CN106278131A - 一种利用赤泥制备煤矿残采区充填膏体的方法 - Google Patents
一种利用赤泥制备煤矿残采区充填膏体的方法 Download PDFInfo
- Publication number
- CN106278131A CN106278131A CN201610565602.0A CN201610565602A CN106278131A CN 106278131 A CN106278131 A CN 106278131A CN 201610565602 A CN201610565602 A CN 201610565602A CN 106278131 A CN106278131 A CN 106278131A
- Authority
- CN
- China
- Prior art keywords
- red mud
- colliery
- stope filling
- filling mastic
- residual
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种利用赤泥制备煤矿残采区充填膏体的方法。该方法在测试赤泥含水率、颗粒直径、渗透系数和膨胀系数的基础上，通过球磨得到了制备煤矿残采区充填膏体的超细粉体，然后对煤矸石进行了破碎和筛分，得到了制备煤矿残采区充填膏体的粗骨料和细骨料，最后对超细粉体溶液进行了中和，并辅以水、减水剂、早强剂、膨胀剂和缓凝剂，混合均匀，制备得到煤矿残采区的充填膏体。本发明不仅解决了残采区膏体充填材料来源范围小的问题，可以科学地预防和控制残采区动力灾害的发生、保障可持续发展，而且合理高效地利用了广泛堆积的赤泥、减轻了对周围环境的污染危害。
Description
技术领域
本发明涉及煤矿胶结充填材料技术领域，尤其是涉及一种利用赤泥制备煤矿残采区充填膏体的方法，主要适用于煤矿地下残采区的治理。
背景技术
受先期地方小煤窑的私挖滥采等影响，我国地下残采区的赋存面积逐年增加。地下残采区的广泛分布容易引发地表开裂与沉陷、弃采煤炭资源自然发火、有毒气体泄露等灾害，进而严重影响地表建筑物、水体和铁路等的稳定性。同时，地下残采区遗留煤柱群纵横交错，其在长期集中载荷、邻近煤层采动影响、采空区积水、自然发火和地层高温等因素的耦合作用下，会由表及里地发生片帮冒落，进而发生承载面积减小和支撑强度弱化等现象，并引发坍塌破坏。当采场遗留煤柱瞬时失稳产生的冲击波转移扩散到邻近煤柱时，可能引发采场遗留煤柱的链式失稳与破坏，进而引发前述动力灾害，威胁群众的生命财产安全。
近年来，地下残采区的治理越来越成为广大技术人员与研究学者关注的焦点。膏体充填技术是合理治理残采区的重要举措，其不仅能充分利用煤矸石、粉煤灰和废弃混凝土等堆积物，而且可以科学地预防和控制残采区动力灾害的发生，并保障可持续发展。然而，由于地下残采区的赋存面积较大，加之煤矸石、粉煤灰和废弃混凝土的来源范围小，其在数量上难以满足膏体充填治理煤矿地下残采区的需求。因此，亟需一种成本较低、来源范围广泛且满足强度要求和输送要求的残采区膏体充填材料来解决上述问题。
赤泥是指氧化铝生产过程中所排放的废渣，由于含有大量呈红色的氧化铁，因此被称为赤泥。我国氧化铝工业所产生的赤泥排放量大，目前主要采用地面露天堆存的方式来处理，这不仅占用了大量宝贵的土地资源、消耗了过多的堆放场地建设和管理费用，而且极易对地下水体、土壤和大气等造成极大的危害。随着赤泥堆放场地及其环境污染等问题的凸显，赤泥的合理高效利用成为亟需解决的问题。
