CN106273907A - A kind of compound glass bottle cap and preparation method thereof - Google Patents
A kind of compound glass bottle cap and preparation method thereof Download PDFInfo
- Publication number
- CN106273907A CN106273907A CN201610638972.2A CN201610638972A CN106273907A CN 106273907 A CN106273907 A CN 106273907A CN 201610638972 A CN201610638972 A CN 201610638972A CN 106273907 A CN106273907 A CN 106273907A
- Authority
- CN
- China
- Prior art keywords
- glass
- layer
- bottle cap
- compound
- make
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of compound glass bottle cap, glass-ceramic layer including inner side, be provided with a floor height Pyrex layer outside described glass-ceramic layer, one layer of simple glass layer be set outside described high-boron-silicon glass layer, described simple glass layer is provided with a layer polypropylene plastic layer as.The present invention, by arranging the glassy layer of multilamellar, adds the service life of glass cap, and internal glass-ceramic layer adds plurality of raw materials, anti-electromagnetic radiation, and outer layer arranges the polypropylene plastics bed of material, anti-fight, strengthens radiation proof function, safety and stability.
Description
Technical field
The present invention relates to closure field, specifically a kind of compound glass bottle cap and preparation method thereof.
Background technology
What the most most of glass caps were typically all employing is all the devitrified glass of simple glass or thickening,
Or high-boron-silicon glass is made, external make plus basic plastic sheeting, have basic high temperature resistant, intensity high；
The devitrified glass thickeied and the bottle cap made of high-boron-silicon glass use for a long time and inside and outside are heated uneven, easily cause quick-fried
Split, cause danger.
Summary of the invention
It is an object of the present invention to provide a kind of multi-level, prevent explosion, be hardly damaged, use safe compound glass bottle cap.
In order to solve above-mentioned technical problem, the technical solution used in the present invention is:
A kind of compound glass bottle cap, including the glass-ceramic layer of inner side, is provided with a floor height boron outside described glass-ceramic layer
Silica glass layer, arranges one layer of simple glass layer, described simple glass layer is provided with a strata outside described high-boron-silicon glass layer
Acrylic plastic layer.
Further, described devitrified glass layer thickness is 1-2mm.
Further, described Pyrex layer thickness is 1-2mm.
Preferably, described simple glass layer is 1.5mm.
As preferably, the described polypropylene plastics bed of material is 1mm.
The manufacture method of described compound glass bottle cap, comprises the following steps:
1) making of devitrified glass
A, choose simple glass heating and melting, make solution, according to weight every 100kg solution adds 1kg aluminium oxide,
0.5kg cerium oxide, 0.5kg Barium monoxide, 1kg glass fining agent, 0.3kg Fluororystal mica, 0.5kg Lithium metasilicate, mixing, make mixing
Liquid；
B: choose one piece of clean monolithic metal, mixed liquor is poured on iron plate, cool down rapidly, make sparkling and crystal-clear glass；
C: smashed by the glass made in step b, puts in grinding tool, glass fragment thickness 1.5-2.5mm, puts into 1200 and takes the photograph
The heating furnace of family name's degree heats 20 minutes, takes out in glass fragment is placed into mould and Temperature fall, make glass-ceramic layer；
3) making of first finished product
A: the high-boron-silicon glass will purchased on market, simple glass, then the glass blocks cutting into formed objects is pulverized, and adds
Thermal softening makes high-boron-silicon glass layer；
B: by the glass cover that makes according to, the order polyethylene of glass-ceramic layer-high-boron-silicon glass layer-simple glass layer
Glue bond together, and puts into the heating heating indoor 12 hours that temperature is 400 degrees Celsius, then takes out, and obtains just finished product；
C: at the polypropylene plastics liquid that first finished product simple glass layer of surface spraying 1mm is thick, dry and make compound glass
Lid；
3) making of finished product
A: by the compound glass made according to actual size requirement, make compound glass bottle cap.
The invention has the beneficial effects as follows:
The present invention, by arranging the glassy layer of multilamellar, adds the service life of glass cap, internal glass-ceramic layer
Adding plurality of raw materials, anti-electromagnetic radiation, outer layer arranges the polypropylene plastics bed of material, anti-fight, strengthens radiation proof function, safety and stability.
Detailed description of the invention
In order to the technological means of the present invention, creation characteristic, reach purpose and be easy to understand with effect, further below
Illustrate the present invention.
