CN106277803A - A kind of manufacture method of zinc oxide varistor silver slurry glass dust - Google Patents
A kind of manufacture method of zinc oxide varistor silver slurry glass dust Download PDFInfo
- Publication number
- CN106277803A CN106277803A CN201610673796.6A CN201610673796A CN106277803A CN 106277803 A CN106277803 A CN 106277803A CN 201610673796 A CN201610673796 A CN 201610673796A CN 106277803 A CN106277803 A CN 106277803A
- Authority
- CN
- China
- Prior art keywords
- glass dust
- silver slurry
- glass
- zinc oxide
- manufacture method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the manufacture method of a kind of zinc oxide varistor silver slurry glass dust, by optimizing glass powder formula, the oxide of refining glass dust is weighed, put into after mix homogeneously in alumina crucible, being refined by Muffle furnace, smelting temperature is 1150 DEG C, is incubated 30min.Melting terminate after by melten glass liquid through shrend, pulverize after, carry out rolling ball milling 48h by ball, material, alcohol quality than for 3:1:2.After ball milling terminates, glass paste is dried at 75 DEG C in convulsion baking oven after 400 mesh filter-cloth filterings 3h.Powder beater slurry glass dust is used to break up after drying, the present invention can meet silver slurry burning till under 500 680 DEG C of different temperature conditionss, silver slurry is made to have versatility, with the base material of zinc oxide, there is good adhesive force, quality is high, uniformity is improved simultaneously, the optimization of silver slurry glass dust, stabilizes the quality of silver slurry.
Description
Technical field
The invention belongs to electric slurry and make field, be specifically related to a kind of zinc oxide varistor silver slurry glass dust
Manufacture method.
Background technology
Developing rapidly of electronics and information industry, has driven electric slurry and the development of silver slurry industry, silver slurry and electronics slurry thereof
Material series of products are to be most widely used a kind of precious metal material maximum with consumption in electronics industry, are to produce various electronics unit
Basic and the key function material of device products.
The composition of silver slurry includes: silver slurry, organic carrier, glass dust, remaining various oxide;In process of production, glass
Powder is except as the binding agent in electric slurry, the dispersant also starched in the operation of rolling as silver;Burning due to different manufacturers
Becoming temperature different, required glass powder just differs, and causes silver to starch versatility in process of production poor.
Summary of the invention
Goal of the invention: the problem existed for prior art, the present invention provides a kind of zinc oxide varistor silver slurry to use
The manufacture method of glass dust, the method preparation makes silver slurry have versatility, has good adhesive force, matter with the base material of zinc oxide
Amount height, uniformity is improved simultaneously, the optimization of silver slurry glass dust, stabilizes the quality of silver slurry.
Technical scheme: the manufacture method of a kind of zinc oxide varistor silver slurry glass dust, comprises the following steps:
Step 1, by glass dust according to following ingredients proportion formula, the Bi of 65-75%2O3, 12-16%B2O3, 3-5%
SiO2, 7-10%ZnO, 2-3%Al2O3, 1-3%Cr2O3;
Step 2, is weighed the oxide of refining glass dust, puts in crucible, refined by Muffle furnace after mix homogeneously,
Smelting temperature is 1000-1300 DEG C, is incubated 30min;
Step 3, melting terminate after by melten glass liquid through shrend, pulverize after, enter than for 3:1:2 by ball, material, alcohol quality
Row rolling ball milling 48h, ball milling obtains glass paste after terminating;
Step 4, dries 3h after 400 mesh filter-cloth filterings in convulsion baking oven by glass paste at 75 DEG C;
Step 5, breaks up glass dust after drying, rolling.
Specifically, the formula of described glass dust is the Bi of 70% according to following ingredients proportion2O3, 14%B2O3, 4%SiO2,
8%ZnO, 2%Al2O3, 2%Cr2O3。
Specifically, described crucible is alumina crucible.
Specifically, in described step 2, smelting temperature is 1150 DEG C.
Specifically, powder beater is used to be broken up by glass dust after described step 5 being dried.
Beneficial effect: compared with prior art, it is an advantage of the current invention that: after silver slurry glass dust improves, silver slurry glass dust
Good stability, has good adhesive force with the base material of zinc oxide, and quality is high, and uniformity is improved, silver slurry glass dust
Optimize, stabilize the quality of silver slurry.
Accompanying drawing explanation
Fig. 1 be optimize before and after heat before and after glass dust is comprehensive analyzes.
Detailed description of the invention
Below in conjunction with the accompanying drawings and detailed description of the invention, it is further elucidated with the present invention.