综上，亟需寻找一种既能解决残采区膏体充填材料来源范围小的问题，又能合理有效地利用广泛堆积赤泥的方法，进而科学地预防和避免残采区动力灾害的发生，并减轻对周围环境的污染危害。
发明内容
本发明旨在提供一种利用赤泥制备煤矿残采区充填膏体的方法，不仅解决了残采区膏体充填材料来源范围小的问题，可以科学地预防和控制残采区动力灾害的发生、保障可持续发展，而且合理高效地利用了广泛堆积的赤泥、减轻了对周围环境的污染危害。
本发明是通过以下技术方案实现的：
一种利用赤泥制备煤矿残采区充填膏体的方法，在测试赤泥含水率、颗粒直径、渗透系数和膨胀系数的基础上，通过球磨得到了制备煤矿残采区充填膏体的超细粉体，然后对煤矸石进行了破碎和筛分，得到了制备煤矿残采区充填膏体的粗骨料和细骨料，最后对超细粉体溶液进行了中和，并辅以水、减水剂、早强剂、膨胀剂和缓凝剂，混合均匀，制备得到煤矿残采区的充填膏体。所述技术方案具体按照以下步骤进行：
（1）收集工业废弃赤泥，分拣清理杂质和具备放射性、重金属污染的成分；
（2）测试赤泥的含水率、颗粒直径、渗透系数和膨胀系数，选取满足下述要求的赤泥：
含水率为20%~70%，颗粒直径≤2.4mm，渗透系数为0.6×10-5cm/sec~2.4×10-5cm/sec，膨胀系数为4.0×10-6~3.0×10-5；
（3）将步骤（2）选取的赤泥进行球磨，得到制备煤矿残采区充填膏体的超细粉体；
（4）利用颚式破碎机对煤矸石进行破碎，并将粒径大于15mm的煤矸石颗粒进行二次破碎，使筛分得到的煤矸石颗粒直径分布均小于15mm；
（5）分别用网眼为5mm和15mm的振动筛将步骤（4）中破碎的煤矸石进行筛分，得到制备煤矿残采区充填膏体的细骨料和粗骨料；
（6）利用步骤（3）制备的超细粉体，配制质量浓度为60%的赤泥水溶液，测试其pH值；
（7）向步骤（6）中制备的赤泥溶液中缓慢注入中和液，使其pH=7；
（8）向步骤（7）得到的浆液中加入粗骨料、细骨料和调节剂，混合均匀后，得到质量浓度为75%~90%的煤矿残采区充填膏体。
优选地，所述的步骤（3）中制备煤矿残采区充填膏体的超细粉体的比表面积大于300m2/kg。
优选地，所述的步骤（5）中，粒径为1mm~5mm的煤矸石为细骨料，粒径为5mm~15mm的煤矸石为粗骨料。
优选地，所述的步骤（7）中，中和液为盐酸、硫酸、硝酸或醋酸中的一种或几种，其能有效地避免赤泥对地下水位的侵蚀。
优选地，所述的步骤（8）制备的充填膏体各组分的重量配比为：粗骨料：23%~49%；细骨料：20%~25%；超细粉体：20%~25%；水：10%~25%；调节剂：1%~2%。
优选地，所述的步骤（8）中调节剂包括减水剂、早强剂、膨胀剂和缓凝剂，其中减水剂选用密胺系减水剂或聚羧酸系高效减水剂，其能在残采区充填膏体和易性不变的情况下，减少拌合用水量并提高其强度性能；早强剂选用氯化钙、无水硫酸钠或三乙醇胺，其能够提高残采区充填膏体的早期抗压强度；膨胀剂选用氧化镁，其能够引发残采区充填膏体的体积膨胀，进而产生一定的预应力，实现控制收缩开裂；缓凝剂选用葡萄糖酸钠或柠檬酸钠，其能够延迟残采区充填膏体的硬化时间。
进一步地，所述调节剂各组分的重量配比为：减水剂：20%~50%；早强剂：10%~50%；膨胀剂：10%~50%；缓凝剂：20%~50%。
本发明的有益效果：
