CN106280208A - A kind of lead-acid accumulator aging resistance moulds shell preparation method - Google Patents
A kind of lead-acid accumulator aging resistance moulds shell preparation method Download PDFInfo
- Publication number
- CN106280208A CN106280208A CN201610631446.3A CN201610631446A CN106280208A CN 106280208 A CN106280208 A CN 106280208A CN 201610631446 A CN201610631446 A CN 201610631446A CN 106280208 A CN106280208 A CN 106280208A
- Authority
- CN
- China
- Prior art keywords
- lead
- injection
- acid accumulator
- aging resistance
- aluminium hydroxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of lead-acid accumulator aging resistance and mould shell preparation method, it comprises the following steps: (1) prepares surface modification bamboo fibre;(2) modified aluminium hydroxide is prepared;(3) modified zeolite powder is prepared;(4) injection mo(u)lding.The present invention is to moulding on the basis of shell material formula is optimized improvement, optimize injection-mold process parameter simultaneously, using the direct injection molding process of injection machine to obtain housing, processing step is simple, workable, energy consumption is low, production efficiency is high, is suitable for industrialized production, and prepared girdle of moulding is protected, production cost is low, fire-retardant and mechanical performance is excellent with weatherability.
Description
Technical field
The present invention relates to lead-acid accumulator manufacturing technology field, especially relate to a kind of lead-acid accumulator aging resistance and mould shell system
Preparation Method.
Background technology
Lead-acid accumulator through the development in more than 150 years, technology maturation, with low cost, excellent performance, be widely used in handing over
Numerous economic fields such as logical, communication, electric power, military affairs, navigation, aviation, become the indispensable important electrochmical power source of one.Electricity
Pond shell is as one of lead-acid accumulator three-major-items, and it is used for carrying all of components such as pole plate, dividing plate, electrolyte, it is desirable to
There is preferable resistance to acids and bases, high intensity and good processability.
Current lead-acid accumulator housing generally obtains through injection mo(u)lding with ABS resin for primary raw material, but conventional ABS
, there is certain potential safety hazard, and weather resistance be poor with mechanical performance in resins fire retardant poor-performing, in storage, machine-shaping
, there are the problems such as mechanical property deterioration, the hardening embrittlement of material in journey and recurring structure change in time during using, while by
Hygroscopicity in ABS resin and the sensitivity to moisture are relatively big, are difficult to the driest to it, the most easily cause product surface to go out
Existing spray filamentary silver stricture of vagina phenomenon, and at present for ensureing that ABS resin can be the driest, generally use improve baking temperature or dry time
Between mode, so or cause energy consumption high, or cause production efficiency to be substantially reduced.
Summary of the invention
The present invention is to solve the problems referred to above existing for the lead-acid accumulator of prior art, it is provided that a kind of technique step
Rapid simple, workable, energy consumption is low, and production efficiency is high, and the lead-acid accumulator aging resistance of applicable industrialized production is moulded shell and prepared
Method, prepared girdle of moulding protects, and production cost is low, fire-retardant and mechanical performance is excellent with weatherability.
To achieve these goals, the present invention is by the following technical solutions:
A kind of lead-acid accumulator aging resistance of the present invention moulds shell preparation method, comprises the following steps:
(1) prepare surface modification bamboo fibre: added by bamboo fibre in chlorosulfonic acid, be heated to 80 ~ 100 DEG C of swelling 1 ~ 3h, cooling, mistake
Filter, filtrate is washed with water to pH be neutrality, vacuum drying, add and wetting agent carried out soak after 30 ~ 60min in 95 ~ 105
Dry at DEG C, obtain surface modification bamboo fibre, stand-by.Chlorosulfonic acid can make bamboo fibre boundling the most swelling so that it is dispersion, is conducive to
Improve its dispersibility, it is simple to wetting agent is abundant, homogeneous immersion;Wetting agent can make the bamboo fibre surface after drying can form one layer
Protecting film, it is to avoid material damages when injection mo(u)lding, ensures the reservation length of bamboo fibre as far as possible, it addition, the bamboo of soaking mistake is fine
Dimension table surface roughness also becomes big, and forms more chemical bond between resin, increases the coefficient of friction between resin, so that
Interface shear strength increases, and improves toughness.
