CN106273918A - A kind of light protection laminated glass - Google Patents

A kind of light protection laminated glass Download PDF

Info

Publication number
CN106273918A
CN106273918A CN201610669928.8A CN201610669928A CN106273918A CN 106273918 A CN106273918 A CN 106273918A CN 201610669928 A CN201610669928 A CN 201610669928A CN 106273918 A CN106273918 A CN 106273918A
Authority
CN
China
Prior art keywords
accounts
parts
thin film
glass
stiffened
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610669928.8A
Other languages
Chinese (zh)
Inventor
王恒春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI HENGCHUN GLASS Co Ltd
Original Assignee
ANHUI HENGCHUN GLASS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI HENGCHUN GLASS Co Ltd filed Critical ANHUI HENGCHUN GLASS Co Ltd
Priority to CN201610669928.8A priority Critical patent/CN106273918A/en
Publication of CN106273918A publication Critical patent/CN106273918A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of light protection laminated glass, the mass fraction of its component and each component is that sodium silicate accounts for 34 52 parts, calcium silicates accounts for 28 35 parts, silicon dioxide accounts for 17 26 parts, potassium oxide accounts for 23 parts, and aluminium sesquioxide accounts for 11 24 parts, and magnesium oxide accounts for 38 parts, calcium oxide accounts for 34 parts, bichromate account for 58 parts, ferrum oxide account for 56 parts；Being pasted with a stiffened PC thin film, an optical grade PC thin film on the two sides of PVB film respectively, stiffened PC thin film all attaches with PVB film with optical grade PC thin film under hot mastication state, and by roll squeezer pressing, bubble removing；Nanometer viscose glue is all used to adhere between glass plate and stiffened PC thin film, optical grade PC thin film.Present invention improves the dispensing of existing simple glass, add glass bond strength, and the laminated glass of the present invention has anti-ultraviolet, the anti-infrared and performance of absorption major part visible ray.

