CN106274389A - A kind of multi-functional front windshield - Google Patents

A kind of multi-functional front windshield Download PDF

Info

Publication number
CN106274389A
CN106274389A CN201610659641.7A CN201610659641A CN106274389A CN 106274389 A CN106274389 A CN 106274389A CN 201610659641 A CN201610659641 A CN 201610659641A CN 106274389 A CN106274389 A CN 106274389A
Authority
CN
China
Prior art keywords
front windshield
adhesive linkage
reflector layer
layer
bonded
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610659641.7A
Other languages
Chinese (zh)
Inventor
李国祥
常青
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU YICHENG GLASS CO LTD
Original Assignee
BENGBU YICHENG GLASS CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU YICHENG GLASS CO LTD filed Critical BENGBU YICHENG GLASS CO LTD
Priority to CN201610659641.7A priority Critical patent/CN106274389A/en
Publication of CN106274389A publication Critical patent/CN106274389A/en
Pending legal-status Critical Current

Abstract

A kind of multi-functional front windshield, this front windshield is made up of glass basis, adhesive linkage, reflector layer, polarizing layer；Described adhesive linkage is bonded in described glass basis towards one side in car body, and described reflector layer is bonded in described glass basis towards one side outside car body, and described polarizing layer is bonded on described reflector layer.By by front windshield by glass basis, adhesive linkage, reflector layer, polarizing layer forms so that this windshield has the extraneous sunlight of reflection, absorbs ultraviolet component, though summer be in sunlight directly shine body temperature of getting off also will not be too high.Can be bonded on adhesive linkage when glass basis fragmentation, ambient temperature is too low will not produce frost or icing, is simultaneously adapted to driving at night.