该发明在测试赤泥含水率、颗粒直径、渗透系数和膨胀系数的基础上，通过球磨得到了制备煤矿残采区充填膏体的超细粉体，然后对煤矸石进行了破碎和筛分，得到了制备煤矿残采区充填膏体的粗骨料和细骨料，最后对超细粉体溶液进行了中和，并辅以水、减水剂、早强剂、膨胀剂和缓凝剂，混合均匀，制备得到煤矿残采区的充填膏体。本发明不仅解决了残采区膏体充填材料来源范围小的问题，可以科学地预防和控制残采区动力灾害的发生、保障可持续发展，而且合理高效地利用了广泛堆积的赤泥、减轻了对周围环境的污染危害。
具体实施方式
为了对本发明的技术目标、特征和效果有更清楚的理解，现对一种利用赤泥制备煤矿残采区充填膏体的方法作进一步详细的阐述与说明。
实施例1：
步骤一，收集山西省柳林县森泽铝厂的废弃赤泥，分拣排除树干、枝叶、细铁丝和具备放射性、重金属污染的成分。
步骤二，按照《土工实验方法标准》（GB/T50123—1999）介绍的方法测试赤泥的含水率、颗粒直径、渗透系数和膨胀系数，结果表明：赤泥呈现粉粒状，含水率为62.4%，颗粒直径均小于2.4mm，渗透系数为1.12×10-5cm/sec，膨胀系数为0.85×10-5。
步骤三，采用X射线荧光光谱分析、极谱分析、电子探针分析、原子吸收光谱分析和发射光谱分析相结合的方法来检测赤泥的化学成分，结果表明：赤泥中SiO2的含量占22.14%，CaO的含量占34.0%，Fe2O3的含量占11.10%，Al2O3的含量占13.50%，MgCl2的含量占3.00%，TiO2的含量占4.24%，K2CO3的含量占1.47%，Na2SO4的含量占4.00%。
步骤四，将上述选取的赤泥进行球磨，得到制备煤矿残采区充填膏体的超细粉体，其比表面积为360m2/kg；
步骤五，利用颚式破碎机对煤矸石进行破碎，并将粒径大于15mm的煤矸石颗粒进行二次破碎，使筛分得到的煤矸石颗粒粒径分布均小于15mm；
步骤六，分别用网眼为5mm和15mm的振动筛将破碎的煤矸石进行筛分，得到制备煤矿残采区充填膏体的细骨料和粗骨料，其中细骨料的粒径为1mm~5mm，粗骨料的粒径为5mm~15mm；
步骤七，利用步骤四制备的超细粉体，配制质量浓度为60%的水溶液，并采用pH计测试其pH值，结果表明：赤泥溶液的pH值为8.7；
步骤八，采用酸式滴定管，逐渐向步骤七得到的赤泥溶液中注入稀盐酸，使其pH=7；
步骤九，向步骤八得到的超细粉体浆液中加入粗骨料、细骨料和调节剂，混合均匀后，得到质量浓度为82%的煤矿残采区充填膏体，充填膏体中各组分的重量分别为：粗骨料33kg，细骨料23kg，超细粉体25kg，水18kg，聚羧酸系高效减水剂0.20kg，无水硫酸钠0.30kg，氧化镁0.25kg，葡萄糖酸钠0.25kg。
采用塌落度筒测定残采区充填膏体的坍落度为18cm、扩展度为39cm，采用ICAR流变仪测试残采区充填膏体的剪切屈服应力为318Pa、塑性粘度为8.2Pa·s，前述参数均满足煤矿残采区充填膏体流动性能的要求；利用本实施例所得的残采区充填膏体制备标准试样，采用微机控制电液伺服万能试验机测试残采区充填试样在第28天的单轴抗压强度，其值为8.94MPa。综上，符合残采区充填膏体的输送性能和力学性能的要求，其可以被广泛推广用于煤矿残采区的治理。
实施例2：
步骤一，收集山西省柳林县森泽铝厂的废弃赤泥，分拣排除树干、枝叶、细铁丝和具备放射性、重金属污染的成分。
步骤二，按照《土工实验方法标准》（GB/T50123—1999）介绍的方法测试赤泥的含水率、颗粒直径、渗透系数和膨胀系数，结果表明：赤泥呈现粉粒状，含水率为62.4%，颗粒直径均小于2.0mm，渗透系数为1.12×10-5cm/sec，膨胀系数为0.85×10-5。