Description

A kind of light protection laminated glass
Technical field
The present invention relates to field of glass production technology, a kind of light protection laminated glass.
Background technology
Along with extensively application and the raising of glass industries technology of glass, various non-browning glasses are also extensively made by people With, most common of which cover plate is exactly the glass that anti-light irradiates, and it is single that existing light cover plate often protects direction One, and the physical property of glass itself is not improved, in order to increase resistance to cold and summer-heat and the shock resistance of light cover plate Performance, people often increase tempering operation, or patch rupture pressure disc.This mode adds glass production cycle and cost, and glass is prevented Protect the single use category that also limit glass of performance.
Summary of the invention
In order to solve above-mentioned technical problem, the present invention provides a kind of light protection laminated glass.
The technical problem to be solved realizes by the following technical solutions:
A kind of light protection laminated glass, including two sides glass plate and the PVB film between the glass plate of two sides, described glass The component of glass plate and the mass fraction of each component are that sodium silicate accounts for 34-52 part, and calcium silicates accounts for 28-35 part, and silicon dioxide accounts for 17-26 Part, potassium oxide accounts for 2-3 part, and aluminium sesquioxide accounts for 11-24 part, and magnesium oxide accounts for 3-8 part, and calcium oxide accounts for 3-4 part, and bichromate accounts for 5- 8 parts, ferrum oxide account for 5-6 part.
A stiffened PC thin film, an optical grade PC thin film it is pasted with respectively on the two sides of described PVB film.
Described stiffened PC thin film all attaches with PVB film with optical grade PC thin film under hot mastication state, and by roll squeezer Pressing, to remove bubble bubble removing in film；Nanometer viscose glue is all used to enter between glass plate and stiffened PC thin film, optical grade PC thin film Row adheres to.
The invention has the beneficial effects as follows: invention not only improves the dispensing of existing simple glass, optimize glass network Internal structure, adds glass bond strength, adds resistance to cold and summer-heat and the shock resistance of simple glass, and basic at this The bichromate of upper employing reasonable mixture ratio and magnesium oxide, utilize chromium element so that glass has anti-ultraviolet, anti-infrared and suction Receive the performance of major part visible ray, improve the scope of application of glass.Cause sight line not to improve laminated glass refraction light Good situation, with the addition of optical grade PC thin film, is used for improving light penetration.Owing to laminated glass is often used for needing strength anti- In the environment protected, such as Herba Plantaginis windshield and house door and window, in laminated glass, therefore add stiffened PC thin film, improve interlayer The hardness of glass and protection intensity.
Detailed description of the invention
In order to make technological means that the present invention realizes and creation characteristic be easy to understand, below the present invention is explained further State.
Embodiment one
A kind of light protection laminated glass, including two sides glass plate and the PVB film between the glass plate of two sides, described glass The component of glass plate and the mass fraction of each component are that sodium silicate accounts for 34 parts, and calcium silicates accounts for 28 parts, and silicon dioxide accounts for 17 parts, potassium oxide Accounting for 2 parts, aluminium sesquioxide accounts for 11 parts, and magnesium oxide accounts for 3 parts, and calcium oxide accounts for 3 parts, bichromate account for 5 parts, ferrum oxide account for 5 parts.
A stiffened PC thin film, an optical grade PC thin film it is pasted with respectively on the two sides of described PVB film.
Described stiffened PC thin film all attaches with PVB film with optical grade PC thin film under hot mastication state, and by roll squeezer Pressing, to remove bubble in film；Nanometer viscose glue is all used to glue between glass plate and stiffened PC thin film, optical grade PC thin film Attached.
Embodiment two
A kind of light protection laminated glass, including two sides glass plate and the PVB film between the glass plate of two sides, described glass The component of glass plate and the mass fraction of each component are that sodium silicate accounts for 52 parts, and calcium silicates accounts for 35 parts, and silicon dioxide accounts for 26 parts, potassium oxide Accounting for 3 parts, aluminium sesquioxide accounts for 24 parts, and magnesium oxide accounts for 8 parts, and calcium oxide accounts for 4 parts, bichromate account for 8 parts, ferrum oxide account for 6 parts.
Laminated glass structure is identical with embodiment one with processing mode.
Embodiment three
A kind of light protection laminated glass, including two sides glass plate and the PVB film between the glass plate of two sides, described glass The component of glass plate and the mass fraction of each component are that sodium silicate accounts for 44 parts, and calcium silicates accounts for 32 parts, and silicon dioxide accounts for 20 parts, potassium oxide Accounting for 2.5 parts, aluminium sesquioxide accounts for 17 parts, and magnesium oxide accounts for 5 parts, and calcium oxide accounts for 3.5 parts, bichromate account for 7 parts, ferrum oxide account for 5.5 Part.
Laminated glass structure is identical with embodiment one with processing mode.
The ultimate principle of the present invention, principal character and advantages of the present invention have more than been shown and described.The technology of the industry The personnel simply present invention it should be appreciated that the present invention is not restricted to the described embodiments, described in above-described embodiment and description Principle, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, these change and Improvement both falls within scope of the claimed invention.Claimed scope is by appending claims and equivalence thereof Thing defines.

Claims (2)

1. a light protection laminated glass, including two sides glass plate and the PVB film between the glass plate of two sides, its feature exists In: the component of described glass plate and the mass fraction of each component are that sodium silicate accounts for 34-52 part, and calcium silicates accounts for 28-35 part, titanium dioxide Silicon accounts for 17-26 part, and potassium oxide accounts for 2-3 part, and aluminium sesquioxide accounts for 11-24 part, and magnesium oxide accounts for 3-8 part, and calcium oxide accounts for 3-4 part, weight Chromate accounts for 5-8 part, ferrum oxide accounts for 5-6 part；
A stiffened PC thin film, an optical grade PC thin film it is pasted with respectively on the two sides of described PVB film.
A kind of light protection laminated glass the most according to claim 1, it is characterised in that: described stiffened PC thin film and optics Level PC thin film all attaches with PVB film under hot mastication state, and by roll squeezer pressing, bubble removing；Glass plate is thin with stiffened PC Nanometer viscose glue is all used to adhere between film, optical grade PC thin film.
CN201610669928.8A 2016-08-15 2016-08-15 A kind of light protection laminated glass Pending CN106273918A (en)