(2) modified aluminium hydroxide is prepared: be first dispersed in water by aluminium hydroxide and be configured to dividing of mass percentage concentration 5 ~ 10%
Dissipate liquid, after being heated with stirring to 70 ~ 80 DEG C, add dispersion liquid adds by the tripolycyanamide for aluminium hydroxide quality 10 ~ 15% and mix all
Even, obtain reactant liquor;Press the tripolycyanamide amount with formaldehyde material again than 1:2 ~ 3, formalin is dropped to constant temperature in reactant liquor anti-
Answer 4 ~ 8h, reactant is filtered, washing, dried, obtain modified aluminium hydroxide, stand-by.Can by tripolycyanamide and formaldehyde crosslinking
Form thin film in surface of aluminum hydroxide, the heat stability of aluminium hydroxide can be improved, more can make aluminium hydroxide and resin base
Interface bond strength between body is greatly improved, and dispersive property is the most excellent.
(3) modified zeolite powder is prepared: by zeolite powder in 300 ~ 500 DEG C of temperature lower calcination 30 ~ 60min, after cooling, be dipped in matter
Measure supersound process 30 ~ 40min in the salpeter solution that concentration is 5 ~ 10%, zeolite powder is placed in after filtration ultrasonic place in modifying agent again
Reason 30 ~ 60min, at 70 ~ 80 DEG C, drying modified zeolite powder, stand-by.
(4) injection mo(u)lding: by 40 ~ 50 parts of ABS resin, 20 ~ 30 parts of polyvinyl chloride resins, 5 ~ 10 parts of surface modification bamboo fibres, 5 ~ 10
Part modified aluminium hydroxide, 5 ~ 10 parts of chlorinated polyethylenees, 1 ~ 3 part of lubricant, 3 ~ 5 parts of modified zeolite powders, 0.5 ~ 1 part of antioxidant AT-
After the weight of 1078,0.5 ~ 1 part of dibutyltin dilaurate of 10,0.1 ~ 0.5 part of antioxidant weighs each component, will
ABS resin and polyvinyl chloride resin are placed in dehydrated alcohol and soak and stir 5 ~ 10min, dry, and will add note after each component mix homogeneously
Molding machine injection mo(u)lding, after through checking the qualified lead-acid accumulator aging resistance that i.e. obtains to mould shell.The formula moulding shell material is entered by the present invention
Row Optimal improvements, adds quantitative polyvinyl chloride resin in ABS resin, by both material synergism, and be aided with antioxidant AT-10,
Antioxidant 1078 and the resistance to thermal oxidation stability system of dibutyltin dilaurate composition so that the weatherability moulding shell obtains significantly
Improve, the problem efficiently solving the jaundice that becomes fragile poor, the most aging of housing weather resistance, and the mechanicalness of material can be improved simultaneously
Can, dibutyltin dilaurate is except as optothermal stabilizer, making material have excellent light stability and the work of the transparency
With outward, its another effect is the melt viscosity that can improve whole material system, i.e. improves processing fluidity, solves because adding surface
Cause integral material processing fluidity to reduce after modified bamboo fiber, aluminium hydroxide and modified zeolite powder to be unfavorable for moulding asking of casing forming
Topic;Aluminium hydroxide is a kind of cheap fire retardant, extensively applies in fire proofing, but it needs bigger addition (logical
Often need more than 20%) just there is fire retardation, itself and ABS resin, polyvinyl chloride resin poor compatibility simultaneously, and dispersibility in the material
Difference, the present invention uses modified aluminium hydroxide as fire retardant, excellent fireproof performance, good thermal stability, and good dispersion, with
Interfacial bonding property between material system is improved;Use modified zeolite powder can have choosing as fire-retardant accelerator, modified zeolite powder
The absorption selected, through particle, it is possible to being effectively improved the flame retarding efficiency of modified aluminium hydroxide, modified zeolite powder can be as carrier simultaneously
Absorption antioxidant AT-10 and antioxidant 1078, make antioxidant AT-10 and antioxidant 1078 be dispersed among material, and make
It plays a role for a long time, uses modified aluminium hydroxide and modified zeolite powder as flame-retardant system, can greatly reduce modified hydroxide
The usage amount of aluminum, good flame retardation effect;There is the preferable compatibility between surface modification bamboo fibre and resin matrix, resin can be greatly improved
The mechanical performance of matrix and thermostability;ABS resin and polyvinyl chloride resin are placed in dehydrated alcohol by the present invention soak and stir 5 ~
10min is dried, and utilizes the volatile characteristic of ethanol to make the moisture on ABS resin and polyvinyl chloride resin surface fully to remove, thoroughly solves
Easily there is the problem of spray filamentary silver stricture of vagina phenomenon in product surface, easy and simple to handle, and energy consumption is low, is carrying out excellent to moulding shell material formula
Changing on the basis of improving, use the direct injection molding process of injection machine to obtain housing, processing step is simple, workable, raw
Product efficiency is high.