A kind of manufacture method of zinc oxide varistor silver slurry glass dust,
Glass dust formula:
Components Name | Component ratio (Wt%) |
Bi2O3 | 70 |
B2O3 | 14 |
SiO2 | 4 |
ZnO | 8 |
Al2O3 | 2 |
Cr2O3 | 2 |
By optimizing glass powder formula, the oxide of refining glass dust is weighed, after mix homogeneously, puts into aluminium oxide
In crucible, being refined by Muffle furnace, smelting temperature is 1150 DEG C, be incubated 30min, melting terminate after by melten glass liquid through water
After quenching, pulverizing, carry out rolling ball milling 48h by ball, material, alcohol quality than for 3:1:2, after ball milling terminates, by glass paste through 400 mesh
In convulsion baking oven, at 75 DEG C, dry 3h after filter-cloth filtering, after drying, use powder beater slurry glass dust to break up;By glass softening point
Be reduced to about 500 DEG C, reduce volatile component within 680 DEG C simultaneously, make glass in the range of 500 DEG C-680 DEG C stable with
Molten state exists;This glass that can use in the range of 500 DEG C-680 DEG C wide, can meet different firing temperatures, makes to own
Silver slurry has preferably Technological adaptability.
Embodiment 1
(1) refining glass dust 500g, makes process: weighed by the oxide of refining glass dust, put in crucible, stirring
Uniformly, quenched by the refining of Muffle furnace high temperature, shrend, powder, ball milling, filtration, after baking operation, analyze its hot overall characteristic.
(2) take again and test the same working condition, amplifying volume of production refining glass dust 2kg, the most further
Demonstrate the hot overall characteristic of glass dust.
Before and after many experiments, optimization, the comprehensive analysis of heat before and after glass dust is as it is shown in figure 1, as seen from the figure, before optimization
Glass dust is differential thermal curve extremely unstable in the range of 520 DEG C-600 DEG C, has many places heat release endothermic peak, and this shows the slurry prepared
Foaming, silver layer problems of crack may be caused by these heat absorption heat releases in this range, and decrease the attached of silver layer and substrate
Put forth effort;After optimization, glass is without mass loss in the range of 500 DEG C-680 DEG C, and the most non-volatile composition volatilizees, it was demonstrated that prepared by this formula
Glass formed stable glass network structure, not free single-component substance;This is understood by differential thermal analysis
Glass produces endothermic peak at 480 DEG C, it was demonstrated that when 480 DEG C, glass starts to soften, and in the range of 500 DEG C-680 DEG C, differential thermal curve is put down
Surely, there is no heat release and endothermic peak, it was demonstrated that glass does not has crystallize in the range of 500 DEG C-680 DEG C, exist with stable molten condition,
And the slurry prepared to burn till postadhesion power good;
The most visible:
(1), after silver slurry glass dust improves, the adhesive force of silver slurry is good.
(2) mode that silver slurry glass dust improves is through repeatedly groping, and inquires into, and optimizes, and after which being solidified, revises formula
Technique electronic silver paste glass dust, it is ensured that the uniformity of batch production.
(3), after improving, silver slurry glass dust good stability, the adhesive force of silver slurry is preferable.
(4) raising of product quality, improves demand.
Claims (5)
1. the manufacture method of a zinc oxide varistor silver slurry glass dust, it is characterised in that comprise the following steps:
Step 1, by glass dust according to following ingredients proportion formula, the Bi of 65-75%2O3, 12-16%B2O3, 3-5%SiO2, 7-
10%ZnO, 2-3%Al2O3, 1-3%Cr2O3;
Step 2, is weighed the oxide of refining glass dust, puts in crucible, refined by Muffle furnace after mix homogeneously, melting
Temperature is 1000-1300 DEG C, is incubated 30min;
Step 3, melting terminate after by melten glass liquid after shrend, powder are quenched, roll than for 3:1:2 by ball, material, alcohol quality
Dynamic ball milling 48h, ball milling obtains glass paste after terminating;
Step 4, dries 3h after 400 mesh filter-cloth filterings in convulsion baking oven by glass paste at 75 DEG C;
Step 5, breaks up glass dust after drying, rolling.
The manufacture method of a kind of zinc oxide varistor silver slurry glass dust the most according to claim 1, its feature exists
In: the formula of described glass dust is the Bi of 70% according to following ingredients proportion2O3, 14%B2O3, 4%SiO2, 8%ZnO, 2%
Al2O3, 2%Cr2O3。
The manufacture method of a kind of zinc oxide varistor silver slurry glass dust the most according to claim 1, its feature exists
In: described crucible is alumina crucible.
The manufacture method of a kind of zinc oxide varistor silver slurry glass dust the most according to claim 1, its feature exists
In: in described step 2, smelting temperature is 1150 DEG C.
The manufacture method of a kind of zinc oxide varistor silver slurry glass dust the most according to claim 1, its feature exists
In: use powder beater to be broken up by glass dust after described step 5 is dried.