CN106278010B - The method disturbed using the pre-control electromagnetism Leibo of conductive shield mortar - Google Patents
The method disturbed using the pre-control electromagnetism Leibo of conductive shield mortar Download PDFInfo
- Publication number
- CN106278010B CN106278010B CN201610580898.3A CN201610580898A CN106278010B CN 106278010 B CN106278010 B CN 106278010B CN 201610580898 A CN201610580898 A CN 201610580898A CN 106278010 B CN106278010 B CN 106278010B
- Authority
- CN
- China
- Prior art keywords
- conductive
- conductive shield
- fibre fabric
- mortar
- shield
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of method that pre-control electromagnetism Leibo using conductive shield mortar is disturbed, including the configuration of conductive shield mortar, the configuration of conductive shield concrete, steel reinforced concrete conductive fibre fabric make；Building is carried out outer roofing and wall using conductive shield mortar and is painted using above-mentioned shielding brick, conductive shield concrete masonry units；Building is using steel reinforced concrete conductive fibre fabric as metallic shield formula door curtain material.Easy for construction, excellent working effect of the invention.
Description
Technical field
The present invention relates to a kind of method of multidigit pre-control building intelligence system electromagnetism Leibo interference.
Background technology
Intelligence system is in building field using more and more extensive, it has also become the important component of building, it is intelligently
The extensive use united in building field brings great convenience to people's life and work, is imitated to improve people's quality of life with work
Rate has played great role.But since intelligence system is extremely sensitive to electromagnetism Leibo, easily goes to pot, bring lives and properties
Security threat, must implement this building intelligence system electromagnetism Leibo interference pre-control.
The content of the invention
It is an object of the invention to provide a kind of pre-control electromagnetism Leibo using conductive shield mortar of good working effect
The method of interference.
The present invention technical solution be：
A kind of method that pre-control electromagnetism Leibo using conductive shield mortar is disturbed, it is characterized in that：Comprise the following steps：
（One）Conductive shield mortar configures
Select Portland cement 100kg, flyash 50kg, copolymer condensation rubber powder 5kg, propyl methocel
5kg, granular polystyrene 1m3, clipped wire 5kg, grade conducting fiber 2kg, amount is than being configured and being stirred evenly, shape more than
Into conductive shield mortar；This conductive shield mortar is suitable for that there is the outer roofing and wall of intelligent building construction to paint use.
There is its major function insulation to shield, and intercept the functions such as electromagnetism Leibo interference.
（Two）Conductive shield concrete collocation method
Cement, stone, yellow ground, clipped wire, conducting fiber, water configuration is selected to form；Configured, stirred in the following proportions
Mix uniformly；
Conductive shield concrete material configures：Cement 343kg, yellow ground 621kg, stone 261kg, water 175kg, clipped wire
5kg, conducting fiber 4kg；Amount ratio is configured more than；Above material basic demand is 425 portland cement of cement selection；
Yellow ground is medium coarse sand；Stone is 246 stones；Water is neutral free from admixture water；Clipped wire filament length≤5mm, string diameter≤2mm；It is conductive fine
Tie up filament length≤10mm；
（Three）Steel reinforced concrete conductive fibre fabric makes
Mixed using conductive fiber and steel wire and be made into rigidity conductive fibre fabric, conductive fibre fabric select 150D/1 fiber lines or
120D wires, conductive fibre fabric is made into loom；Conductive fibre cloth is applied to the special cloth of movable folding type screened room, can also apply
In metallic shield formula door curtain etc..
Building uses above-mentioned conductive shield concrete masonry units, and carries out outer roofing and wall using conductive shield mortar
Paint；Building is using steel reinforced concrete conductive fibre fabric as metallic shield formula door curtain material.
Easy for construction, excellent working effect of the invention.
With reference to embodiment, the invention will be further described.