步骤三，采用X射线荧光光谱分析、极谱分析、电子探针分析、原子吸收光谱分析和发射光谱分析相结合的方法来检测赤泥的化学成分，结果表明：赤泥中SiO2的含量占22.14%，CaO的含量占34.0%，Fe2O3的含量占11.10%，Al2O3的含量占13.50%，MgCl2的含量占3.00%，TiO2的含量占4.24%，K2CO3的含量占1.47%，Na2SO4的含量占4.00%。
步骤四，将上述选取的赤泥进行球磨，得到制备煤矿残采区充填膏体的超细粉体，其比表面积为360m2/kg；
步骤五，利用颚式破碎机对煤矸石进行破碎，并将粒径大于15mm的煤矸石颗粒进行二次破碎，使筛分得到的煤矸石颗粒粒径分布均小于15mm；
步骤六，分别用网眼为5mm和15mm的振动筛将破碎的煤矸石进行筛分，得到制备煤矿残采区充填膏体的细骨料和粗骨料，其中细骨料的粒径为1mm~5mm，粗骨料的粒径为5mm~15mm；
步骤七，利用步骤四制备的超细粉体，配制质量浓度为60%的水溶液，并采用pH计测试其pH值，结果表明：赤泥溶液的pH值为8.7；
步骤八，采用酸式滴定管，逐渐向步骤七得到的赤泥溶液中注入硫酸，使其pH=7；
步骤九，向步骤八得到的超细粉体浆液中加入粗骨料、细骨料和调节剂，混合均匀后，得到质量浓度为77%的煤矿残采区充填膏体，充填膏体中各组分的重量分别为：粗骨料30kg，细骨料24kg，超细粉体22kg，水23kg，聚羧酸系高效减水剂0.30kg，无水硫酸钠0.20kg，氧化镁0.3kg，葡萄糖酸钠0.2kg。
采用塌落度筒测定残采区充填膏体的坍落度为22cm、扩展度为37cm，采用ICAR流变仪测试残采区充填膏体的剪切屈服应力为323Pa、塑性粘度为8.1Pa·s，前述参数均满足煤矿残采区充填膏体流动性能的要求；利用本实施例所得的残采区充填膏体制备标准试样，采用微机控制电液伺服万能试验机测试残采区充填试样在第28天的单轴抗压强度，其值为8.68MPa。综上，符合残采区充填膏体的输送性能和力学性能的要求，其可以被广泛推广用于煤矿残采区的治理。
实施例3：
步骤一，收集山西省柳林县森泽铝厂的废弃赤泥，分拣排除树干、枝叶、细铁丝和具备放射性、重金属污染的成分。
步骤二，按照《土工实验方法标准》（GB/T50123—1999）介绍的方法测试赤泥的含水率、颗粒直径、渗透系数和膨胀系数，结果表明：赤泥呈现粉粒状，含水率为62.4%，颗粒直径均小于2.0mm，渗透系数为1.12×10-5cm/sec，膨胀系数为0.85×10-5。
步骤三，采用X射线荧光光谱分析、极谱分析、电子探针分析、原子吸收光谱分析和发射光谱分析相结合的方法来检测赤泥的化学成分，结果表明：赤泥中SiO2的含量占22.14%，CaO的含量占34.0%，Fe2O3的含量占11.10%，Al2O3的含量占13.50%，MgCl2的含量占3.00%，TiO2的含量占4.24%，K2CO3的含量占1.47%，Na2SO4的含量占4.00%。
步骤四，将上述选取的赤泥进行球磨，得到制备煤矿残采区充填膏体的超细粉体，其比表面积为360m2/kg；
步骤五，利用颚式破碎机对煤矸石进行破碎，并将粒径大于15mm的煤矸石颗粒进行二次破碎，使筛分得到的煤矸石颗粒粒径分布均小于15mm；
步骤六，分别用网眼为5mm和15mm的振动筛将破碎的煤矸石进行筛分，得到制备煤矿残采区充填膏体的细骨料和粗骨料，其中细骨料的粒径为1mm~5mm，粗骨料的粒径为5mm~15mm；
步骤七，利用步骤四制备的超细粉体，配制质量浓度为60%的水溶液，并采用pH计测试其pH值，结果表明：赤泥溶液的pH值为8.7；
步骤八，采用酸式滴定管，逐渐向步骤七得到的赤泥溶液中注入硝酸，使其pH=7；