As preferably, in step (1), described wetting agent is made up of the component of following mass percent: 40 ~ 50% polytetrafluoros
Ethylene dispersion emulsion, 0.1 ~ 0.2% quaternary ammonium salt, 0.3 ~ 0.5% polyoxyethylene stearic acid ester, 0.1 ~ 0.3% silane coupler KH-
550,1 ~ 3% nano-silicon nitride, surplus is water.Wetting agent in the present invention is key point, and politef dispersion emulsion is main one-tenth
Membrane, polyoxyethylene stearic acid ester is auxiliary film former, and quaternary ammonium salt is antistatic additive, and silane resin acceptor kh-550 is dispersion, emulsifying
Agent, can make nano-silicon nitride dispersed, and nano-silicon nitride has the heat dispersion of excellence, can improve thermal diffusivity, and can adhere to
The specific surface area of bamboo fibre can be increased in film surface, increase the contact area of bamboo fibre and resin matrix, improve both combinations
Intensity, beneficially raising mould shell mechanical property, it is most important that produce between nano-silicon nitride particle and matrix when moulding shell stress
Micro-crack, absorbable outside energy, nano-silicon nitride plays the effect of stress concentration point simultaneously, makes nano-silicon nitride surrounding resin
Occur big plastic deformation to absorb impact energy, thus reach toughness reinforcing effect, be conducive to improving mechanical performance.
As preferably, in step (3), described modifying agent is made up of the component of following mass percent: 3 ~ 5% polyoxyethylenes
Alkene, 0.1 ~ 0.5% silane resin acceptor kh-550, surplus is water.
As preferably, in step (4), described lubricant is ethylene bis stearamide, magnesium stearate, zinc stearate and poly-second
One or more in alkene wax.
As preferably, in step (4), concretely comprising the following steps of injection mo(u)lding: the injection → molding → pressurize → demoulding → cooling.
As preferably, injection molding material barrel temperature is 220 ~ 230 DEG C;Mould temperature is 50 ~ 60 DEG C;Dwell pressure 75 ~
85MPa, dwell time 5 ~ 7s.
Therefore, there is advantages that
(1) in ABS resin, add quantitative polyvinyl chloride resin, by both material synergism, and be aided with antioxidant AT-10, antioxygen
Agent 1078 and the resistance to thermal oxidation stability system of dibutyltin dilaurate composition so that the weatherability moulding shell is significantly carried
Height, the problem efficiently solving the jaundice that becomes fragile poor, the most aging of housing weather resistance;
(2) with the addition of dibutyltin dilaurate, solve because adding surface modification bamboo fibre, aluminium hydroxide and modified zeolite powder
After cause integral material processing fluidity reduce be unfavorable for moulding casing forming problem;
(3) use modified aluminium hydroxide and modified zeolite powder as flame-retardant system, the use of modified aluminium hydroxide can be greatly reduced
Amount, good flame retardation effect;
(4) to moulding on the basis of shell material formula is optimized improvement, optimize injection-mold process parameter simultaneously, use note
The direct injection molding process of molding machine obtains housing, and workable, energy consumption is low, and production efficiency is high, is suitable for industrialized production, prepares
Girdle of moulding protect, production cost is low, fire-retardant and mechanical performance is excellent with weatherability.
Detailed description of the invention
Below by detailed description of the invention, the present invention will be further described.