Embodiment
A kind of method that pre-control electromagnetism Leibo using conductive shield mortar is disturbed, it is characterized in that：Comprise the following steps：
（One）Shielding brick makes:
（1）Main material and its configuration
Including cement, yellow ground, stone, cinder, conductive fiber, clipped wire, mass ratio is cement:Yellow ground:Stone:Coal
Slag:Conductive fiber:Clipped wire:Water=20:20:30:20:5:5:1-10；
（2）Manufacture craft：A. special material is processed：Cinder is crushed, and particle diameter is grade；Conductive fiber filament length≤
10mm, string diameter≤2mm；Clipped wire filament length≤5mm, string diameter≤2mm；B. configure：A variety of materials is configured in proportion；C. stir
Mix：A variety of materials is stirred；D enters mould；E is extruded；F is conserved；G is cut by design specification, forms shielding
Property Concrete brick；
Function utilizes.Conventional tile body function utilizes.B. electric action.C. the effect of electromagnetism Leibo is intercepted.D. shielding action.
（Two）Conductive shield mortar configures
Select Portland cement 100kg, flyash 50kg, copolymer condensation rubber powder 5kg, propyl methocel
5kg, granular polystyrene 1m3, clipped wire 5kg, grade conducting fiber 2kg, amount is than being configured and being stirred evenly, shape more than
Into conductive shield mortar；This conductive shield mortar is suitable for that there is the outer roofing and wall of intelligent building construction to paint use.
There is its major function insulation to shield, and intercept the functions such as electromagnetism Leibo interference.
（Three）Conductive shield concrete collocation method
Cement, stone, yellow ground, clipped wire, conducting fiber, water configuration is selected to form；Configured, stirred in the following proportions
Mix uniformly；
Conductive shield concrete material configures：Cement 343kg, yellow ground 621kg, stone 261kg, water 175kg, clipped wire
5kg, conducting fiber 4kg；Amount ratio is configured more than；
Above material basic demand is 425 portland cement of cement selection；Yellow ground is medium coarse sand；Stone is 246 stones；Water
For neutral free from admixture water；Clipped wire filament length≤5mm, string diameter≤2mm；Conductive fiber filament length≤10mm；
（Four）Steel reinforced concrete conductive fibre fabric makes
Mixed using conductive fiber and steel wire and be made into rigidity conductive fibre fabric, conductive fibre fabric select 150D/1 fiber lines or
120D wires, conductive fibre fabric is made into loom；Conductive fibre cloth is applied to the special cloth of movable folding type screened room, can also apply
In metallic shield formula door curtain etc..
Building using above-mentioned shielding brick, conductive shield concrete masonry units, and using conductive shield mortar into
The outer roofing and wall of row paints；Building is using steel reinforced concrete conductive fibre fabric as metallic shield formula door curtain material.
Claims (1)
1. a kind of method that pre-control electromagnetism Leibo using conductive shield mortar is disturbed, it is characterized in that：Comprise the following steps：
（One）Conductive shield mortar configures
Portland cement 100kg, flyash 50kg, copolymer is selected to be condensed rubber powder 5kg, propyl methocel 5kg, gather
Benzene particle 1m3, clipped wire 5kg, grade conducting fiber 2kg, amount is formed conductive than being configured and being stirred evenly more than
Shielding mortar；
（Two）Conductive shield concrete collocation method
Cement, stone, yellow ground, clipped wire, conducting fiber, water configuration is selected to form；Configured in the following proportions, stirring is equal
It is even；
Conductive shield concrete material configures：Cement 343kg, yellow ground 621kg, stone 261kg, water 175kg, clipped wire 5kg,
Conducting fiber 4kg；Amount ratio is configured more than；
Above material requirements is 425 portland cement of cement selection；Yellow ground is medium coarse sand；Stone is 246 stones；Water is neutral nothing
Water impurity；Clipped wire filament length≤5mm, string diameter≤2mm；Conductive fiber filament length≤10mm；
（Three）Steel reinforced concrete conductive fibre fabric makes
Mixed using conductive fiber and steel wire and be made into steel reinforced concrete conductive fibre fabric, conductive fibre fabric selects 150D/1 fiber lines and 120D steel
Silk thread, conductive fibre fabric is made into loom；Conductive fibre fabric is applied to the special cloth of movable folding type screened room, applies also for
Metallic shield formula door curtain；
Building uses above-mentioned conductive shield concrete masonry units, and carries out outer roofing and wall powder using conductive shield mortar
Brush；Building is using steel reinforced concrete conductive fibre fabric as metallic shield formula door curtain material.