步骤九，向步骤八得到的超细粉体浆液中加入粗骨料、细骨料和调节剂，混合均匀后，得到质量浓度为83%的煤矿残采区充填膏体，充填膏体中各组分的重量分别为：粗骨料39kg，细骨料22kg，超细粉体20kg，水17kg，聚羧酸系高效减水剂0.60kg，无水硫酸钠0.40kg，氧化镁0.6kg，葡萄糖酸钠0.4kg。
采用塌落度筒测定残采区充填膏体的坍落度为24cm、扩展度为41cm，采用ICAR流变仪测试残采区充填膏体的剪切屈服应力为336Pa、塑性粘度为9.1Pa·s，前述参数均满足煤矿残采区充填膏体流动性能的要求；利用本实施例所得的残采区充填膏体制备标准试样，采用微机控制电液伺服万能试验机测试残采区充填试样在第28天的单轴抗压强度，其值为10.05MPa。综上，符合残采区充填膏体的输送性能和力学性能的要求，其可以被广泛推广用于煤矿残采区的治理。
以上所述为本发明的优选实施方式，应当指出，在不脱离本发明所述技术实质与原理的前提下对上述实施方法作出的任何改进与修润，均属于本发明技术方案的保护范围。
Claims (7)
1.一种利用赤泥制备煤矿残采区充填膏体的方法，其特征在于，包括以下步骤：
（1）收集废弃赤泥，分拣清理杂质和具备放射性、重金属污染的成分；
（2）测试赤泥的含水率、颗粒直径、渗透系数和膨胀系数，选取满足下述要求的赤泥：
含水率为20%~70%，颗粒直径≤2.4mm，渗透系数为0.6×10-5cm/sec~2.4×10-5cm/sec，膨胀系数为4.0×10-6~3.0×10-5；
（3）将步骤（2）选取的赤泥进行球磨，得到制备煤矿残采区充填膏体的超细粉体；
（4）利用颚式破碎机对煤矸石进行破碎，使其颗粒直径分布均小于15mm；
（5）分别用网眼为5mm和15mm的振动筛将步骤（4）中破碎的煤矸石进行筛分，得到制备煤矿残采区充填膏体的细骨料和粗骨料；
（6）利用步骤（3）制备的超细粉体，配制质量浓度为60%的赤泥水溶液，测试其pH值；
（7）向步骤（6）中制备的赤泥溶液中缓慢注入中和液，使其pH=7；
（8）向步骤（7）得到的浆液中加入粗骨料、细骨料和调节剂，混合均匀后，得到质量浓度为75%~90%的煤矿残采区充填膏体。
2.根据权利要求1所述的利用赤泥制备煤矿残采区充填膏体的方法，其特征在于，所述的步骤（3）中超细粉体的比表面积大于300m2/kg。
3.根据权利要求1所述的利用赤泥制备煤矿残采区充填膏体的方法，其特征在于，所述的步骤（5）中，粒径为1mm~5mm的煤矸石为细骨料，粒径为5mm~15mm的煤矸石为粗骨料。
4.根据权利要求1所述的利用赤泥制备煤矿残采区充填膏体的方法，其特征在于，所述的步骤（7）中和液为盐酸、硫酸、硝酸或醋酸中的一种或几种。
5.根据权利要求1所述的利用赤泥制备煤矿残采区充填膏体的方法，其特征在于，所述的步骤（8）中，制备的充填膏体各组分的重量配比为：粗骨料：23%~49%；细骨料：20%~25%；超细粉体：20%~25%；水：10%~25%；调节剂：1%~2%。
6.根据权利要求1所述的利用赤泥制备煤矿残采区充填膏体的方法，其特征在于，所述步骤（8）中调节剂包括减水剂、早强剂、膨胀剂和缓凝剂，其中减水剂选用密胺系减水剂或聚羧酸系高效减水剂，早强剂选用氯化钙、无水硫酸钠或三乙醇胺，膨胀剂选用氧化镁，缓凝剂选用葡萄糖酸钠或柠檬酸钠。
7.根据权利要求6所述的利用赤泥制备煤矿残采区充填膏体的方法，其特征在于，所述调节剂各组分的重量配比为：减水剂：20%~50%；早强剂：10%~50%；膨胀剂：10%~50%；缓凝剂：20%~50%。