Embodiment 1
(1) prepare surface modification bamboo fibre: added by bamboo fibre in chlorosulfonic acid, be heated to 100 DEG C of swelling 3h, cooling, filter, will
It is neutrality that filtrate washes with water to pH, is vacuum dried, and adds and dries at 105 DEG C, i.e. after carrying out in wetting agent soaking 60min
Obtaining surface modification bamboo fibre, stand-by, wherein, wetting agent is made up of the component of following mass percent: 50% politef dispersion
Emulsion, 0.2% quaternary ammonium salt, 0.5% polyoxyethylene stearic acid ester, 0.3% silane resin acceptor kh-550,3% nano-silicon nitride, surplus is
Water;
(2) modified aluminium hydroxide is prepared: first aluminium hydroxide is dispersed in water the dispersion liquid being configured to mass percentage concentration 10%,
After being heated with stirring to 80 DEG C, add dispersion liquid adds by the tripolycyanamide for aluminium hydroxide quality 15% and mix uniformly, obtain reactant liquor;
Press the tripolycyanamide amount with formaldehyde material again than 1:3, formalin is dropped to isothermal reaction 8h in reactant liquor, by reactant mistake
Filter, washing, dried, obtain modified aluminium hydroxide, stand-by;
(3) preparing modified zeolite powder: by zeolite powder in 500 DEG C of temperature lower calcination 60min, being dipped in mass concentration after cooling is 10%
Salpeter solution in supersound process 40min, zeolite powder is placed in supersound process 60min in modifying agent again, after filtration at 80 DEG C
Drying modified zeolite powder, stand-by, modifying agent is made up of the component of following mass percent: 5% polyethylene glycol oxide, 0.5% silicon
Alkane coupling agent KH-550, surplus is water;
(4) injection mo(u)lding: by 50KgABS resin, 30KgPVC resin, 10Kg surface modification bamboo fibre, 10Kg modification hydroxide
Aluminum, 10Kg chlorinated polyethylene, 3Kg lubricant (Tissuemat E), 5Kg modified zeolite powder, 1Kg antioxidant AT-10,0.5Kg antioxygen
Agent 1078, after the weight proportion of 1Kg dibutyltin dilaurate weighs each component, is placed in anhydrous by ABS resin and polyvinyl chloride resin
Ethanol soaks and stirs 10min, dries, after each component mix homogeneously, will add injection machine injection mo(u)lding, after close through inspection
Lattice i.e. obtain lead-acid accumulator aging resistance and mould shell, concretely comprising the following steps of injection mo(u)lding: the injection → molding → pressurize → demoulding → cooling,
Injection molding material barrel temperature is 230 DEG C;Mould temperature is 60 DEG C;Dwell pressure 85MPa, dwell time 7s.
Embodiment 2
(1) prepare surface modification bamboo fibre: added by bamboo fibre in chlorosulfonic acid, be heated to 80 DEG C of swelling 1h, cooling, filter, will
It is neutrality that filtrate washes with water to pH, is vacuum dried, and adds and dries at 95 DEG C, i.e. after carrying out in wetting agent soaking 30min
Obtaining surface modification bamboo fibre, stand-by, wherein, wetting agent is made up of the component of following mass percent: 40% politef dispersion
Emulsion, 0.1% quaternary ammonium salt, 0.3% polyoxyethylene stearic acid ester, 0.1% silane resin acceptor kh-550,1% nano-silicon nitride, surplus is
Water;
(2) modified aluminium hydroxide is prepared: first aluminium hydroxide is dispersed in water the dispersion liquid being configured to mass percentage concentration 5%, stirs
Mix after being heated to 70 DEG C, add dispersion liquid adds by the tripolycyanamide for aluminium hydroxide quality 10% and mix uniformly, obtain reactant liquor;Again
By the amount of tripolycyanamide and formaldehyde material than 1:2, formalin is dropped to isothermal reaction 4h in reactant liquor, by reactant mistake
Filter, washing, dried, obtain modified aluminium hydroxide, stand-by;
(3) preparing modified zeolite powder: by zeolite powder in 300 DEG C of temperature lower calcination 30min, being dipped in mass concentration after cooling is 5%
Supersound process 30min in salpeter solution, is placed in supersound process 30min in modifying agent again by zeolite powder after filtration, dry at 70 DEG C
Doing and i.e. obtain modified zeolite powder, stand-by, modifying agent is made up of the component of following mass percent: 3% polyethylene glycol oxide, 0.1% silane
Coupling agent KH-550, surplus is water;
(4) injection mo(u)lding: by 40KgABS resin, 20KgPVC resin, 5Kg surface modification bamboo fibre, 5Kg modified aluminium hydroxide,
5Kg chlorinated polyethylene, 1Kg lubricant (ethylene bis stearamide), 3Kg modified zeolite powder, 0.5Kg antioxidant AT-10,0.1Kg
Antioxidant 1078, after the weight proportion of 0.5Kg dibutyltin dilaurate weighs each component, puts ABS resin and polyvinyl chloride resin
In dehydrated alcohol, soak and stir 5min, dry, after each component mix homogeneously, will add injection machine injection mo(u)lding, after through inspection
Test the qualified lead-acid accumulator aging resistance that i.e. obtains and mould shell, concretely comprising the following steps of injection mo(u)lding: injection → molding → pressurize → demoulding →
Cooling, injection molding material barrel temperature is 220 DEG C;Mould temperature is 50 DEG C;Dwell pressure 75MPa, dwell time 5s.