Description

A kind of multi-functional front windshield
Technical field
The present invention relates to technical field of glass materials, be specifically related to a kind of multi-functional front windshield.
Background technology
The development of Modern Car external form is closely bound up with the development of glass technology.Before more than 40 years, car front windshield glass Glass has used single-piece to bend windshield, and has gradually abandoned the windshield of plane.The car windshield of today The general large curved surface type all doing an integral width formula, has certain radian up and down.No matter this bend glass is from processing Process, still from the point of view of the cooperation of assembly, is all that a kind of technology requires the highest product because it relate to vehicle, intensity, The problems such as heat insulation, assembling.In the market ordinary windscreen except meet basic Radix Saposhnikoviae, keep off the rain, printing opacity and peace Outside congruence requires, function is the most single, can not well reflect extraneous sunlight thus keep when such as summer, outdoor temperature was higher , easily there is that outer surface freezes or frost causes and cannot normally use winter in vehicle interior temperature.
Summary of the invention
The present invention solves the problems referred to above, it is provided that one have reflective, ultraviolet can be absorbed, stable chemical performance is many Function front windshield.
The technical problem to be solved uses following technical scheme to realize:
A kind of multi-functional front windshield, described front windshield is by glass basis, adhesive linkage, reflector layer, polarizing layer group Become；Described adhesive linkage is bonded in described glass basis towards one side in car body, and described reflector layer is bonded in described glass basis court One side outside car body, described polarizing layer is bonded on described reflector layer.
Described adhesive linkage, reflector layer, polarizing layer is clear layer.
Described glass basis is made up of the raw material of following weight portion:
Cullet slag 45-60 part, silicon dioxide 30-45 part, sodium carbonate 5-8 part, iron sesquioxide 1-3 part, boron oxide 0.5-2.5 part, calcium silicates 4-7 part, potassium carbonate 10-12 part, aluminium oxide 2-5 part, silver chloride 0.2-0.8 part, manganese dioxide 1.3- 1.5 parts, calcium fluoride 0.3-0.7 part, phosphorus pentoxide 0.5-0.8 part.
Described adhesive linkage is made up of the raw material of following weight portion:
Expanded polystyrene (EPS) 20-30 part, polyphthalamide 10-15 part, polyphenylene sulphone resin 15-20 part, polycyclic Oxidative ethane 10-20 part, polyarylate 12-18 part.
Described reflector layer is made up of the raw material of following weight portion:
Yttrium oxide 5-8g, magnesium oxide 2-4g, titanium dioxide 7-10g, silicon dioxide 2-3g, zirconium oxide 3-6g, reflective Powder 4-9g, sodium silicate 2-5g, potassium oxide 2-4g, pearl essence 3-7g, potassium carbonate 5-7g, aluminium silicate 4-5g.
Described polarizing layer is made by after the dyed stretching of polyvinyl alcohol film.
The invention have the benefit that
(1), by front windshield is made up of glass basis, adhesive linkage, reflector layer, polarizing layer so that this glass that keeps out the wind Glass has the extraneous sunlight of reflection, absorbs ultraviolet component, though summer be in sunlight directly shine body temperature of getting off also will not be too high.
(2), have an accident cause front windshield to crush time, glass fragment can be bonded on adhesive linkage, will not produce Disorderly fly disorderly to spatter thus hurt sb.'s feelings and cause second accident.
(3), when outside air temperature too low especially winter or north cold area, at windshield towards outer surface one side Frost or icing will not be produced and cause sight line unintelligible.
(4) even if, driving at night opposite dazzle light is radiated on this front windshield and also do not interferes with normal driving.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below knot Close embodiment, the present invention is expanded on further.
Embodiment 1
A kind of multi-functional front windshield, described front windshield is by glass basis, adhesive linkage, reflector layer, polarizing layer group Become；Described adhesive linkage is bonded in described glass basis towards one side in car body, and described reflector layer is bonded in described glass basis court One side outside car body, described polarizing layer is bonded on described reflector layer.
Described adhesive linkage, reflector layer, polarizing layer is clear layer.
Described glass basis is made up of the raw material of following weight portion:
Cullet slag 45 parts, silicon dioxide 30 parts, sodium carbonate 5 parts, iron sesquioxide 1 part, boron oxide 0.5 part, calcium silicates 4 Part, potassium carbonate 10 parts, aluminium oxide 2 parts, silver chloride 0.2 part, manganese dioxide 1.3 parts, 0.3 part of calcium fluoride, phosphorus pentoxide 0.5 Part.
Described adhesive linkage is made up of the raw material of following weight portion:
Expanded polystyrene (EPS) 20 parts, polyphthalamide 10 parts, polyphenylene sulphone resin 15 parts, poly(ethylene oxide) 10 Part, polyarylate 12 parts.
Described reflector layer is made up of the raw material of following weight portion:
Yttrium oxide 5g, magnesium oxide 2g, titanium dioxide 7g, silicon dioxide 2g, zirconium oxide 3g, reflective powder 4g, sodium silicate 2g, potassium oxide 2g, pearl essence 3g, potassium carbonate 5g, aluminium silicate 4g.
Described polarizing layer is made by after the dyed stretching of polyvinyl alcohol film.
Embodiment 2
A kind of multi-functional front windshield, described front windshield is by glass basis, adhesive linkage, reflector layer, polarizing layer group Become；Described adhesive linkage is bonded in described glass basis towards one side in car body, and described reflector layer is bonded in described glass basis court One side outside car body, described polarizing layer is bonded on described reflector layer.
Described adhesive linkage, reflector layer, polarizing layer is clear layer.
Described glass basis is made up of the raw material of following weight portion:
Cullet slag 55 parts, silicon dioxide 40 parts, sodium carbonate 7 parts, iron sesquioxide 2 parts, boron oxide 2 parts, calcium silicates 6 Part, potassium carbonate 11 parts, aluminium oxide 4 parts, silver chloride 0.6 part, manganese dioxide 1.4 parts, 0.5 part of calcium fluoride, phosphorus pentoxide 0.7 Part.
Described adhesive linkage is made up of the raw material of following weight portion:
Expanded polystyrene (EPS) 25 parts, polyphthalamide 13 parts, polyphenylene sulphone resin 18 parts, poly(ethylene oxide) 15 Part, polyarylate 16 parts.
Described reflector layer is made up of the raw material of following weight portion:
Yttrium oxide 7g, magnesium oxide 3g, titanium dioxide 8g, silicon dioxide 2g, zirconium oxide 5g, reflective powder 7g, sodium silicate 4g, potassium oxide 3g, pearl essence 5g, potassium carbonate 6g, aluminium silicate 4g.
Described polarizing layer is made by after the dyed stretching of polyvinyl alcohol film.
Embodiment 3
A kind of multi-functional front windshield, described front windshield is by glass basis, adhesive linkage, reflector layer, polarizing layer group Become；Described adhesive linkage is bonded in described glass basis towards one side in car body, and described reflector layer is bonded in described glass basis court One side outside car body, described polarizing layer is bonded on described reflector layer.
Described adhesive linkage, reflector layer, polarizing layer is clear layer.
Described glass basis is made up of the raw material of following weight portion:
Cullet slag 60 parts, silicon dioxide 45 parts, sodium carbonate 8 parts, iron sesquioxide 3 parts, boron oxide 2.5 parts, calcium silicates 7 Part, potassium carbonate 12 parts, aluminium oxide 5 parts, silver chloride 0.8 part, manganese dioxide 1.5 parts, 0.7 part of calcium fluoride, phosphorus pentoxide 0.8 Part.
Described adhesive linkage is made up of the raw material of following weight portion:
Expanded polystyrene (EPS) 30 parts, polyphthalamide 15 parts, polyphenylene sulphone resin 20 parts, poly(ethylene oxide) 20 Part, polyarylate 18 parts.
Described reflector layer is made up of the raw material of following weight portion:
Yttrium oxide 8g, magnesium oxide 4g, titanium dioxide 10g, silicon dioxide 3g, zirconium oxide 6g, reflective powder 9g, sodium silicate 5g, potassium oxide 4g, pearl essence 7g, potassium carbonate 7g, aluminium silicate 5g.
Described polarizing layer is made by after the dyed stretching of polyvinyl alcohol film.
The ultimate principle of the present invention, principal character and advantages of the present invention have more than been shown and described.The technology of the industry The personnel only present invention it should be appreciated that the present invention is not restricted to the described embodiments, described in above-described embodiment and description Preference, be not intended to limit the present invention, without departing from the spirit and scope of the present invention, the present invention also has various Changes and improvements, these changes and improvements both fall within scope of the claimed invention.Claimed scope is by institute Attached claims and equivalent thereof define.