The open a kind of compound glass bottle cap of the present invention, including the glass-ceramic layer of inner side, sets outside described glass-ceramic layer
There is a floor height Pyrex layer, one layer of simple glass layer is set outside described high-boron-silicon glass layer, described simple glass layer sets
It is equipped with a layer polypropylene plastic layer.
Described devitrified glass layer thickness is 1-2mm.
Described Pyrex layer thickness is 1-2mm.
Described simple glass layer is 1.5mm.
The described polypropylene plastics bed of material is 1mm.
The manufacture method of described compound glass bottle cap, comprises the following steps:
1) making of devitrified glass
A, choose simple glass heating and melting, make solution, according to weight every 100kg solution adds 1kg aluminium oxide,
0.5kg cerium oxide, 0.5kg Barium monoxide, 1kg glass fining agent, 0.3kg Fluororystal mica, 0.5kg Lithium metasilicate, mixing, make mixing
Liquid；
B: choose one piece of clean monolithic metal, mixed liquor is poured on iron plate, cool down rapidly, make sparkling and crystal-clear glass；
C: smashed by the glass made in step b, puts in grinding tool, glass fragment thickness 1.5-2.5mm, puts into 1200 and takes the photograph
The heating furnace of family name's degree heats 20 minutes, takes out in glass fragment is placed into mould and Temperature fall, make glass-ceramic layer；
4) making of first finished product
A: the high-boron-silicon glass will purchased on market, simple glass, then the glass blocks cutting into formed objects is pulverized, and adds
Thermal softening makes high-boron-silicon glass layer；
B: by the glass cover that makes according to, the order polyethylene of glass-ceramic layer-high-boron-silicon glass layer-simple glass layer
Glue bond together, and puts into the heating heating indoor 12 hours that temperature is 400 degrees Celsius, then takes out, and obtains just finished product；
C: at the polypropylene plastics liquid that first finished product simple glass layer of surface spraying 1mm is thick, dry and make compound glass
Lid；
3) making of finished product
A: by the compound glass made according to actual size requirement, make compound glass bottle cap.
Invention described above embodiment, is not intended that limiting the scope of the present invention.Any in the present invention
Spirit and principle within amendment, equivalent and the improvement etc. made, should be included in the claim protection model of the present invention
Within enclosing.
Claims (6)
1. a compound glass bottle cap, it is characterised in that include the glass-ceramic layer of inner side, be provided with outside described glass-ceramic layer
One floor height Pyrex layer, arranges one layer of simple glass layer outside described high-boron-silicon glass layer, described simple glass layer is arranged
There is a layer polypropylene plastic layer.
Compound glass bottle cap the most according to claim 1, it is characterised in that described devitrified glass layer thickness is 1-2mm.
Compound glass bottle cap the most according to claim 1, it is characterised in that described Pyrex layer thickness is 1-2mm.
Compound glass bottle cap the most according to claim 1, it is characterised in that described simple glass layer is 1.5mm.
Compound glass bottle cap the most according to claim 1, it is characterised in that the described polypropylene plastics bed of material is 1mm.
6. the manufacture method of compound glass bottle cap as claimed in claim 1, it is characterised in that comprise the following steps:
1) making of devitrified glass
A, choose simple glass heating and melting, make solution, according to weight every 100kg solution adds 1kg aluminium oxide, 0.5kg
Cerium oxide, 0.5kg Barium monoxide, 1kg glass fining agent, 0.3kg Fluororystal mica, 0.5kg Lithium metasilicate, mixing, make mixed liquor；
B: choose one piece of clean monolithic metal, mixed liquor is poured on iron plate, cool down rapidly, make sparkling and crystal-clear glass；
C: smashed by the glass made in step b, puts in grinding tool, glass fragment thickness 1.5-2.5mm, puts into 1200 degrees Celsius
Heating furnace in heat 20 minutes, take out glass fragment and be placed in mould and Temperature fall, make glass-ceramic layer；
2) making of first finished product
A: the high-boron-silicon glass will purchased on market, simple glass, then the glass blocks cutting into formed objects is pulverized, and heats soft
Change and make high-boron-silicon glass layer；
B: by the glass cover that makes according to, the order polyethylene of glass-ceramic layer-high-boron-silicon glass layer-simple glass layer is gluing
Unify, and put into the heating heating indoor 12 hours that temperature is 400 degrees Celsius, then take out, obtain just finished product；
C: at the polypropylene plastics liquid that first finished product simple glass layer of surface spraying 1mm is thick, dry and make compound glass lid；
3) making of finished product
A: by the compound glass made according to actual size requirement, make compound glass bottle cap.