Embodiment 3
(1) prepare surface modification bamboo fibre: added by bamboo fibre in chlorosulfonic acid, be heated to 85 DEG C of swelling 2h, cooling, filter, will
It is neutrality that filtrate washes with water to pH, is vacuum dried, and adds and dries at 102 DEG C, i.e. after carrying out in wetting agent soaking 50min
Obtaining surface modification bamboo fibre, stand-by, wherein, wetting agent is made up of the component of following mass percent: 45% politef dispersion
Emulsion, 0.15% quaternary ammonium salt, 0.4% polyoxyethylene stearic acid ester, 0.2% silane resin acceptor kh-550,2% nano-silicon nitride, surplus
For water;
(2) modified aluminium hydroxide is prepared: first aluminium hydroxide is dispersed in water the dispersion liquid being configured to mass percentage concentration 7%, stirs
Mix after being heated to 75 DEG C, add dispersion liquid adds by the tripolycyanamide for aluminium hydroxide quality 12% and mix uniformly, obtain reactant liquor;Again
By the amount of tripolycyanamide and formaldehyde material than 1:2.5, formalin is dropped to isothermal reaction 5h in reactant liquor, by reactant mistake
Filter, washing, dried, obtain modified aluminium hydroxide, stand-by;
(3) preparing modified zeolite powder: by zeolite powder in 380 DEG C of temperature lower calcination 40min, being dipped in mass concentration after cooling is 7%
Supersound process 35min in salpeter solution, is placed in supersound process 40min in modifying agent again by zeolite powder after filtration, dry at 75 DEG C
Doing and i.e. obtain modified zeolite powder, stand-by, modifying agent is made up of the component of following mass percent: 4% polyethylene glycol oxide, 0.3% silane
Coupling agent KH-550, surplus is water;
(4) injection mo(u)lding: by 45KgABS resin, 25KgPVC resin, 12Kg surface modification bamboo fibre, 7Kg modified aluminium hydroxide,
6Kg chlorinated polyethylene, 2Kg lubricant (ethylene bis stearamide mixes with magnesium stearate 1:3 in mass ratio), 4Kg modified zeolite
Powder, 0.8Kg antioxidant AT-10,0.3Kg antioxidant 1078, the weight proportion of 0.7Kg dibutyltin dilaurate weighs each group
After Fen, ABS resin and polyvinyl chloride resin are placed in dehydrated alcohol and soak and stir 8min, dry, add after each component mix homogeneously
Enter injection machine injection mo(u)lding, after through checking the qualified lead-acid accumulator aging resistance that i.e. obtains to mould shell, concretely comprising the following steps of injection mo(u)lding:
Injection → molding → pressurize → the demoulding → cooling, injection molding material barrel temperature is 225 DEG C;Mould temperature is 55 DEG C;Dwell pressure
80MPa, dwell time 6s.
The lead-acid accumulator aging resistance prepared by the present invention moulds shell material oxygen index (OI) >=30%, and fire resistance exceedes plastics
Material is flammable performance standard V-0 level flame-retardant standard, other indices (all performing according to GB/T 23754-2009) are:
Mass change: 0.3%;
Impact resistance: less than-30 DEG C flawlesses of low temperature;
Thermostability: 70 ± 2 DEG C, variable quantity: 0.2mm after 3 hours;
Air pressure resistance: variable quantity: 0.1mm
Proof voltage: 20000V is the most breakdown
Reduction potassium permanganate: 0.4ml/g.
Each index exceeds well over GB/T 23754-2009 " Plumbic acid accumulator container " standard-required, wherein heat-resistant deforming temperature >=
102 DEG C, having excellent heat stability and ageing resistace, hot strength performs according to GB/T 1040 up to 65Mpa(, selects
I pattern sample, draw speed is 10mm/min), bending modulus performs according to GB/T9341 up to 3150Mpa(), Charpy Impact
Intensity (breach) (performing according to GB/T1043) is up to 35KJ/m2。
Embodiment described above is the one preferably scheme of the present invention, not makees the present invention any pro forma
Limit, on the premise of without departing from the technical scheme described in claim, also have other variant and remodeling.