Claims (6)

1. a multi-functional front windshield, it is characterised in that: this front windshield by glass basis, adhesive linkage, reflector layer, partially Photosphere forms；Described adhesive linkage is bonded in described glass basis towards one side in car body, and described reflector layer is bonded in described glass Matrix is towards one side outside car body, and described polarizing layer is bonded on described reflector layer.
A kind of multi-functional front windshield the most as claimed in claim 1, it is characterised in that: described adhesive linkage, reflector layer, polarisation Layer is clear layer.
A kind of multi-functional front windshield the most as claimed in claim 1, it is characterised in that described glass basis is by following weight The raw material composition of part:
Cullet slag 45-60 part, silicon dioxide 30-45 part, sodium carbonate 5-8 part, iron sesquioxide 1-3 part, boron oxide 0.5-2.5 Part, calcium silicates 4-7 part, potassium carbonate 10-12 part, aluminium oxide 2-5 part, silver chloride 0.2-0.8 part, manganese dioxide 1.3-1.5 part, fluorine Change calcium 0.3-0.7 part, phosphorus pentoxide 0.5-0.8 part.
A kind of multi-functional front windshield the most as claimed in claim 1, it is characterised in that described adhesive linkage is by following weight portion Raw material composition:
Expanded polystyrene (EPS) 20-30 part, polyphthalamide 10-15 part, polyphenylene sulphone resin 15-20 part, polycyclic oxygen second Alkane 10-20 part, polyarylate 12-18 part.
A kind of multi-functional front windshield the most as claimed in claim 1, it is characterised in that described reflector layer is by following weight portion Raw material composition:
Yttrium oxide 5-8g, magnesium oxide 2-4g, titanium dioxide 7-10g, silicon dioxide 2-3g, zirconium oxide 3-6g, reflective powder 4- 9g, sodium silicate 2-5g, potassium oxide 2-4g, pearl essence 3-7g, potassium carbonate 5-7g, aluminium silicate 4-5g.
A kind of multi-functional front windshield the most as claimed in claim 1, it is characterised in that described polarizing layer is thin by polyvinyl alcohol Make after the dyed stretching of film.
CN201610659641.7A 2016-08-11 2016-08-11 A kind of multi-functional front windshield Pending CN106274389A (en)