, and mixing time is 12min；
Step 3, by adding thixotropic agent under the conditions of constant temperature 60 DEG C, naturally cools to room temperature after stirring, mixing speed is
1800r/min, mixing time is 7min；
Step 4, i.e. can get final products after stirring at normal temperature 1.5min.
The foregoing is only one embodiment of the invention, be not limiting as the present invention, all employing equivalents or equivalent transformation
The technical scheme that obtained of mode, all fall within protection scope of the present invention.
Claims (9)
1. the noble metal preparation of a silk screen printing, it is characterised in that: it carries out noble metal decoration, described base at substrate surface
Material includes pottery, glass or porcelain, and described decorating method uses direct silk screen printing or indirect screen printing.
2. according to the noble metal preparation of a kind of silk screen printing described in claims 1, it is characterised in that described decoration formula
Including precious metal material, binding agent, thixotropic agent, solvent and defoamer, its proportioning is as follows: precious metal material 22-30 part, binding agent
20-45 part, thixotropic agent 0.1-3 part, solvent 30-45 part and defoamer 0.5-2 part.
3. according to the noble metal preparation of a kind of silk screen printing described in claims 2, it is characterised in that described noble metal material
Material uses mercaptan gold/palladium/platinum or noble metal organic compound.
4. according to the noble metal preparation of a kind of silk screen printing described in claims 3, it is characterised in that described noble metal has
Machine compound uses industrialization organic precious metal compounds, uses isooctyl acid silver/rhodium/bismuth/chromium/aluminum/silicon.
5. according to the noble metal preparation of a kind of silk screen printing described in claims 2, it is characterised in that described binding agent is adopted
With plasticizing methacrylic resin.
6. according to the noble metal preparation of a kind of silk screen printing described in claims 2, it is characterised in that described thixotropic agent is
Castor oil hydrogenated, polyamide wax, the mixture of polyureas.
7. according to the noble metal preparation of a kind of silk screen printing described in claims 6, it is characterised in that described thixotropic agent
Regulation ratio is castor oil hydrogenated: polyamide wax: polyureas=1:0.3-0.5:0.1-0.4.
8. according to the noble metal preparation of a kind of silk screen printing described in claims 2, it is characterised in that described solvent uses
Ketohexamethylene, naphthane or ketone.
9. according to the noble metal preparation of a kind of silk screen printing described in claims 2, it is characterised in that its preparation process is such as
Under:
Step 1, weighs raw material on request；
Step 2, heats mix and blend by binding agent, precious metal material and solvent, until stirring, heating-up temperature is 60-70
DEG C, mixing speed is 1000-2000r/min, and mixing time is 10-15min；
Step 3, by adding thixotropic agent under the conditions of constant temperature 60 DEG C, naturally cools to room temperature after stirring, mixing speed is 1500-
2000r/min, mixing time is 5-9min；
Step 4, i.e. can get final products after stirring at normal temperature 1-2min.