Claims (6)
1. a lead-acid accumulator aging resistance moulds shell preparation method, it is characterised in that comprise the following steps:
(1) prepare surface modification bamboo fibre: added by bamboo fibre in chlorosulfonic acid, be heated to 80 ~ 100 DEG C of swelling 1 ~ 3h, cooling, mistake
Filter, filtrate is washed with water to pH be neutrality, vacuum drying, add and wetting agent carried out soak after 30 ~ 60min in 95 ~ 105
Dry at DEG C, obtain surface modification bamboo fibre, stand-by;
(2) modified aluminium hydroxide is prepared: first aluminium hydroxide is dispersed in water the dispersion being configured to mass percentage concentration 5 ~ 10%
Liquid, after being heated with stirring to 70 ~ 80 DEG C, adds to add in dispersion liquid by the tripolycyanamide for aluminium hydroxide quality 10 ~ 15% and mixes uniformly,
Obtain reactant liquor;Press the tripolycyanamide amount with formaldehyde material again than 1:2 ~ 3, formalin is dropped in reactant liquor isothermal reaction 4 ~
8h, filters reactant, washing, dried, obtains modified aluminium hydroxide, stand-by;
(3) modified zeolite powder is prepared: by zeolite powder in 300 ~ 500 DEG C of temperature lower calcination 30 ~ 60min, be dipped in quality after cooling dense
Degree be 5 ~ 10% salpeter solution in supersound process 30 ~ 40min, again zeolite powder is placed in after filtration in modifying agent supersound process 30 ~
60min, at 70 ~ 80 DEG C, drying modified zeolite powder, stand-by;
(4) injection mo(u)lding: by 40 ~ 50 parts of ABS resin, 20 ~ 30 parts of polyvinyl chloride resins, 5 ~ 10 parts of surface modification bamboo fibres, 5 ~ 10 parts change
Property aluminium hydroxide, 5 ~ 10 parts of chlorinated polyethylenees, 1 ~ 3 part of lubricant, 3 ~ 5 parts of modified zeolite powders, 0.5 ~ 1 part of antioxidant AT-10,
After the weight of 1078,0.5 ~ 1 part of dibutyltin dilaurate of 0.1 ~ 0.5 part of antioxidant weighs each component, by ABS tree
Fat and polyvinyl chloride resin are placed in dehydrated alcohol and soak and stir 5 ~ 10min, dry, and will add injection machine after each component mix homogeneously
Injection mo(u)lding, after through checking the qualified lead-acid accumulator aging resistance that i.e. obtains to mould shell.
A kind of lead-acid accumulator aging resistance the most according to claim 1 moulds shell preparation method, it is characterised in that step (1)
In, described wetting agent is made up of the component of following mass percent: 40 ~ 50% politef dispersion emulsions, 0.1 ~ 0.2% quaternary ammonium
Salt, 0.3 ~ 0.5% polyoxyethylene stearic acid ester, 0.1 ~ 0.3% silane resin acceptor kh-550,1 ~ 3% nano-silicon nitride, surplus is water.
A kind of lead-acid accumulator aging resistance the most according to claim 1 moulds shell preparation method, it is characterised in that step (3)
In, described modifying agent is made up of the component of following mass percent: 3 ~ 5% polyethylene glycol oxides, 0.1 ~ 0.5% silane coupler KH-
550, surplus is water.
A kind of lead-acid accumulator aging resistance the most according to claim 1 moulds shell preparation method, it is characterised in that step (4)
In, described lubricant is one or more in ethylene bis stearamide, magnesium stearate, zinc stearate and Tissuemat E.
A kind of lead-acid accumulator aging resistance the most according to claim 1 moulds shell preparation method, it is characterised in that step (4)
In, concretely comprising the following steps of injection mo(u)lding: the injection → molding → pressurize → demoulding → cooling.
A kind of lead-acid accumulator aging resistance the most according to claim 5 moulds shell preparation method, it is characterised in that injection charging basket
Temperature is 220 ~ 230 DEG C;Mould temperature is 50 ~ 60 DEG C;Dwell pressure 75 ~ 85MPa, dwell time 5 ~ 7s.