CN106279909A - A kind of Noctilucent material - Google Patents
A kind of Noctilucent material Download PDFInfo
- Publication number
- CN106279909A CN106279909A CN201610702136.6A CN201610702136A CN106279909A CN 106279909 A CN106279909 A CN 106279909A CN 201610702136 A CN201610702136 A CN 201610702136A CN 106279909 A CN106279909 A CN 106279909A
- Authority
- CN
- China
- Prior art keywords
- parts
- defoamer
- noctilucent
- surfactant
- density polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of Noctilucent material, be made up of the raw material of following weight portion: linear high-density polyethylene 15 20 parts, 10 20 parts of fluorescent material, copper oxide 12 15 parts, aluminium oxide 10 15 parts, light stabilizer 10 12 parts, magnesium silicate 15 20 parts, 12 15 parts of surfactant, activation auxiliary agent 15 20 parts and defoamer 12 15 parts.The Noctilucent material cost of material that the present invention provides is low, good product performance, and using effect is good, and the life-span is long, and noctilucence brightness is big, environmental protection and energy saving, is conducive to promoting.
Description
Technical field
The present invention relates to a kind of Noctilucent material, belong to chemical material field.
Background technology
Along with the progress of science and technology, the research of fluorescence is got more and more by people, and the range of application of fluorescent material is increasingly
Extensively.Fluorescent material in addition to as dyestuff, also organic pigment, Optical Bleaching Agent, photooxidant, coating, chemistry and biochemical analysis,
The fields such as solar energy catcher, anti-fake mark, pharmaceutical indications and laser have obtained wider application.
Summary of the invention
The shortcoming lacked for Noctilucent material on market, the present invention provides a kind of Noctilucent material.The noctilucence that the present invention provides
Material feedstock low cost, good product performance, using effect is good, and the life-span is long, and noctilucence brightness is big, environmental protection and energy saving, is conducive to promoting.
The present invention provides a kind of Noctilucent material, is made up of the raw material of following parts by weight:
Linear high-density polyethylene 15-20 part, fluorescent material 10-20 part, copper oxide 12-15 part, aluminium oxide 10-15 part, light
Stabilizer 10-12 part, magnesium silicate 15-20 part, surfactant 12-15 part, activation auxiliary agent 15-20 part and defoamer 12-15 part.
On the basis of technique scheme, the present invention has also done following improvement.
Further, described Noctilucent material, it is made up of the raw material of following weight portion:
Linear high-density polyethylene 15 parts, 10 parts of fluorescent material, copper oxide 12 parts, aluminium oxide 10 parts, light stabilizer 10 parts, silicon
15 parts of magnesium of acid, 12 parts of surfactant, activation auxiliary agent 15 parts and defoamer 12 parts.
Further, described Noctilucent material, it is made up of the raw material of following weight portion:
Linear high-density polyethylene 20 parts, 20 parts of fluorescent material, copper oxide 15 parts, aluminium oxide 15 parts, light stabilizer 12 parts, silicon
20 parts of magnesium of acid, 15 parts of surfactant, activation auxiliary agent 120 parts and defoamer 115 parts.
Further, described light stabilizer is hindered amine.
Further, described surfactant is stearic acid or dodecylbenzene sodium sulfonate.
Further, described defoamer is organic silicon defoamer.
Beneficial effects of the present invention:
The Noctilucent material cost of material that the present invention provides is low, and good product performance, using effect is good, and the life-span is long, noctilucence brightness
Greatly, environmental protection and energy saving, be conducive to promoting.
Detailed description of the invention
Being described principle and the feature of the present invention below in conjunction with instantiation, example is served only for explaining this
Bright, it is not intended to limit the scope of the present invention.
Embodiment 1
A kind of Noctilucent material, is made up of the raw material of following weight portion:
Linear high-density polyethylene 15 parts, 10 parts of fluorescent material, copper oxide 12 parts, aluminium oxide 10 parts, light stabilizer 10 parts, silicon
15 parts of magnesium of acid, 12 parts of surfactant, activation auxiliary agent 15 parts and defoamer 12 parts.
Described light stabilizer is hindered amine, and described surfactant is stearic acid or dodecylbenzene sodium sulfonate, described in disappear
Infusion is organic silicon defoamer.
Preparation method:
1) first the linear high-density polyethylene in said components and fluorescent material are prepared as respectively the powder of 100～300 mesh
Body, and dried, stirring mixing；
2) then by remaining raw material, being gradually added into and stir mixing, until adding completely, making each powder constituents uniformly mix
Close, compound under cryogenic, evacuation, stand more than 2 hours, standby.
Embodiment 2
A kind of luminescent coating, is made up of the component of following weight portion:
Linear high-density polyethylene 20 parts, 20 parts of fluorescent material, copper oxide 15 parts, aluminium oxide 15 parts, light stabilizer 12 parts, silicon
20 parts of magnesium of acid, 15 parts of surfactant, activation auxiliary agent 120 parts and defoamer 115 parts.
Described light stabilizer is hindered amine, and described surfactant is stearic acid or dodecylbenzene sodium sulfonate, described in disappear
Infusion is organic silicon defoamer.
Preparation method:
1) first the linear high-density polyethylene in said components and fluorescent material are prepared as respectively the powder of 100～300 mesh
Body, and dried, stirring mixing；
2) then by remaining raw material, being gradually added into and stir mixing, until adding completely, making each powder constituents uniformly mix
Close, compound under cryogenic, evacuation, stand more than 2 hours, standby.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all spirit in the present invention and
Within principle, any modification, equivalent substitution and improvement etc. made, should be included within the scope of the present invention.
Claims (6)
1. a Noctilucent material, it is characterised in that be made up of the raw material of following parts by weight:
Linear high-density polyethylene 15-20 part, fluorescent material 10-20 part, copper oxide 12-15 part, aluminium oxide 10-15 part, light are stable
Agent 10-12 part, magnesium silicate 15-20 part, surfactant 12-15 part, activation auxiliary agent 15-20 part and defoamer 12-15 part.
A kind of Noctilucent material the most according to claim 1, it is characterised in that be made up of the raw material of following weight portion:
Linear high-density polyethylene 15 parts, 10 parts of fluorescent material, copper oxide 12 parts, aluminium oxide 10 parts, light stabilizer 10 parts, magnesium silicate
15 parts, 12 parts of surfactant, activation auxiliary agent 15 parts and defoamer 12 parts.
A kind of Noctilucent material the most according to claim 1, it is characterised in that be made up of the raw material of following weight portion:
Linear high-density polyethylene 20 parts, 20 parts of fluorescent material, copper oxide 15 parts, aluminium oxide 15 parts, light stabilizer 12 parts, magnesium silicate
20 parts, 15 parts of surfactant, activation auxiliary agent 120 parts and defoamer 115 parts.
A kind of Noctilucent material the most according to claim 1, it is characterised in that described light stabilizer is hindered amine.
A kind of Noctilucent material the most according to claim 1, it is characterised in that described surfactant is stearic acid or 12
Sodium alkyl benzene sulfonate.
A kind of Noctilucent material the most according to claim 1, it is characterised in that described defoamer is organic silicon defoamer.