CN106280145A - A kind of Kynoar plastic sheeting - Google Patents
A kind of Kynoar plastic sheeting Download PDFInfo
- Publication number
- CN106280145A CN106280145A CN201610641857.0A CN201610641857A CN106280145A CN 106280145 A CN106280145 A CN 106280145A CN 201610641857 A CN201610641857 A CN 201610641857A CN 106280145 A CN106280145 A CN 106280145A
- Authority
- CN
- China
- Prior art keywords
- kynoar
- parts
- plastic sheeting
- thin film
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Kynoar plastic sheeting, including the component of following weight portion: Kynoar 40 55 parts；Nano filling 12 15 parts；Drip agent 58 parts；High fat melting resin powder 69 parts；Sodium salicylate 1 1.2 parts；Dispersant 1.5 2.5 parts；Glycerol 0.5 1.5 parts.The invention has the beneficial effects as follows: with Kynoar as raw material, the Nano filling added and other component, can play the effect that plasticising is toughness reinforcing, considerably increase the tear-resistant intensity of thin film thin film, improve the stability of thin film, greatly strengthen the service life of thin film.
Description
Technical field
The present invention relates to a kind of plastic sheeting, particularly relate to a kind of Kynoar plastic sheeting.
Background technology
Kynoar is important a member in fluoroplastics family, but due to poor fluidity, melt-processed difficulty, film forming is more
Difficult.On the other hand, Kynoar has prominent high-low temperature resistant, resistance to chemical attack and a weatherability, excellent electrical insulating property,
Through being applied to industry, civilian many fields.These premium properties of Kynoar meet the solar cell package back of the body just
The requirement of plate film protection tunic, but pure Kynoar raw material there is also film forming difficulty, easy buckling deformation after film forming, and heat is received
The high deficiency of shrinkage, therefore in the urgent need to being modified pure Kynoar raw material.
Therefore, for solving the problems referred to above, a kind of new technical scheme of special offer.
Summary of the invention
The present invention provides a kind of Kynoar plastic sheeting.
The technical solution used in the present invention is:
A kind of Kynoar plastic sheeting, including the component of following weight portion:
Kynoar 40-55 part；
Nano filling 12-15 part；
Drip agent 5-8 part；
High fat melting resin powder 6-9 part；
Sodium salicylate 1-1.2 part；
Dispersant 1.5-2.5 part；
Glycerol 0.5-1.5 part.
Preferably, described high fat melting resin powder uses linear low density polyethylene.
Preferably, described dispersant is Tissuemat E or paraffin.
Preferably, described Nano filling is nano silicon or nano-calcium carbonate.
Preferably, described drip agent is fatty acid glyceride or alcohol acid anhydride fatty acid ester.
The invention has the beneficial effects as follows: with Kynoar as raw material, the Nano filling of interpolation and other component, can be to thin
Film plays the effect that plasticising is toughness reinforcing, considerably increases the tear-resistant intensity of thin film, improves the stability of thin film, greatly strengthen
The service life of thin film.
Detailed description of the invention
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, this embodiment
It is only used for explaining the present invention, is not intended that the restriction to protection scope of the present invention.
Embodiment 1
A kind of Kynoar plastic sheeting, including the component of following weight portion:
Kynoar 40 parts；
Nano silicon 12 parts；
Fatty acid glyceride 5 parts；
Linear low density polyethylene 6 parts；
Sodium salicylate 1 part；
Tissuemat E 1.5 parts；
Glycerol 0.5 part.
Embodiment 2
A kind of Kynoar plastic sheeting, including the component of following weight portion:
Kynoar 48 parts；
Nano-calcium carbonate 13 parts；
Alcohol acid anhydride fatty acid ester 6 parts；
Linear low density polyethylene 7 parts；
Sodium salicylate 1.1 parts；
2 parts of paraffin；
Glycerol 1 part.
Embodiment 3
A kind of Kynoar plastic sheeting, including the component of following weight portion:
Kynoar 55 parts；
Nano silicon 15 parts；
Alcohol acid anhydride fatty acid ester 8 parts；
Linear low density polyethylene 9 parts；
Sodium salicylate 1.2 parts；
Tissuemat E 2.5 parts；
Glycerol 1.5 parts.
The invention has the beneficial effects as follows: with Kynoar as raw material, the Nano filling of interpolation and other component, can be to thin
Film plays the effect that plasticising is toughness reinforcing, considerably increases the tear-resistant intensity of thin film, improves the stability of thin film, greatly strengthen
The service life of thin film.
The above, be only presently preferred embodiments of the present invention, is not the limit that the present invention makees any other form
System, and any amendment made according to the technical spirit of the present invention or equivalent variations, still fall within present invention model required for protection
Enclose.
Claims (5)
1. a Kynoar plastic sheeting, it is characterised in that: include the component of following weight portion:
Kynoar 40-55 part；
Nano filling 12-15 part；
Drip agent 5-8 part；
High fat melting resin powder 6-9 part；
Sodium salicylate 1-1.2 part；
Dispersant 1.5-2.5 part；
Glycerol 0.5-1.5 part.
A kind of Kynoar plastic sheeting the most according to claim 1, it is characterised in that: described high fat melting resin powder
Use linear low density polyethylene.
A kind of Kynoar plastic sheeting the most according to claim 1, it is characterised in that: described dispersant is polyethylene
Wax or paraffin.
A kind of Kynoar plastic sheeting the most according to claim 1, it is characterised in that: described Nano filling is nanometer
Silicon dioxide or nano-calcium carbonate.
A kind of Kynoar plastic sheeting the most according to claim 1, it is characterised in that: described drip agent is glyceride
Fat acid esters or alcohol acid anhydride fatty acid ester.